Tuning Pd-to-Ag Ratio to Enhance the Synergistic Activity of Fly Ash-Supported PdxAgy Bimetallic Nanoparticles

Fly ash (FA)-supported bimetallic nanoparticles (PdxAgy/FA) with varying Pd:Ag ratios were prepared by coprecipitation of Pd and Ag involving in situ reduction of Pd(II) and Ag(I) salts in aqueous medium. All the supported nanoparticles were thoroughly characterized with the aid of powder X-ray diffraction (PXRD), X-ray photoelectron spectroscopy (XPS), electron microscopy (field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM)), and elemental analyses, which include inductively coupled plasma-optical emission spectroscopy (ICP-OES) and energy-dispersive X-ray spectroscopy (EDS). A gradual broadening and shifting of PXRD peaks, ascribable to Ag, to higher angles with an increase in the Pd:Ag ratio affirms the alloying of interface between Pd and Ag nanoparticles. The coexistence of Pd and Ag was further confirmed by EDS elemental mapping as well as by the presence of bimetallic lattices on the FA surface, as evident from the high-resolution TEM analysis. The dependency of crystallite size and average size of bimetallic nanoparticles on Ag loading (mol %) was elucidated with the help of a combination of PXRD and TEM studies. Based on XPS analysis, the charge transfer phenomenon between contacting Pd-Ag sites could be evident from the shifting of 3d core electron binding energy for both Pd and Ag compared with monometallic Pd and Ag nanoparticles. Following a pseudo-first-order reaction kinetics, all the nanocatalysts were able to efficiently reduce 4-nitrophenol into 4-aminophenol in aqueous NaBH4. The superior catalytic performance of the bimetallic nanocatalysts (PdxAgy/FA) over their monometallic (Pd100/FA and Ag100/FA) analogues has been demonstrated. Moreover, the tunable synergistic effect of the bimetallic systems has been explored in detail by varying the Pd:Ag mol ratio in a systematic manner which in turn allowed us to achieve an optimum reaction rate (k = 1.050 min-1) for the nitrophenol reduction using a Pd25Ag75/FA system. Most importantly, all the bimetallic nanocatalysts explored here exhibited excellent normalized rate constants (K ≈ 6000-15,000 min-1 mmol-1) compared with other supported bimetallic Pd-Ag nanocatalysts reported in the literature.

Fly ash supported Pd-Ag bimetallic nanoparticles exhibiting a synergistic catalytic effect for the reduction of nitrophenol

Coal fly ash (FA) supported Pd-Ag bimetallic nanoparticles (FA-Pd-Ag) were prepared by reducing Pd(II) and Ag(I) salts together onto the dispersed solid support in aqueous medium. Electron microscope analysis (FE-SEM, HRTEM) in combination with elemental mapping (EDS) suggests that the nanoparticles are well dispersed on fly ash with an average diameter of 6-8 nm. The powder XRD analysis indicates that alloying of the interface occurs between Pd and Ag nanoparticles in FA-Pd-Ag, while XPS reveals that charge transfer takes place between the Pd and Ag moieties that come into contact with each other. The FA-Pd-Ag in aqueous NaBH4 solution exhibits an efficient catalytic reduction of 4-nitrophenol into 4-aminophenol and follows pseudo-first-order reaction kinetics (kPd-Ag = 0.7176 min-1). The higher rate constant for FA-Pd-Ag compared to that for their monometallic analogues (FA-Pd (kPd = 0.5449 min-1)) and (FA-Ag (kAg = 0.5572 min-1)) as well as their physical mixture ((FA-Pd + FA-Ag) (kPd+Ag = 0.4075 min-1)) suggests the synergistic catalytic effect of the bimetallic system. Moreover, the present bimetallic nanocatalyst exhibits the highest normalized rate constant (KPd-Ag ≈ 51 100 min-1 mmol-1) compared to the reported bimetallic Pd-Ag nanocatalysts.

Preparation and catalytic performance of a molecularly imprinted Pd complex catalyst for Suzuki cross-coupling reactions

A molecularly imprinted Pd complex catalyst was successfully designed and prepared on a SiO₂ surface for shape-selective Suzuki cross-coupling reaction.