Interaction of Poly L-Lactide and Tungsten Disulfide Nanotubes Studied by in Situ X-ray Scattering during Expansion of PLLA/WS2NT Nanocomposite Tubes

In situ synchrotron X-ray scattering was used to reveal the transient microstructure of poly(L-lactide) (PLLA)/tungsten disulfide inorganic nanotubes (WS₂NTs) nanocomposites. This microstructure is formed during the blow molding process (“tube expansion”) of an extruded polymer tube, an important step in the manufacturing of PLLA-based bioresorbable vascular scaffolds (BVS). A fundamental understanding of how such a microstructure develops during processing is relevant to two unmet needs in PLLA-based BVS: increasing strength to enable thinner devices and improving radiopacity to enable imaging during implantation. Here, we focus on how the flow generated during tube expansion affects the orientation of the WS₂NTs and the formation of polymer crystals by comparing neat PLLA and nanocomposite tubes under different expansion conditions. Surprisingly, the WS₂NTs remain oriented along the extrusion direction despite significant strain in the transverse direction while the PLLA crystals (c-axis) form along the circumferential direction of the tube. Although WS₂NTs promote the nucleation of PLLA crystals in nanocomposite tubes, crystallization proceeds with largely the same orientation as in neat PLLA tubes. We suggest that the reason for the unusual independence of the orientations of the nanotubes and polymer crystals stems from the favorable interaction between PLLA and WS₂NTs. This favorable interaction leads WS₂NTs to disperse well in PLLA and strongly orient along the axis of the PLLA tube during extrusion. As a consequence, the nanotubes are aligned orthogonally to the circumferential stretching direction, which appears to decouple the orientations of PLLA crystals and WS₂NTs.

Supramolecular Interactions in Hybrid Polylactide Blends-The Structures, Mechanisms and Properties

The conformation of polylactide (PLA) chains can be adjusted by supramolecular interactions (the formation of hydrogen bonds or host-guest complexes) with appropriate organic molecules. The structures formed due to those intermolecular interactions may act as crystal nuclei in the PLA matrix ("soft templating"). In this review, the properties of several supramolecular nucleating systems based on synthetic organic nucleators (arylamides, hydrazides, and 1,3:2,4-dibenzylidene-d-sorbitol) are compared to those achieved with biobased nucleating agents (orotic acid, humic acids, fulvic acids, nanocellulose, and cyclodextrins) that can also improve the mechanical properties of PLA. The PLA nanocomposites containing both types of nucleating agents/additives are discussed and evaluated in the context of their biomedical applicability.

Effect of loadings of nanocellulose on the significantly improved crystallization and mechanical properties of biodegradable poly(ε-caprolactone)

Biodegradable poly(ε-caprolactone) (PCL)/nanocellulose (NC) nanocomposites were prepared using solvent-free melt processing techniques with various NC contents. Both the nonisothermal and isothermal melt crystallization processes of PCL/NC nanocomposites were significantly accelerated by adding NC. The nonisothermal melt crystallization peak temperature obviously increased from 18.8 °C for neat PCL to 30.9 °C for the PCL/NC nanocomposite with 10 wt% NC content at a cooling rate of 10 °C min^-1; moreover, the half-time isothermal crystallization at 40 °C significantly decreased from 12.2 min for neat PCL to 2.0 min. Apparently, NC enhanced PCL's crystallization rate. The crystalline morphology study confirmed the increased nucleation density of PCL spherulites, indicating the role of NC as an efficient nucleating agent. Moreover, the loading of NC did not change the crystal structure of PCL, and with increase in NC content, the Young's modulus and yield strength increased; however, the elongation-at-break and the breaking strength decreased. Compared with pure PCL, the thermomechanical properties of PCL/NC nanocomposites were significantly improved. These biodegradable PCL/NC nanocomposites showed excellent crystallization capabilities and tailored mechanical properties, thus proving their potential as a substitute for traditional commercial plastics.

Enhancement of the properties of biosourced poly(3-hydroxybutyrate-co-4-hydroxybutyrate) by the incorporation of natural orotic acid

The aim of this study is to use natural orotic acid (OA) as a sustainable, environmentally friendly additive to improve the crystallization, rheological, thermal, mechanical, and biodegradation properties of bacterially synthesized poly(3-hydroxybutyrate-co-4-hydroxybutyrate) (P34HB). OA was found to be an efficient nucleating agent for P34HB, and dramatically enhanced both non-isothermal and isothermal crystallization rates. The incorporation of OA increased nucleation density and decreased spherulite size, but had little effect on the crystalline structure. The rheological properties of the P34HB were greatly improved by the solid filler OA, particularly when a percolation network structure was formed in the blends. The thermal stability of P34HB was strongly enhanced, as exemplified by the ~23 °C increase in the onset thermal decomposition temperature (T_o) for the blend loaded with 5 wt% OA compared to that of pure P34HB. Moreover, the yield strength and elongation at break of P34HB containing 0.5 wt% OA increased by 25% and 119%, respectively. The most intriguing result was the clear enhancement in the enzymatic hydrolysis rates of the P34HB/OA blends compared to that of neat P34HB. The synergetic improvement in these properties may be of significant importance for the wider practical application of biosourced P34HB.

N, N’-sebacic bis(hydrocinnamic acid) dihydrazide: A crystallization accelerator for poly(L-lactic acid)

Developing more organic nucleating agent with different molecular structure is very instructive to improve the crystallization of poly(L-lactic acid) (PLLA) and explore the crystallization mechanism. In this study, N, N’-sebacic bis(hydrocinnamic acid) dihydrazide (HAD) was synthesized to serve as a nucleating agent for PLLA. The effects of HAD on the non-isothermal crystallization, melting behavior, thermal stability and optical performance of PLLA were investigated by differential scanning calorimeter (DSC), thermogravimetric analysis (TGA), and light transmittance meter. The melt crystallization behavior showed that HAD was able to promote the crystallization of PLLA via heterogenous nucleation in cooling, and it was found that, upon the cooling of 1°C/min, the incorporation of 1 wt% HAD made the crystallization temperature and non-isothermal crystallization enthalpy increase from 94.5°C and 0.1 J/g to 131.6°C and 48.5 J/g comparing with the pure PLLA. Additionally, the melt crystallization significantly depended on the cooling rate and the final melting temperature. For the cold crystallization, when the nucleation density from HAD and PLLA itself was saturated, the influence of the HAD concentration on the cold crystallization process of the PLLA/HAD samples is negligible. The melting behavior after isothermal or non-isothermal crystallization further confirmed the crystallization accelerating effect of HAD for PLLA, and the appearance of the double melting peaks was attributed to the melting-recrystallization. Unfortunately, the addition of HAD decreased the thermal stability and light transmittance of PLLA.