Synthesis of Imidazole-Compound-Coated Copper Nanoparticles with Promising Antioxidant and Sintering Properties

In this study, we present a facile method for preparing oxidation-resistant Cu nanoparticles through a liquid-phase reduction with imidazole compounds (imidazole, 2-methylimidazole, 2-phenylimidazole, and benzimidazole) that serve as protective and dispersing agents. Through a complexation reaction between Cu atoms, the imidazole compounds can form a protective film on the Cu nanoparticles to prevent the particles from rapidly oxidizing. We compared the effects of the four kinds of imidazole compounds on the oxidation resistance and sintering properties of Cu particles. The Cu particles prepared with benzimidazole could be stored in the air for 30 days without being oxidized. After sintering at 300 °C and 2 MPa, the joint of the particles could reach a shear strength of 32 MPa, which meets the requirements for microelectronic packaging.

Transparent Electronics for Wearable Electronics Application

Recent advancements in wearable electronics offer seamless integration with the human body for extracting various biophysical and biochemical information for real-time health monitoring, clinical diagnostics, and augmented reality. Enormous efforts have been dedicated to imparting stretchability/flexibility and softness to electronic devices through materials science and structural modifications that enable stable and comfortable integration of these devices with the curvilinear and soft human body. However, the optical properties of these devices are still in the early stages of consideration. By incorporating transparency, visual information from interfacing biological systems can be preserved and utilized for comprehensive clinical diagnosis with image analysis techniques. Additionally, transparency provides optical imperceptibility, alleviating reluctance to wear the device on exposed skin. This review discusses the recent advancement of transparent wearable electronics in a comprehensive way that includes materials, processing, devices, and applications. Materials for transparent wearable electronics are discussed regarding their characteristics, synthesis, and engineering strategies for property enhancements. We also examine bridging techniques for stable integration with the soft human body. Building blocks for wearable electronic systems, including sensors, energy devices, actuators, and displays, are discussed with their mechanisms and performances. Lastly, we summarize the potential applications and conclude with the remaining challenges and prospects.

Copper micro/nanoparticles based catalytic conversion of 4-nitrobenzaldehyde to 4-nitrobenzoic acid

Copper nanoparticles (CuNPs) have generated a great deal of interest in recent years, especially in catalysis are one of the promising materials in the advancement of copper-based technological applications. We synthesized copper nanoparticles through chemical reduction method using L- ascorbic acid at two different quantities and their spherical and flower like morphologies revealed by FE-SEM. This study also augmented with the catalytic conversion of 4-nitrobenzaldehyde to 4-nitrobenzoic acid using stated copper nanoparticles as a heterogeneous catalyst. Kinetic studies on the conversion of 4-nitrobenzaldehyde to 4-nitrobenzoic acid with time intervals of 30 min up to 180 min revealed the time required for the completion of the reaction. 1H NMR corroborated the product so obtained by the use of CuNPs as a catalyst, and ATR-IR analysis. A simple method of melting point exploited here to confirm the final product is a value-added. Thus, this simple analytical tool can boost the morale of researchers with limited resources in graduate and post-graduate laboratories.

Biosynthesis of copper nanoparticles using aqueous Tilia extract: antimicrobial and anticancer activities

A cost-effective method for the biosynthesis of copper nanoparticles (Cu-NPLs) using Tilia extract under optimum conditions has been presented. The use of Tilia extracts for the synthesis of Cu-NPLs has been investigated for the first time. The Cu-NPLs are stable due to in situ bio-capping by the Tilia extract residues. Formation of metallic Cu was revealed by UV-vis and XRD analyses. UV-vis of Cu-NPLs showed an SPR characteristic peak at 563 nm (energy bandgap = 2.1 eV). Morphology and size of the as-prepared Cu-NPLs were determined using SEM and TEM studies. TEM observations show that the produced Cu-NPLs are hemispherical in shape with different diameters in the range 4.7-17.4 nm. The electrical conductivity of the Cu-NPLs was determined as 1.04 × 10-6 S cm-1 (at T = 120 K). The antimicrobial studies exhibited relatively high activity against pathogenic bacteria like Gram-positive & Gram-negative bacteria. Anticancer studies demonstrated the in vitro cytotoxicity value of Cu-NPLs against tested human colon cancer Caco-2 cells, human hepatic cancer HepG2 cells and human breast cancer Mcf-7 cells. To conclude, Cu-NPLs are promising in electronic devices and they possess a potential anticancer application for some human cancer therapy as well.

Integration of polyelectrolyte enhanced ultrafiltration and chemical reduction for metal-containing wastewater treatment and metal recovery

Chemical reduction was firstly employed to treat synthetic wastewaters of various compositions prepared to simulate the retentate stream of polyelectrolyte enhanced ultrafiltration (PEUF). With fixed Cu:polyethylenimine (PEI) monomer:dithionite molar ratio, increasing copper concentration increases copper removal efficiency. Under fixed Cu:dithionite molar ratio and fixed Cu concentration, increasing PEI monomer:copper molar ratio decreases copper removal efficiency. The formation of nano-sized copper particles, which readily pass through 0.45 μm filter used for sample pretreatment before residual copper analysis, might be the reason behind the decreasing copper removal efficiency observed. Particle size analysis shows that the size of copper particles, which are formed through reduction reaction, increases with decreasing pH value and increasing reaction time. As ultrafiltration is capable of removing these nano-sized particles, integration of chemical reduction and PEUF is proposed to simultaneously achieve regeneration of polyelectrolyte and recovery of copper in one process. Results show that the proposed process could achieve almost complete copper removal without being affected by reaction pH.

Recovery of Cu(II) by chemical reduction using sodium dithionite: effect of pH and ligands

Wastewaters containing Cu(II) and ligands are ubiquitous in various industrial sectors, and efficacy of copper removal processes, especially precipitation, is greatly compromised by ligands. Chemical reduction, being commonly employed for production of metal nanoparticles, is also effective for metal removal. Adjustment of pH and addition of ligands are important to control the particle size in metallic nanoparticle production. Exploiting the fact that ligands and metals coexist in many wastewaters, chemical reduction was employed to treat ligand-containing wastewater in this study. The experimental result shows that depending on pH, type of ligands, and copper:ligand molar ratio, copper could be removed by either the reduction or precipitation mechanism. Almost complete copper removal could be achieved by the reduction mechanism under optimal condition for solutions containing either EDTA (ethylenediaminetetraacetic acid) or citrate ligands. For solutions containing ammonia, depending on pH and Cu:ammonia molar ratio, copper was removed by both precipitation and reduction mechanisms. At pH of 9.0, formation of nano-sized particles, which readily pass through a 0.45 μm filter used for sample pretreatment before residual copper analysis, results in the lowest copper removal efficiency. Both cuprous oxide and metallic copper are identified in the solids produced, and the possible explanations are provided.