Self-Healable Antifouling Zwitterionic Hydrogel Based on Synergistic Phototriggered Dynamic Disulfide Metathesis Reaction and Ionic Interaction

A self-healable antifouling hydrogel based on zwitterionic block copolymer was prepared via reversible addition-fragmentation chain transfer polymerization and Diels-Alder "click" chemistry. The hydrogel consists of a core-cross-linked zwitterionic block copolymer having poly(furfuryl methacrylate) as core and poly(dimethyl-[3-(2-methyl-acryloylamino)-propyl]-(3-sulfopropyl)ammonium) (poly(sulfobetaine)) as shell. The core was cross-linked with dithiobismaleimidoethane. The block copolymers were characterized by dynamic light scattering, field emission scanning electron microscopy, high-resolution transmission electron microscopy, atomic force microscopy (AFM), differential scanning calorimetry, water contact angle, and small-angle X-ray scattering analyses. This zwitterionic hydrogel showed self-healing activity via combined effect of phototriggered dynamic disulfide metathesis reaction and zwitterionic interaction, which was monitored by optical microscopy and AFM depth profilometry. The mechanical properties of the hydrogel before and after self-healing were studied using depth-sensing nanoindentation method. It was observed that the prepared zwitterionic hydrogel could reduce the formation of biofilm, which was established by studying the bovine serum albumin (model protein) adsorption over the coating. This multifunctional hydrogel can pave a new direction in antifouling self-healable gel coating applications.

Thermo-reversible self-healing in a fluorous crosslinked copolymer

Self-healing in a fluorous copolymer material enhances its safety index and extends its working lifetime.

A new class of dual responsive self-healable hydrogels based on a core crosslinked ionic block copolymer micelle prepared via RAFT polymerization and Diels-Alder "click" chemistry

Amphiphilic diblock copolymers of poly(furfuryl methacrylate) (PFMA) with cationic poly(2-(methacryloyloxy)ethyltrimethyl ammonium chloride) (PFMA-b-PMTAC) and anionic poly(sodium 4-vinylbenzenesulfonate) (PFMA-b-PSS) were prepared via reversible addition fragmentation chain-transfer (RAFT) polymerization by using PFMA as a macro-RAFT agent. The formation of the block copolymer was confirmed by FTIR and ¹H NMR analyses. In water, the amphiphilic diblock copolymers, (PFMA-b-PMTAC) and (PFMA-b-PSS), formed micelles with PFMA in the core and the rest of the hydrophilic polymers like PMTAC and PSS in the corona. The PFMA core was crosslinked by using Diels-Alder (DA) "Click" chemistry in water at 60 °C where bismaleimide acted as a crosslinker. Afterwards, both the core crosslinked micelles were mixed at an almost equal charge ratio which was determined by zeta potential analysis to prepare the self-assembled hydrogel. The de-crosslinking of the hydrophobic PFMA core in the self-assembled hydrogel via rDA reaction took place at 165 °C as determined from DSC analysis. This hydrogel showed self-healing behavior using ionic interaction (in the presence of water) and DA chemistry (in the presence of heat).

Dynamic covalent polymers

This Highlight presents an overview of the rapidly growing field of dynamic covalent polymers. This class of polymers combines intrinsic reversibility with the robustness of covalent bonds, thus enabling formation of mechanically stable, polymer-based materials that are responsive to external stimuli. It will be discussed how the inherent dynamic nature of the dynamic covalent bonds on the molecular level can be translated to the macroscopic level of the polymer, giving access to a range of applications, such as stimuli-responsive or self-healing materials. A primary distinction will be made based on the type of dynamic covalent bond employed, while a secondary distinction will be based on the consideration whether the dynamic covalent bond is used in the main chain of the polymer or whether it is used to allow side chain modification of the polymer. Emphasis will be on the chemistry of the dynamic covalent bonds present in the polymer, in particular in relation to how the specific (dynamic) features of the bond impart functionality to the polymer material, and to the conditions under which this dynamic behavior is manifested. © 2016 The Authors. Journal of Polymer Science Part A: Polymer Chemistry Published by Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016, 54, 3551-3577.