Alkali/alkaline-earth metal-modified MnOx supported on three-dimensionally ordered macroporous-mesoporous TixSi1-xO2 catalysts: Preparation and catalytic performance for soot combustion

The performance of catalysts used in after-treatment systems is the key factor for the removal of diesel soot, which is an important component of atmospheric fine particle emissions. Herein, three-dimensionally ordered macroporous-mesoporous Ti_xSi_1-xO₂ (3DOM-m Ti_xSi_1-xO₂) and its supported MnO_x catalysts doped with different alkali/alkaline-earth metals (AMnO_x/3DOM-m Ti_0.7Si_0.3O₂ (A: Li, Na, K, Ru, Cs, Mg, Ca, Sr, Ba)) were prepared by mesoporous template (P123)-assisted colloidal crystal template (CCT) and incipient wetness impregnation methods, respectively. Physicochemical characterizations of the catalysts were performed using scanning electron microscopy, X-ray diffraction, N₂ adsorption-desorption, H₂ temperature-programmed reduction, O₂ temperature-programmed desorption, NO temperature-programmed oxidation, and Raman spectroscopy techniques; then, we evaluated their catalytic performances for the removal of diesel soot particles. The results show that the 3DOM-m Ti_0.7Si_0.3O₂ supports exhibited a well-defined 3DOM-m nanostructure, and AMnO_x nanoparticles with 10-50 nm were evenly dispersed on the inner walls of the uniform macropores. In addition, the as-prepared catalysts exhibited good catalytic performance for soot combustion. Among the prepared catalysts, CsMnO_x/3DOM-m Ti_0.7Si_0.3O₂ had the highest catalytic activity for soot combustion, with T₁₀, T₅₀, and T₉₀ (the temperatures corresponding to soot conversion rates of 10%, 50%, and 90%) values of 285, 355, and 393°C, respectively. The high catalytic activity of the CsMnO_x/3DOM-m Ti_0.7Si_0.3O₂ catalysts was attributed to their excellent low-temperature reducibility and homogeneous macroporous-mesoporous structure, as well as to the synergistic effects between Cs and Mn species and between CsMnO_x and the Ti_0.7Si_0.3O₂ support.

Effect of oxygen vacancy and highly dispersed MnOx on soot combustion in cerium manganese catalyst

Cerium manganese bimetallic catalysts have become the focus of current research because of their excellent catalytic performance for soot combustion. Two series of cerium manganese catalysts (Na-free catalysts and Na-containing catalysts) were prepared by coprecipitation method and characterized using XRD, N₂ adsorption-desorption, SEM, Raman, XPS, H₂-TPR, O₂-TPD, Soot-TPR-MS and in situ IR. The effects of abundant oxygen vacancies and surface highly dispersed MnO_x on soot catalytic combustion of cerium manganese catalysts prepared by different precipitants were analyzed. The activity test results show that the active oxygen species released by a large number of oxygen vacancies in the cerium manganese catalyst are more favorable to the soot catalytic combustion than MnO_x which is highly dispersed on the surface of the catalyst and has good redox performance at low temperature. Because the catalytic effect of MnO_x on the surface of Na-free catalysts is more dependent on the contact condition between the catalyst and the soot, this phenomenon can be observed more easily under the loose contact condition than under the tight contact condition. The activity cycle test results show that these two series of catalysts show good stability and repeated use will hardly cause any deactivation of the catalysts.

Preparation of K Modified Three-Dimensionally Ordered Macroporous MnCeOx/Ti0.7Si0.3O2 Catalysts and Their Catalytic Performance for Soot Combustion

Soot particles in diesel engine exhaust is one of the main reasons for hazy weather and elimination of them is urgent for environmental protection. At present, it is still a challenge to develop new catalysts with high efficiency and low cost. In this paper, a kind of K modified three-dimensionally ordered macroporous (3DOM) MnCeOx/Ti0.7Si0.3O2 catalysts are designed and synthesized by a sample method. Due to the macroporous structure and synergistic effect of K, Mn, and Ce, the KnMnCeOx/Ti0.7Si0.3O2 (KnMnCeOx/M-TSO) catalysts exhibit good catalytic performance for soot combustion. The catalytic activity of K0.5MnCeOx/M-TSO was the best, and the T10, T50, and T90 are 287, 336, and 367 °C, respectively. After the prepared catalyst was doped with K, the physicochemical properties and catalytic performance changed significantly. In addition, the K0.5MnCeOx/M-TSO catalyst also somewhat exhibits sulfur tolerance owing to it containing Ti. Because of its simple synthesis, high activity, and low cost, the prepared KnMnCeOx/M-TSO catalysts are regarded as a promising candidate for application.

Construction of a hollow structure in La0.9K0.1CoO3−δ nanofibers via grain size control by Sr substitution with an enhanced catalytic performance for soot removal

The hollow structure is formed by Sr²⁺ doping in La_0.9K_0.1CoO_3−δ nanofibers for decreasing the grain size, which can improve the contact efficiency of soot–catalyst–gas as well as the intrinsic activity, responsible for the enhancement in activity.