Wellbore Stability through Novel Catechol-Chitosan Biopolymer Encapsulator-Based Drilling Mud

The problem of wellbore stability has a marked impact on oil and gas exploration and development in the process of drilling. Marine mussel proteins can adhere and encapsulate firmly on deep-water rocks, providing inspiration for solving borehole stability problem and this ability comes from catechol groups. In this paper, a novel biopolymer was synthesized with chitosan and catechol (named “SDGB”) by Schiff base-reduction reaction, was developed as an encapsulator in water-based drilling fluids (WBDF). In addition, the chemical enhancing wellbore stability performance of different encapsulators were investigated and compared. The results showed that there were aromatic ring structure, amines, and catechol groups in catechol-chitosan biopolymer molecule. The high shale recovery rate demonstrated its strong shale inhibition performance. The rock treated by catechol-chitosan biopolymer had higher tension shear strength and uniaxial compression strength than others, which indicates that it can effectively strengthen the rock and bind loose minerals in micro-pore and micro-fracture of rock samples. The rheological and filtration property of the WBDF containing catechol-chitosan biopolymer is stable before and after 130 °C/16 h hot rolling, demonstrating its good compatibility with other WBDF agents. Moreover, SDGB could chelate with metal ions, forming a stable covalent bond, which plays an important role in adhesiveness, inhibition, and blockage.

Study on the Shale Hydration Inhibition Performance of Triethylammonium Acetate

Shale inhibitor is an additive for drilling fluids that can be used to inhibit shale hydration expansion and dispersion, and prevent wellbore collapse. Small molecular quaternary ammonium salt can enter the interlayer of clay crystal, and enables an excellent shale inhibition performance. In this paper, a novel ionic shale inhibitor, triethylammonium acetate (TEYA), was obtained by solvent-free synthesis by using acetic acid and triethylamine as raw materials. The final product was identified as the target product by Fourier transform infrared spectroscopy (FT-IR). The inhibition performance of TEYA was studied by the mud ball immersion test, linear expansion test, rolling recovery test and particle size distribution test. The results demonstrated that the shale inhibitor shows a good shale hydration inhibition performance. The inhibition mechanism was studied by FT-IR and X-ray diffraction (XRD), respectively; the results showed that triethylammonium acetate TEYA could enter the crystal layer of clay and inhibit it through physical adsorption.

The Inhibition Property and Mechanism of a Novel Low Molecular Weight Zwitterionic Copolymer for Improving Wellbore Stability

In this work, a novel low molecular weight zwitterionic copolymer for improving wellbore stability, which is expected to be an alternative to the current shale inhibitors, was obtained by copolymerization of tris hydroxyethyl allyl ammonium bromide (THAAB), 2-acrylamido-2- methyl propane sulfonic acid (AMPS) and acrylamide (AM), initiated by a redox initiation system in an aqueous solution. The copolymer, denoted as SX-1, was characterized by FT-IR, TGA-DSC, and GPC. Results demonstrated that the molecular weight of SX-1 was approximately 13,683 g/mol and it displayed temperature resistance up to 225 °C. Regarding the inhibition performance, evaluation experiments showed the hot rolling recovery of a Longmaxi shale sample in 2.0 wt % SX-1 solutions was up to 90.31% after hot rolling for 16 h at 120 °C. The Linear swelling height of Na-MMT artificial core in 2.0 wt % SX-1 solution was just 4.74 mm after 16 h. Methods including particle size analysis, FTIR, XRD, and SEM were utilized to study the inhibition mechanism of SX-1; results demonstrated that SX-1 had entered into the inner layer of sodium montmorillonite (Na-MMT) and adsorbed on the inner surface, and the micro-structure of Na-MMT was successfully changed by SX-1. The particle size of Na-MMT in distilled water was 8.05 μm, and it was observed that its size had increased to 603 μm after the addition of 2.0 wt % of SX-1. Its superior properties make this novel low molecular weight copolymer promising for ensuring wellbore stability, particularly for high temperature wells.

Ultrafast igniting, imidazolium based hypergolic ionic liquids with enhanced hydrophobicity

Exploring ultrafast igniting and hydrolytically stable ionic liquids (ILs) has a wide scope in hypergolic rocket fuels.