Glass-Transition-Temperature-Independent Form II to I Phase Transition of Low-Molar-Mass Isotactic Polybutene-1

Effect of Annealing Process and Molecular Weight on the Polymorphic Transformation from Form II to Form I of Poly(1-butene)

Poly(1-butene) (PB-1) resin has excellent mechanical properties, outstanding creep resistance, environmental stress crack resistance and other excellent properties. However, PB-1 resin experiences a crystal transformation for a period, which seriously affects the production efficiency and directly restricts its large-scale commercial production and application. The factors affecting the crystal transformation of PB-1 are mainly divided into external and internal factors. External factors include crystallization temperature, thermal history, nucleating agent, pressure, solvent induction, etc., and internal factors include chain length, copolymerization composition, isotacticity, its distribution, etc. In this study, to avoid the interference of molecular weight distribution on crystallization behavior, five PB-1 samples with narrow molecular weight distribution (between 1.09 and 1.44) and different molecular weights (from 23 to 710 k) were chosen to research the influence of temperature and time in the step-by-step annealing process and molecular weight on the crystal transformation by differential scanning calorimetry (DSC). When the total annealing time was the same, the step-by-step annealing process can significantly accelerate the rate of transformation from crystal form II to I. PB-1 samples with different molecular weights have the same dependence on annealing temperature, and the optimal nucleation temperature (i.e., low annealing temperature, T_l) and growth temperature (i.e., high annealing temperature, T_h) were -10 °C and 40 °C, respectively. At these two temperatures, the crystal form I obtained by step-by-step annealing had the highest content; other lower or higher annealing temperatures would reduce the rate of crystal transformation. When the annealing temperature was the same, crystal form I first increased with annealing time t_l, then gradually reached a plateau, but the time to reach a plateau was different. The crystalline form I contents of the samples with lower molecular weight increased linearly with annealing time t_h. However, the crystalline form I contents of the samples with higher molecular weight increased rapidly with annealing time t_h at the beginning, and then transformation speed from form II to form I slowed down, which implied that controlling T_l/t_l and T_h/t_h can tune the different contents of form I and form II. At the same T_l/t_l or T_h/t_h, with increasing molecular weight, the transformation speed from form II to form I via the step-by-step annealing process firstly increased and then slowed down due to the competition of the number of linked molecules and molecular chain mobility during crystallization. This study definitely provides an effective method for accelerating the transformation of poly(1-butene) crystal form, which not only has important academic significance, but also has vital industrial application.

Investigation of the synergistic effect of melt-extension and nanofiller on the crystal-crystal phase transition from form II to I of isotactic polybutene-1

New questions and conjectures are raised on the crystal-crystal phase transition of isotactic polybutene-1 (iPB-1) containing nanofiller in the flow field. In this work, we investigate the phase transition from flow-induced oriented form II to I in iPB-1 blends with multi-walled carbon nanotubes (MWCNTs) with a homemade two-drum extensional rheometer combined with in situ wide-angle X-ray diffraction (WAXD) measurements. The MWCNTs show a limited promoting effect on the phase transition kinetics under quiescent conditions, while the phase transition kinetic is highly accelerated with the impose of melt-extension. When the loading extension strain is 0.5 or 2.0, the half time of phase transition (t_1/2) is shortened from tens of hours to a few hours, depending on the melt-extension strain and the MWCNTs content in iPB-1. When the extension strain increases to 3.5, t_1/2 decreases to about 30 min, which is independent of the MWCNTs content in all iPB-1 blends except in blends with MWCNTs content of 1%, where the phase transition rate in the middle and late stages is restrained. It's speculated that flow-induced molecular orientation or shish-kebab morphology affects the internal stress or stress transfer. The addition of a nanofiller enlarged the effect of melt-extension through strengthening the localized intensity of flow field. In general, the combination of nanofiller and melt-extension can obviously promote the phase transition kinetics.