Catalytic Effects of Aniline Polymerization Assisted by Oligomers

Synthesis and Characterization of a Novel Nanosized Polyaniline

Polyaniline (PANI) is a conductive polymer easily converted into a conducting state. However, its limited mechanical properties have generated interest in fabricating PANI composites with other polymeric materials. In this study, a PANI-prevulcanized latex composite film was synthesized and fabricated in two phases following chronological steps. The first phase determined the following optimum parameters for synthesizing nanosized PANI, which were as follows: an initial molar ratio of 1, a stirring speed of 600 rpm, a synthesis temperature of 25 °C, purification via filtration, and washing using dopant acid, acetone, and distilled water. The use of a nonionic surfactant, Triton X-100, at 0.1% concentration favored PANI formation in a smaller particle size of approximately 600 nm and good dispersibility over seven days of observation compared to the use of anionic sodium dodecyl sulfate. Ultraviolet-visible spectroscopy (UV-Vis) showed that the PANI synthesized using a surfactant was in the emeraldine base form, as the washing process tends to decrease the doping level in the PANI backbone. Our scanning electron microscopy analysis showed that the optimized synthesis parameters produced colloidal PANI with an average particle size of 695 nm. This higher aspect ratio explained the higher conductivity of nanosized PANI compared to micron-sized PANI. Following the chronological steps to determine the optimal parameters produced a nanosized PANI powder. The nanosized PANI had higher conductivity than the micron-sized PANI because of its higher aspect ratio. When PANI is synthesized in smaller particle sizes, it has higher conductivity. Atomic force microscopy analysis showed that the current flow is higher across a 5 µm2 scanned area of nanosized PANI because it has a larger surface area. Thus, more sites for the current to flow through were present on the nanosized PANI particles.

Conducting Polyaniline for Antifouling Ultrafiltration Membranes: Solutions and Challenges

Conjugated polyaniline can impact the field of water filtration membranes due to its hydrophilic and antibacterial nature, facile and inexpensive synthesis procedure, heat and acid tolerance, and unique doping/dedoping chemistry. However, the gelation effect, its rigid backbone, and the limited hydrophilicity of polyaniline severely restrict the adaptability to membranes and their antifouling performance. This Mini Review summarizes important works of polyaniline-related ultrafiltration membranes, highlighting solutions to conquer engineering obstacles in processing and challenges in enhancing surface hydrophilicity with an emphasis on chemistry. As a pH-responsive polymer convertible to a conductive salt, this classic material should continue to bring unconventional advances into the realm of water filtration membranes.