Poly(butylene succinate-co-terephthalate) nanofibrous membrane composited with cyclodextrin polymer for superhydrophilic property

The Relationship between Microstructure and Mechanical Properties of PBST Two-Component Crystalline Random Copolymers with Different BT Contents

The mechanical properties of two-component crystalline random copolymers are primarily based on their microstructure. At the same time, the influence of the composition on the crystallization behavior and crystal structure of these materials is also well known. Thus, in this study, a poly (butylene succinate-co-butylene terephthalate) random copolymer (PBST) with different molar ratios of butylene terephthalate (BT) was prepared. A systematic analysis of the crystallization behavior, crystal structure, and mechanical properties of PBST with different BT contents was carried out using WAXD, SAXS, and DSC analyses. The investigations showed that PBST-37.5 containing 37.5 mol% of BT content had the lowest strength and highest elasticity among the different compositions. This was because the two-component crystallization of poly (butylene terephthalate) (PBT) and poly (butylene succinate) (PBS) was greatly inhibited at the corresponding BT composition and the crystal growth was the least perfect, imparting poor strength to the PBT-37.5. Alternately, when the content of BT was 32.5 mol% in the PBST, the PBS segment could crystallize, and both PBT and PBS crystals were formed in the PBST-32.5. Thus, PBST-32.5 showed a higher material hardness than PBST-37.5. In contrast, when the BT content was greater than 37.5 mol% in the PBST, only PBT crystals existed in the PBST copolymer. Further, as the BT content increased, the crystal size of PBT gradually increased, which led to a closer packing of the crystal arrangement, increasing the crystallinity. This led to a gradual increase in the strength of the PBST material and a gradual decrease in its elasticity.

Enzymatic Degradation of Acrylic Acid-Grafted Poly(butylene succinate-co-terephthalate) Nanocomposites Fabricated Using Heat Pressing and Freeze-Drying Techniques

Biodegradable acrylic acid-grafted poly(butylene succinate-co-terephthalate) (g-PBST)/organically modified layered zinc phenylphosphonate (m-PPZn) nanocomposites were effectively fabricated containing covalent bonds between the g-PBST and m-PPZn. The results of wide-angle X-ray diffraction and transmission electron microscopy revealed that the morphology of the g-PBST/m-PPZn nanocomposites contained a mixture of partially exfoliated or intercalated conformations. The isothermal crystallization behavior of the nanocomposites showed that the half-time for crystallization of 5 wt % g-PBST/m-PPZn nanocomposites was less than 1 wt % g-PBST/m-PPZn nanocomposites. This finding reveals that increasing the loading of m-PPZn can increase the crystallization rate of nanocomposites. Degradation tests of g-PBST/m-PPZn nanocomposites fabricated using the heat pressing and the freeze-drying process were performed by lipase from Pseudomonas sp. The degradation rates of g-PBST-50/m-PPZn nanocomposites were significantly lower than those of g-PBST-70/m-PPZn nanocomposites. The g-PBST-50 degraded more slowly due to the higher quantity of aromatic group and increased stiffness of the polymer backbone. The degradation rate of the freeze-drying specimens contained a more extremely porous conformation compared to those fabricated using the heat pressing process.

Aliphatic Polyester Nanofibers Functionalized with Cyclodextrins and Cyclodextrin-Guest Inclusion Complexes

The fabrication of nanofibers by electrospinning has gained popularity in the past two decades; however, only in this decade, have polymeric nanofibers been functionalized using cyclodextrins (CDs) or their inclusion complexes (ICs). By combining electrospinning of polymers with free CDs, nanofibers can be fabricated that are capable of capturing small molecules, such as wound odors or environmental toxins in water and air. Likewise, combining polymers with cyclodextrin-inclusion complexes (CD-ICs), has shown promise in enhancing or controlling the delivery of small molecule guests, by minor tweaking in the technique utilized in fabricating these nanofibers, for example, by forming core⁻shell or multilayered structures and conventional electrospinning, for controlled and rapid delivery, respectively. In addition to small molecule delivery, the thermomechanical properties of the polymers can be significantly improved, as our group has shown recently, by adding non-stoichiometric inclusion complexes to the polymeric nanofibers. We recently reported and thoroughly characterized the fabrication of polypseudorotaxane (PpR) nanofibers without a polymeric carrier. These PpR nanofibers show unusual rheological and thermomechanical properties, even when the coverage of those polymer chains is relatively sparse (~3%). A key advantage of these PpR nanofibers is the presence of relatively stable hydroxyl groups on the outer surface of the nanofibers, which can subsequently be taken advantage of for bioconjugation, making them suitable for biomedical applications. Although the number of studies in this area is limited, initial results suggest significant potential for bone tissue engineering, and with additional bioconjugation in other areas of tissue engineering. In addition, the behaviors and uses of aliphatic polyester nanofibers functionalized with CDs and CD-ICs are briefly described and summarized. Based on these observations, we attempt to draw conclusions for each of these combinations, and the relationships that exist between their presence and the functional behaviors of their nanofibers.