Synthesis and anti-aging property in acrylonitrile-butadiene rubber of non-aromatic dendritic antioxidant with amine groups

Synthesis and Properties of a Novel Reactive and Low-Migration-Resistant Antioxidant and Its Application in Rubber Composites

The addition of antioxidants to rubber is one of the most economical and effective methods for delaying rubber aging. However, antioxidant migration can cause environmental pollution. To address this issue, a new reactive antioxidant was synthesized via the chemical bonding of glycidyl methacrylate (GMA) and p-aminodiphenylamine (PPDA). The product was characterized by Fourier-transform infrared spectroscopy, which confirmed the successful reaction between GMA and PPDA, resulting in a compound with the expected structure. The mixture was then combined with a composite of styrene-butadiene rubber and carbon black. The tensile strength, antioxidant properties, migration, and RPA of the resulting materials were tested and compared with those of the commercial antioxidants N-(1,3-dimethylbutyl)-N'-phenyl-p-phenylenediamine, N-isopropyl-N'-phenyl-1,4-phenylenediamine, and poly(1,2-dihydro-2,2,4-trimethylquinoline). After the glycidyl methacrylate antioxidant was grafted onto p-aminodiphenylamine, it became highly compatible with and dispersed in the rubber matrix. The antiaging and antimigration properties of the rubber antioxidants were enhanced without damaging the mechanical properties of the rubber matrix. The short-term and long-term antiaging and antimigration properties of this antioxidant are superior to those of commercially available antioxidants.

Effect of Nitrogen-Doped Graphene Oxide on the Aging Behavior of Nitrile-Butadiene Rubber

Nitrogen-doped graphene oxide (GO), namely, NG, was prepared by o-phenylenediamine (OPD) grafting onto GO. The structure and morphology of NG were characterized by FITR, XRD, SEM, EDS, Raman spectroscopy, and TGA. OPD was linked to the GO surface by covalent bonds, and the absorption peak of the C=N bond in the phenazine structure was identified in the FITR spectra. The aging resistance properties of nitrile-butadiene rubber (NBR)-NG composites was investigated by mechanical testing, before and after aging. The resistance of the NBR/NG composites with the addition of 3 phr NG fillers was the highest. The aging mechanism was investigated by TGA-DSC, DMA, equilibrium swelling testing, and ATR-FTIR. The results showed that NG could effectively inhibit chain cross-linking in NBR.