Experimental and computational chemical studies on the corrosion inhibition of new pyrimidinone derivatives for copper in nitric acid

Experimental and theoretical studies of the efficiency of metal-organic frameworks (MOFs) in preventing aluminum corrosion in hydrochloric acid solution

Aluminum corrosion inhibitors "{[CuI (CN)2(phen) CuII (CN)2(phen)]5H2O},(MOF1) and {[CuI(CN)2(phen)CuII(CN)2(phen)]5H2O}@TiO2 (MOF1@TiO2) were studied in one molar HCl solution". The ML results for three different temperatures (25-45 °C) were compared with the results of PDP and EIS analyses. The adsorption of inhibitors on Al surfaces has been calculated and discussed by a Langmuir isotherm. The inhibitors that were created showed great effectiveness, with a noticeable increase in their inhibitory efficiency as the dosage was raised and the temperature was lowered. Inhibition efficiency each amounted to 88.6%, 84.5% at 400 ppm and 25 °C for MOF1@TiO2 and MOF1, respectively. Analyzing the polarization curves of synthesized inhibitors revealed that they were mixed-type inhibitors. Al was found to be surface inhibited when coated with a thin film of inhibitors, and "Al's surface morphology was assessed by different techniques such as scanning electron microscopy (SEM), energy dispersive X-ray (EDX) and atomic force microscope (AFM)". "Theoretical models like quantum chemical and molecular dynamics simulation authenticated the experimental observation". The MOFs exhibit exceptional corrosion resistance against Al when exposed to acidic environments, according to several tests.

Synthesis and Characterization of New Polymeric Ionic Liquids as Corrosion Inhibitors for Carbon Steel in a Corrosive Medium: Experimental, Spectral, and Theoretical Studies

A novel series of polymeric ionic liquids (ILs) based on benzimidazolium chloride derivatives, namely, 1,3-diheptyl-2-(2-phenyl-propyl)-3H-benzimidazol-1-ium chloride (IL1), 1,3-dioctyl-2-(2-phenyl-propyl)-3H-benzimidazol-1-ium chloride (IL2), and 1,3-Bis-decyl-2-(2-phenyl-propyl)-3H-benzoimidazol-1-ium chloride (IL3), were synthesized and chemically elucidated by Fourier transform infrared spectroscopy, 1H NMR, 13C NMR, and elemental analysis. Their influence as corrosion suppressors were investigated for C-steel corrosion in 1 M HCl, by weight loss (WL), potentiodynamic polarization (PDP), and electrochemical impedance spectroscopy (EIS) methods, revealing that their exclusive addition decreased corrosion with mounting concentrations. These assays demonstrated that novel ILs are efficient inhibitors at relatively low dosages. The efficacy of the synthesized ILs reached 79.7, 92.2 and 96.9%, respectively, at 250 ppm and 303 K. Parameters for activation and adsorption were calculated and are discussed. The Tafel polarization results demonstrated that the investigated ILs support the suppression of both cathodic and anodic reactions, acting as mixed type inhibitors. Langmuir's adsorption isotherm was confirmed as the best fitted isotherm, describing the physical-chemical adsorption capability of used ILs on the C-steel surface with the change in the free energy of adsorption, ΔG°ads = 32.6-37.2 kJ mol-1. The efficacy of the synthesized ILs was improved by increasing the doses, and the temperature reached 86.6, 96.1, and 98.4%, respectively, at 318 K. Surface morphology was proved by Fourier Transform Infrared spectroscopy, X-ray photoelectron spectroscopy, and atomic force microscopy (AFM), and then, changes in test solutions were checked by Ultraviolet-visible spectroscopy. Theoretical modeling (density functional theory and Monte Carlo) revealed the correlation between the IL's molecular chemical structure and its anticorrosive property.

Novel porphyrin derivatives as corrosion inhibitors for stainless steel 304 in acidic environment: synthesis, electrochemical and quantum calculation studies

A Novel 5,10,15,20-tetra (thiophen-2-yl) porphyrin (P1) and 5,10,15,20-tetrakis (5-Bromothiophen-2-yl) porphyrin (P2) were successfully synthesized, and their chemical structures were proved based on its correct elemental analysis and spectral data (IR and 1H-NMR). These compounds were examined as corrosion inhibitors for stainless steel 304 (SS304) in 2 M HCl utilizing mass reduction (MR) and electrochemical tests at inhibitor concentration (1 × 10-6-21 × 10-6 M). The protection efficiency (IE %) was effectively enhanced with improving the concentration of investigated compounds and reached 92.5%, 88.5% at 21 × 10-6 M for P1 & P2, respectively and decreases with raising the temperature. Langmuir's isotherm was constrained as the best fitted isotherm depicts the physical-chemical adsorption capabilities of P1 & P2 on SS304 surface with change in ΔGoads = 22.5 kJ mol-1. According to the PDP data reported, P1 and P2 work as mixed find inhibitors to suppress both cathodic and anodic processes. Porphyrin derivatives (P1 & P2) are included on the surface of SS304, according to surface morphology techniques SEM/EDX and AFM. Quantum calculations (DFT) and Monte Carlo simulation (MC) showed the impact of the chemical structure of porphyrin derivatives on their IE %.