Elastic and Conductive Cross-linked Anion Exchange Membranes Based on Polyphenylene Oxide and Poly(vinyl alcohol) for H2 -O2 Fuel Cells

A series of cross-linked AEMs (c-DQPPO/PVA) are synthesized by using rigid polyphenylene oxide and flexible poly(vinyl alcohol) as the backbones. Dual cations are grafted on the PPO backbone to improve the ion exchange capacity (IEC), while glutaraldehyde is introduced to enhance compatibility and reduce swelling ratio of AEMs. In addition to the enhanced mechanical properties resulting from the rigid-flexible cross-linked network, c-DQPPO/PVA AEMs also exhibit impressive ionic conductivity, which can be attributed to their high IEC, good hydrophilicity of PVA, and well-defined micro-morphology. Additionally, due to confined dimension behavior and ordered micro-morphology, c-DQPPO/PVA AEMs demonstrate excellent chemical stability. Specifically, c-DQPPO/PVA-7.5 exhibits a wet-state tensile strength of 12.5 MPa and an elongation at break of 53.0 % at 25 °C. Its OH- conductivity and swelling degree at 80 °C are measured to be 125.7 mS cm-1 and 8.2 %, respectively, with an IEC of 3.05 mmol g-1 . After 30 days in a 1 M NaOH solution at 80 °C, c-DQPPO/PVA-7.5 experiences degradation rates of 12.8 % for tensile strength, 27.4 % for elongation at break, 14.7 % for IEC, and 19.2 % for ion conductivity. With its excellent properties, c-DQPPO/PVA-7.5 exhibits a peak power density of 0.751 W cm-2 at 60 °C in an H2 -O2 fuel cell.

Overcoming the Electrode Challenges of High-Temperature Proton Exchange Membrane Fuel Cells

Proton exchange membrane fuel cells (PEMFCs) are becoming a major part of a greener and more sustainable future. However, the costs of high-purity hydrogen and noble metal catalysts alongside the complexity of the PEMFC system severely hamper their commercialization. Operating PEMFCs at high temperatures (HT-PEMFCs, above 120 °C) brings several advantages, such as increased tolerance to contaminants, more affordable catalysts, and operations without liquid water, hence considerably simplifying the system. While recent progresses in proton exchange membranes for HT-PEMFCs have made this technology more viable, the HT-PEMFC viscous acid electrolyte lowers the active site utilization by unevenly diffusing into the catalyst layer while it acutely poisons the catalytic sites. In recent years, the synthesis of platinum group metal (PGM) and PGM-free catalysts with higher acid tolerance and phosphate-promoted oxygen reduction reaction, in conjunction with the design of catalyst layers with improved acid distribution and more triple-phase boundaries, has provided great opportunities for more efficient HT-PEMFCs. The progress in these two interconnected fields is reviewed here, with recommendations for the most promising routes worthy of further investigation. Using these approaches, the performance and durability of HT-PEMFCs will be significantly improved.

Practical ex-Situ Technique To Measure the Chemical Stability of Anion-Exchange Membranes under Conditions Simulating the Fuel Cell Environment

Anion-exchange membrane (AEM) degradation during fuel cell operation represents the main challenge that hampers the implementation of AEM fuel cells (AEMFCs). Reported degradation values of AEMs are difficult to reproduce as no standard methods are used. The present use of different techniques based on exposure of membranes to aqueous KOH solutions under different conditions and measuring different outputs during time does not allow for a reliable and meaningful comparison of reported degradation data of different AEMs. In this study, we present a practical and reproducible ex-situ technique to measure AEM degradation in conditions that mimic an operando fuel cell environment. In this novel technique, we measure the change of the true hydroxide conductivity of the AEM over time, while exposing it to different relative humidity conditions. The technique does not make use of liquid alkaline solution, thus simulating real fuel cell conditions and providing a good baseline for comparative degradation studies.

Micro-block versus random quaternized poly(arylene ether sulfones) with highly dense quaternization units for anion exchange membranes

A systematic study was carried out to investigate the effect of different distributions of conducting groups in segments for poly(arylene ether sulfone)s.