Comparison of Bond Stability Between Dual-Cure Resin Cements and Pretreated Glass-Infiltrated Alumina Ceramics

Influence of Different Surface Pretreatments of Zirconium Dioxide Reinforced Lithium Disilicate Ceramics on the Shear Bond Strength of Self-Adhesive Resin Cement

Aim

To analyze the influence of different surface pretreatments of zirconium dioxide reinforced lithium disilicate ceramics on the shear bond strength of self-adhesive resin cement.

Materials and methods

Eighty-four zirconium reinforced lithium disilicate disc Vita suprinity (Vita Zahnfabrick, Bad Säckingen, Germany) 14x12x2 mm specimens were fabricated according to the manufacturer's recommendations. The specimens were embedded in acrylic resin blocks and randomly divided in seven groups (n=12/each) accorrding to the treatment: Group 1- 10% hydrofluoric acid; Group 2- silane; Group 3- hydrofluoric and silane; Group 4- sandblasting with silane; Group 5- Er: YAG laser+ silane; Group 6- Nd: YAG laser + silane; and the control group, in which the specimens were not treated. Round shape composite discs (Filtek Bulk fill, 3M ESPE, St.Paul, Minnesota, USA) with 3.5 mm diameter, were made for shear bond strength testing, and then cemented to the ceramic sample surface using composite cement (RelyX U200 Automix, 3M ESPE, Neuss, Germany). After cementing the composite disc on the sample, the samples were subjected to shear bond strength test of 10 N with a “stress rate” of 1 MPa / s. To determine the nature of the fracture (adhesive, cohesive or adhesive-cohesive), the broken samples were examined under a stereomicroscope. The ANOVA test and the Tukey test were used to compare the values ​​of the bond strength characteristics between different types of materials. All tests were performed with a significance level of α = 0.05.

Results

There was a significant difference in the shear bond strength of self-adhesive cement to dental lithium-disilicate ceramics reinforced with zirconium dioxide after different preparation protocols (p<0, 05). The treatment of lithium disilicate ceramics reinforced with zirconium dioxide by silanization, sandblasting + silanization, Nd: YAG + silanization resulted in significantly higher bond strength compared to the control group. There was statistically higher bond strength of self-adhesive cement after pretreatment of lithium disilicate ceramics Nd: YAG + silanization compared to Er: YAG + silanization (p <0.05). Adhesive fracture dominated in the control group, sandblasting + silanization group, and in the laser groups, while mixed fracture dominated in other groups.

Conclusion

Under the limitations of this study, the Nd:YAG irradiation with silanization could be used as pretreatment for providing greater shear bond strength of self-adhesive resin cement to zirconium reinforced lithium disilicate.

Influence of Er:YAG laser surface treatment on flexural and bond strengths to glass-infiltrated zirconia-reinforced ceramic

To evaluate the effect of Er:YAG laser conditioning of a glass-infiltrated alumina-based zirconia-reinforced ceramic on its flexural strength and on bonding to a resin cement. Sixteen blocks (5 × 5 × 4 mm) and 50 discs (Ø 12 mm, 1 mm thickness) of In-Ceram Zirconia (ICZ) obtained from CAD-CAM blocks were infiltrated with glass. For the microtensile bond strength (μTBS) test, all blocks were treated with aluminum oxide (AOX) and divided into 4 groups (n = 4): G1 (AOX), no combined surface treatment; G2 (ROC), tribochemical silica-coating; G3 (EY200), Er:YAG laser 200 mJ/15 Hz; and G4 (EY250), Er:YAG laser 250 mJ/10 Hz. The ceramic blocks were silanated and cemented with a resin cement (Panavia F2.0/Kuraray) to composite resin blocks and subjected to the μTBS test. For the flexural strength evaluation, the discs were divided into 5 groups (n = 10) as described above, in addition to a control group (G5 - CTRL, mirror-polished without further treatment). Each surface treatment was submitted to qualitative evaluation under SEM. One-way ANOVA (α = 5%) revealed the highest bond strength value for EY200 with no significant difference from ROC. The groups AOX and EY250 showed similar μTBS values that were statistically lower than those of EY200. For flexural strength, ROC was the only group with significantly lower values when compared with the CTRL. The use of Er:YAG laser at 200 mJ/15 Hz can be considered an innovative and effective alternative for surface conditioning of ICZ since it did not reduce the flexural strength of the ceramic and improved the resin cement bond to this substrate.

Evaluation Of The Effect Of Different Surface Treatments, Aging And Enzymatic Degradation On Zirconia-Resin Micro-Shear Bond Strength

Purpose

The purpose of this study was to evaluate the effect of surface treatments on zirconia-resin bonding and the effect of aging on bond durability for one year.

Method

Three hundred and twenty zirconia blocks were divided into 4 equal study groups. Group 1 (control): as-sintered, group 2: (GB): grit-blasted, group 3: (LAS): laser-etched, group 4: (SIE): selective infiltration etching. Composite cylinders were bonded to the zirconia with resin cement and ceramic primer. Aging was performed following 3 different aging protocols: thermocycling, storage in distilled water, or storage in an enzymatic esterase solution. Micro-shear bond strength test (μSBS) was recorded using a universal testing machine. μSBS values were analyzed using two-way Analysis of Variance followed by Tukey post-hoc tests. Level of significance was set at 0.05.

Results

GB, LAS and SIE groups showed significantly higher values when compared to control. Groups GB, LAS and SIE reported a significant decrease up to 50% in μSBS after water storage and enzymatic degradation, while control group reported a 90% decrease. Failure analysis showed mainly adhesive failure for control group, while the percentage of cohesive failure in resin cement was higher in SIE group compared to GB and LAS groups.

Conclusion

Water aging and esterase solutions played a significant role by increasing bond degradation. A minimum of one-year water and esterase storage medium should be used to evaluate the durability of the bond between resin cement and zirconia.