Calcium Phosphate Bone Cements Incorporated with Black Phosphorus Nanosheets Enhanced Osteogenesis

Fenton-like Reaction Inspired "·OH Catalyzed" Osteogenic Process for the Treatment of Osteoporosis

Inspired by the Fenton-like reaction, this work combines copper peroxide (CP) nanoparticles with black phosphorus (BP) nanosheets to form a hydroxyl radical (·OH)-centered "catalytic" osteogenic system. CP-produced ·OH interacts with BP to rapidly produce a large amount of phosphate ions, thus accelerating self-mineralization and promoting bone formation. In turn, BP not only exerts anti-inflammatory effects, thereby providing a favorable microenvironment for bone formation, but also offsets the potential toxicity of CP induced by reactive oxygen species (ROS). Together with copper ions (Cu2+), phosphate ions are also released as a byproduct of this process, which can contribute to the comprehensive promotion of osteogenesis.

Incorporation of black phosphorus nanosheets into poly(propylene fumarate) biodegradable bone cement to enhance bioactivity and osteogenesis

BACKGROUND

Injectable bone cement is commonly used in clinical orthopaedics to fill bone defects, treat vertebral compression fractures, and fix joint prostheses during joint replacement surgery. Poly(propylene fumarate) (PPF) has been proposed as a biodegradable and injectable alternative to polymethylmethacrylate (PMMA) bone cement. Recently, there has been considerable interest in two-dimensional (2D) black phosphorus nanomaterials (BPNSs) in the biomedical field due to their excellent photothermal and osteogenic properties. In this study, we investigated the biological and physicochemical qualities of BPNSs mixed with PPF bone cement created through thermal cross-linking.

METHODS

PPF was prepared through a two-step process, and BPNSs were prepared via a liquid phase stripping method. BP/PPF was subsequently prepared through thermal cross-linking, and its characteristics were thoroughly analysed. The mechanical properties, cytocompatibility, osteogenic performance, degradation performance, photothermal performance, and in vivo toxicity of BP/PPF were evaluated.

RESULTS

BP/PPF exhibited low cytotoxicity levels and mechanical properties similar to that of bone, whereas the inclusion of BPNSs promoted preosteoblast adherence, proliferation, and differentiation on the surface of the bone cement. Furthermore, 200 BP/PPF demonstrated superior cytocompatibility and osteogenic effects, leading to the degradation of PPF bone cement and enabling it to possess photothermal properties. When exposed to an 808-nm laser, the temperature of the bone cement increased to 45-55 °C. Furthermore, haematoxylin and eosin-stained sections from the in vivo toxicity test did not display any anomalous tissue changes.

CONCLUSION

BP/PPF exhibited mechanical properties similar to that of bone: outstanding photothermal properties, cytocompatibility, and osteoinductivity. BP/PPF serves as an effective degradable bone cement and holds great potential in the field of bone regeneration.

Black Phosphorus Accelerates Bone Regeneration Based on Immunoregulation

A fundamental understanding of inflammation and tissue healing suggests that the precise regulation of the inflammatory phase, both in terms of location and timing, is crucial for bone regeneration. However, achieving the activation of early inflammation without causing chronic inflammation while facilitating quick inflammation regression to promote bone regeneration continues to pose challenges. This study reveals that black phosphorus (BP) accelerates bone regeneration by building an osteogenic immunological microenvironment. BP amplifies the acute pro-inflammatory response and promotes the secretion of anti-inflammatory factors to accelerate inflammation regression and tissue regeneration. Mechanistically, BP creates an osteoimmune-friendly microenvironment by stimulating macrophages to express interleukin 33 (IL-33), amplifying the inflammatory response at an early stage, and promoting the regression of inflammation. In addition, BP-mediated IL-33 expression directly promotes osteogenic differentiation of bone marrow mesenchymal stem cells (BMSCs), which further facilitates bone repair. To the knowledge, this is the first study to reveal the immunomodulatory potential of BP in bone regeneration through the regulation of both early-stage inflammatory responses and later-stage inflammation resolution, along with the associated molecular mechanisms. This discovery serves as a foundation for the clinical use of BP and is an efficient approach for managing the immune microenvironment during bone regeneration.

Neuro-bone tissue engineering: emerging mechanisms, potential strategies, and current challenges

The skeleton is a highly innervated organ in which nerve fibers interact with various skeletal cells. Peripheral nerve endings release neurogenic factors and sense skeletal signals, which mediate bone metabolism and skeletal pain. In recent years, bone tissue engineering has increasingly focused on the effects of the nervous system on bone regeneration. Simultaneous regeneration of bone and nerves through the use of materials or by the enhancement of endogenous neurogenic repair signals has been proven to promote functional bone regeneration. Additionally, emerging information on the mechanisms of skeletal interoception and the central nervous system regulation of bone homeostasis provide an opportunity for advancing biomaterials. However, comprehensive reviews of this topic are lacking. Therefore, this review provides an overview of the relationship between nerves and bone regeneration, focusing on tissue engineering applications. We discuss novel regulatory mechanisms and explore innovative approaches based on nerve-bone interactions for bone regeneration. Finally, the challenges and future prospects of this field are briefly discussed.

Novel bone cement based on calcium phosphate composited CNT curcumin with improved strength and antitumor properties

In this study, carboxylated carbon nanotube (CNT)-loaded curcumin (CUR) was blended into calcium phosphate cement (CPC) owing to the poor mechanical properties and single function of CPC as a bone-filling material, and CNT-CUR-CPC with improved strength and antitumor properties was obtained. The failure strength, hydrophilicity, in vitro bioactivity, bacteriostatic activity, antitumor activity, and cell safety of CNT-CUR-CPC were evaluated. The experimental results indicated that the failure strength of CNT-CUR-CPC increased from 25.05 to 45.05 MPa (p < 0.001) and its contact angle decreased from 20.37° to 15.27° (p < 0.001) after the CNT-CUR complex was added into CPC at the rate of 5 wt% and blended. Following soaking in simulated body fluid (m-SBF), the main components of CNT-CUR-CPC were hydroxyapatite (HA) and carbonate hydroxyapatite (HCA). The incorporation of CNT-CUR was beneficial for the deposition of PO43- and CO32-, and it promoted the crystallization of HA and HCA. For CNT-CUR-CPC, the inhibition zone diameter on Staphylococcus aureus was 10.2 ± 1.02 mm (p < 0.001) and it exhibited moderate sensitivity, whereas the inhibition zone diameter on Escherichia coli was 8.3 ± 0.23 mm (p < 0.001) and it exhibited low sensitivity. When compared with the CPC, the cell proliferation rate (RGR %) of the CNT-CUR-CPC decreased by 7.73% (p > 0.05) at 24 h, 17.89% (p < 0.05) at 48 h, and 24.43% (p < 0.001) at 72 h when MG63 cells were cultured on it. In particular, after the MG63 cells were cultured with the CNT-CUR-CPC for 48 h, the number of newly proliferating MG63 cells was significantly reduced, and their growth and adhesion on the surface of the CNT-CUR-CPC were inhibited when compared with the CPC. When 3T3-E1 cells were exposed to the m-SBF immersion solution of CNT-CUR-CPC, the cell proliferation rate (RGR %) was ≥80% (p > 0.05) and the cytotoxicity grade was 0-1. The 3T3-E1 cells were cultured with the m-SBF soaking solution of CNT-CUR-CPC for 24 h, and no significant changes in cell morphology or cytotoxicity were observed. After the 3T3-E1 cells were cultured on CNT-CUR-CPC for 48 h, they could stick to and grow on its surface without adverse reactions. CNT-CUR-CPC had a hemolysis rate of 4.3% (p > 0.05) and did not result in hemolysis and hemagglutination. The obtained CNT-CUR-CPC scaffold material exhibited effective antibacterial activity and cell safety, and could achieve a certain antitumor effect, which has a wide application potential in bone tissue engineering.

Bifunctional electrospun poly (L-lactic acid) membranes incorporating black phosphorus nanosheets and nano-zinc oxide for enhanced biocompatibility and antibacterial properties in catheter materials

For several decades, urinary tract infections caused by catheter-associated devices have negatively impacted not only medical device utilization, but also patient health. As such, the creation of catheter materials with both superior biocompatibility and antibacterial properties has become necessary. This study aimed to produce electrospun membranes based on polylactic acid (PLA) with the incorporation of black phosphorus nanosheets (BPNS) and nano-zinc oxide (nZnO) particles, as well as a mixture of both, in order to design bifunctional membranes with enhanced bioactivity and antibacterial features. The optimum spinning process was determined through examination of various PLA mass concentrations, spinning solution propelling speeds, and receiving drum rotating speeds, with emphasis on the mechanical properties of PLA membranes. Additionally, the antibacterial properties and cytocompatibility of the ZnO-BP/PLA antibacterial membranes were explored. Results demonstrated that the ZnO-BP/PLA antibacterial membranes displayed a rich porous structure, with uniform distribution of nZnO particles and BPNS. With the increase of polylactic acid concentration and the decrease of spinning solution advancing and drum rotation speeds, the mechanical properties of the fiber membrane were significantly improved. Furthermore, the composite membranes exhibited remarkable photothermal therapy (PTT) capabilities when aided by the synergistic effect of BP nanosheets and ZnO. This was achieved through near-infrared (NIR) irradiation, which not only dissipated the biofilm but also enhanced the release capability of Zn²⁺. Consequently, the composite membrane demonstrated an improved inhibitory effect on both Escherichia coli and Staphylococcus aureus. The results of cytotoxicity and adhesion experiments also indicated good cytocompatibility, with cells growing normally on the surface of the ZnO-BP/PLA antibacterial membrane. Overall, these findings validate the utilization of both BPNS and n-ZnO fillers in the creation of novel bifunctional PLA-based membranes, which possess both biocompatibility and antibacterial properties for interventional catheter materials.