Emerging investigator series: microplastic-based leachate formation under UV irradiation: the extent, characteristics, and mechanisms

Effect of Biofouling on the Sorption of Organic Contaminants by Microplastics

Microplastics in the aquatic environment are susceptible to colonization by surrounding microorganisms, which form biofilms over the microplastic's surface. These biofilm-laden microplastics can then interact with a diverse array of contaminants. In the present study, biofilms were grown on microplastics in a laboratory setting using Pseudomonas aeruginosa as a model biofilm-forming bacterium for periods of 5 to 15 days. The sorption of three organic compounds representing different levels of hydrophobicity, namely methylene blue (MB), phenanthrol, and phenanthrene, was used to evaluate the effect of biofilm biomass on the adsorption of organic contaminants to microplastics. The sorption of MB and phenanthrol was found to increase with biofouling time, indicating affinity between these contaminants and the biofilm biomass on the particle. However, the presence of a biofilm did not influence the sorption of phenanthrene on the microplastics. These results suggest that the hydrophobicity of organic contaminants plays a major role in how biofouling of microplastics will influence contaminant sorption by microplastics. For some contaminants, biofilm can enhance the role of microplastics as contaminant vectors. These findings emphasize the need to understand the biomass load on environmental microplastics and the contaminants that associate with it for an accurate representation of the risk associated with microplastics in the environment. Environ Toxicol Chem 2024;00:1-9. © 2024 The Authors. Environmental Toxicology and Chemistry published by Wiley Periodicals LLC on behalf of SETAC.

Effect of oxygen-containing functional groups on the micromechanical behavior of biodegradable plastics and their formation of microplastics during aging

Biodegradable plastics (BPs) are more prone to generate harmful microplastics (MPs) in a short time, which have always been ignored. Oxygenated functional group formation is considered to be a key indicator for assessing microplastic formation, while it is difficult to characterize at a very early stage. The micromechanical properties of the aging plastic during the formation of the MPs are highly influenced by the evolution of oxygen-containing functional groups, however, their relationship has rarely been revealed. Herein, we compared changes in the physicochemical properties of BPs and non-degradable plastic bags during aging in artificial seawater, soil, and air. The results showed that the oxidation of plastics in the air was the most significant, with the most prominent oxidation in BPs. The accumulation of carbonyl groups leads to a significant increase in the micromechanical properties and surface brittleness of the plastic, further exacerbating the formation of MPs. It was also verified by the FTIR, 2D-COS, AFM, and Raman spectroscopy analyses. Furthermore, the increased adhesion and roughness caused by oxygen-containing functional groups suggest that the environmental risks of BPs cannot be ignored. Our findings suggest that the testing of micromechanical properties can predicate the formation of the MPs at an early stage.

Ecotoxicity of polylactic acid microplastic fragments to Daphnia magna and the effect of ultraviolet weathering

Biodegradable plastics (BPs) are widely used as alternatives to non-BPs due to their inherent ability to undergo facile degradation. However, the ecotoxicological impact of biodegradable microplastics (MPs) rarely remains scientific documented especially to aquatic ecosystem and organisms compared to conventional microplastics. Therefore, this study aimed to investigate the ecotoxicity of biodegradable polylactic acid (PLA) MPs to Daphnia magna with that of conventional polyethylene (PE) MPs with and without ultraviolet (UV) treatment (4 weeks). The acute toxicity (48 h) of PLA MPs was significantly higher than that of PE MPs, potentially attributable to their elevated bioconcentration resulting from their higher density. UV treatment notably reduced the particle size of PLA MPs and induced new hydrophilic functional groups containing oxygen. Thus, the acute lethal toxicity of PLA MPs exhibited noteworthy increase, compared to before UV treatment after UV treatment, which was greater than that of UV-PE MPs. In addition, UV-PLA MPs showed markedly elevated reactive oxygen species concentration in D. magna compared to positive control. However, there was no significant increase in the level of lipid peroxidation, possibly due to successful defense by antioxidant enzymes (superoxide dismutase and catalase). These findings highlight the ecotoxicological risks of biodegradable MPs to aquatic organisms, which require comprehensive long-term studies.