Recent Progress on Engineering Highly Efficient Porous Semiconductor Photocatalysts Derived from Metal-Organic Frameworks

Porous structures offer highly accessible surfaces and rich pores, which facilitate the exposure of numerous active sites for photocatalytic reactions, leading to excellent performances. Recently, metal-organic frameworks (MOFs) have been considered ideal precursors for well-designed semiconductors with porous structures and/or heterostructures, which have shown enhanced photocatalytic activities. In this review, we summarize the recent development of porous structures, such as metal oxides and metal sulfides, and their heterostructures, derived from MOF-based materials as catalysts for various light-driven energy-/environment-related reactions, including water splitting, CO₂ reduction, organic redox reaction, and pollution degradation. A summary and outlook section is also included.

Efficient degradation of atrazine by BiOBr/UiO-66 composite photocatalyst under visible light irradiation: Environmental factors, mechanisms and degradation pathways

Atrazine, a typical herbicide, has caused extensive concern due to its wide application and persistance. In this work, a visible light responsive photocatalyst BiOBr/UiO-66 was synthesized and applied to the degradation of atrazine. The BiOBr/UiO-66 materials exhibited significantly enhanced photocatalytic performance on the degradation of atrazine under visible light irradiation compared to pure BiOBr. Moreover, the effects of typical environment factors (i.e. pH, common anions, inorganic cations and water matrix) on the degradation of atrazine were investigated extensively. Results showed that atrazine was degraded with the fastest rate at the strong acidity conditions of pH = 3.1 in the investigated pH region (3.1-9.4). The photocatalytic degradation of atrazine was obviously inhibited by HCO₃^- and SO₄^2-. However, Cl^- had negligible influence on the degradation of atrazine. Inorganic cations had little influence on the degradation of atrazine. Futhermore, the water matrix showed apparent impacts on the photocatalytic degradation of atrazine by BiOBr/UiO-66. In mineral water, tap water and river water, the removal efficiency of atrazine was evidently lower than that in pure water. The main active species that responsible for the degradation of atrazine by BiOBr/UiO-66 were determined to be ·O₂^- and h⁺. Ultimately, the degradation pathways of atrazine were proposed based on the intermediates detected by LC-MS/MS.

In6S7 nanoparticle-embedded and sulfur and nitrogen co-doped microporous carbons derived from In(tdc)2 metal-organic framework

Indium sulfide nanoparticle (NP)-embedded microporous carbons co-doped with S- and N-dopants are easily prepared by a direct carbonization of the as-prepared In(iii)-based metal-organic framework (In-MOF), [Et₂NH₂][In(tdc)₂]·DEF, containing ditopic S-containing 2,5-thiophenedicarboxylate (tdc^2-) bridging linkers as a potential source of S-dopant. The charge on the anionic framework of [In(tdc)₂]^- is balanced by Et₂NH₂⁺, which is also a potential N-dopant. Simultaneous embedding of In-based NPs, S-, and N-co-doping is achieved in a simple single step carbonization of In-MOF. Three porous carbon materials (PCMs), PCM-700, PCM-800, and PCM-900, are obtained from the carbonization of In-MOF at 700, 800, and 900 °C, respectively. The gas sorption analysis indicates them as good CO₂ sorbents. The photocatalytic degradation of methyl orange by PCMs under visible light irradiation is also effectively operable owing to the photocatalytically active semiconducting indium sulfide NP with a small bandgap. The main component of indium sulfide NPs is revealed as In₆S₇ based on the powder X-ray diffraction pattern. Small amounts of metallic In and In₂S₃ are also observed. The specific capacitances of PCMs are also estimated from the galvanostatic charge/discharge curves. PCM-900 exhibits the highest gravimetric specific capacitance of 99.0 F g^-1 at a current density of 0.05 A g^-1.

Ferrocene particles incorporated into Zr-based metal–organic frameworks for selective phenol hydroxylation to dihydroxybenzenes

Ferrocene@UiO-66 exhibited high catalytic activity for phenol hydroxylation with H₂O₂ at room temperature in water.

Highly Porous Carbon Derived from MOF-5 as a Support of ORR Electrocatalysts for Fuel Cells

The development of highly competent electrocatalysts for the sluggish oxygen reduction reaction (ORR) at cathodes of proton-exchange membrane fuel cells (PEMFCs) is extremely important for their long-term operation and wide applications. Herein, we present highly efficient ORR electrocatalysts based on Pt/Ni bimetallic nanoparticles dispersed on highly porous carbon obtained via pyrolysis of a metal-organic framework MOF-5. In comparison to the commercial Pt/C (20%), the electrocatalyst Pt-Ni/PC 950 (15:15%) in this study exhibits a pronounced positive shift of 90 mV in Eonset. In addition, it also demonstrates excellent long-term stability and durability during the 500-cycle continue-oxygen-supply (COS) accelerating durability tests (ADTs). The significantly improved activity and stability of Pt-Ni/PC 950 (15:15%) can be attributed to the Pt electron interaction with Ni and carbon support as has been proved in X-ray and microscopic analysis.