Chen X, Huang Z, Zhang S, Li H. Assembled collagen films modified using polyacrylic acid with improved mechanical properties via mineralization. J Mater Chem B 2024; 12:6643-6653. [PMID: 38873745 DOI: 10.1039/d4tb00828f] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 06/15/2024]
Abstract
The imperative task of enforcing collagen materials holds paramount significance in the field of hard tissue repair. We hereby present mineralized collagen fiber films via mineralization with improved mechanical properties. Self-extracted collagen was assembled into an array with an aligned fibrous pattern and then modified with polyacrylic acid (PAA) followed by mineralization in cationic polyacrylamide (CPAM)-SBF. Biomineralization occurred at the inner and outer surface of the assembled collagen fiber films. A tensile strength of up to 40.38 ± 3.08 MPa of mineralized collagen was obtained, for the first time, which may be attributed to the synergistic effect of polyanion and polycation on the mineralization process of assembled intrafibrillar collagen fibers. It was argued that PAA may facilitate the intra-fiber interaction of collagen, which extends the elongation at break of collagen fibers. This study introduces a pioneering approach for the preparation of mineralized collagen materials with superior mechanical properties, which would be beneficial for hard tissue repair.
Collapse
Affiliation(s)
- Xiaohui Chen
- College of Chemistry and Materials Science, Jinan University, Guangdong, 511443, P.R. China.
- Engineering Research Center of Artificial Organs and Materials, Jinan University, Guangdong, 510632, P.R. China
| | - Zhilin Huang
- College of Chemistry and Materials Science, Jinan University, Guangdong, 511443, P.R. China.
- Engineering Research Center of Artificial Organs and Materials, Jinan University, Guangdong, 510632, P.R. China
| | - Shuyun Zhang
- Guangdong Second Provincial General Hospital, Postdoctoral Research Station of Basic Medicine, School of Medicine, Jinan University, Guangdong, 510220, P.R. China.
| | - Hong Li
- College of Chemistry and Materials Science, Jinan University, Guangdong, 511443, P.R. China.
- Engineering Research Center of Artificial Organs and Materials, Jinan University, Guangdong, 510632, P.R. China
| |
Collapse
|
2
|
Zheng B, Zhao L, Chen L, Lai H, Wang C, Chen Y, Shao C, Tang R, Gu X. Phosphorylation of collagen fibrils enhances intrafibrillar mineralization and dentin remineralization. NANOSCALE 2024; 16:11633-11641. [PMID: 38687191 DOI: 10.1039/d4nr00652f] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 05/02/2024]
Abstract
The hierarchical assembly of nanoapatite within a type I collagen matrix was achieved through biomimetic mineralization in vitro, cooperatively regulated by non-collagenous proteins and small biomolecules. Here, we demonstrated that IP6 could significantly promote intrafibrillar mineralization in two- and three-dimensional collagen models through binding to collagen fibrils via hydrogen bonds (the interaction energy ∼10.21 kJ mol-1), as confirmed by the FTIR spectra and isothermal experimental results. In addition, we find that IP6 associated with dental collagen fibrils can also enhance the remineralization of calcium-depleted dentin and restore its mechanical properties similar to the natural dentin within 4 days. The promoting effect is mainly due to the chemical modification of IP6, which alters the interfacial physicochemical properties of collagen fibrils, strengthening the interaction of calcium phosphate minerals and mineral ions with collagen fibrils. This strategy of interfacial regulation to accelerate the mineralization of collagen fibrils is essential for dental repair and the development of a clinical product for the remineralization of hard tissue.
Collapse
Affiliation(s)
- Bo Zheng
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Hangzhou 310006, China.
| | - Luyi Zhao
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Hangzhou 310006, China.
| | - Lelu Chen
- Department of Stomatology, The Second Affiliated Hospital, Zhejiang University School of Medicine, Hangzhou 310009, China
| | - Haiyan Lai
- Department of Stomatology, The First Affiliated Hospital, College of Medicine, Zhejiang University, Hangzhou 310003, China.
| | - Chengze Wang
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Hangzhou 310006, China.
| | - Yi Chen
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Hangzhou 310006, China.
| | - Changyu Shao
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Hangzhou 310006, China.
| | - Ruikang Tang
- Department of Chemistry, Zhejiang University, Hangzhou 310027, China.
| | - Xinhua Gu
- Department of Stomatology, The First Affiliated Hospital, College of Medicine, Zhejiang University, Hangzhou 310003, China.
| |
Collapse
|
3
|
Jeong JK, Kim TH, Choi H, Cho ES. Impaired breakdown of Herwig's epithelial root sheath disturbs tooth root development. Dev Dyn 2024; 253:423-434. [PMID: 37850829 DOI: 10.1002/dvdy.667] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/26/2023] [Revised: 09/13/2023] [Accepted: 09/27/2023] [Indexed: 10/19/2023] Open
Abstract
BACKGROUND Wnt/β-catenin signaling plays a variety of roles in both the dental epithelium and mesenchyme at most stages of tooth development. In this study, we verified the roles of Hertwig's epithelial root sheath (HERS) breakdown in tooth root development. This breakdown results in formation of epithelial cell rests of Malassez (ERM). RESULTS Following induction of β-catenin stabilization in the epithelium of developing tooth at the moment of HERS breakdown, HERS failed to break down for ERM formation. HERS with stabilized β-catenin was altered into a multicellular layer enveloping elongated root dentin with higher expression of junctional proteins such as Zo-1 and E-cadherin. Importantly, this impairment of HERS breakdown led to arrest of further root elongation. In addition, the portion of root dentin enveloped by the undissociated HERS remained in a hypomineralized state. The odontoblasts showed ectopically higher expression of pyrophosphate regulators including Ank and Npp1, whereas Tnap expression was unchanged. CONCLUSIONS Our data suggest that Wnt/β-catenin signaling is decreased in HERS for ERM formation during root development. Furthermore, ERM formation is important for further elongation and dentin mineralization of the tooth roots. These findings may provide new insight to understand the contribution of ERM to root formation.
Collapse
Affiliation(s)
- Ju-Kyung Jeong
- Cluster for Craniofacial Development and Regeneration Research, Institute of Oral Biosciences, Jeonbuk National University School of Dentistry, Jeonju, South Korea
| | - Tak-Heun Kim
- Cluster for Craniofacial Development and Regeneration Research, Institute of Oral Biosciences, Jeonbuk National University School of Dentistry, Jeonju, South Korea
| | - Hwajung Choi
- Cluster for Craniofacial Development and Regeneration Research, Institute of Oral Biosciences, Jeonbuk National University School of Dentistry, Jeonju, South Korea
| | - Eui-Sic Cho
- Cluster for Craniofacial Development and Regeneration Research, Institute of Oral Biosciences, Jeonbuk National University School of Dentistry, Jeonju, South Korea
| |
Collapse
|
4
|
Zhang Y, Wang Y, Zhang Z, Wang Z, Shao C, Hannig M, Zhou Z, Fu B. Intrafibrillar mineralization of type I collagen with calcium carbonate and strontium carbonate induced by polyelectrolyte-cation complexes. NANOSCALE ADVANCES 2024; 6:467-480. [PMID: 38235102 PMCID: PMC10791124 DOI: 10.1039/d3na00705g] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 08/30/2023] [Accepted: 11/22/2023] [Indexed: 01/19/2024]
Abstract
Calcium carbonate (CaCO3), possessing excellent biocompatibility, bioactivity, osteoconductivity and superior biodegradability, may serve as an alternative to hydroxyapatite (HAp), the natural inorganic component of bone and dentin. Intrafibrillar mineralization of collagen with CaCO3 was achieved through the polymer-induced liquid precursor (PILP) process for at least 2 days. This study aims to propose a novel pathway for rapid intrafibrillar mineralization with CaCO3 by sequential application of the carbonate-bicarbonate buffer and polyaspartic acid (pAsp)-Ca suspension. Fourier transform infrared (FTIR) spectroscopy, zeta potential measurements, atomic force microscopy/Kelvin probe force microscopy (AFM/KPFM), and three-dimensional stochastic optical reconstruction microscopy (3D STORM) demonstrated that the carbonate-bicarbonate buffer significantly decreased the surface potential of collagen and CO32-/HCO3- ions could attach to collagen fibrils via hydrogen bonds. The electropositive pAsp-Ca complexes and free Ca2+ ions are attracted to and interact with CO32-/HCO3- ions through electrostatic attractions to form amorphous calcium carbonate that crystallizes gradually. Moreover, like CaCO3, strontium carbonate (SrCO3) can deposit inside the collagen fibrils through this pathway. The CaCO3-mineralized collagen gels exhibited better biocompatibility and cell proliferation ability than SrCO3. This study provides a feasible strategy for rapid collagen mineralization with CaCO3 and SrCO3, as well as elucidating the tissue engineering of CaCO3-based biomineralized materials.
Collapse
Affiliation(s)
- Yizhou Zhang
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| | - Yiru Wang
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| | - Zhengyi Zhang
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| | - Zhe Wang
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| | - Changyu Shao
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| | - Matthias Hannig
- Clinic of Operative Dentistry, Periodontology and Preventive Dentistry, Saarland University 66421 Homburg Germany
| | - Zihuai Zhou
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| | - Baiping Fu
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Zhejiang Provincial Clinical Research Center for Oral Diseases, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province Hangzhou 310000
| |
Collapse
|
5
|
Wu H, Shao C, Shi J, Hu Z, Zhou Y, Chen Z, Tang R, Xie Z, Jin W. Hyaluronic acid-mediated collagen intrafibrillar mineralization and enhancement of dentin remineralization. Carbohydr Polym 2023; 319:121174. [PMID: 37567692 DOI: 10.1016/j.carbpol.2023.121174] [Citation(s) in RCA: 3] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/21/2023] [Accepted: 07/01/2023] [Indexed: 08/13/2023]
Abstract
Non-collagenous proteins (NCPs) in the extracellular matrix (ECM) of bone and dentin are known to play a critical regulatory role in the induction of collagen fibril mineralization and are embedded in hyaluronic acid (HA), which acts as a water-retaining glycosaminoglycan and provides necessary biochemical and biomechanical cues. Our previous study demonstrated that HA could regulate the mineralization degree and mechanical properties of collagen fibrils, yet its kinetics dynamic mechanism on mineralization is under debate. Here, we further investigated the role of HA on collagen fibril mineralization and the possible mechanism. The HA modification can significantly promote intrafibrillar collagen mineralization by reducing the electronegativity of the collagen surface to enhance calcium ions (Ca2+) binding capacity to create a local higher supersaturation. In addition, the HA also provides additional nucleation sites and shortens the induction time of amorphous calcium phosphate (ACP)-mediated hydroxyapatite (HAP) crystallization, which benefits mineralization. The acceleration effect of HA on intrafibrillar collagen mineralization is also confirmed in collagen hydrogel and in vitro dentin remineralization. These findings offer a physicochemical view of the regulation effect of carbohydrate polymers in the body on biomineralization, the fine prospect for an ideal biomaterial to repair collagen-mineralized tissues.
Collapse
Affiliation(s)
- Haiyan Wu
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China
| | - Changyu Shao
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China
| | - Jue Shi
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China
| | - Zihe Hu
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China
| | - Yanyan Zhou
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China
| | - Zhuo Chen
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China
| | - Ruikang Tang
- Department of Chemistry, Zhejiang University, Hangzhou 310027, China
| | - Zhijian Xie
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China.
| | - Wenjing Jin
- Stomatology Hospital, School of Stomatology, Zhejiang University School of Medicine, Clinical Research Center for Oral Diseases of Zhejiang Province, Key Laboratory of Oral Biomedical Research of Zhejiang Province, Cancer Center of Zhejiang University, Engineering Research Center of Oral Biomaterials and Devices of Zhejiang Province, Hangzhou 310000, China.
| |
Collapse
|
6
|
Li Y, Liu M, Xue M, Kang Y, Liu D, Wen Y, Zhao D, Guan B. Engineered Biomaterials Trigger Remineralization and Antimicrobial Effects for Dental Caries Restoration. Molecules 2023; 28:6373. [PMID: 37687202 PMCID: PMC10489995 DOI: 10.3390/molecules28176373] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/19/2023] [Revised: 07/26/2023] [Accepted: 08/07/2023] [Indexed: 09/10/2023] Open
Abstract
Dental caries is the most prevalent chronic disease globally, significantly impacting individuals' quality of life. A key reason behind the failure of implanted restorations is their biological inactivity, meaning they are unable to form crosslinks with the surrounding tooth structures, thus making patients susceptible to implant loss and recurrent tooth decay. For the treatment of caries, antibacterial medicine and remineralization are effective means of treating the recurrence of caries. Owing to the rapid progression in the biomaterials field, several biomaterials have been reported to display antimicrobial properties and aid in dentin remineralization. Bioactive materials hold considerable potential in diminishing biofilm accumulation, inhibiting the process of demineralization, enabling dentin remineralization, and combating bacteria related to caries. Bioactive materials, such as fluoride, amorphous calcium phosphate, bioactive glass, collagen, and resin-based materials, have demonstrated their effectiveness in promoting dentin remineralization and exerting antibacterial effects on dental caries. However, the concentration of fluoride needs to be strictly controlled. Although amorphous calcium phosphate can provide the necessary calcium and phosphorus ions for remineralization, it falls short in delivering the mechanical strength required for oral mastication. Resin-based materials also offer different advantages due to the complexity of their design. In this review, we delve into the application of advanced bioactive materials for enhancing dentin remineralization and antibacterial properties. We eagerly anticipate future developments in bioactive materials for the treatment of dental caries.
Collapse
Affiliation(s)
- Yuexiao Li
- Department of Oral and Maxillofacial Surgery, School and Hospital of Stomatology, China Medical University, Shenyang 110022, China
| | - Minda Liu
- Department of Oral and Maxillofacial Surgery, School and Hospital of Stomatology, China Medical University, Shenyang 110022, China
| | - Mingyu Xue
- School and Hospital of Stomatology, China Medical University, Shenyang 110002, China
| | - Yuanyuan Kang
- School and Hospital of Stomatology, China Medical University, Shenyang 110002, China
| | - Dongjuan Liu
- School and Hospital of Stomatology, China Medical University, Shenyang 110002, China
| | - Yan Wen
- School and Hospital of Stomatology, China Medical University, Shenyang 110002, China
| | - Duoyi Zhao
- Department of Orthopedics, The Fourth Affiliated Hospital of China Medical University, Shenyang 110032, China
| | - Boyu Guan
- Department of Oral and Maxillofacial Surgery, School and Hospital of Stomatology, China Medical University, Shenyang 110022, China
- School and Hospital of Stomatology, China Medical University, Shenyang 110002, China
| |
Collapse
|
7
|
Zhu X, Wang C, Bai H, Zhang J, Wang Z, Li Z, Zhao X, Wang J, Liu H. Functionalization of biomimetic mineralized collagen for bone tissue engineering. Mater Today Bio 2023; 20:100660. [PMID: 37214545 PMCID: PMC10199226 DOI: 10.1016/j.mtbio.2023.100660] [Citation(s) in RCA: 4] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/28/2023] [Revised: 04/18/2023] [Accepted: 05/04/2023] [Indexed: 05/24/2023] Open
Abstract
Mineralized collagen (MC) is the basic unit of bone structure and function and is the main component of the extracellular matrix (ECM) in bone tissue. In the biomimetic method, MC with different nanostructures of neo-bone have been constructed. Among these, extra-fibrous MC has been approved by regulatory agencies and applied in clinical practice to play an active role in bone defect repair. However, in the complex microenvironment of bone defects, such as in blood supply disorders and infections, MC is unable to effectively perform its pro-osteogenic activities and needs to be functionalized to include osteogenesis and the enhancement of angiogenesis, anti-infection, and immunomodulation. This article aimed to discuss the preparation and biological performance of MC with different nanostructures in detail, and summarize its functionalization strategy. Then we describe the recent advances in the osteo-inductive properties and multifunctional coordination of MC. Finally, the latest research progress of functionalized biomimetic MC, along with the development challenges and future trends, are discussed. This paper provides a theoretical basis and advanced design philosophy for bone tissue engineering in different bone microenvironments.
Collapse
Affiliation(s)
- Xiujie Zhu
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - Chenyu Wang
- Department of Plastic and Reconstruct Surgery, The First Hospital of Jilin University, 1 Xinmin Street, Changchun, 130021, PR China
| | - Haotian Bai
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - Jiaxin Zhang
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - Zhonghan Wang
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - Zuhao Li
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - Xin Zhao
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - Jincheng Wang
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| | - He Liu
- Department of Orthopedics, The Second Hospital of Jilin University, 4110 Yatai Street, Changchun, 130041, PR China
| |
Collapse
|
8
|
Indurkar A, Choudhary R, Rubenis K, Locs J. Role of carboxylic organic molecules in interfibrillar collagen mineralization. Front Bioeng Biotechnol 2023; 11:1150037. [PMID: 37091348 PMCID: PMC10113455 DOI: 10.3389/fbioe.2023.1150037] [Citation(s) in RCA: 4] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/23/2023] [Accepted: 03/20/2023] [Indexed: 04/07/2023] Open
Abstract
Bone is a composite material made up of inorganic and organic counterparts. Most of the inorganic counterpart accounts for calcium phosphate (CaP) whereas the major organic part is composed of collagen. The interfibrillar mineralization of collagen is an important step in the biomineralization of bone and tooth. Studies have shown that synthetic CaP undergoes auto-transformation to apatite nanocrystals before entering the gap zone of collagen. Also, the synthetic amorphous calcium phosphate/collagen combination alone is not capable of initiating apatite nucleation rapidly. Therefore, it was understood that there is the presence of a nucleation catalyst obstructing the auto-transformation of CaP before entering the collagen gap zone and initiating rapid nucleation after entering the collagen gap zone. Therefore, studies were focused on finding the nucleation catalyst responsible for the regulation of interfibrillar collagen mineralization. Organic macromolecules and low-molecular-weight carboxylic compounds are predominantly present in the bone and tooth. These organic compounds can interact with both apatite and collagen. Adsorption of the organic compounds on the apatite nanocrystal governs the nucleation, crystal growth, lattice orientation, particle size, and distribution. Additionally, they prevent the auto-transformation of CaP into apatite before entering the interfibrillar compartment of the collagen fibril. Therefore, many carboxylic organic compounds have been utilized in developing CaP. In this review, we have covered different carboxylate organic compounds governing collagen interfibrillar mineralization.
Collapse
Affiliation(s)
- Abhishek Indurkar
- Rudolfs Cimdins Riga Biomaterials Innovations and Development Centre of RTU, Institute of General Chemical Engineering, Faculty of Materials Science and Applied Chemistry, Riga Technical University, Riga, Latvia
- Baltic Biomaterials Centre of Excellence, Headquarters at Riga Technical University, Riga, Latvia
| | - Rajan Choudhary
- Rudolfs Cimdins Riga Biomaterials Innovations and Development Centre of RTU, Institute of General Chemical Engineering, Faculty of Materials Science and Applied Chemistry, Riga Technical University, Riga, Latvia
- Baltic Biomaterials Centre of Excellence, Headquarters at Riga Technical University, Riga, Latvia
| | - Kristaps Rubenis
- Rudolfs Cimdins Riga Biomaterials Innovations and Development Centre of RTU, Institute of General Chemical Engineering, Faculty of Materials Science and Applied Chemistry, Riga Technical University, Riga, Latvia
- Baltic Biomaterials Centre of Excellence, Headquarters at Riga Technical University, Riga, Latvia
| | - Janis Locs
- Rudolfs Cimdins Riga Biomaterials Innovations and Development Centre of RTU, Institute of General Chemical Engineering, Faculty of Materials Science and Applied Chemistry, Riga Technical University, Riga, Latvia
- Baltic Biomaterials Centre of Excellence, Headquarters at Riga Technical University, Riga, Latvia
- *Correspondence: Janis Locs,
| |
Collapse
|
9
|
Oguma H, Matsuda Y, Yoshihara K, Okuyama K, Sakurai M, Saito T, Inoue S, Yoshida Y. Prevention of Root Caries Using Oxalic Acid. MATERIALS (BASEL, SWITZERLAND) 2023; 16:1454. [PMID: 36837083 PMCID: PMC9966124 DOI: 10.3390/ma16041454] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 12/10/2022] [Revised: 01/12/2023] [Accepted: 02/01/2023] [Indexed: 06/18/2023]
Abstract
Certain dentin hypersensitivity treatment materials include oxalic acid to coat dentin surfaces with minerals, while certain organic acids possess a remineralization effect. Herein, an organic acid that inhibits the demineralization and coating of root surfaces was evaluated. Specimens were produced using five non-carious extracted bovines. Four different acids were used: oxalic acid (OA), malonic acid (MA), polyacrylic acid (PA), and succinic acid (SA). Each acid was applied to the root surface and washed using distilled water or a remineralization solution, and the surface was observed using scanning electron microscopy (SEM). All the surfaces of each specimen, barring the polished surface, were covered with wax and immersed in an automatic pH cycling system for two weeks. Dentin demineralization was analyzed using transverse microradiography (TMR) before and after pH cycling. SEM analysis demonstrated that the three acid groups demineralized the dentin surface, whereas the OA group generated crystals covering the dentin surface, even in a distilled water environment. TMR analysis revealed that the OA groups showed significantly lower integrated mineral loss compared with the other groups, even in the distilled water environment. The results suggest that OA generates insoluble calcium oxalate crystals on the dentin and suppresses demineralization even under low saliva conditions.
Collapse
Affiliation(s)
- Hidetoshi Oguma
- Division of General Dentistry, Hokkaido University Hospital, Sapporo 060-8586, Japan
| | - Yasuhiro Matsuda
- Division of Clinical Cariology and Endodontology, Department of Oral Rehabilitation, School of Dentistry, Health Sciences University of Hokkaido, Tobetsu 061-0293, Japan
| | - Kumiko Yoshihara
- Health and Medical Research Institute, National Institute of Advanced Industrial Science and Technology (AIST), Takamatsu 761-0395, Japan
| | - Katsushi Okuyama
- Department of Dental Materials Science, Asahi University School of Dentistry, Mizuho 501-0296, Japan
| | - Masahiko Sakurai
- Division of Clinical Cariology and Endodontology, Department of Oral Rehabilitation, School of Dentistry, Health Sciences University of Hokkaido, Tobetsu 061-0293, Japan
| | - Takashi Saito
- Division of Clinical Cariology and Endodontology, Department of Oral Rehabilitation, School of Dentistry, Health Sciences University of Hokkaido, Tobetsu 061-0293, Japan
| | - Satoshi Inoue
- Division of General Dentistry, Hokkaido University Hospital, Sapporo 060-8586, Japan
| | - Yasuhiro Yoshida
- Department of Biomaterials and Bioengineering, Faculty of Dental Medicine, Hokkaido University, Sapporo 060-8586, Japan
| |
Collapse
|
10
|
Chen L, Zeng Z, Li W. Poly(acrylic acid)-Assisted Intrafibrillar Mineralization of Type I Collagen: A Review. Macromol Rapid Commun 2023; 44:e2200827. [PMID: 36662644 DOI: 10.1002/marc.202200827] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/19/2022] [Revised: 01/06/2023] [Indexed: 01/21/2023]
Abstract
The mineralization of type I collagen is a biological process occurring in vertebrates by which some hard tissues such as bone and dentin are constructed. Due to the extensive clinical needs for bone defect repair and remineralization of mineral-depleted dentin, biomimetic mineralization of collagen is attracting more and more interests. Synthetic analogs of noncollagenous proteins are necessary for directing the in vitro mineralization. In this paper, the function and mechanism of poly(acrylic acid) (PAA) in regulating the mineralization, especially intrafibrillar mineralization (IM) of collagen are reviewed. As two mineralization patterns (extrafibrillar and intrafibrillar) co-exist in natural hard tissues, differences between them in terms of microstructure, biodegradation, cytocompatibility, osteoinduction in vitro, and performance in vivo are systematically compared. Then the roles of PAA in biomimetic collagen IM within one-analog and two-analog systems are discussed, respectively. Moreover, mineralization of some self-mineralizable collagen matrices is described. Due to the interactions between collagen and PAA play a crucial role in the processes of collagen mineralization, some reference researches are also provided involving the collagen/PAA interactions in some other fields. Finally, this review is ended with an outlook for future potential improvements based on the collection of existing bottlenecks in this field.
Collapse
Affiliation(s)
- Lei Chen
- Department of Bio-medical Engineering, Southern University of Science and Technology, Shenzhen, 518055, P. R. China
| | - Zhiyong Zeng
- Key Laboratory of Eco-Textiles, Ministry of Education, College of Textile Science and Engineering, Jiangnan University, Wuxi, 214122, P. R. China
| | - Wenbing Li
- Key Laboratory of Eco-Textiles, Ministry of Education, College of Textile Science and Engineering, Jiangnan University, Wuxi, 214122, P. R. China
| |
Collapse
|
11
|
Wang B, Han F, You R, Chen C, Xie H. Polyphenols Can Improve Resin-Dentin Bond Durability by Promoting Amorphous Calcium Phosphate Nanoparticles to Backfill the Dentin Matrix. Int J Nanomedicine 2023; 18:1491-1505. [PMID: 36998600 PMCID: PMC10046144 DOI: 10.2147/ijn.s395631] [Citation(s) in RCA: 3] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/07/2022] [Accepted: 03/14/2023] [Indexed: 04/01/2023] Open
Abstract
Objective To investigate the effects of proanthocyanidins (PA), myricetin, resveratrol, and kaempferol on the modification of dentin collagen and the inhibition of matrix metalloproteinase (MMP) activity, and to evaluate their contributions to the biomimetic remineralization and resin-dentin bonding performance. Methods Attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) and in situ zymography were applied to verify the collagen modification and MMP activity inhibition induced by these four polyphenols. Scanning electron microscopy/energy dispersive spectrometer (SEM/EDS) analysis, X-ray diffraction (XRD), ATR-FTIR, Vickers hardness numbers (VHN), and micro-computed tomography (micro-CT) were performed to characterize the remineralized dentin. Microtensile bond strength (μTBS) and nanoleakage were investigated to evaluate the effects of the four polyphenols on resin-dentin bonding durability. Results ATR-FTIR and in situ zymography confirmed that these four polyphenols could modify dentin collagen and inhibit MMP activity, respectively. Chemoanalytic characterization exhibited the efficacies of the four polyphenols in promoting dentin biomimetic remineralization. The surface hardness of PA-pretreated dentin was the greatest. Micro-CT results demonstrated that the PAs group possessed the highest amount of dentin surface minerals and the lowest amount of deep-layer minerals. The surface and deep-layer mineral contents of the Myr group were higher than Res and Kae groups. Treatment with these four polyphenols significantly increased the initial μTBS compared with the control group without primer conditioning. μTBS decreased significantly during aging, and the decrease was more severe in the PAs and Kae groups than in the Myr and Res groups. With or without aging, the polyphenol groups exhibited relatively less fluorescence. However, the Myr and Res groups showed less serious nanoleakage after aging. Conclusion PA, myricetin, resveratrol, and kaempferol can modify dentin collagen, inhibit MMP activity, promote biomimetic remineralization, and improve resin-dentin bond durability. Compared with PA and kaempferol, myricetin and resveratrol are more effective in improving resin-dentin bonding.
Collapse
Affiliation(s)
- Beibei Wang
- Department of Prosthodontics, Affiliated Stomatology Hospital, Nanjing Medical University; Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, 210029, People’s Republic of China
| | - Fei Han
- Department of Prosthodontics, Affiliated Stomatology Hospital, Nanjing Medical University; Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, 210029, People’s Republic of China
| | - Ran You
- Department of Prosthodontics, Affiliated Stomatology Hospital, Nanjing Medical University; Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, 210029, People’s Republic of China
| | - Chen Chen
- Department of Endodontics, Affiliated Stomatology Hospital, Nanjing Medical University; Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, 210029, People’s Republic of China
| | - Haifeng Xie
- Department of Prosthodontics, Affiliated Stomatology Hospital, Nanjing Medical University; Jiangsu Province Key Laboratory of Oral Diseases, Jiangsu Province Engineering Research Center of Stomatological Translational Medicine, Nanjing, 210029, People’s Republic of China
- Correspondence: Haifeng Xie, Affiliated Stomatology Hospital, Nanjing Medical University, Han-Zhong Road 136th, Nanjing, 210029, People’s Republic of China, Tel +8625 69593081, Fax +8625 86516414, Email
| |
Collapse
|