Grain size dependent high-pressure elastic properties of ultrafine micro/nanocrystalline grossular

We have performed sound velocity and unit cell volume measurements of three synthetic, ultrafine micro/nanocrystalline grossular samples up to 50 GPa using Brillouin spectroscopy and synchrotron X-ray diffraction. The samples are characterized by average grain sizes of 90 nm, 93 nm and 179 nm (hereinafter referred to as samples Gr90, Gr93, and Gr179, respectively). The experimentally determined sound velocities and elastic properties of Gr179 sample are comparable with previous measurements, but slightly higher than those of Gr90 and Gr93 under ambient conditions. However, the differences diminish with increasing pressure, and the velocity crossover eventually takes place at approximately 20-30 GPa. The X-ray diffraction peaks of the ultrafine micro/nanocrystalline grossular samples significantly broaden between 15-40 GPa, especially for Gr179. The velocity or elasticity crossover observed at pressures over 30 GPa might be explained by different grain size reduction and/or inhomogeneous strain within the individual grains for the three grossular samples, which is supported by both the pressure-induced peak broadening observed in the X-ray diffraction experiments and transmission electron microscopy observations. The elastic behavior of ultrafine micro/nanocrystalline silicates, in this case, grossular, is both grain size and pressure dependent.

Comparative Compressibilities of Silicate Spinels: Anomalous Behavior of (Mg,Fe)2SiO4

Compressibilities of five silicate spinels, including gamma-Mg(2)SiO(4), gamma-Fe(2)SiO(4), Ni(2)SiO(4) and two ferromagnesian compositions, were determined on crystals positioned in the same high-pressure mount. Subjection of all crystals simultaneously to the same pressure revealed differences in compressibility that resulted from compositional differences. Ferromagnesian silicate spinels showed an anomalous 13 percent increase in bulk modulus with increasing iron content, from Mg(2)SiO(4) (184 gigapascals) to Fe(2)SiO(4) (207 gigapascals). This result suggests that ferrous iron and magnesium, which behave similarly under crustal conditions, are chemically more distinct at high pressures characteristic of the transition zone and lower mantle.