Directing nitrogen-doped carbon support chemistry for improved aqueous phase hydrogenation catalysis

Influencing stability and performance through directing nitrogen-doping in carbon support materials.

Carbon incorporation in Pd(111) by adsorption and dehydrogenation of ethene

The decomposition of ethene on the Pd(111) surface was studied at effective pressures in the 10(-8) to 10(-7) mbar range and at sample temperatures between 300 and 700 K, using an effusive capillary array beam doser for directional adsorption, LEED, AES, temperature programmed reaction, and TDS. In the temperature range of 350-440 K increasingly stronger dehydrogenation of the ethene molecule is observed. Whereas at 350 K an ethylidyne adlayer is still present after adsorption, already at temperatures around 440 K complete coverage of the surface by carbon is attained, while the bulk still retains the properties of pure Pd. Beyond 440 K a steady-state surface C coverage is established, which decreases with temperature and is determined by detailed balancing between the ethene gas-phase adsorption rate and the migration rate of carbon into the Pd bulk. This process gives rise to the formation of a "partially carbon-covered Pd(x)C(y) surface". Above 540 K the surface-bulk diffusion of adsorbed carbon becomes fast, and in the UHV experiment the ethene adsorption rate becomes limited by the ethene gas-phase supply. The carbon bulk migration rate and the steady-state carbon surface coverage were determined as a function of the sample temperature and the ethene flux. An activation energy of 107 kJ mol(-1) for the process of C diffusion from surface adsorption sites into the subsurface region was derived in the temperature range of 400-650 K by modeling the C surface coverage as a function of temperature on the basis of steady-state reaction kinetics, assuming a first-order process for C surface-subsurface diffusion and a second-order process for C(ads) formation by dissociative C2H4 adsorption.

Surface State and Composition of a Disperse Pd Catalyst after Its Exposure to Ethylene

Pd black was exposed to ethylene alone or in its mixture with hydrogen at 300 and 573 K. The samples were investigated by X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS). Room temperature introduction of C(2)H(4) (also in the presence of H(2)) induced a binding-energy (BE) shift in the Pd 3d doublet and changed its full width at half-maximum (fwhm). The UPS features indicate shifting of electrons from the Pd d-band to Pd-H, Pd-C, and even Pd-OH species. Vinylidene (BE approximately 284.1 eV) may be the most abundant individual surface species on disperse Pd black, along with carbon in various stages of polymerization: "disordered C" (BE approximately 284 eV), graphite (approximately 284.6 eV), and ethylene polymer (approximately 286 eV), and also some "atomic" C (BE approximately 283.5 eV). Introduction of H(2) followed by ethylene brought about stronger changes in the state of Pd than exposure in the reverse sequence. This may indicate that the presence of some surface C may hinder the decomposition of bulk PdH. Formation of Pd hydride was blocked when ethylene was introduced prior to H(2). The C 1s intensity increased, the low-binding-energy C components disappeared, and graphitic carbon (BE approximately equal to 284.6 eV) prevailed after ethylene treatment at 573 K. The loss of the Pd surface state and "PdH" signal were observed in the corresponding valence band and UPS spectra. Hydrogen treatment at 540 K was not able to decrease the concentration of surface carbon and re-establish the near-surface H-rich state. UPS showed overlayer-type C in these samples. The interaction of Pd with components from the feed gas modified its electronic structure that is consistent with lattice strain induced by dissolution of carbon and hydrogen into Pd, as indicated by the d-band shift and the dilution of the electron density at E(F).