Synthesis of core-shell structured dual-mesoporous silica spheres with tunable pore size and controllable shell thickness

Tailored Hollow Mesoporous Carbon Nanospheres from Soft Emulsions Enhance Kinetics in Sodium Batteries

Mesoporous materials endowed with a hollow structure offer ample opportunities due to their integrated functionalities; however, current approaches mainly rely on the recruitment of solid rigid templates, and feasible strategies with better simplicity and tunability remain infertile. Here, we report a novel emulsion-driven coassembly method for constructing a highly tailored hollow architecture in mesoporous carbon, which can be completely processed on oil-water liquid interfaces instead of a solid rigid template. Such a facile and flexible methodology relies on the subtle employment of a 1,3,5-trimethylbenzene (TMB) additive, which acts as both an emulsion template and a swelling agent, leading to a compatible integration of oil droplets and composite micelles. The solution-based assembly process also shows high controllability, endowing the hollow carbon mesostructure with a uniform morphology of hundreds of nanometers and tunable cavities from 0 to 130 nm in diameter and porosities (mesopore sizes 2.5-7.7 nm; surface area 179-355 m2 g-1). Because of the unique features in permeability, diffusion, and surface access, the hollow mesoporous carbon nanospheres exhibit excellent high rate and cycling performances for sodium-ion storage. Our study reveals a cooperative assembly on the liquid interface, which could provide an alternative toolbox for constructing delicate mesostructures and complex hierarchies toward advanced technologies.

Silicon-containing nanomedicine and biomaterials: materials chemistry, multi-dimensional design, and biomedical application

The invention of silica-based bioactive glass in the late 1960s has sparked significant interest in exploring a wide range of silicon-containing biomaterials from the macroscale to the nanoscale. Over the past few decades, these biomaterials have been extensively explored for their potential in diverse biomedical applications, considering their remarkable bioactivity, excellent biocompatibility, facile surface functionalization, controllable synthesis, etc. However, to expedite the clinical translation and the unexpected utilization of silicon-composed nanomedicine and biomaterials, it is highly desirable to achieve a thorough comprehension of their characteristics and biological effects from an overall perspective. In this review, we provide a comprehensive discussion on the state-of-the-art progress of silicon-composed biomaterials, including their classification, characteristics, fabrication methods, and versatile biomedical applications. Additionally, we highlight the multi-dimensional design of both pure and hybrid silicon-composed nanomedicine and biomaterials and their intrinsic biological effects and interactions with biological systems. Their extensive biomedical applications span from drug delivery and bioimaging to therapeutic interventions and regenerative medicine, showcasing the significance of their rational design and fabrication to meet specific requirements and optimize their theranostic performance. Additionally, we offer insights into the future prospects and potential challenges regarding silicon-composed nanomedicine and biomaterials. By shedding light on these exciting research advances, we aspire to foster further progress in the biomedical field and drive the development of innovative silicon-composed nanomedicine and biomaterials with transformative applications in biomedicine.

Unraveling the Adsorption Behavior of Thymol on Carbon and Silica Nanospheres for Prolonged Antibacterial Activity: Experimental and DFT Studies

Functionalization of thymol (Thy) on nanocarriers is a key step in achieving prolonged antimicrobial activity. This requires nanomaterials with uniform particle diameters and suitable thymol sorption. Herein, hollow carbon (HC) and SiO2-carbon core-shell (SiO2@C) were investigated due to their diverse morphologies and ease of surface modification. HC (14 ± 1 nm size) and SiO2@C (10 ± 1.5 nm size) were synthesized by the Stöber method before thymol was loaded by incipient wetness impregnation. Nanoparticle physicochemical properties were characterized by advanced techniques, including X-ray photoelectron spectroscopy (XPS) and near-edge X-ray absorption fine structure (NEXAFS). Adsorption energies of thymol on the carbon and SiO2 surfaces were elucidated by density functional theory (DFT) simulations. Moreover, the in vitro thymol release profiles and antibacterial activity were evaluated. The experimental results indicated that the oxy-carbon surface species of HC led to longer thymol release profiles than the -OH group of SiO2@C. The DFT calculations revealed that the weaker physical interaction of thymol on HC was better for drug release than that on SiO2@C. Thus, a longer thymol release profile of HC with hollow structures showed better antibacterial performance against Gram-positive bacteria Staphylococcus aureus than that of SiO2@C with core-shell structures. This work confirms the important role of carbon morphology and specific functional groups in thymol release profiles for the further development of inhibition products.

FRET-Modulated Fluorescence Lifetime-Traceable Nanocarriers for Multidrug Release Monitoring and Synergistic Therapy

In situ monitoring multidrug release in complex cellular microenvironments is significant, and currently, it is still a great challenge. In this work, a smart nanocarrier with the capability of codelivery of small molecules and gene materials as well as with Förster resonance energy transfer (FRET)-modulated fluorescence lifetime is fabricated by integrating gold nanoparticles (the acceptor) into dual-mesoporous silica loaded with multiple drugs (the donor). Once internalized into tumor cells, in weakly acidic environments, the conformation switch of the polymer grafted on nanocarriers causes its shedding from the mesopores, triggering the release of drugs. Simultaneously, based on the strong overlap between the emission spectrum of donors and the absorption spectrum of the acceptors, any slight fluctuation of the dissociation of the drugs from nanocarriers can result in a change in the FRET-modulated lifetime signal due to the extraordinarily sensitive FRET signal to the separation distance between donors and acceptors. All these implied the potential applications of this nanoplatform in various biomedical fields that require the codelivery and real-time monitoring of multidrug-based synergistic therapy.

Emulsion-oriented assembly for Janus double-spherical mesoporous nanoparticles as biological logic gates

The ability of Janus nanoparticles to establish biological logic systems has been widely exploited, yet conventional non/uni-porous Janus nanoparticles are unable to fully mimic biological communications. Here we demonstrate an emulsion-oriented assembly approach for the fabrication of highly uniform Janus double-spherical MSN&mPDA (MSN, mesoporous silica nanoparticle; mPDA, mesoporous polydopamine) nanoparticles. The delicate Janus nanoparticle possesses a spherical MSN with a diameter of ~150 nm and an mPDA hemisphere with a diameter of ~120 nm. In addition, the mesopore size in the MSN compartment is tunable from ~3 to ~25 nm, while those in the mPDA compartments range from ~5 to ~50 nm. Due to the different chemical properties and mesopore sizes in the two compartments, we achieve selective loading of guests in different compartments, and successfully establish single-particle-level biological logic gates. The dual-mesoporous structure enables consecutive valve-opening and matter-releasing reactions within one single nanoparticle, facilitating the design of single-particle-level logic systems.

Fe3O4-SiO2 Mesoporous Core/Shell Nanoparticles for Magnetic Field-Induced Ibuprofen-Controlled Release

Hybrid magnetic nanoparticles made up of an iron oxide, Fe₃O₄, core and a mesoporous SiO₂ shell with high magnetization and a large surface area were proposed as an efficient drug delivery platform. The core/shell structure was synthesized by two seed-mediated growth steps combining solvothermal and sol-gel approaches and using organic molecules as a porous scaffolding template. The system presents a mean particle diameter of 30(5) nm (9 nm magnetic core diameter and 10 nm silica shell thickness) with superparamagnetic behavior, saturation magnetization of 32 emu/g, and a significant AC magnetic-field-induced heating response (SAR = 63 W/g_Fe3O4, measured at an amplitude of 400 Oe and a frequency of 307 kHz). Using ibuprofen as a model drug, the specific surface area (231 m²/g) of the porous structure exhibits a high molecule loading capacity (10 wt %), and controlled drug release efficiency (67%) can be achieved using the external AC magnetic field for short time periods (5 min), showing faster and higher drug desorption compared to that of similar stimulus-responsive iron oxide-based nanocarriers. In addition, it is demonstrated that the magnetic field-induced drug release shows higher efficiency compared to that of the sustained release at fixed temperatures (47 and 53% for 37 and 42 °C, respectively), considering that the maximum temperature reached during the exposure to the magnetic field is well below (31 °C). Therefore, it can be hypothesized that short periods of exposure to the oscillating field induce much greater heating within the nanoparticles than in the external solution.

A review on the latest developments of mesoporous silica nanoparticles as a promising platform for diagnosis and treatment of cancer

Cancer is the second cause of human mortality after cardiovascular disease around the globe. Conventional cancer therapies are chemotherapy, radiation, and surgery. In fact, due to the lack of absolute specificity and high drug concentrations, early recognition and treatment of cancer with conventional approaches have become challenging issues in the world. To mitigate against the limitations of conventional cancer chemotherapy, nanomaterials have been developed. Nanomaterials exhibit particular properties that can overcome the drawbacks of conventional therapies such as lack of specificity, high drug concentrations, and adverse drug reactions. Among nanocarriers, mesoporous silica nanoparticles (MSNs) have gained increasing attention due to their well-defined pore size and structure, high surface area, good biocompatibility and biodegradability, ease of surface modification, and stable aqueous dispersions. This review highlights the current progress with the use of MSNs for the delivery of chemotherapeutic agents for the diagnosis and treatment of cancer. Various stimuli-responsive gatekeepers, which endow the MSNs with on-demand drug delivery, surface modification strategies for targeting purposes, and multifunctional MSNs utilized in drug delivery systems (DDSs) are also addressed. Also, the capability of MSNs as flexible imaging platforms is considered. In addition, physicochemical attributes of MSNs and their effects on cancer therapy with a particular focus on recent studies is emphasized. Moreover, major challenges to the use of MSNs for cancer therapy, biosafety and cytotoxicity aspects of MSNs are discussed.

Confined Construction of Ultrasmall Molybdenum Disulfide-Loaded Porous Silica Particles for Efficient Tumor Therapy

Recently, molybdenum sulfide (MoS₂) has shown great application potential in tumor treatment because of its good photothermal properties. Unfortunately, most of the current molybdenum disulfide-based nanotherapeutic agents suffer from complex preparation processes, low photothermal conversion efficiencies, and poor structural/compositional regulation. To address these issues, in this paper, a facile "confined solvothermal" method is proposed to construct an MoS²-loaded porous silica nanosystem (designated as MoS₂@P-hSiO₂). The maximum photothermal efficiency of 79.5% of molybdenum-based materials reported in the literature at present was obtained due to the ultrasmall MoS₂ nanoclusters and the rich porous channels. Furthermore, both in vitro and in vivo experiments showed that the cascade hybrid system (MoS₂/GOD@P-hSiO₂) after efficient loading of glucose oxidase (GOD) displayed a significant tumor-suppressive effect and good biosafety through the combined effects of photothermal and enzyme-mediated cascade catalytic therapy. Consequently, this hybrid porous network system combining the in situ solvothermal strategy of inorganic functional components and the efficient encapsulation of organic enzyme macromolecules can provide a new pathway to construct synergistic agents for the efficient and safe treatment of tumors.

Mesoporous silica nanocarriers as drug delivery systems for anti-tubercular agents: a review

The treatment and management of tuberculosis using conventional drug delivery systems remain challenging due to the setbacks involved. The lengthy and costly treatment regime and patients' non-compliance have led to drug-resistant tuberculosis, which is more difficult to treat. Also, anti-tubercular drugs currently used are poor water-soluble drugs with low bioavailability and poor therapeutic efficiency except at higher doses which causes drug-related toxicity. Novel drug delivery carrier systems such as mesoporous silica nanoparticles (MSNs) have been identified as nanomedicines capable of addressing the challenges mentioned due to their biocompatibility. The review discusses the sol-gel synthesis and chemistry of MSNs as porous drug nanocarriers, surface functionalization techniques and the influence of their physico-chemical properties on drug solubility, loading and release kinetics. It outlines the physico-chemical characteristics of MSNs encapsulated with anti-tubercular drugs.

Cationic and Anionic Antimicrobial Agents Co-Templated Mesostructured Silica Nanocomposites with a Spiky Nanotopology and Enhanced Biofilm Inhibition Performance

HIGHLIGHTS

A ‘dual active templating’ strategy is firstly reported, using cationic and anionic bactericidal agents as co-templates for the preparation of antibacterial silica nanocomposite with spiky nanotopography. The spiky nanocomposite exhibited enhanced antibacterial and biofilm inhibition performance, compared to pure antimicrobial cationic agent templated smooth silica nanocomposite.

ABSTRACT

Silica-based materials are usually used as delivery systems for antibacterial applications. In rare cases, bactericidal cationic surfactant templated silica composites have been reported as antimicrobial agents. However, their antibacterial efficacy is limited due to limited control in content and structure. Herein, we report a “dual active templating” strategy in the design of nanostructured silica composites with intrinsic antibacterial performance. This strategy uses cationic and anionic structural directing agents as dual templates, both with active antibacterial property. The cationic-anionic dual active templating strategy further contributes to antibacterial nanocomposites with a spiky surface. With controllable release of dual active antibacterial agents, the spiky nanocomposite displays enhanced anti-microbial and anti-biofilm properties toward Staphylococcus epidermidis. These findings pave a new avenue toward the designed synthesis of novel antibacterial nanocomposites with improved performance for diverse antibacterial applications. [Image: see text]

SUPPLEMENTARY INFORMATION

The online version contains supplementary material available at 10.1007/s40820-022-00826-4.

Nanoarchitectured prototypes of mesoporous silica nanoparticles for innovative biomedical applications

Despite exceptional morphological and physicochemical attributes, mesoporous silica nanoparticles (MSNs) are often employed as carriers or vectors. Moreover, these conventional MSNs often suffer from various limitations in biomedicine, such as reduced drug encapsulation efficacy, deprived compatibility, and poor degradability, resulting in poor therapeutic outcomes. To address these limitations, several modifications have been corroborated to fabricating hierarchically-engineered MSNs in terms of tuning the pore sizes, modifying the surfaces, and engineering of siliceous networks. Interestingly, the further advancements of engineered MSNs lead to the generation of highly complex and nature-mimicking structures, such as Janus-type, multi-podal, and flower-like architectures, as well as streamlined tadpole-like nanomotors. In this review, we present explicit discussions relevant to these advanced hierarchical architectures in different fields of biomedicine, including drug delivery, bioimaging, tissue engineering, and miscellaneous applications, such as photoluminescence, artificial enzymes, peptide enrichment, DNA detection, and biosensing, among others. Initially, we give a brief overview of diverse, innovative stimuli-responsive (pH, light, ultrasound, and thermos)- and targeted drug delivery strategies, along with discussions on recent advancements in cancer immune therapy and applicability of advanced MSNs in other ailments related to cardiac, vascular, and nervous systems, as well as diabetes. Then, we provide initiatives taken so far in clinical translation of various silica-based materials and their scope towards clinical translation. Finally, we summarize the review with interesting perspectives on lessons learned in exploring the biomedical applications of advanced MSNs and further requirements to be explored.

Spherical Silica Modified with Magnesium and Ruthenium-Synthesis, Characterization and Catalytic Properties

The design of different bimetallic catalysts is an important area of catalytic research in the context of their possible applications in the cascade processes, meeting the requirements of the so-called green chemistry. In this study, such catalysts were obtained by the incorporation of magnesium species into spherical silica, which was in the next step covered with porous silica and modified with ruthenium species. The structure and chemical composition of the materials obtained were determined by XRD measurements, low temperature N₂ adsorption/desorption, SEM, ICP-OES and XPS methods. The catalytic activities of materials obtained were tested in 2-propanol decomposition and hydrogenation of levulinic acid. The results obtained confirmed the successful coverage of nanospheres with porous silica. A much higher concentration of ruthenium species was found on the surface of the catalysts than in their bulk. The opposite relationship was observed for magnesium species. The modification of nanospheres with silica had a positive effect on the catalytic activity of the materials obtained. For the most active sample, i.e., Ru/NS/3Mg/NS, 49% of levulinic acid conversion in its hydrogenation process was reported with γ-valerolactone as the only product.

Hierarchically porous calcium-silicon nanosphere-enabled co-delivery of microRNA-210 and simvastatin for bone regeneration

The regenerative repair of large bone defects is a major problem in orthopedics and clinical medicine. The key problem is the lack of ability of existing bone graft materials to promote osteogenesis and angiogenesis. Previous studies have shown that the osteogenic or angiogenic abilities of these materials could be significantly improved by adding miRNA or small-molecule drugs to bone graft materials; however, the synergistic effect arising from this combination is not clear. Therefore, we proposed to construct a dual drug delivery system that could simultaneously achieve the co-encapsulation and co-delivery of miRNA and small-molecule drugs to explore the effect of a dual drug delivery system on bone repair. In this study, we constructed dual-sized pore structure calcium-silicon nanospheres (DPNPs) and achieved the co-encapsulation of miR-210, angiogenic gene drugs, and simvastatin (Siv), a small-molecule osteogenic drug, through metal-ion coordination and physical adsorption. In vitro and in vivo osteogenic and angiogenic experiments showed that the dual drug delivery system (Siv/DPNP/miR-210) exhibited better properties than those of the individual unloaded and single drug-loaded systems and could significantly accelerate the process of bone repair, which provides a novel strategy for the regeneration and repair of bone defects.

Recent Advances in Mesoporous Silica Nanoparticles for Targeted Drug Delivery applications

Nanotechnology provides the means to design and fabricate delivery vehicles capable of overcoming physiologically imposed obstacles and undesirable side effects of systemic drug delivery. This protocol allows maximal targeting effectiveness and therefore enhances therapeutic efficiency. In recent years, mesoporous silica nanoparticles (MSNPs) have sparked interest in the nanomedicine research community, particularly for their promising applications in cancer treatment. The intrinsic physio-chemical stability, facile functionalization, high surface area, low toxicity, and great loading capacity for a wide range of chemotherapeutic agents make MSNPs very appealing candidates for controllable drug delivery systems. Importantly, the peculiar nanostructures of MSNPs enabled them to serve as an effective drug, gene, protein, and antigen delivery vehicle for a variety of therapeutic regimens. For these reasons, in this review article, we underscore the recent progress in the design and synthesis of MSNPs and the parameters influencing their characteristic features and activities. In addition, the process of absorption, dissemination, and secretion by injection or oral management of MSNPs are also discussed, as they are key directions for the potential utilization of MSNPs. Factors influencing the in vivo fate of MSNPs will also be highlighted, with the main focus on particle size, morphology, porosity, surface functionality, and oxidation. Given that combining other functional materials with MSNPs may increase their biological compatibility, monitor drug discharge, or improve absorption by tumor cells coated MSNPs; these aspects are also covered and discussed herein.

Functionalized nanoprobes for in situ detection of telomerase

Telomerase, a special ribonucleoprotein reverse transcriptase, can maintain the length and stability of telomeres and plays an important role in cell proliferation and differentiation. Due to the distinguishable expression level in normal cells and cancer cells, telomerase has become an important biomarker for cancer diagnosis and prognosis evaluation. Despite major breakthroughs in the field of telomerase detection, the extracts in the cell lysate are still the first choice as the analyte nevertheless, which will bring serious inaccuracies compared with the real intracellular activity. With the development of nanotechnology and nanomaterials, extraordinary progress has been made in telomerase detection by employing different versatile nanoprobes. In this review, we list the superiority of nanoprobes and systematically summarize the applications of nanoprobes in telomerase detection from the aspects of various nanomaterials and discuss the current challenges and potential trends in the future design of nanoprobes.

Nanocellulose as template to prepare rough-hydroxy rich hollow silicon mesoporous nanospheres (R-nCHMSNs) for drug delivery

Drug-delivery technology is an effective way to promote drug absorption and efficacy. Mesoporous hollow silica material and small-molecule drug ibuprofen were used as a carrier model and as model drug, respectively. By quantum chemical calculation (density functional theory and frontier orbital theory), it was found that the content of geminal silanols on the material surface played a decisive role in the release of the different drugs. The rough hollow materials are easily adsorbed and have a large loading capacity, and so we fabricated a mesoporous hollow silica material (R-nCHMSNs) with a rough surface and rich geminal silanols by using hydroxyl-rich nanocellulose as a template. The content and types of hydroxyl groups on the material surface were studied by ²⁹Si NMR. The loading and delivery of ibuprofen and lysozyme were studied in detail. Materials with rich geminal silanols exhibited excellent delivery properties for different drugs, which shows great potential and research value for drug delivery.

PEG-Coated Large Mesoporous Silicas as Smart Platform for Protein Delivery and Their Use in a Collagen-Based Formulation for 3D Printing

Silica-based mesoporous systems have gained great interest in drug delivery applications due to their excellent biocompatibility and high loading capability. However, these materials face challenges in terms of pore-size limitations since they are characterized by nanopores ranging between 6-8 nm and thus unsuitable to host large molecular weight molecules such as proteins, enzymes and growth factors (GFs). In this work, for an application in the field of bone regeneration, large-pore mesoporous silicas (LPMSs) were developed to vehicle large biomolecules and release them under a pH stimulus. Considering bone remodeling, the proposed pH-triggered mechanism aims to mimic the release of GFs encased in the bone matrix due to bone resorption by osteoclasts (OCs) and the associated pH drop. To this aim, LPMSs were prepared by using 1,3,5-trimethyl benzene (TMB) as a swelling agent and the synthesis solution was hydrothermally treated and the influence of different process temperatures and durations on the resulting mesostructure was investigated. The synthesized particles exhibited a cage-like mesoporous structure with accessible pores of diameter up to 23 nm. LPMSs produced at 140 °C for 24 h showed the best compromise in terms of specific surface area, pores size and shape and hence, were selected for further experiments. Horseradish peroxidase (HRP) was used as model protein to evaluate the ability of the LPMSs to adsorb and release large biomolecules. After HRP-loading, LPMSs were coated with a pH-responsive polymer, poly(ethylene glycol) (PEG), allowing the release of the incorporated biomolecules in response to a pH decrease, in an attempt to mimic GFs release in bone under the acidic pH generated by the resorption activity of OCs. The reported results proved that PEG-coated carriers released HRP more quickly in an acidic environment, due to the protonation of PEG at low pH that catalyzes polymer hydrolysis reaction. Our findings indicate that LPMSs could be used as carriers to deliver large biomolecules and prove the effectiveness of PEG as pH-responsive coating. Finally, as proof of concept, a collagen-based suspension was obtained by incorporating PEG-coated LPMS carriers into a type I collagen matrix with the aim of designing a hybrid formulation for 3D-printing of bone scaffolds.

Nanoarchitecting Hierarchical Mesoporous Siliceous Frameworks: A New Way Forward

Owing to their attractive physicochemical and morphological attributes, mesoporous silica nanoparticles (MSNs) have attracted increasing attention over the past two decades for their utilization in diversified fields. Despite the success, these highly stable siliceous frameworks often suffer from several shortcomings of compatibility issues, uncontrollable degradability leading to long-term retention in vivo, and substantial unpredictable toxicity risks, as well as deprived drug encapsulation efficiency, which could limit their applicability in medicine. Along this line, various advancements have been made in re-engineering the stable siliceous frameworks, such as the incorporation of diverse molecular organic, as well as inorganic (cationic and anionic) species and monitoring the processing, as well as formulation parameters, resulting in the hetero-nanostructures of irregular-shaped (Janus and multi-podal) and dynamically-modulated (deformable solids) architectures with high morphological complexity. Insightfully, this review gives a brief emphasis on re-engineering such stable siliceous frameworks through modifying their intrinsic structural and physicochemical attributes. In conclusion, we recapitulate the review with exciting perspectives.

Mesoporous Nanoarchitectures for Electrochemical Energy Conversion and Storage

Mesoporous materials have attracted considerable attention because of their distinctive properties, including high surface areas, large pore sizes, tunable pore structures, controllable chemical compositions, and abundant forms of composite materials. During the last decade, there has been increasing research interest in constructing advanced mesoporous nanomaterials possessing short and open channels with efficient mass diffusion capability and rich accessible active sites for electrochemical energy conversion and storage. Here, the synthesis, structures, and energy-related applications of mesoporous nanomaterials are the main focus. After a brief summary of synthetic methods of mesoporous nanostructures, the delicate design and construction of mesoporous nanomaterials are described in detail through precise tailoring of the particle sizes, pore sizes, and nanostructures. Afterward, their applications as electrode materials for lithium-ion batteries, supercapacitors, water-splitting electrolyzers, and fuel cells are discussed. Finally, the possible development directions and challenges of mesoporous nanomaterials for electrochemical energy conversion and storage are proposed.

Silica Mesoporous Structures: Effective Nanocarriers in Drug Delivery and Nanocatalysts

The application of silica mesoporous structures in drug delivery and the removal of pollutants and organic compounds through catalytic reactions is increasing due to their unique characteristics, including high loading capacities, tunable pores, large surface areas, sustainability, and so on. This review focuses on very well-studied class of different construction mesoporous silica nano(particles), such as MCM-41, SBA-15, and SBA-16. We discuss the essential parameters involved in the synthesis of these materials with providing a diverse set of examples. In addition, the recent advances in silica mesoporous structures for drug delivery and catalytic applications are presented to fill the existing gap in the literature with providing some promising examples on this topic for the scientists in both industry and academia active in the field. Regarding the catalytic applications, mesoporous silica particles have shown some promises to remove the organic pollutants and to synthesize final products with high yields due to the ease with which their surfaces can be modified with various ligands to create appropriate interactions with target molecules. In the drug delivery process, as nanocarriers, they have also shown very good performance thanks to the easy surface functionalization but also adjustability of their porosities to providing in-vivo and in-vitro cargo delivery at the target site with appropriate rate.

Mesoporous silica nanoparticles: facile surface functionalization and versatile biomedical applications in oncology

Mesoporous silica nanoparticles (MSNs) have received increasing interest due to their tunable particle size, large surface area, stable framework, and easy surface modification. They are increasingly being used in varying applications as delivery vehicles including bio-imaging, drug delivery, biosensors and tissue engineering etc. Precise structure control and the ability to modify surface properties of MSNs are important for their applications. This review summarises the different synthetic methods for the preparation of well-ordered MSNs with tunable pore volume as well as the approaches of drugs loading, especially highlighting the facile surface functionalization for various purposes and versatile biomedical applications in oncology. Finally, the challenges of clinical transformation of MSNs-based nanomedicines are further discussed.

Nanoarchitectured Structure and Surface Biofunctionality of Mesoporous Silica Nanoparticles

Mesoporous silica nanoparticles (MSNs), one of the important porous materials, have garnered interest owing to their highly attractive physicochemical features and advantageous morphological attributes. They are of particular importance for use in diverse fields including, but not limited to, adsorption, catalysis, and medicine. Despite their intrinsic stable siliceous frameworks, excellent mechanical strength, and optimal morphological attributes, pristine MSNs suffer from poor drug loading efficiency, as well as compatibility and degradability issues for therapeutic, diagnostic, and tissue engineering purposes. Collectively, the desirable and beneficial properties of MSNs have been harnessed by modifying the surface of the siliceous frameworks through incorporating supramolecular assemblies and various metal species, and through incorporating supramolecular assemblies and various metal species and their conjugates. Substantial advancements of these innovative colloidal inorganic nanocontainers drive researchers in promoting them toward innovative applications like stimuli (light/ultrasound/magnetic)-responsive delivery-associated therapies with exceptional performance in vivo. Here, a brief overview of the fabrication of siliceous frameworks, along with discussions on the significant advances in engineering of MSNs, is provided. The scope of the advancement in terms of structural and physicochemical attributes and their effects on biomedical applications with a particular focus on recent studies is emphasized. Finally, interesting perspectives are recapitulated, along with the scope toward clinical translation.

Interfacial separation of concentrated dye mixtures from solution with environmentally compatible nitrogenous-silane nanoparticles modified with Helianthus annuus husk extract

The capacity of an adsorbent to bind and remove dye from solution greatly depends on the type of functionalization present on the nanoparticles surface, and its interaction with the dye molecules. Within this study, nitrogenous silane nanoparticles were hydrothermally synthesized resulting in the formation of rapid and highly efficient adsorbents for concentrated mixed dyes. The amorphous silane nanoparticles exhibited a monolayer based mechanism of mixed dye adsorption with removal capacities between 416.67 and 714.29 mg/g of adsorbent. Dye removal was predominantly due to the electrostatic attraction between the positively charged silane nanoparticles (13.22-8.20 mV) and the negatively charged dye molecules (-54.23 mV). Addition of H. annuus extract during synthesis resulted in three times the surface area and 10 times increased pore volume compared to the positive control. XPS analysis showed that silane treatments had various nitrogen containing functionalities at their surface responsible for binding dye. The weak colloidal stability of silane particles (13.22-8.20 mV) was disrupted following dye binding, resulting in their rapid coagulation and flocculation which facilitated the separation of bound dye molecules from solution. The suitability for environmental applications using these treatments was supported by a bacterial viability assay showing >90% cell viability in treated dye supernatants.

Hollow multishell structures exercise temporal–spatial ordering and dynamic smart behaviour

A hollow multishell structure (HoMS) is an assembly of multiple shells with voids between the individual shells. Accessible through nanopores, these voids represent separate reaction environments in the same assembly, such that HoMSs have unique properties that are applicable to diverse fields. These applications have mostly exploited the large specific surface area, high loading capacity and/or buffering effect of HoMSs, benefiting the mass/energy transmission and effective surface area. In comparison, the temporal-spatial ordering of reactions, as well as the dynamic smart behaviour of HoMSs, have been less explored but are also emphasized in this Perspective. We first describe the synthesis of HoMSs and the thermodynamic and kinetic aspects of their formation. We then consider the composition and structural functionalization of each shell within a HoMS and then highlight how these enable applications based on temporal-spatial ordering and dynamic smart behaviour.

Galvanic synthesis of AgPd bimetallic catalysts from Ag clusters dispersed in a silica matrix

AgPd bimetallic clusters dispersed in a silica matrix were made by a top down synthetic strategy and used as selective hydrogenation catalysts.

Hydrophobic mesoporous silicon dioxide for improving foam stability

In this study, mesoporous SiO₂ nanoparticles (MSNs) were synthesized via a sol–gel method and modified with (3-chloropropyl) trimethoxysilane to make them hydrophobic (MMSNs). The material was characterized via SEM, TEM, FT-IR, DLS, BET and contact angle measurements. The MMSNs have good foam stability, so that the foam properties of the added particles have been increased by 38.4% in an oil/SDS solution. Simultaneously, it becomes a promising material for foam stabilization in order to enhance the oil recovery because it is bio-compatibile and environment friendly. Also, it provides a novel application-stable foam for mesoporous materials.

In this study, mesoporous SiO₂ nanoparticles (MSNs) were synthesized via a sol–gel method and modified with (3-chloropropyl) trimethoxysilane to make them hydrophobic (MMSNs).

Patchy Templated Synthesis of Macroporous Colloidal Hollow Spheres and Their Application as Catalytic Microreactors

Porous colloidal hollow spheres have been applied to diversified fields over the past few decades. However, developing simple and efficient methods to prepare such porous hollow spheres with macro pores remains a challenge. To address this problem, we present a patchy templated synthesis route, which can be used to prepare such colloidal hollow spheres that have macro pores through the shells. This was achieved by using patchy poly(styrene-co-sodium styrenesulfonate) spheres as the template and poly(allylamine hydrochloride) as binding molecules. SiO₂ can site-selectively only grow on one kind of patch, resulting in the formation of porous hollow spheres. The pore sizes can be tuned from ∼50 to 400 nm. The resulting porous hollow spheres have a Janus character so that Au nanoparticles can only be attached to the interior surfaces in situ, which can be used as catalytic microreactors and show the catalytic performance of pore size dependence.

Core-Shell Structure Design of Hollow Mesoporous Silica Nanospheres Based on Thermo-Sensitive PNIPAM and pH-Responsive Catechol-Fe3+ Complex

A kind of core-shell hybrid nanoparticle comprised of a hollow mesoporous silica nanoparticles (HMS) core and a copolymer shell bearing N-(3,4-dihydroxyphenethyl) methacrylamide (DMA) and N-isopropylacrylamide (NIPAM) as responsive moieties was prepared. Moreover, the factors that could impact the surface morphology and hierarchical porous structure were discussed. In the presence of Fe3+, catechol-Fe3+ complexes were formed to achieve pH-responsive polymer shell, combining with thermal-sensitiveness of poly(N-isopropylacrylamide). Doxorubicin (DOX) was applied as a model drug and the behaviors of its loading/release behaviors were investigated to prove the idea. The results exhibited a significant drug loading capacity of 8.6% and embed efficiency of 94.6% under 1 mg ml-1 DOX/PBS solution. In fact, the loading capacity of drug can be easily improved to as high as 28.0% by increasing the DOX concentration. The vitro cytotoxicity assay also indicated that the as-prepared nanoparticles have no significant cytotoxicity on RAW 264.7 cells. The in vitro experiment showed that the cumulative release of DOX was obviously dependent on the temperature and pH values. This pH/temperature-sensitive hollow mesoporous silica nanosphere is expected to have potential applications in controlled drug release.

Fabrication and in situ functionalisation of mesoporous silica films by the physical entrapment of functional and responsive block copolymer structuring agents

Stimuli-responsive mesoporous silica films were prepared by evaporation-induced self-assembly through the physical entrapment of a functional block copolymer structuring agent, which simultaneously serves to functionalise the mesopore. These polymer-silica hybrid materials exhibit remarkable ionic permselectivity under highly filled conditions, and offer the potential for local polymer functionalisation for enhanced and tunable ionic permselectivity. This innovative and simple approach for the in situ functionalisation of mesoporous silica has the potential to improve how we approach the design of complex architectures at the nanoscale for enhanced transport, and is thus relevant for a variety of technologies based on molecular transport in nanoscale pores including separation, sensing, catalysis, and energy conversion.

In situ Analysis of Cancer Cells Based on DNA Signal Amplification and DNA Nanodevices

Cancer is a global disease which has been disturbing researchers in medicine and seriously threatens patients' health and lifetime around the world in the past several decades. Due to the characteristics of cancer cells, such as uncontrollable cell proliferation, cell invasion and metastasis to surrounding tissues, lower grade of differentiation, higher telomerase activity and others, it has been one of the most usual lethal factors, next to heart disease in incidence. Cancer mortality can be decreased by early diagnosis, and the people who with treatment at an early stage have an obvious improved survival rate. Consequently, early detection is significant for better understanding the pathogenesis of cancer and improving the prognosis of patients. In situ detection technique is a vital tool for imaging and cellular pathology research, which can provide effective information about tumor markers in the early cancer detection. In view of low expression of most tumor markers in the early stage of cancers, detection techniques based on DNA signal amplification and DNA nanodevices can provide a strong support for the diagnosis and detection of cancers. In this review, we summarize the research progress of different analytical techniques for detecting various tumor markers that have been reported in recent years. We compare different DNA amplification and nanodevices, then provide guidance and suggestions for better understanding in situ analysis of cancer cells.

Insights into Compositional and Structural Effects of Bimetallic Hollow Mesoporous Nanospheres toward Ethanol Oxidation Electrocatalysis

A one-pot soft-templating method is reported to fabricate nanosized bimetallic PdAg hollow mesoporous nanospheres (HMSs) for electrocatalytic ethanol oxidation reaction (EOR). The synthesis relies on the "dual-template" surfactant of dioctadecyldimethylammonium chloride that drives in situ growth of mesoporous frameworks on the surface of vesicles into the HMSs with radially opened mesochannels. The synthetic protocol is extendable to engineer elemental compositions and hierarchical nanostructures of PdAg nanoalloys. This system thus provides a direct yet solid platform to understand catalytic add-in synergies of PdAg HMSs toward electrochemical EOR. By evaluating compositional and structural features separately, bimetallic Pd₆₅Ag₃₅ HMSs display the highest EOR activity with a mass activity of 4.61 A mg_Pd^-1. Mechanism studies indicate that synergistically electronic and bifunctional effects as well as structural advantages of Pd₆₅Ag₃₅ HMSs kinetically optimize the removal of poisoning carbonaceous intermediates and accelerate the diffusion processes (the rate-determining step), and thus promote the EOR performance accordingly.

Sequential Protein-Responsive Nanophotosensitizer Complex for Enhancing Tumor-Specific Therapy

A major challenge in cancer treatment is the development of effective tumor-specific therapeutic methods that have minimal side effects. Recently, a photodynamic therapy (PDT) technique using activatable photosensitizers (aPSs) has shown great potential for cancer-specific treatment. Here, we develop a sequential protein-responsive aPS (PcC4-MSN-O1) that is based on zinc(II) phthalocyanine derivative (PcC4)-entrapped mesoporous silica nanoparticles (MSNs) and a wrapping DNA (O1) as a biogate. Inside the nanostructure of PcC4-MSN-O1, PcC4 shows self-quenching photoactivity. However, when PcC4-MSN-O1 sequentially reacts with telomerase and albumin, its photoactivity is dramatically turned on. Therefore, PcC4-MSN-O1 displays selective phototoxicity against cancer cells ( e.g., HeLa) over normal cells ( e.g., HEK-293). Following systemic PcC4-MSN-O1 administration, there is an obvious accumulation in HeLa tumors of xenograft-bearing mice, and laser irradiation clearly induces the inhibition of tumor growth. Moreover, the time-modulated activation process in tumors and the relatively fast excretion of PcC4-MSN-O1 indicate its advantages in reducing potential side effects.

In Vitro and In Vivo Evaluation of Core-Shell Mesoporous Silica as a Promising Water-Insoluble Drug Delivery System: Improving the Dissolution Rate and Bioavailability of Celecoxib With Needle-Like Crystallinity

The objective of our study was to prepare mesoporous silica nanoparticles with a core-shell structure (CSMSNs) and improve the dissolution and bioavailability of celecoxib (Cxb), a water-insoluble drug, by changing its needle-like crystal form. CSMSNs are prepared by a core-shell segmentation self-assembly method. The S_BET and V_t of CSMSNs were 890.65 m²/g and 1.23 cm³/g, respectively. Cxb was incorporated into CSMSNs by the solvent evaporation method. The gastrointestinal irritancy of the CSMSNs was evaluated by a gastric mucosa irritation test. In vitro dissolution and in vivo pharmacokinetic tests were carried out to study the improvement in the dissolution behavior and oral bioavailability of Cxb. In conclusion, gastric mucosa irritation study indicated the good biocompatibility of CSMSNs. The cumulative dissolution of CSMSNs-Cxb is 86.2% within 60 min in SIF solution, which may be ascribed to the crystal form change caused by control of the nanochannel for CSMSNs. Moreover, CSMSNs could enhance the 9.9-fold AUC of Cxb. The cumulative dissolution and bioavailability of Cxb were both significantly enhanced by CSMSNs. CSMSNs with a core-shell structure are suitable as a carrier for a poorly water-soluble drug (Cxb).

Core-Shell Magnetic Mesoporous Silica Microspheres with Large Mesopores for Enzyme Immobilization in Biocatalysis

Magnetic mesoporous silica microspheres with core-shell structure and large pores are highly desired in macromolecules delivery and biocatalysis, biospeparation, and adsorption. In this work, a controllable solvent evaporation induced solution-phase interface co-assembly approach was developed to synthesize core-shell structural magnetic mesoporous silica microspheres with ultralarge mesopore size (denoted as LP-MMS). The synthesis was achieved by employing large-molecular-weight amphiphilic block copolymers poly(ethylene oxide)- block-poly(methyl methacrylate) (PEO- b-PMMA) and small surfactant cetyltrimethylammonium bromide as co-templates, which can co-assemble with silica source in tetrahydrofuran/water solutions. The obtained LP-MMS microspheres possess uniform rasberry-like morphology with a diameter of 600 nm, large primary spherical mesopores (ca. 36 nm), large specific surface area (348 m²/g), high specific pore volume (0.59 cm³/g), and fast magnetic responsivity with high magnetization (15.9 emu/g). The mesopore morphology can be transformed from spherical to cylindrical through introducing a shearing force during the interfacial co-assembly in the synthesis system. The designed LP-MMS microspheres turn out to be good carriers for enzyme (trypsin) immobilization with a high loading capacity of 80 μg/mg and demonstrate excellent biocatalysis efficiency up to 99.1% for protein digestion within 30 min and good recycling stability with negligible decay in digestion efficiency after reuse for five times.

Confined growth of multiple gold nanorices in dual-mesoporous silica nanospheres for improved computed tomography imaging and photothermal therapy

INTRODUCTION

In this work, we have developed a novel "confined-growth" strategy to synthesize PEGylated multiple gold nanorices-encapsulated dual-mesoporous silica nanospheres (designated as PEGylated MGNRs@DMSSs) containing both small mesopores (2.5 nm) in the shell and large mesopores (21.7 nm) in the core based on a well-established, seed-mediated growth method. The photothermal effect and CT imaging ability were also studied.

METHODS

The nanoparticles were characterized by Fourier transform infrared (FT-IR) spectra, N2 absorption isotherms, Field-emission scanning electron microscopy (FE-SEM), Transmission electron microscopy (TEM), Inductively coupled plasma atomic emission spectroscopy (ICP-AES) and Confocal microscopy.

RESULTS

The longitudinally-localized surface (LSPR) absorption properties of MGNRs@DMSSs can be easily tuned by altering the amount of HAuCl4 in the gold growth solution. Additionally, the resultant PEGylated MGNRs@DMSSs have monodispersed, spherical morphology and good colloidal stability in an aqueous solution. More importantly, when exposed to NIR irradiation, the PEGylated MGNRs@DMSSs exhibit both higher temperature increments and better photothermal effects than that of single PEGylated gold nanorods at nearly an equivalent LSPR absorption. In addition, as CT contrast agents, the PEGylated MGNRs@DMSSs display a better CT imaging performance, in comparison with single PEGylated gold nanorods at the same Au concentration.

CONCLUSION

Taken together, results indicate the potential for MGNRs@DMSSs used in CT imaging-guided photothermal therapy. Such a simple "confined-growth" strategy within a porous matrix offers a promising platform to design and prepare novel metal(s) oxide@silica nanocomposites for use in further cancer bio-imaging and therapy.

Hierarchically Porous Silica Prepared with Anionic Polyelectrolyte-Nonionic Surfactant Mesomorphous Complex as Dynamic Template

Hierarchically porous silica KIT-6 and SBA-15 mesostructures were successfully synthesized by using a mesomorphous complex of a nonionic triblock copolymer (pluronic P123) and an anionic polyelectrolyte (polyacrylic acid) as the dynamic template. The obtained mesoporous silica materials possessed both ordered mesopores (∼7 nm) and nanopores (∼15-50 nm), and the long-range order of the mesophase was not perturbed by the embedded larger secondary nanopores. Moreover, hierarchically porous silica KIT-6 exhibited enhanced adsorption capacity in enzyme and protein immobilization, which was attributed to the hierarchically porous structure.