Surface Characteristics and Biocompatibility of Ultrafine-Grain Ti after Sandblasting and Acid Etching for Dental Implants

Application of advanced surface modification techniques in titanium-based implants: latest strategies for enhanced antibacterial properties and osseointegration

Titanium-based implants, renowned for their excellent mechanical properties, corrosion resistance, and biocompatibility, have found widespread application as premier implant materials in the medical field. However, as bioinert materials, they often face challenges such as implant failure caused by bacterial infections and inadequate osseointegration post-implantation. Thus, to address these issues, researchers have developed various surface modification techniques to enhance the surface properties and bioactivity of titanium-based implants. This review aims to outline several key surface modification methods for titanium-based implants, including acid etching, sol-gel method, chemical vapor deposition, electrochemical techniques, layer-by-layer self-assembly, and chemical grafting. It briefly summarizes the advantages, limitations, and potential applications of these technologies, presenting readers with a comprehensive perspective on the latest advances and trends in the surface modification of titanium-based implants.

Enhancing immune modulation and bone regeneration on titanium implants by alleviating the hypoxic microenvironment and releasing bioactive ions

Bone implantation inevitably causes damage to surrounding vasculature, resulting in a hypoxic microenvironment that hinders bone regeneration. Although titanium (Ti)-based devices are widely used as bone implants, their inherent bioinert surface leads to poor osteointegration. Herein, a strontium peroxide (SrO2)-decorated Ti implant, Ti_P@SrO2, was constructed through coating with poly-L-lactic acid (PLLA) to alleviate the hypoxic microenvironment and transform the bioinert surface of the implant into a bioactive surface. PLLA degradation resulted in an acidic microenvironment and the release of SrO2 nanoparticles. The acidic microenvironment then accelerated the decomposition of SrO2, resulting in the release of O2 and Sr ions. O2 released from Ti_P@SrO2 can alleviate the hypoxic microenvironment, thus enhancing cell proliferation in an O2-insufficient microenvironment. Furthermore, under hypoxic and normal microenvironments, Ti_P@SrO2 enhanced alkaline phosphatase activity and bone-related gene expression in C3H10T1/2 cells with the continuous release of Sr ions. Meanwhile, Ti_P@SrO2 suppressed M1 polarization and promoted M2 polarization of bone marrow-derived monocytes under hypoxic and normal conditions. Furthermore, in a rat implantation model, the implant enhanced new bone formation and improved osteointegration after modification with SrO2. In summary, the newly designed O2- and Sr ion-releasing Ti implants are promising for applications in bone defects.

Nonthermal Atmospheric Pressure Plasma Treatment of Endosteal Implants for Osseointegration and Antimicrobial Efficacy: A Comprehensive Review

The energy state of endosteal implants is dependent on the material, manufacturing technique, cleaning procedure, sterilization method, and surgical manipulation. An implant surface carrying a positive charge renders hydrophilic properties, thereby facilitating the absorption of vital plasma proteins crucial for osteogenic interactions. Techniques to control the surface charge involve processes like oxidation, chemical and topographical adjustments as well as the application of nonthermal plasma (NTP) treatment. NTP at atmospheric pressure and at room temperature can induce chemical and/or physical reactions that enhance wettability through surface energy changes. NTP has thus been used to modify the oxide layer of endosteal implants that interface with adjacent tissue cells and proteins. Results have indicated that if applied prior to implantation, NTP strengthens the interaction with surrounding hard tissue structures during the critical phases of early healing, thereby promoting rapid bone formation. Also, during this time period, NTP has been found to result in enhanced biomechanical fixation. As such, the application of NTP may serve as a practical and reliable method to improve healing outcomes. This review aims to provide an in-depth exploration of the parameters to be considered in the application of NTP on endosteal implants. In addition, the short- and long-term effects of NTP on osseointegration are addressed, as well as recent advances in the utilization of NTP in the treatment of periodontal disease.

Surface Modification and Functionalities for Titanium Dental Implants

Dental implants have become the mainstream strategy for oral restoration, and implant materials are the most important research hot spot in this field. So far, Ti implants dominate all kinds of implants. The surface properties of the Ti implant play decisive roles in osseointegration and antibacterial performance. Surface modifications can significantly change the surface micro/nanotopography and composition of Ti implants, which will effectively improve their hydrophilicity, mechanical properties, osseointegration performance, antibacterial performance, etc. These optimizations will thus improve implant success and service life. In this paper, the latest surface modification techniques of Ti dental implants are systematically and comprehensively reviewed. The various biomedical functionalities of surface modifications are discussed in-depth. Finally, a profound comment on the challenges and opportunities of this frontier is proposed, and the most promising directions for the future were explored.

Electrochemical and biological characterization of Ti-Nb-Zr-Si alloy for orthopedic applications

The performance of current biomedical titanium alloys is limited by inflammatory and severe inflammatory conditions after implantation. In this study, a novel Ti-Nb-Zr-Si (TNZS) alloy was developed and compared with commercially pure titanium, and Ti-6Al-4V alloy. Electrochemical parameters of specimens were monitored during 1 h and 12 h immersion in phosphate buffered saline (PBS) as a normal, PBS/hydrogen peroxide (H₂O₂) as an inflammatory, and PBS/H₂O₂/albumin/lactate as a severe inflammatory media. The results showed an effect of the H₂O₂ in inflammatory condition and the synergistic behavior of H₂O₂, albumin, and lactate in severe inflammatory condition towards decreasing the corrosion resistance of titanium biomaterials. Electrochemical tests revealed a superior corrosion resistance of the TNZS in all conditions due to the presence of silicide phases. The developed TNZS was tested for subsequent cell culture investigation to understand its biocompatibility nature. It exhibited favorable cell-materials interactions in vitro compared with Ti-6Al-4V. The results suggest that TNZS alloy might be a competitive biomaterial for orthopedic applications.

Wettability and biological responses of titanium surface's biomimetic hexagonal microstructure

In this research, an experiment was conducted on how the surface wettability and biocompatibility of staplers' titanium nails impact the healing of gastrointestinal tissue. Firstly, the bionic hexagonal structure was prepared on the surface of Ti metal by laser processing technology, and the laser textured titanium samples were observed by scanning electron microscope. Then, the liquid-solid contact angle-measuring instrument was used to characterize the wettability of titanium samples. Finally, cells were cultured on the surface of different titanium samples, CCK8 assay and qRT-PCR were carried out to investigate cell adhesion and collagen secretion on the surface of different samples. The results showed that the bionic hexagonal surface increased the surface roughness, reduced the liquid-solid contact angle, and promoted the adhesion and collagen secretion of fibroblasts. The increased wettability provided a better growth environment for cell growth. Microtexture is an important factor affecting the behavior of cells and its size parameters regulate cell gene expression, which is worthy of further study.

Design of Cefotaxime Sodium-Loaded Polydopamine Coatings with Controlled Surface Roughness for Titanium Implants

The success rate of dental implants is limited by peri-implant infection and insufficient osseointegration. Therefore, reducing the occurrence of peri-implantitis and promoting osseointegration are in demand. A roughened surface has commonly been applied to improve the osseointegration of implants, but it will accelerate the attachment of bacteria. We have developed novel antibiotic-decorated titanium (Ti) surfaces by the immobilization of dopamine and cefotaxime sodium (CS) simultaneously. Moreover, the surface roughness of the polydopamine (PDA)/CS coating was controlled by the changes in polymerization times as determined by atomic force microscopy. Then, all antibiotic-grafted Ti surfaces could effectively prevent the adhesion and proliferation of both Escherichia coli and Streptococcus mutans in comparison to the pristine control. For the culture and osteogenic differentiation of human umbilical mesenchymal stem cells (hUMSCs) on the substrate surface, PDA/CS coating with polymerization times less than 30 min showed acceptable biocompatibility, but the upregulation of marker genes and proteins was detected when the polymerization time was more than 30 min. Moreover, the best calcium deposition results were found in the 30 min PDA/CS group with or without the addition of osteogenic factors. Therefore, our PDA/CS coating with a polymerization time of 30 min holds great potential to design dental implants with dual bacteriostatic and osteogenic properties.

RF Magnetron Sputtering of Substituted Hydroxyapatite for Deposition of Biocoatings

Functionalization of titanium (Ti)-based alloy implant surfaces by deposition of calcium phosphates (CaP) has been widely recognized. Substituted hydroxyapatites (HA) allow the coating properties to be tailored based on the use of different Ca substitutes. The formation of antibacterial CaP coatings with the incorporation of Zn or Cu by an RF magnetron sputtering is proposed. The influence of RF magnetron targets elemental composition and structure in the case of Zn-HA and Cu-HA, and the influence of substrate's grain size, the substrate's temperature during the deposition, and post-deposition heat treatment (HT) on the resulting coatings are represented. Sintering the targets at 1150 °C resulted in a noticeable structural change with an increase in cell volume and lattice parameters for substituted HA. The deposition rate of Cu-HA and Zn-HA was notably higher compared to stochiometric HA (10.5 and 10) nm/min vs. 9 ± 0.5 nm/min, respectively. At the substrate temperature below 100 °C, all deposited coatings were found to be amorphous with an atomic short-range order corresponding to the {300} plane of crystalline HA. All deposited coatings were found to be hyper-stochiometric with Ca/P ratios varying from 1.9 to 2.5. An increase in the substrate temperature to 200 °C resulted in the formation of equiaxed grain structure on both coarse-grained (CG) and nanostructured (NS) Ti. The use of NS Ti notably increased the scratch resistance of the deposited coatings from18 ± 1 N to 22 ± 2 N. Influence of HT in air or Ar atmosphere is also discussed. Thus, the deposition of Zn- or Cu-containing CaP is a complex process that could be fine-tuned using the obtained research results.

Evaluation of Biocompatibility of 316 L Stainless Steels Coated with TiN, TiCN, and Ti-DLC Films

In this study, TiN, TiCN, and Ti-diamond-like carbon (Ti-DLC) films were coated on 316 L stainless steel (AISI 316 L) substrate surface by physical vapor deposition. The biocompatibility of the three films (TiN, TiCN, and Ti-DLC) and three metals (AISI 316 L, Ti, and Cu) was compared on the basis of the differences in the surface morphology, water contact angle measurements, CCK-8 experiment results, and flow cytometry test findings. The biocompatibility of the TiN and TiCN films is similar to that of AISI 316 L, which has good biocompatibility. However, the biocompatibility of the Ti-DLC films is relatively poor, which is mainly due to the inferior hydrophobicity and large amount of sp2 phases. The presence of TiC nanoclusters on the surface of the Ti-DLC film aggravates the inferior biocompatibility. Compared to the positive Cu control group, the Ti-DLC film had a higher cell proliferation rate and lower cell apoptosis rate. Although the Ti-DLC film inhibited cell survival to a certain extent, it did not show obvious cytotoxicity. TiN and TiCN displayed excellent performance in promoting cell proliferation and reducing cytotoxicity; thus, TiN and TiCN can be considered good orthodontic materials, whereas Ti-DLC films require further improvement.

Preparation of Zirconium Hydrogen Phosphate Coatings on Sandblasted/Acid-Etched Titanium for Enhancing Its Osteoinductivity and Friction/Corrosion Resistance

Background

Sandblasted/acid-etched titanium (SLA-Ti) implants are widely used for dental implant restoration in edentulous patients. However, the poor osteoinductivity and the large amount of Ti particles/ions released due to friction or corrosion will affect its long-term success rate.

Purpose

Various zirconium hydrogen phosphate (ZrP) coatings were prepared on SLA-Ti surface to enhance its friction/corrosion resistance and osteoinduction.

Methods

The mixture of ZrCl₄ and H₃PO₄ was first coated on SLA-Ti and then calcined at 450°C for 5 min to form ZrP coatings. In addition to a series of physiochemical characterization such as morphology, roughness, wettability, and chemical composition, their capability of anti-friction and anti-corrosion were further evaluated by friction-wear test and by potential scanning. The viability and osteogenic differentiation of MC3T3-E1 cells on different substrates were investigated via MTT, mineralization and PCR assays.

Results

The characterization results showed that there were no significant changes in the morphology, roughness and wettability of ZrP-modified samples (SLA-ZrP0.5 and SLA-ZrP0.7) compared with SLA group. The results of electrochemical corrosion displayed that both SLA-ZrP0.5 and SLA-ZrP0.7 (especially the latter) had better corrosion resistance than SLA in normal saline and serum-containing medium. SLA-ZrP0.7 also exhibited the best friction resistance and great potential to enhance the spreading, proliferation and osteogenic differentiation of MC3T3-E1 cells.

Conclusion

We determined that SLA-ZrP0.7 had excellent comprehensive properties including anti-corrosion, anti-friction and osteoinduction, which made it have a promising clinical application in dental implant restoration.

[Research progress on the biological properties of the surface nanocrystals of typical medical metal materials]

Biomedical metal materials have always been a major biomedical material with a large and wide range of clinical use due to their excellent properties such as high strength and toughness, fatigue resistance, easy forming, and corrosion resistance. They are also the preferred implant material for hard tissues (bones and teeth that need to withstand higher loads) and interventional stents. And nano-medical metal materials have better corrosion resistance and biocompatibility. This article focuses on the changes and improvements in the properties of several typical medical metal materials surfaces after nanocrystallization, and discusses the current problems and development prospects of nano-medical metal materials.