Gazińska MA, Krokos A. Tunable structure and linear viscoelastic properties of poly(glycerol adipate urethane)-based elastomeric composites for tissue regeneration. J Mech Behav Biomed Mater 2024; 153:106493. [PMID: 38484428 DOI: 10.1016/j.jmbbm.2024.106493] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/09/2024] [Revised: 02/21/2024] [Accepted: 03/01/2024] [Indexed: 03/26/2024]
Abstract
Elastomeric biocomposites based on poly(glycerol adipate urethane) and hydroxyapatite were fabricated for tissue regeneration. The poly(glycerol adipate urethane) (PGAU) elastomeric composite matrices were obtained by chemical crosslinking of the poly(glycerol adipate) prepolymer (pPGA) with diisocyanate derivative of L-lysine. Two series of composites varying in the amount of L-lysine diisocyanate ethyl ester (LDI) used as a crosslinking agent were manufactured. As a ceramic filler both unmodified and L-lysine surface-modified hydroxyapatite (HAP) particles were used. The novelty of our research consists in the manufactured elastomeric materials and characterization of their linear viscoelastic (LVE) properties. The LVE properties of the composites were investigated by means of dynamic thermomechanical analysis. Frequency sweep and amplitude sweep measurements were performed in shear mode. The influence of the crosslinking agent (LDI) amount, HAP content and surface modification of HAP on the LVE properties of the composites was determined based on the analysis of the master curves of storage (G') and loss (G″) moduli and of tanδ of the composites. Depending on the amount of LDI, HAP and surface modification, the materials differ in the values of rubber elasticity plateau modulus (G0) and G' and G″ determined at selected shear frequencies and at the glassy state. G0 ranges from 278 kPa to 3.98 MPa, G' in the glassy state is within the range of 219 MPa-459 MPa. The G0 values of the PGAU-based composites are within the stiffness range of soft tissue. In view of the choice of HAP as the ceramic component and the G0 values, elastomeric composites have the potential to be used as filling materials in small bone defects (due to their mechanical similarity to osteoid) as well as materials for cartilage tissue regeneration.
Collapse
Affiliation(s)
- Małgorzata Anna Gazińska
- Department of Polymer Engineering and Technology, Faculty of Chemistry, Wrocław University of Science and Technology, Wybrzeże Wyspiańskiego 27, 50-370, Wrocław, Poland.
| | - Anna Krokos
- Department of Polymer Engineering and Technology, Faculty of Chemistry, Wrocław University of Science and Technology, Wybrzeże Wyspiańskiego 27, 50-370, Wrocław, Poland
| |
Collapse
|
2
|
Middendorf JM, Barocas VH. MRI‐based degeneration grades for lumbar facet joints do not correlate with cartilage mechanics. JOR Spine 2023. [DOI: 10.1002/jsp2.1246] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Indexed: 01/12/2023] Open
Affiliation(s)
- Jill M. Middendorf
- Department of Mechanical Engineering Johns Hopkins University Baltimore Maryland USA
| | - Victor H. Barocas
- Department of Biomedical Engineering University of Minnesota Minneapolis Minnesota USA
| |
Collapse
|
3
|
Stading M. Physical properties of a model set of solid, texture-modified foods. J Texture Stud 2021; 52:578-586. [PMID: 33599283 DOI: 10.1111/jtxs.12592] [Citation(s) in RCA: 3] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/13/2021] [Revised: 01/28/2021] [Accepted: 01/31/2021] [Indexed: 01/28/2023]
Abstract
Those suffering from swallowing disorders, or dysphagia, require texture-modified foods for safe swallowing. The texture is modified according to the severity of the disorder, as maintained by the guidelines outlining classes of texture-modified foods, ranging from viscous soups to soft, solid foods. As a basis for studies of bolus rheology and oral response of solid texture-modified foods, a set of well-defined, solid foods has been identified and characterized regarding texture and physical properties. Gelled food is compared to both the firmer timbale class and to the corresponding regular food. Foods eaten at room temperature were chosen to avoid temperature effects: bread, cheese, tomato, and the combination into a sandwich. All foods were tested as gel, timbale, and regular food. The texture was determined by compression and penetration tests, thereby showing a decrease in strength (compression stress), stiffness (modulus), and penetration force for increased degree of modification. The moisture content increased with increased degree of modification. The structural change from room to oral temperature was monitored by the complex shear modulus that showed a decrease with increasing temperature. Cheese and the gelatine-based tomato gel showed a distinct melting when the temperature was increased to 37°C. The texture-modified foods were softer and moister in all aspects as compared to the regular foods, which follows the intended modification. The classes for the texture-modified foods were qualitatively comparable to other national classification systems with regard to solid foods, but there is a lack of objective, physics-based classification of texture, especially for solid, texture-modified foods.
Collapse
Affiliation(s)
- Mats Stading
- RISE Research Institutes of Sweden, Gothenburg, Sweden.,Chalmers University of Technology, Gothenburg, Sweden
| |
Collapse
|
4
|
Middendorf JM, Diamantides N, Shortkroff S, Dugopolski C, Kennedy S, Cohen I, Bonassar LJ. Multiscale mechanics of tissue-engineered cartilage grown from human chondrocytes and human-induced pluripotent stem cells. J Orthop Res 2020; 38:1965-1973. [PMID: 32125023 DOI: 10.1002/jor.24643] [Citation(s) in RCA: 8] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 05/13/2019] [Revised: 02/17/2020] [Accepted: 02/29/2020] [Indexed: 02/04/2023]
Abstract
Tissue-engineered cartilage has shown promising results in the repair of focal cartilage defects. However, current clinical techniques rely on an extra surgical procedure to biopsy healthy cartilage to obtain human chondrocytes. Alternatively, induced pluripotent stem cells (iPSCs) have the ability to differentiate into chondrocytes and produce cartilaginous matrix without the need to biopsy healthy cartilage. However, the mechanical properties of tissue-engineered cartilage with iPSCs are unknown and might be critical to long-term tissue function and health. This study used confined compression, cartilage on glass tribology, and shear testing on a confocal microscope to assess the macroscale and microscale mechanical properties of two constructs seeded with either chondrocyte-derived iPSCs (Ch-iPSCs) or native human chondrocytes. Macroscale properties of Ch-iPSC constructs provided similar or better mechanical properties than chondrocyte constructs. Under compression, Ch-iPSC constructs had an aggregate modulus that was two times larger than chondrocyte constructs and was closer to native tissue. No differences in the shear modulus and friction coefficients were observed between Ch-iPSC and chondrocyte constructs. On the microscale, Ch-iPSC and chondrocyte constructs had different depth-dependent mechanical properties, neither of which matches native tissue. These observed depth-dependent differences may be important to the function of the implant. Overall, this comparison of multiple mechanical properties of Ch-iPSC and chondrocyte constructs shows that using Ch-iPSCs can produce equivalent or better global mechanical properties to chondrocytes. Therefore, iPSC-seeded cartilage constructs could be a promising solution to repair focal cartilage defects. The chondrocyte constructs used in this study have been implanted into humans for clinical trials. Therefore, Ch-iPSC constructs could also be used clinically in place of the current chondrocyte construct.
Collapse
Affiliation(s)
- Jill M Middendorf
- Sibley School of Mechanical Engineering, Cornell University, Ithaca, New York
| | - Nicole Diamantides
- Meinig School of Biomedical Engineering, Cornell University, Ithaca, New York
| | | | | | | | - Itai Cohen
- Department of Applied Engineering and Physics, Cornell University, Ithaca, New York.,Department of Physics, Cornell University, Ithaca, New York
| | - Lawrence J Bonassar
- Sibley School of Mechanical Engineering, Cornell University, Ithaca, New York.,Meinig School of Biomedical Engineering, Cornell University, Ithaca, New York
| |
Collapse
|
5
|
Middendorf JM, Dugopolski C, Kennedy S, Blahut E, Cohen I, Bonassar LJ. Heterogeneous matrix deposition in human tissue engineered cartilage changes the local shear modulus and resistance to local construct buckling. J Biomech 2020; 105:109760. [PMID: 32276782 DOI: 10.1016/j.jbiomech.2020.109760] [Citation(s) in RCA: 8] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/15/2019] [Revised: 02/05/2020] [Accepted: 03/20/2020] [Indexed: 12/11/2022]
Abstract
Human tissue engineered cartilage is a promising solution for focal cartilage defects, but these constructs do not have the same local mechanical properties as native tissue. Most clinically relevant engineered cartilage constructs seed human chondrocytes onto a collagen scaffold, which buckles at low loads and strains. This buckling creates local regions of high strain that could cause cell death and damage the engineered tissue. Since human tissue engineered cartilage is commonly grown in-vivo prior to implantation, new matrix deposition could improve the local implant mechanics and prevent local tissue buckling. However, the relationship between local biochemical composition and the local mechanics or local buckling probability has never been quantified. Therefore, this study correlated the local biochemical composition of human tissue engineered cartilage constructs using Fourier transform infrared spectroscopy (FTIR) with the local shear modulus and local buckling probability. The local shear modulus and local buckling probability were obtained using a confocal elastography technique. The local shear modulus increased with increases in local aggrecan content in the interior region (inside the scaffold). A minimum amount of aggrecan was required to prevent local construct buckling at physiologic strains. Since the original scaffold was primarily composed of collagen, increases in collagen content due to new matrix deposition was minimal and had little effect on the mechanical properties. Thus, we concluded that aggrecan deposition inside the scaffold pores is the most effective way to improve the mechanical function and prevent local tissue damage in human tissue engineered cartilage constructs.
Collapse
Affiliation(s)
- Jill M Middendorf
- Sibley School of Mechanical Engineering, Cornell University, Ithaca, NY, USA
| | | | | | | | - Itai Cohen
- Physics, Cornell University, Ithaca, NY, USA
| | - Lawrence J Bonassar
- Sibley School of Mechanical Engineering, Cornell University, Ithaca, NY, USA; Meinig School of Biomedical Engineering Cornell University, Ithaca, NY, USA.
| |
Collapse
|
6
|
Gao T, Chen T, Feng C, He X, Mu C, Anzai JI, Li G. Design and fabrication of flexible DNA polymer cocoons to encapsulate live cells. Nat Commun 2019; 10:2946. [PMID: 31270421 PMCID: PMC6610073 DOI: 10.1038/s41467-019-10845-2] [Citation(s) in RCA: 44] [Impact Index Per Article: 8.8] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/04/2018] [Accepted: 05/31/2019] [Indexed: 12/20/2022] Open
Abstract
The capability to encapsulate designated live cells into a biologically and mechanically tunable polymer layer is in high demand. Here, an approach to weave functional DNA polymer cocoons has been proposed as an encapsulation method. By developing in situ DNA-oriented polymerization (isDOP), we demonstrate a localized, programmable, and biocompatible encapsulation approach to graft DNA polymers onto live cells. Further guided by two mutually aided enzymatic reactions, the grafted DNA polymers are assembled into DNA polymer cocoons at the cell surface. Therefore, the coating of bacteria, yeast, and mammalian cells has been achieved. The capabilities of this approach may offer significant opportunities to engineer cell surfaces and enable the precise manipulation of the encapsulated cells, such as encoding, handling, and sorting, for many biomedical applications.
Collapse
Affiliation(s)
- Tao Gao
- Center for Molecular Recognition and Biosensing, School of Life Sciences, Shanghai University, 200444, Shanghai, P.R. China
- Jiangsu Key Laboratory for Molecular and Medical Biotechnology, College of Life Sciences, Nanjing Normal University, 210023, Nanjing, P.R. China
| | - Tianshu Chen
- Center for Molecular Recognition and Biosensing, School of Life Sciences, Shanghai University, 200444, Shanghai, P.R. China
| | - Chang Feng
- State Key Laboratory of Pharmaceutical Biotechnology, School of Life Sciences, Nanjing University, 210023, Nanjing, P.R. China
| | - Xiang He
- School of Biomedical Engineering, Shanghai Jiao Tong University, 200240, Shanghai, P.R. China
| | - Chaoli Mu
- State Key Laboratory of Pharmaceutical Biotechnology, School of Life Sciences, Nanjing University, 210023, Nanjing, P.R. China
| | - Jun-Ichi Anzai
- Graduate School of Pharmaceutical Sciences, Tohoku University, Aramaki, Aoba-ku, Sendai, 980-8578, Japan
| | - Genxi Li
- Center for Molecular Recognition and Biosensing, School of Life Sciences, Shanghai University, 200444, Shanghai, P.R. China.
- State Key Laboratory of Pharmaceutical Biotechnology, School of Life Sciences, Nanjing University, 210023, Nanjing, P.R. China.
| |
Collapse
|
7
|
Middendorf JM, Griffin DJ, Shortkroff S, Dugopolski C, Kennedy S, Siemiatkoski J, Cohen I, Bonassar LJ. Mechanical properties and structure-function relationships of human chondrocyte-seeded cartilage constructs after in vitro culture. J Orthop Res 2017; 35:2298-2306. [PMID: 28169453 DOI: 10.1002/jor.23535] [Citation(s) in RCA: 15] [Impact Index Per Article: 2.1] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 08/09/2016] [Accepted: 01/27/2017] [Indexed: 02/04/2023]
Abstract
Autologous Chondrocyte Implantation (ACI) is a widely recognized method for the repair of focal cartilage defects. Despite the accepted use, problems with this technique still exist, including graft hypertrophy, damage to surrounding tissue by sutures, uneven cell distribution, and delamination. Modified ACI techniques overcome these challenges by seeding autologous chondrocytes onto a 3D scaffold and securing the graft into the defect. Many studies on these tissue engineered grafts have identified the compressive properties, but few have examined frictional and shear properties as suggested by FDA guidance. This study is the first to perform three mechanical tests (compressive, frictional, and shear) on human tissue engineered cartilage. The objective was to understand the complex mechanical behavior, function, and changes that occur with time in these constructs grown in vitro using compression, friction, and shear tests. Safranin-O histology and a DMMB assay both revealed increased sulfated glycosaminoglycan (sGAG) content in the scaffolds with increased maturity. Similarly, immunohistochemistry revealed increased lubricin localization on the construct surface. Confined compression and friction tests both revealed improved properties with increased construct maturity. Compressive properties correlated with the sGAG content, while improved friction coefficients were attributed to increased lubricin localization on the construct surfaces. In contrast, shear properties did not improve with increased culture time. This study suggests the various mechanical and biological properties of tissue engineered cartilage improve at different rates, indicating thorough mechanical evaluation of tissue engineered cartilage is critical to understanding the performance of repaired cartilage. © 2017 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 35:2298-2306, 2017.
Collapse
Affiliation(s)
- Jill M Middendorf
- Sibley School of Mechanical and Aerospace Engineering, Cornell University, Ithaca, New York
| | - Darvin J Griffin
- Meinig School of Biomedical Engineering, Cornell University, Ithaca, New York
| | | | | | | | | | - Itai Cohen
- Department of Physics, Cornell University, Ithaca, New York
| | - Lawrence J Bonassar
- Sibley School of Mechanical and Aerospace Engineering, Cornell University, Ithaca, New York.,Meinig School of Biomedical Engineering, Cornell University, Ithaca, New York
| |
Collapse
|
8
|
Warnock JJ, Fox DB, Stoker AM, Beatty M, Cockrell M, Janicek JC, Cook JL. Culture of equine fibroblast-like synoviocytes on synthetic tissue scaffolds towards meniscal tissue engineering: a preliminary cell-seeding study. PeerJ 2014; 2:e353. [PMID: 24765587 PMCID: PMC3994628 DOI: 10.7717/peerj.353] [Citation(s) in RCA: 7] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/02/2014] [Accepted: 03/28/2014] [Indexed: 11/25/2022] Open
Abstract
Introduction. Tissue engineering is a new methodology for addressing meniscal injury or loss. Synovium may be an ideal source of cells for in vitro meniscal fibrocartilage formation, however, favorable in vitro culture conditions for synovium must be established in order to achieve this goal. The objective of this study was to determine cellularity, cell distribution, and extracellular matrix (ECM) formation of equine fibroblast-like synoviocytes (FLS) cultured on synthetic scaffolds, for potential application in synovium-based meniscal tissue engineering. Scaffolds included open-cell poly-L-lactic acid (OPLA) sponges and polyglycolic acid (PGA) scaffolds cultured in static and dynamic culture conditions, and PGA scaffolds coated in poly-L-lactic (PLLA) in dynamic culture conditions. Materials and Methods. Equine FLS were seeded on OPLA and PGA scaffolds, and cultured in a static environment or in a rotating bioreactor for 12 days. Equine FLS were also seeded on PGA scaffolds coated in 2% or 4% PLLA and cultured in a rotating bioreactor for 14 and 21 days. Three scaffolds from each group were fixed, sectioned and stained with Masson’s Trichrome, Safranin-O, and Hematoxylin and Eosin, and cell numbers and distribution were analyzed using computer image analysis. Three PGA and OPLA scaffolds from each culture condition were also analyzed for extracellular matrix (ECM) production via dimethylmethylene blue (sulfated glycosaminoglycan) assay and hydroxyproline (collagen) assay. PLLA coated PGA scaffolds were analyzed using double stranded DNA quantification as areflection of cellularity and confocal laser microscopy in a fluorescent cell viability assay. Results. The highest cellularity occurred in PGA constructs cultured in a rotating bioreactor, which also had a mean sulfated glycosaminoglycan content of 22.3 µg per scaffold. PGA constructs cultured in static conditions had the lowest cellularity. Cells had difficulty adhering to OPLA and the PLLA coating of PGA scaffolds; cellularity was inversely proportional to the concentration of PLLA used. PLLA coating did not prevent dissolution of the PGA scaffolds. All cell scaffold types and culture conditions produced non-uniform cellular distribution. Discussion/Conclusion. FLS-seeding of PGA scaffolds cultured in a rotating bioreactor resulted in the most optimal cell and matrix characteristics seen in this study. Cells grew only in the pores of the OPLA sponge, and could not adhere to the PLLA coating of PGA scaffold, due to the hydrophobic property of PLA. While PGA culture in a bioreactor produced measureable GAG, no culture technique produced visible collagen. For this reason, and due to the dissolution of PGA scaffolds, the culture conditions and scaffolds described here are not recommended for inducing fibrochondrogenesis in equine FLS for meniscal tissue engineering.
Collapse
Affiliation(s)
- Jennifer J Warnock
- Comparative Orthopaedic Laboratory, University of Missouri , Columbia, MO , USA
| | - Derek B Fox
- Comparative Orthopaedic Laboratory, University of Missouri , Columbia, MO , USA
| | - Aaron M Stoker
- Comparative Orthopaedic Laboratory, University of Missouri , Columbia, MO , USA
| | - Mark Beatty
- VA Nebraska-Western Iowa Health Care System and University of Nebraska Medical Center College of Dentistry , Lincoln, NE , USA
| | - Mary Cockrell
- Comparative Orthopaedic Laboratory, University of Missouri , Columbia, MO , USA
| | - John C Janicek
- Comparative Orthopaedic Laboratory, University of Missouri , Columbia, MO , USA
| | - James L Cook
- Comparative Orthopaedic Laboratory, University of Missouri , Columbia, MO , USA
| |
Collapse
|
9
|
Yin Z, Schmid TM, Yasar TK, Liu Y, Royston TJ, Magin RL. Mechanical characterization of tissue-engineered cartilage using microscopic magnetic resonance elastography. Tissue Eng Part C Methods 2014; 20:611-9. [PMID: 24266395 DOI: 10.1089/ten.tec.2013.0408] [Citation(s) in RCA: 35] [Impact Index Per Article: 3.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 12/19/2022] Open
Abstract
Knowledge of mechanical properties of tissue-engineered cartilage is essential for the optimization of cartilage tissue engineering strategies. Microscopic magnetic resonance elastography (μMRE) is a recently developed MR-based technique that can nondestructively visualize shear wave motion. From the observed wave pattern in MR phase images the tissue mechanical properties (e.g., shear modulus or stiffness) can be extracted. For quantification of the dynamic shear properties of small and stiff tissue-engineered cartilage, μMRE needs to be performed at frequencies in the kilohertz range. However, at frequencies greater than 1 kHz shear waves are rapidly attenuated in soft tissues. In this study μMRE, with geometric focusing, was used to overcome the rapid wave attenuation at high frequencies, enabling the measurement of the shear modulus of tissue-engineered cartilage. This methodology was first tested at a frequency of 5 kHz using a model system composed of alginate beads embedded in agarose, and then applied to evaluate extracellular matrix development in a chondrocyte pellet over a 3-week culture period. The shear stiffness in the pellet was found to increase over time (from 6.4 to 16.4 kPa), and the increase was correlated with both the proteoglycan content and the collagen content of the chondrocyte pellets (R(2)=0.776 and 0.724, respectively). Our study demonstrates that μMRE when performed with geometric focusing can be used to calculate and map the shear properties within tissue-engineered cartilage during its development.
Collapse
Affiliation(s)
- Ziying Yin
- 1 Department of Bioengineering, University of Illinois at Chicago , Chicago, Illinois
| | | | | | | | | | | |
Collapse
|
10
|
Articular cartilage tissue regeneration—current research strategies and outlook for the future. Eur Surg 2013. [DOI: 10.1007/s10353-013-0217-9] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 10/26/2022]
|
11
|
Silverberg JL, Dillavou S, Bonassar L, Cohen I. Anatomic variation of depth-dependent mechanical properties in neonatal bovine articular cartilage. J Orthop Res 2013; 31:686-91. [PMID: 23280608 DOI: 10.1002/jor.22303] [Citation(s) in RCA: 28] [Impact Index Per Article: 2.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 08/14/2012] [Accepted: 12/04/2012] [Indexed: 02/04/2023]
Abstract
Articular cartilage has well known depth-dependent structure and has recently been shown to have similarly non-uniform depth-dependent mechanical properties. Here, we study anatomic variation of the depth-dependent shear modulus and energy dissipation rate in neonatal bovine knees. The regions we specifically focus on are the patellofemoral groove, trochlea, femoral condyle, and tibial plateau. In every sample, we find a highly compliant region within the first 500 µm of tissue measured from the articular surface, where the local shear modulus is reduced by up to two orders of magnitude. Comparing measurements taken from different anatomic sites, we find statistically significant differences localized within the first 50 µm. Histological images reveal these anatomic variations are associated with differences in collagen density and fiber organization.
Collapse
Affiliation(s)
- Jesse L Silverberg
- Department of Physics, Cornell University, C10 Clark Hall, Ithaca, NY 14853-2501, USA.
| | | | | | | |
Collapse
|
12
|
Bichara DA, O'Sullivan NA, Pomerantseva I, Zhao X, Sundback CA, Vacanti JP, Randolph MA. The tissue-engineered auricle: past, present, and future. TISSUE ENGINEERING PART B-REVIEWS 2011; 18:51-61. [PMID: 21827281 DOI: 10.1089/ten.teb.2011.0326] [Citation(s) in RCA: 102] [Impact Index Per Article: 7.8] [Reference Citation Analysis] [Abstract] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 11/13/2022]
Abstract
The reconstruction, repair, and regeneration of the external auricular framework continue to be one of the greatest challenges in the field of tissue engineering. To replace like with like, we should emulate the native structure and composition of auricular cartilage by combining a suitable chondrogenic cell source with an appropriate scaffold under optimal in vitro and in vivo conditions. Due to the fact that a suitable and reliable substitute for auricular cartilage has yet to be engineered, hand-carved autologous costal cartilage grafts and ear-shaped porous polyethylene implants are the current treatment modalities for auricular reconstruction. However, over the last decade, significant advances have been made in the field of regenerative medicine and tissue engineering. A variety of scaffolds and innovative approaches have been investigated as alternatives to using autologous carved costal cartilage or porous polyethylene implants. A review of recent developments and the current state of the art and science is presented, focusing on scaffolds, cell sources, seeding densities, and mechanical characteristics of tissue-engineered auricular cartilage.
Collapse
Affiliation(s)
- David A Bichara
- Plastic Surgery Research Laboratory, Division of Plastic Surgery, Harvard Medical School, Massachusetts General Hospital, Boston, Massachusetts 02114, USA
| | | | | | | | | | | | | |
Collapse
|
13
|
Borzacchiello A, Gloria A, Mayol L, Dickinson S, Miot S, Martin I, Ambrosio L. Natural/synthetic porous scaffold designs and properties for fibro-cartilaginous tissue engineering. J BIOACT COMPAT POL 2011. [DOI: 10.1177/0883911511420149] [Citation(s) in RCA: 45] [Impact Index Per Article: 3.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/16/2022]
Abstract
The goal of this study was to produce and characterize the scaffolds by combining the advantages of both natural and synthetic polymers for engineering fibro-cartilaginous tissues. Porous three-dimensional composite scaffolds were produced based on glycosaminoglycans and hyaluronic acid (HYAFF11) reinforced with polycaprolactone. The mechanical properties of scaffolds were evaluated as a function of time and compared with those of scaffolds seeded with human chondrocytes (constructs) and cultured in vitro up to 6 weeks. The composite scaffolds had a porosity of 68% with interconnected macropores with average pore sizes of 200 μm, an equilibrium swelling of 350%, and a predominant elastic behavior, typical of a macromolecular gel. The composite constructs maintained chondrocyte phenotype and degraded with the deposition of macromolecules synthesized by the cells. The scaffold presented mechanical properties and the ability to dissipate energy similar to the fibro-cartilaginous tissue.
Collapse
Affiliation(s)
- A. Borzacchiello
- Institute of Composite and Biomedical Materials-C.N.R and Interdisciplinary Research Centre on Biomaterials-University of Naples “Federico II” Piazzale Tecchio 80, 80125 Naples, Italy,
| | - A. Gloria
- Institute of Composite and Biomedical Materials-C.N.R and Interdisciplinary Research Centre on Biomaterials-University of Naples “Federico II” Piazzale Tecchio 80, 80125 Naples, Italy
| | - L. Mayol
- School of Biotechnological Sciences, Department of Pharmaceutical and Toxicological Chemistry, University of Naples, Federico , Via D. Montesano 49, 80131 Naples, Italy
| | - Sally Dickinson
- Department of Cellular & Molecular Medicine, University of Bristol, Bristol BS8 1TD, UK
| | - S. Miot
- Departments of Surgery and of Biomedicine, University Hospital Basel, Switzerland
| | - I. Martin
- Departments of Surgery and of Biomedicine, University Hospital Basel, Switzerland
| | - L. Ambrosio
- Institute of Composite and Biomedical Materials-C.N.R and Interdisciplinary Research Centre on Biomaterials-University of Naples “Federico II” Piazzale Tecchio 80, 80125 Naples, Italy
| |
Collapse
|
14
|
Erisken C, Kalyon DM, Wang H. Viscoelastic and Biomechanical Properties of Osteochondral Tissue Constructs Generated From Graded Polycaprolactone and Beta-Tricalcium Phosphate Composites. J Biomech Eng 2010; 132:091013. [DOI: 10.1115/1.4001884] [Citation(s) in RCA: 25] [Impact Index Per Article: 1.8] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/08/2022]
Abstract
The complex micro-/nanostructure of native cartilage-to-bone insertion exhibits gradations in extracellular matrix components, leading to variations in the viscoelastic and biomechanical properties along its thickness to allow for smooth transition of loads under physiological movements. Engineering a realistic tissue for osteochondral interface would, therefore, depend on the ability to develop scaffolds with properly graded physical and chemical properties to facilitate the mimicry of the complex elegance of native tissue. In this study, polycaprolactone nanofiber scaffolds with spatially controlled concentrations of β-tricalcium phosphate nanoparticles were fabricated using twin-screw extrusion-electrospinning process and seeded with MC3T3-E1 cells to form osteochondral tissue constructs. The objective of the study was to evaluate the linear viscoelastic and compressive properties of the native bovine osteochondral tissue and the tissue constructs formed in terms of their small-amplitude oscillatory shear, unconfined compression, and stress relaxation behavior. The native tissue, engineered tissue constructs, and unseeded scaffolds exhibited linear viscoelastic behavior for strain amplitudes less than 0.1%. Both native tissue and engineered tissue constructs demonstrated qualitatively similar gel-like behavior as determined using linear viscoelastic material functions. The normal stresses in compression determined at 10% strain for the unseeded scaffold, the tissue constructs cultured for four weeks, and the native tissue were 0.87±0.08 kPa, 3.59±0.34 kPa, and 210.80±8.93 kPa, respectively. Viscoelastic and biomechanical properties of the engineered tissue constructs were observed to increase with culture time reflecting the development of a tissuelike structure. These experimental findings suggest that viscoelastic material functions of the tissue constructs can provide valuable inputs for the stages of in vitro tissue development.
Collapse
Affiliation(s)
| | | | - Hongjun Wang
- Stevens Institute of Technology, Hoboken, NJ 07030
| |
Collapse
|
15
|
Moyer HR, Wang Y, Farooque T, Wick T, Singh KA, Xie L, Guldberg RE, Williams JK, Boyan BD, Schwartz Z. A New Animal Model for Assessing Cartilage Repair and Regeneration at a Nonarticular Site. Tissue Eng Part A 2010; 16:2321-30. [DOI: 10.1089/ten.tea.2009.0245] [Citation(s) in RCA: 17] [Impact Index Per Article: 1.2] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/12/2022] Open
Affiliation(s)
- Hunter R. Moyer
- Division of Plastic and Reconstructive Surgery, Department of Surgery, Emory University School of Medicine, Atlanta, Georgia
| | - Yun Wang
- Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, Georgia
| | - Tanya Farooque
- Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, Georgia
| | - Timothy Wick
- Department of Biomedical Engineering, University of Alabama at Birmingham, Birmingham, Alabama
| | - Kimberly A. Singh
- Division of Plastic and Reconstructive Surgery, Department of Surgery, Emory University School of Medicine, Atlanta, Georgia
| | - Liqin Xie
- Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, Georgia
| | - Robert E. Guldberg
- Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, Georgia
| | - Joseph K. Williams
- Division of Plastic and Reconstructive Surgery, Department of Surgery, Emory University School of Medicine, Atlanta, Georgia
- Children's Healthcare of Atlanta, Atlanta, Georgia
| | - Barbara D. Boyan
- Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, Georgia
| | - Zvi Schwartz
- Institute for Bioengineering and Bioscience, Georgia Institute of Technology, Atlanta, Georgia
| |
Collapse
|
16
|
|
17
|
Concaro S, Nicklasson E, Ellowsson L, Lindahl A, Brittberg M, Gatenholm P. Effect of cell seeding concentration on the quality of tissue engineered constructs loaded with adult human articular chondrocytes. J Tissue Eng Regen Med 2008; 2:14-21. [PMID: 18265427 DOI: 10.1002/term.60] [Citation(s) in RCA: 16] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/08/2022]
Abstract
Many aspects of the process of in vitro differentiation of chondrocytes in three-dimensional (3D) scaffolds need to be further investigated. Chitosan scaffolds were produced by freeze-drying 3% w/v 90% DDA chitosan gels. The effect of the cell seeding concentration was evaluated by culturing human adult chondrocytes in chitosan scaffolds After the first passage, cells were seeded into chitosan scaffolds with a diameter of 8 mm. The final cell seeding concentration per cm3 of chitosan scaffold was: Group A, 3 x 10(6); Group B, 6 x 10(6); Group C, 12 x 10(6); and Group D, 25 x 10(6) cells. After 14 and 28 days in 3D culture, the constructs were assesed for collagen, glucosaminoglycans and DNA content. The mechanical properties of the constructs were determined using a dynamic oscillatory shear test. The histological aspect of the constructs was evaluated using the Bern score. The collagen and GAG concentration increased, varying the cell seeding concentration. There was a significant increase in proteoglycan and hydroxyproline production between groups C and D. The sulphated GAG content increased significantly in the group D as compared to the other groups. The mechanical properties of the different constructs increased over time, from 9.6 G'/kPa at 14 days of 3D culture to 14.6 G'/kPa at 28 days under the same culture conditions. In this study we were able to determine that concentrations of 12-25 million cells/cm2 are needed to increase the matrix production and mechanical properties of human adult chondrocytes under static conditions.
Collapse
Affiliation(s)
- Sebastian Concaro
- Department of Orthopaedic Surgery, Sahlgrenska University Hospital, Gothenburg, Sweden.
| | | | | | | | | | | |
Collapse
|
18
|
Chiu WT, Wang YH, Tang MJ, Shen MR. Soft substrate induces apoptosis by the disturbance of Ca2+ homeostasis in renal epithelial LLC-PK1 cells. J Cell Physiol 2007; 212:401-10. [PMID: 17311296 DOI: 10.1002/jcp.21037] [Citation(s) in RCA: 11] [Impact Index Per Article: 0.6] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/10/2022]
Abstract
Different rigidities of adhesive collagen substrate affect cellular functions with unclear mechanisms. Here, we cultured a renal epithelial cell line (LLC-PK1) and a tumor cell line (HeLa) on substrates of different rigidities and compared the cell type-specific responses. The culture dish was coated with a very thin layer of collagen gel (control group) or overlaid with collagen gel (soft substrate). LLC-PK1 cells contracted as they grew on collagen gel and the apoptotic bodies obviously appeared with time. The protein levels of procaspase-12 and its downstream target procaspase-3 were decreased when LLC-PK1 cells cultured on collagen gel. Mu-calpain was activated on collagen gel. Collage gel also induced the cleavage of alpha-spectrin which resulted in the disorganization of actin cytoskeleton. In contrast, there was no significant change in cytochrome c revelation, mitochondrial membrane potential, and the protein levels of procaspase-8 and procaspase-9. Moreover, soft substrate caused elevated cytosolic Ca(2+), Ca(2+) overload in ER and upregulation of capacitative calcium entry. Ca(2+) chelator or channel blocker partially rescued the collagen-gel induced apoptosis by inhibiting mu-calpain activation. In contrast, for HeLa cells cultured either on collagen gel or on gel-coated dish, there was no significant change in positive Annexin V staining, no activation of procaspase-12 and no cleavage of mu-calpain. Thus, soft substrate induces apoptosis in LLC-PK1 cells by the disturbance of Ca(2+) homeostasis.
Collapse
Affiliation(s)
- Wen-Tai Chiu
- Institute of Basic Medical Sciences, National Cheng Kung University, Tainan, Taiwan
| | | | | | | |
Collapse
|
19
|
Schulz RM, Bader A. Cartilage tissue engineering and bioreactor systems for the cultivation and stimulation of chondrocytes. EUROPEAN BIOPHYSICS JOURNAL: EBJ 2007; 36:539-68. [PMID: 17318529 DOI: 10.1007/s00249-007-0139-1] [Citation(s) in RCA: 156] [Impact Index Per Article: 9.2] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 07/31/2006] [Revised: 01/23/2007] [Accepted: 01/29/2007] [Indexed: 12/14/2022]
Abstract
Damage to and degeneration of articular cartilage is a major health issue in industrialized nations. Articular cartilage has a particularly limited capacity for auto regeneration. At present, there is no established therapy for a sufficiently reliable and durable replacement of damaged articular cartilage. In this, as well as in other areas of regenerative medicine, tissue engineering methods are considered to be a promising therapeutic component. Nevertheless, there remain obstacles to the establishment of tissue-engineered cartilage as a part of the routine therapy for cartilage defects. One necessary aspect of potential tissue engineering-based therapies for cartilage damage that requires both elucidation and progress toward practical solutions is the reliable, cost effective cultivation of suitable tissue. Bioreactors and associated methods and equipment are the tools with which it is hoped that such a supply of tissue-engineered cartilage can be provided. The fact that in vivo adaptive physical stimulation influences chondrocyte function by affecting mechanotransduction leads to the development of specifically designed bioreactor devices that transmit forces like shear, hydrostatic pressure, compression, and combinations thereof to articular and artificial cartilage in vitro. This review summarizes the basic knowledge of chondrocyte biology and cartilage dynamics together with the exploration of the various biophysical principles of cause and effect that have been integrated into bioreactor systems for the cultivation and stimulation of chondrocytes.
Collapse
Affiliation(s)
- Ronny Maik Schulz
- Department of Cell Techniques and Applied Stem Cell Biology, Center of Biotechnology and Biomedicine, University of Leipzig, Leipzig, Germany.
| | | |
Collapse
|
20
|
Kelly DJ, Crawford A, Dickinson SC, Sims TJ, Mundy J, Hollander AP, Prendergast PJ, Hatton PV. Biochemical markers of the mechanical quality of engineered hyaline cartilage. JOURNAL OF MATERIALS SCIENCE. MATERIALS IN MEDICINE 2007; 18:273-81. [PMID: 17323158 DOI: 10.1007/s10856-006-0689-2] [Citation(s) in RCA: 33] [Impact Index Per Article: 1.9] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 06/15/2006] [Accepted: 09/25/2006] [Indexed: 05/14/2023]
Abstract
The aim of this study was to determine whether or not biochemical markers can be used as surrogate measures for the mechanical quality of tissue engineered cartilage. The biochemical composition of tissue engineered cartilage constructs were altered by varying either (i) the initial cell seeding density of the scaffold (seeding density protocol) or (ii) the length of time the engineered tissue was cultured (culture period protocol). The aggregate or Young's moduli of the constructs were measured (by confined or unconfined compression respectively), and compared with the composition of the extracellular matrix by quantitative measurement of the glycosaminoglycan (GAG), hydroxyproline, collagen I and collagen II and collagen cross-links. The aggregate modulus correlated positively with both GAG and collagen II content, but not with collagen I content. Young's modulus correlated positively with GAG, collagen II and collagen I content, and the ratio of mature to immature cross-links. There was no significant correlation of Young's Modulus with total collagen measured as hydroxyproline content. These results suggested that hydroxyproline determination may be an unreliable indicator of mechanical quality of tissue engineered cartilage, and that a measure of collagen II and GAG content is required to predict the biomechanical quality of tissue engineered cartilage.
Collapse
Affiliation(s)
- Daniel J Kelly
- Centre for Bioengineering, Trinity College, Dublin, Ireland
| | | | | | | | | | | | | | | |
Collapse
|
21
|
Patil S, Li Z, Chan C. Cellular to tissue informatics: approaches to optimizing cellular function of engineered tissue. ADVANCES IN BIOCHEMICAL ENGINEERING/BIOTECHNOLOGY 2006; 102:139-59. [PMID: 17089789 DOI: 10.1007/10_009] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.1] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 05/12/2023]
Abstract
Tissue engineering is a rapidly expanding, multi-disciplinary field in biomedicine. It provides the ability to manipulate living cells and biomaterials for the purpose of restoring, maintaining, and enhancing tissue and organ function. Scientists have engineered various tissues in the body, from skin substitutes to artificial nerves to heart tissues, with varying degrees of success. Although the field of tissue engineering has come a long way since its first successful demonstration by Bisceglie in the 1930s, methods of coaxing them into functional tissues have been predominantly empirical to date. To successfully develop tissue-engineered organs, it is important to understand how to maintain the cells under conditions that maximize their ability to perform their physiological roles, regardless of their environment. In that context, a methodology that combines empirical data with mathematical and statistical techniques, such as metabolic engineering and cellular informatics, to systematically determine the optimal (1) type of cell to use, (2) scaffold properties and the corresponding processing conditions to achieve those properties, and (3) the required types and levels of environmental factors and the operating conditions needed in the bioreactor, will enable the design of viable and functional tissues tailored to the specific requirements of individual situations.
Collapse
Affiliation(s)
- Sachin Patil
- Department of Chemical Engineering and Material Science, Michigan State University, East Lansing 48824, USA
| | | | | |
Collapse
|
22
|
Bueno EM, Bilgen B, Barabino GA. Wavy-Walled Bioreactor Supports Increased Cell Proliferation and Matrix Deposition in Engineered Cartilage Constructs. ACTA ACUST UNITED AC 2005; 11:1699-709. [PMID: 16411815 DOI: 10.1089/ten.2005.11.1699] [Citation(s) in RCA: 42] [Impact Index Per Article: 2.2] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/13/2022]
Abstract
Hydrodynamic forces in bioreactors can decisively influence extracellular matrix deposition in engineered cartilage constructs. In the present study, the reduced fluid shear, high-axial mixing environment provided by a wavy-walled bioreactor was exploited in the cultivation of cartilage constructs using polyglycolic acid scaffolds seeded with bovine articular chondrocytes. Increased growth as defined by weight, cell proliferation and extracellular matrix deposition was observed in cartilage constructs from wavy-walled bioreactors in comparison with those from spinner flasks cultured under the same conditions. The wet weight composition of 4-week constructs from the wavy-walled bioreactor was similar to that of spinner flask constructs, but the former were 60% heavier due to equally higher incorporation of extracellular matrix and 30% higher cell population. It is most likely that increased construct matrix incorporation was a result of increased mitotic activity of chondrocytes cultured in the environment of the wavy-walled bioreactor. A layer of elongated cells embedded in type I collagen formed at the periphery of wavy-walled bioreactor and spinner flask constructs, possibly as a response to local shear forces. On the basis of the robustness and reproducibility of the extracellular matrix composition of cartilage constructs, the wavy-walled bioreactor demonstrated promise as an experimental cartilage tissue-engineering vessel. Increased construct growth in the wavy-walled bioreactor may lead to enhanced mechanical properties and expedited in vitro cultivation.
Collapse
Affiliation(s)
- Ericka M Bueno
- Department of Chemical Engineering, Northeastern University, Boston, Massachusetts 02115, USA
| | | | | |
Collapse
|
23
|
Raimondi MT, Pietrabissa R. Contact pressures at grafted cartilage lesions in the knee. Knee Surg Sports Traumatol Arthrosc 2005; 13:444-50. [PMID: 16170578 DOI: 10.1007/s00167-004-0529-1] [Citation(s) in RCA: 12] [Impact Index Per Article: 0.6] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Received: 11/09/2003] [Accepted: 03/16/2004] [Indexed: 10/26/2022]
Abstract
The use of tissue-engineered cellular constructs is currently under clinical evaluation for the surgical treatment of articular cartilage lesions in the knee. The primary failure mode in such cartilage repair techniques is related to fixation. In addition, the repair tissue is believed to be very fragile in the post-operative period, and unable to support the intra-articular loads. We have developed a laboratory testing protocol in order to quantify the contact pressure distribution that develops on fibrin glue grafts applied to full-thickness cartilage lesions. The contact pressure distribution has been mapped on the contact surface of specimens subject to compression, in three configurations (intact, defect and grafted), at increasing load levels. All the maps show stress concentrations at the rim of the defect and a more uniform stress distribution around the rim after defect grafting. At a contact load of 180 N, the peak contact pressure measured on cartilage is 2.5 MPa. In presence of the graft, the peak pressures on the cartilage area surrounding the defect are reduced by 16%, on average. In contrast, both the mean contact pressure on the graft and the graft's contact area increase. The graft was found to carry around 80% of the total applied contact load, at all load levels tested. Fibrin glue was chosen as a grafting material in our study because it shows material properties very representative of currently-implanted cellular constructs. Thus, the results of this study have quantified aspects of recipient graft sites that may assist in optimising such grafting procedures from a biomechanical point of view.
Collapse
Affiliation(s)
- Manuela T Raimondi
- Laboratory of Biological Structure Mechanics, Dipartimento di Bioingegneria, Politecnico Di Milano, Piazza Leonardo da Vinci 32, 20133 Milan, Italy.
| | | |
Collapse
|
24
|
Chang SCN, Tobias G, Roy AK, Vacanti CA, Bonassar LJ. Tissue engineering of autologous cartilage for craniofacial reconstruction by injection molding. Plast Reconstr Surg 2003; 112:793-9; discussion 800-1. [PMID: 12960860 DOI: 10.1097/01.prs.0000069711.31021.94] [Citation(s) in RCA: 76] [Impact Index Per Article: 3.6] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 10/26/2022]
Abstract
Each year, more than one million patients undergo some type of procedure involving cartilage reconstruction. Polymer hydrogels such as alginate have been demonstrated to be effective carriers of chondrocytes for subcutaneous cartilage formation. The goal of this study was to develop a simple method to create complex structures with good three-dimensional tolerance in order to form cartilage in specific shapes in an autologous animal model. Six alginate implants that had been seeded with autologous chondrocytes through an injection molding process were implanted subcutaneously in sheep, harvested after 6 months, and analyzed histologically, biochemically, and biomechanically, in comparison with original auricular cartilage. Molds of craniofacial implants were prepared with Silastic E RTV (Dow Corning, Midland, Mich.). Chondrocytes were harvested from sheep auricular cartilage and suspended in 2% alginate at a concentration of 50 x 10(6) cells/ml. The mixture of cells and gel was injected into the Silastic molds and removed after 20 minutes. Chondrocyte-alginate constructs were implanted subcutaneously in the necks of the sheep from which the cells had originally been harvested, and the constructs were removed after 30 weeks. Analyses of the implanted constructs indicated cartilage formation with three-dimensional shape retention. The proteoglycan and collagen contents of the constructs increased with time to approximately 80 percent of the values for native tissue. The equilibrium modulus and the hydraulic permeability were 74 and 105 percent of those of native sheep auricular cartilage, respectively.
Collapse
Affiliation(s)
- Sophia C N Chang
- Center for Tissue Engineering, University of Massachusetts Medical School, Worcester, USA
| | | | | | | | | |
Collapse
|
25
|
Saha AK, Mazumdar JN. Dynamics of the cell and its extracellular matrix-a simple mathematical approach. IEEE Trans Nanobioscience 2003; 2:89-93. [PMID: 15382664 DOI: 10.1109/tnb.2003.813921] [Citation(s) in RCA: 9] [Impact Index Per Article: 0.4] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/07/2022]
Abstract
The extracellular matrix (ECM) is produced by the cells and secreted into the surrounding medium, and consists of a complex mixture of structural and functional proteins. It has been recently observed that the ECM can influence the behavior of cell growth in vitro quite remarkably. A simple mathematical model has been constructed based on negative feedback control mechanisms to represent the dynamics of ECM deposition and cellular differentiation. The model analysis shows a strong relationship between the numerical solution and the experimental observations in cell-polymer constructs for the design of engineered cartilage. The current paper may be a useful guide for those who want to explore the studies on cell-matrix interactions.
Collapse
Affiliation(s)
- A K Saha
- IRIS, Swinburne University of Technology, PO Box 218, Hawthorn, Melbourne, Vic. 3122, Australia
| | | |
Collapse
|
26
|
Abstract
Mathematical models to describe extracellular matrix (ECM) deposition and scaffold degradation in cell-polymer constructs for the design of engineered cartilage were developed and validated. The ECM deposition model characterized a product-inhibition mechanism in the concentration of cartilage molecules, collagen and glycosaminoglycans (GAG). The scaffold degradation model used first-order kinetics to describe hydrolysis (not limited by diffusion) of biodegradable polyesters, polyglycolic acid and polylactic acid. Each model was fit to published accumulation and degradation data. As experimental validation, cell-polymer constructs (n=24) and unseeded scaffolds (n=24) were cultured in vitro. Biochemical assays for ECM content and measurements of scaffold mass were performed at 1, 2, 4, 6, 8, or 10 weeks (n=8 per time point). The models demonstrated a strong fit with published data and experimental results (R(2)=0.75 to 0.99) and predicted the temporal total construct mass with reasonable accuracy (30% RMS error). This approach can elucidate mechanisms governing accumulation/degradation and may be coupled with structure-function relationships to describe time-dependent changes in construct elastic properties.
Collapse
Affiliation(s)
- Christopher G Wilson
- Department of Biomedical Engineering, Worcester Polytechnic Institute, Worcester, MA 01609, USA
| | | | | |
Collapse
|
27
|
Harada Y, Tomita N, Wakitani S, Mii Y, Oka M, Tsutsumi S. Use of controlled mechanical stimulation in vivo to induce cartilage layer formation on the surface of osteotomized bone. TISSUE ENGINEERING 2002; 8:969-78. [PMID: 12542942 DOI: 10.1089/107632702320934065] [Citation(s) in RCA: 12] [Impact Index Per Article: 0.5] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 11/13/2022]
Abstract
A micromachine was used to study the response of mesenchymal tissue to mechanically controlled motion in vivo. The middle portion of the coccygeal vertebra of Fischer 344 rats was osteotomized, and continuous bending motion was applied for 4 weeks. The experimental groups were divided into two groups with higher sliding displacement applied at the osteotomized gap of group II. Hyaline cartilage tissue was generated at the osteotomized ends, and was predominantly formed on the side that extended during the bending motion. These newly formed tissues stained intensively with safranin O and toluidine blue, positively with immunostain for type II collagen, but negatively with immunostain for type I collagen. Articular cartilage-like tissues with a surface and a layer structure were obtained in group II, in which higher sliding motion was applied. Light and electron microscopy revealed morphological features similar to those of normal articular cartilage tissue in the superficial and middle zones of the tissues obtained in group II. Collagen fibrils in the superficial zone were found aligned parallel to the smooth surface. Although tidemark formation was not observed in the deep zone, the structure was much more natural than that of any other tissue-engineered cartilage reported to date. These results suggest that controlled sliding stimulation can elicit the generation of articular cartilage structure in vivo.
Collapse
Affiliation(s)
- Yasuji Harada
- International Innovation Center, Kyoto University, Kyoto, Japan
| | | | | | | | | | | |
Collapse
|
28
|
Parsons JW, Coger RN. A new device for measuring the viscoelastic properties of hydrated matrix gels. J Biomech Eng 2002; 124:145-54. [PMID: 12002123 DOI: 10.1115/1.1448822] [Citation(s) in RCA: 8] [Impact Index Per Article: 0.4] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/08/2022]
Abstract
Determinations of the viscoelastic properties of extracellular matrices (ECMs) are becoming increasingly important for accurate predictive modeling of biological systems. Since the interactions of the cells with the ECM and surrounding fluid (e.g., blood, media) each affect cell behavior; it is advantageous to evaluate the ECM's material properties in the presence of the hydrating fluid. Conventional rheometry methods evaluate the bulk material properties of gel materials while displacing the hydrating liquid film. Such systems are therefore nonideal for testing materials such as ECMs, whose properties change with dehydration. The new patent pending, piezoelectrically actuated linear rheometer is designed to eliminate this problem. It uses a single cantilever to apply an oscillating load to the gel and to sense the gel's deflection. Composed of two thin film piezopolymer layers, the cantilever uses one layer as the actuator, and the second piezopolymer layer to measure the lateral movement of its attached probe. The viscoelastic nature of the ECM adds stiffness and damping to the system, resulting in the attenuation and phase shift of the sensor's output voltage. From these parameters, the ECM's shear storage and loss moduli are then determined. Initial tests on the BioMatrix I and type I collagen ECMs reveal that the first prototype of the piezoelectrically actuated linear rheometer is capable of accurately determining the trend and order of magnitude of an ECM's viscoelastic properties. In this paper, details of the rheometer's design and operating principles are described.
Collapse
Affiliation(s)
- Jeffrey W Parsons
- Mechanical Engineering and Engineering Science, University of North Carolina-Charlotte, 28223-0001, USA
| | | |
Collapse
|
29
|
Lu L, Zhu X, Valenzuela RG, Currier BL, Yaszemski MJ. Biodegradable polymer scaffolds for cartilage tissue engineering. Clin Orthop Relat Res 2001:S251-70. [PMID: 11603709 DOI: 10.1097/00003086-200110001-00024] [Citation(s) in RCA: 163] [Impact Index Per Article: 7.1] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Submit a Manuscript] [Subscribe] [Scholar Register] [Indexed: 01/31/2023]
Abstract
Cartilage defects are common, painful conditions and none of the currently available treatment options are satisfactory. Tissue engineering techniques involving scaffolds made from biodegradable synthetic polymers hold great promise for the future. These materials can be manufactured in an injectable form for minimally invasive procedures or in a preformed state to treat large irreparable lesions including arthritis. The mechanical and biologic properties of synthetic polymers can be tailored to different clinical applications and engineering strategies. The scaffold serves as a mechanical substrate for cells and bioactive factors and can help direct and organize the process of regeneration. The ultimate goal of tissue engineering is to recapitulate normal organogenesis to create histologically and functionally normal tissue. A review of the characteristics and potential of synthetic polymers shows that these substances will play a major role in treating cartilage disorders.
Collapse
Affiliation(s)
- L Lu
- Department of Orthopedic Surgery, Mayo Clinic, Rochester, MN 55905, USA
| | | | | | | | | |
Collapse
|
30
|
Affiliation(s)
- C A Heath
- Iowa State University, Department of Chemical Engineering, Ames, IA 50011-2230, USA.
| |
Collapse
|
31
|
Abstract
This article reviews the key developments in the tissue engineering field over the past several years. The issues related to the development of the components of tissue-engineered products including cells, biomaterials, and biomolecules, and their integration into safe and effective products are presented. Moreover, the article outlines the challenges to the commercialization of tissue-engineered products, and highlights the ongoing efforts by the American Society for Testing and Materials (ASTM) in developing standards for tissue-engineered medical products. Furthermore, funding opportunities at the Advanced Technology Program at NIST are presented. Published 2000 John Wiley & Sons, Inc.
Collapse
Affiliation(s)
- M S Chapekar
- Chemistry and Life Sciences Office, National Institute of Standards and Technology, U.S. Department of Commerce, Gaithersburg MD 20899, USA.
| |
Collapse
|
32
|
|