Effect of maximum support attachment angle on intaglio surface trueness of anatomic contour monolithic prostheses manufactured by digital light processing and zirconia suspension

Influence of glazing and aging on the marginal, axial, axio-occlusal, and occlusal fit of 3-unit monolithic zirconia restorations fabricated using additive and subtractive techniques

STATEMENT OF PROBLEM

Studies are sparse on how glazing and aging influence the fit of additively fabricated monolithic zirconia restorations.

PURPOSE

The purpose of this in vitro study was to assess the effect of glazing and aging on the fit of 3-unit monolithic zirconia restorations fabricated using different techniques.

MATERIAL AND METHODS

A total of 32 monolithic zirconia restorations were fabricated for a typodont model by using 4 distinct techniques (subtractive fabrication [SF], stereolithography [SLA], digital light processing [DLP], and lithography-based ceramic manufacturing [LCM]). The silicone replica approach was adopted to measure the discrepancy values for premolar and molar abutments after sintering, glazing, and 1 year of aging. The silicone replicas were sliced into mesiodistal and buccopalatal cross-sections, and digital micrographs of the cross-sections were made with a ×80 stereomicroscope. An inherent measuring program was run to record the discrepancy values (µm). Repeated-measures 2-way ANOVAs with the Bonferroni post hoc test were used to statistically analyze the acquired data. (α=.05).

RESULTS

From the repeated measures 2-way ANOVAs, both the glazing×fabrication technique and the aging×fabrication technique interactions were not statistically significant (P>.05). Glazing significantly influenced premolar abutment marginal (P=.022) and occlusal (P=.007) discrepancy values, as well as molar abutment marginal discrepancy values (P=.047). Aging had a statistically significant effect on premolar abutment marginal (P=.008) and occlusal (P=.011) discrepancy values, as well as molar abutment occlusal discrepancy values (P=.039). In both the glazing and aging data, for all areas of interest, statistically significant differences were detected among the fabrication techniques (P<.05). The LCM group had the lowest discrepancy values, followed by the SLA, SF, and DLP groups.

CONCLUSIONS

The LCM and SLA groups outperformed the other groups in terms of fit accuracy. The glazing and aging procedures altered the discrepancy values. The marginal discrepancy values of all groups were below the threshold of clinical acceptability (<120 µm).

Effect of exposure energy dose on lateral resolution and flexural strength of three-dimensionally printed dental zirconia

PURPOSE

This study aims to evaluate the effects of exposure energy on the lateral resolution and mechanical strength of dental zirconia manufactured using digital light processing (DLP).

MATERIALS AND METHODS

A zirconia suspension and a custom top-down DLP printer were used for in-office manufacturing. The viscosity of the suspension and uniformity of the exposed light intensity were controlled. Based on the exposure energy dose delivered to each layer, the specimens were classified into three groups: low-energy (LE), medium-energy (ME), and high-energy (HE). For each energy group, a simplified molar cube was used to measure the widths of the outline (Xo and Yo) and isthmus (Xi and Yi), and a bar-shaped specimen of the sintered body was tested. A Kruskal-Wallis test for the lateral resolution and one-way analysis of variance for the mechanical strength were performed (α = .05).

RESULTS

The zirconia green bodies of the ME group showed better lateral resolution than those of the LE and HE groups (both P < .001). Regarding the flexural strength of the sintered bodies, the ME group had the highest mean value, whereas the LE group had the lowest mean value (both P < .05). The ME group exhibited fewer agglomerates than the LE group, with no distinctive interlayer pores or surface defects.

CONCLUSION

Based on these findings, the lateral resolution of the green body and flexural strength of the sintered body of dental zirconia could be affected by the exposure energy dose during DLP. The exposure energy should be optimized when fabricating DLP-based dental zirconia.