Oriented face-centered cubic to hexagonal close-packed martensitic transition, grain morphology, and mechanical properties of Co-Cr alloy fabricated by selective laser melting

Electrochemical polishing, characterisation and in vitro evaluation of additively manufactured CoCr stents with personalised designs

Additive manufacturing (AM) technology has paved the way for manufacturing personalised stents. However, there is a notable gap in comprehensive microstructure analyses and in vitro evaluations of the AM CoCr stents using advanced methodologies. To address this gap, this study focuses on investigating the microstructure and in vitro performance of personalised CoCr stents manufactured through micro-laser powder bed fusion (μ-LPBF). The evaluation process begins with the measurements of dimensions and surface roughness, followed by in-depth microstructural analyses. To improve surface roughness and reduce excessive strut size, the μ-LPBF stents undergo electrochemical polishing. Importantly, in vitro stent deployments are carried out in artificial arteries manufactured based on actual patients' data. Compared to the commercial MULTI-LINK VISION CoCr stent, the μ-LPBF personalised stents have rough surface finish (average roughness: 1.55 μm for μ-LPBF vs. 1.09 μm for commercial) and compromised grain microstructures (elongated for μ-LPBF vs. equiaxed for commercial). However, the personalised stents demonstrate better performances in in vitro tests. Notably, compared to the commercial stent in the two studied cases, they deliver larger lumen gains (up to 11.24 %) and reduced recoils (up to 4 times). This study validates the merit of the lesion-specific designs and the feasibility of using AM technology for stent fabrication.

Additively Manufactured Commercial Co-Cr Dental Alloys: Comparison of Microstructure and Mechanical Properties

Laser-powder bed fusion (LPBF) is one of the preferred techniques for producing Co-Cr metal structures for dental prosthodontic appliances. However, there is generally insufficient information about material properties related to the production process and parameters. This study was conducted on samples produced from three different commercially available Co-Cr dental alloys produced on three different LPBF machines. Identically prepared samples were used for tensile, three-point bending, and toughness tests. Light microscopy (LM), scanning electron microscopy (SEM), and electron backscatter diffraction (EBSD) analyses of microstructure were performed after testing. Differences were observed in microstructures, which reflected statistically significant differences in mechanical properties (one-way analysis of variance (ANOVA) and Scheffé post hoc test (α = 0.05)). The material produced on the 3D Systems DMP Dental 100 had 24 times greater elongation ε than the material produced on the Sysma MySint 100 device and the EOS M100 machine. On the other hand, the material produced on the EOS M100 had significantly higher hardness (HV0.2) than the other two produced materials. However, the microstructure of the Sysma specimens with its morphology deviates considerably from the studied group. LPBF-prepared Co-Cr dental alloys demonstrated significant differences in their microstructures and, consequently, mechanical properties.