Actuation Characteristics and Mechanism of Electroactive Plasticized Thermoplastic Polyurethane

Polyurethanes Modified by Ionic Liquids and Their Applications

Polyurethane (PU) refers to the polymer containing carbamate groups in its molecular structure, generally obtained by the reaction of isocyanate and alcohol. Because of its flexible formulation, diverse product forms, and excellent performance, it has been widely used in mechanical engineering, electronic equipment, biomedical applications, etc. Through physical or chemical methods, ionic groups are introduced into PU, which gives PU electrical conductivity, flame-retardant, and antistatic properties, thus expanding the application fields of PU, especially in flexible devices such as sensors, actuators, and functional membranes for batteries and gas absorption. In this review, we firstly introduced the characteristics of PU in chemical and microphase structures and their related physical and chemical performance. To improve the performance of PU, ionic liquids (ILs) were applied in the processing or synthesis of PU, resulting in a new type of PU called ionic PU. In the following part of this review, we mainly summarized the fabrication methods of IL-modified PUs via physical blending and the chemical copolymerization method. Then, we summarized the research progress of the applications for IL-modified PUs in different fields, including sensors, actuators, transistors, antistatic films, etc. Finally, we discussed the future development trends and challenges faced by IL-modified PUs.

Ion Transport in the EMITFSI/PVDF System at Different Temperatures: A Molecular Dynamics Simulation

We used all-atom molecular dynamics simulations to study the ion transport in the 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide/poly(vinylidene fluoride) (EMITFSI/PVDF) system with 40.05 wt % EMITFSI at different temperatures. The glass-transition temperature (T _g = 204 K) of this system shows a good agreement with the experimental value (200 K). With the increase of temperature, the peaks of the pair correlation function show an increasing trend. Interestingly, the coordination numbers of ion pairs and the degree of independent ion motion are mainly affected by the binding energy between ion pairs as the temperature increases. In addition, the ion transport properties with increasing temperature can be studied by the ion-pair relaxation times, ion-pair lifetimes, and diffusion coefficients. The simulation results illustrate that the ion transport is intensified. Especially, the cations can always diffuse faster than the anions. The power law shows that mobilities of anions and cations are seen to exhibit a "superionic" behavior. With the increase of temperature, transference numbers of anions decrease first and then increase and transference numbers of cations show the opposite changes; ionic conductivity increases gradually; and viscosity decreases gradually, indicating that the diffusion resistance of ions decreases. In general, after adding PVDF into the EMITFSI system, the glass-transition temperature and viscosity increase, the ionic conductivity and degree of independent ion motion decrease, and diffusion coefficients of cations decrease faster than those of the anions.

Oxidation-degree-dependent moisture-induced actuation of a graphene oxide film

Multilayered films prepared from graphene oxide (GO) subjected to a single oxidation process (1GO) can actuate in response to moisture, whereas those prepared from GO subjected to two oxidation processes (2GO) lose this ability. To elucidate the origin of this difference, the structures and properties of various multilayered films and their contents were analyzed. According to atomic force microscopy images, the lateral size of the GO monolayer in 2GO (2.0 ± 0.4 μm) was smaller than that in 1GO (3.2 ± 0.4 μm), although this size difference did not affect actuation. Scanning electron microscopy images of the cross sections of both films showed fine multilayered structures and X-ray diffraction measurements showed the moisture sensitive reversible change in the interlayer distances for both films. Both films adsorbed 30 wt% moisture in 60 s with different water contents at the bottom moist sides and top air sides of the films. Nanoindentation experiments showed hardness values (1GO: 156 ± 67 MPa; 2GO: 189 ± 97 MPa) and elastic modulus values (1GO: 4.7 ± 1.7 GPa; 2GO: 5.8 ± 3.2 GPa) typical of GO, with no substantial difference between the films. On the contrary, the 1GO film bent when subjected to a weight equal to its own weight, whereas the 2GO film did not. Such differences in the macroscopic hardness of GO films can affect their moisture-induced actuation ability.