Second-generation proximally coated titanium femoral component: minimum 7-year results

Neocortex Formation in a Tapered Wedge Stem is Not Indicative of Complications or Worse Outcomes

BACKGROUND

The formation of sclerotic bone, a neocortex, distally surrounding total hip arthroplasty (THA) stems may commonly be seen on radiographs around proximally porous coated stems but can be confused with loosening. The goal of this study was to determine the prevalence of the neocortex finding and whether it associated with worse outcomes after THA.

METHODS

A retrospective review of 825 patients with a single tapered wedge stem was performed. Radiographs at 1-year, as well as final follow-up were reviewed for evidence of sclerotic bone (neocortex) surrounding the stem in all 14 Gruen zones. The final attending radiology read of lucency was also recorded. Patients were grouped by the presence of the neocortex. PROMIS Physical Function scores and complications were compared between neocortex groups.

RESULTS

The neocortex group had 558 (68%) patients compared to 267 (32%) in the no neocortex group. The most common Gruen zones for evidence of neocortex were 10 (55%), 11 (52%), and 12 (51%). Seven percent of patients had a finding of lucency on radiology read. There was no difference between groups in terms of dislocations (P = .61), infection (P = .79), fracture rates (P = .54), revision surgery (P = .73), and reoperation for any cause (P = .62). PROMIS PF scores were significantly higher in the neocortex group (P < .0001).

CONCLUSION

The presence of a distal neocortex is a common finding on radiographs after THA with this proximally porous-coated tapered wedge stem and does not portend worse outcomes, nor is it a sign of aseptic loosening, increased revision rates, infection, dislocation, or periprosthetic fracture risk.

Does femoral morphology and stem alignment influence outcomes of cementless total hip arthroplasty with proximally coated double-tapered titanium stems?

INTRODUCTION

Stem subsidence and thigh pain can cause significant patient dissatisfaction after cementless THA. The purpose of this study was to examine the effect of proximal-femoral morphology and stem alignment on clinical outcomes using a double-tapered, cementless titanium femoral component.

METHODS

We retrospectively reviewed 281 consecutive, primary THAs from 2012 to 2014 with a mean follow-up of 4 years. Preoperative radiographs were used to assess femoral neck shaft angle (FNS), canal flare index (CFI), Dorr classification, and greater trochanter (GT) overhang. Postoperative radiographs were used to determine stem alignment and 6-week follow-up radiographs were used to determine subsidence. Clinical outcomes included thigh pain, leg-length discrepancy (LLD), patient-reported outcome measures (PROMs) and revision surgeries.

RESULTS

271 stems (96%) did not subside (<4 mm) and 10 (4%) showed evidence of subsidence (>4 mm). Subsidence was significantly associated with subsequent revision surgery (p < 0.01). 278 stems (99%) were in neutral alignment and 3 in varus (1%). Alignment did not significantly influence subsidence, thigh pain, LLD, revisions, or PROMs. Femoral morphology measures (FNS, CFI, Dorr classification, and GT overhang) were not significantly associated with stem alignment, subsidence, LLD, or revisions. CFI was significantly associated with intraoperative calcar fractures (p = 0.02). GT overhang was associated with thigh pain (p = 0.03) and FNS was inversely associated with postoperative HOOS scores.

CONCLUSIONS

Subsidence and proximal-femoral morphology are potential sources of postoperative morbidity in certain cementless THA patients. In accordance with prior studies, CFI was identified as a potential risk factor for intraoperative calcar fractures. More research into preoperative femoral morphologies, such as GT overhang and FNS, is warranted as these may contribute to unsatisfactory results related to cementless THA.

Does Femoral Morphology Predict the Risk of Periprosthetic Fracture After Cementless Total Hip Arthroplasty?

BACKGROUND

Periprosthetic femur fracture remains a leading mode of early failure following cementless total hip arthroplasty (THA). The purpose of this study is to determine if a specific femoral morphology is associated with an increased risk of acute, periprosthetic fracture after cementless THA.

METHODS

An institutional arthroplasty registry was used to identify 32 primary, cementless THAs revised for acute, postoperative periprosthetic fracture ("fracture" cohort) within 3 months of the index procedure. Patients were matched 1:2 to 64 THAs without fracture ("control" cohort) for age, body mass index, gender, and stem design. Preoperative radiographic measurements performed on anteroposterior pelvis and femur radiographs included the neck-shaft angle, endosteal width at 4 locations, and external cortical diameter at 2 locations. These measurements were used to calculate the morphological cortical index, canal flare index, canal calcar ratio, and canal bone ratio. Postoperative measurements included canal fill and stem alignment. Statistical analyses included clustered regressions, Fisher's exact test, and Student's t-test.

RESULTS

The mean endosteal width at 10 cm distal to the lesser trochanter was greater in fracture patients, although not statistically significant (P = .1). However, this resulted in differences in the canal flare index (P = .03), canal calcar ratio (P = .03), and canal bone ratio (P = .03) between the 2 cohorts. These ratios indicate decreased meta-diaphyseal taper in fracture patients. Preoperative femoral neck-shaft angle was more varus in fracture patients (P = .04).

CONCLUSION

Patients sustaining an acute, periprosthetic fracture with cementless femoral fixation after THA had thinner distal cortices and a decreased meta-diaphyseal taper.

New Approach and Stem Increased Femoral Revision Rate in Total Hip Arthroplasty

This study compared the femoral stem revision and loosening rates in primary total hip arthroplasty between 2 different approaches and stem designs. Recent reports comparing the direct anterior approach with either the posterior or lateral approach showed that patients undergoing the direct anterior approach have less pain and an accelerated functional recovery in the early postoperative period. After converting to an anterior approach, the authors observed an increased rate of femoral stem revision. From 2003 to 2009, a posterior or lateral approach was used to insert 514 stems of 2 designs. These cases included the use of an extensively coated cobalt-chrome stem (n=232) or a straight, dual-tapered, proximally porous-coated titanium stem (n=282). In the following years, from 2009 to 2012, 594 short, proximally coated, titanium tapered-wedge stems were inserted through a direct anterior approach. The revision rates of femoral stems inserted through a posterior approach or a lateral approach were compared with those inserted via a direct anterior approach. No stem revisions occurred in the posterior approach group or the lateral approach group, and 5 stems were revised in the anterior approach group for periprosthetic fracture or aseptic loosening (0.8%). Significantly more stem revisions occurred after the use of the new stem design and a direct anterior approach (P=.04).

In vivo testing of canine prosthetic femoral components with HA-Ti ladder-type coating on vacuum plasma-sprayed Ti substrate

The purpose of the present study was to observe the structure and functional change of the bone-coating-prosthesis interface in vivo and to evaluate the histocompatibility of self-made prosthetic femoral components in the body and the degree of their bonding with the surrounding bone tissues as well as their stability. Six mature beagle dogs underwent bilateral hip replacement with prosthetic femur components. Three groups were established in terms of different coating of prothesis (four joints in each group): atmosphere (A) plasma-sprayed pure titanium (Ti) prosthetic joint with hydroxyapatite (HA) coating (HA+Ti+A group); vacuum (V) plasma-sprayed pure Ti prosthetic joint with HA coating (HA+Ti+V group); vacuum plasma-sprayed pure Ti prosthetic joint with Ti-HA stepped coating (Ti+HAG+Ti+V group). The hip joints were functionally evaluated, and subjected to X-ray examination, biomechanics inspection, and histological examination. As a result, X-ray imaging revealed all prosthetic joints were in a good location and no dislocation of joint was found. Shear strength of interface was significantly higher in Ti+HAG+Ti+V group than in HA+Ti+V group (P<0.05) and HA+Ti+A group (P<0.05) at 28th week. Histological examination showed the amount of newborn bone in Ti+HAG+Ti+V group was more than in HA+Ti+V group and HA+Ti+A group after 28 weeks. It was suggested that vacuum plasma-sprayed pure Ti prosthetic joint with TI-HA stepped coating could improve the bonding capacity of bone-prosthesis, enhance the stability of prosthesis, and increase the fixion of prosthetic femoral components because of better bone growth. This new type of biological material in prosthetic femoral components holds promises for application in clinical practice.

Long-term follow-up results of a second-generation cementless femoral prosthesis with a collar and straight distal fixation channels

PURPOSE

We evaluated the results of more than 10 years of follow-up of total hip arthroplasty using a second-generation cementless femoral prosthesis with a collar and straight distal fixation channels.

MATERIALS AND METHODS

One hundred five patients (129 hips) who underwent surgery between 1991 and 1996 for primary total hip arthroplasty using cementless straight distal fluted femoral stems were followed for more than 10 years. Ninety-four hips in 80 patients were available for clinical and radiologic analysis. The mean age at the time of surgery was 47 years, and the mean duration of follow-up was 14.3 years.

RESULTS

The mean Harris hip scores had improved from 58 points to 88 points at the time of the 10-year follow-up. Activity-related thigh pain was reported in nine hips (10%). At the last follow-up, 93 stems (99%) were biologically stable and one stem (1%) was revised because of loosening. No hip had distal diaphyseal osteolysis. Proximal femoral stress-shielding was reported in 86 hips (91%). We found no significant relationship between collar-calcar contact and thigh pain, stem fixation status, or stress-shielding. The cumulative survival of the femoral stem was 99% (95% confidence interval, 98-100%) after 10 years.

CONCLUSION

The long-term results of total hip arthroplasty using a second-generation cementless femoral prosthesis with a collar and straight distal fixation channels were satisfactory; however, the high rate of proximal stress-shielding and the minimal effect of the collar indicate the need for some changes in the stem design.

Distal fixation of proximally coated tapered stems may predispose to a failure of osteointegration

Despite excellent long-term results of proximally coated tapered wedge femoral stems in noncemented total hip arthroplasty, we have consistently observed a minority fail to achieve osteointegration. We retrospectively reviewed 320 consecutive total hip arthroplasties performed by a single surgeon using a single stem over a 4-year period. Clinical and radiographic parameters were analyzed for risk factors predisposing to a failure of osteointegration, defined as a progressive circumferential radiolucency around the proximal porous coating on both anteroposterior and lateral radiographs. Fifteen stems (4.7%) failed to osteointegrate; 3 underwent femoral revision for persistent thigh pain, whereas the remainder expressed varying degrees of symptomatology. Risk factors associated with failure of osteointegration were male sex, a smaller canal-flare index, larger stem size, and greater canal fill at the mid- and distal-thirds of the stem. Awareness of variability in proximal femoral morphology and problems caused by distal fixation with a proximally coated implant may help avoid this uncommon but potentially serious complication.

Failure modes of 433 metal-on-metal hip implants: how, why, and wear

Metal-on-metal total hip replacements (THRs) and hip resurfacings are coming under increasing scrutiny in light of concerns that they fail because of high wear and elevated metal ions. The aim of this study was to investigate the modes of failure in a collection of 433 metal-on-metal THRs and hip resurfacings and to examine the correlations between the reasons for revision and a range of patient and implant variables considered relevant to implant wear.

Early Post-operative Periprosthetic Femur Fracture in the Presence of a Non-cemented Tapered Wedge Femoral Stem

Non-cemented femoral fixation in hip arthroplasty has become the standard of practice in the USA. However, recent literature has brought attention to an increasing incidence of periprosthetic femur fractures with certain stem designs. This study examines reasons for early periprosthetic femur fractures in patients with a hip arthroplasty performed using a non-cemented tapered wedge stem design. A multivariate analysis using a matched-cohort design was performed to assess any potential risk factors that may predispose to such fractures. Six of 2,220 hips (0.3%) suffered a periprosthetic femur fracture within the first year after surgery; five of six were Vancouver Type B2. The average time to fracture was 9 weeks. This group of patients had a significantly higher canal-flare index and lower canal-calcar ratio. This complication may be preventable by having a better appreciation of the fit between the implant and the bone during pre-operative planning, with the goal of avoiding a proximal-distal mismatch.

Clinical and radiographic results for the Richards Modular Hip System prosthesis in total hip arthroplasty: average 10-year follow-up

The clinical results of total hip arthroplasty using the Richards Modular Hip System prosthesis were evaluated in 41 patients (44 joints). The mean Harris hip score improved from 42 points before surgery to 82 after 1 year, 85 at 5 years, and 79 at the final examination. The average polyethylene wear rate was 0.09 +/- 0.07 mm/y. Forty joints (90.9%) achieved press fit in either of the proximal or the distal stem portion, and only 4 joints (9.1%) failed to achieve press fit in both the proximal and distal stem portions. Although the 10-year survival of the stem was 94.5% and no revisions of the stem were performed, osteolysis was found at high frequency at a distal stem. The high incidence of osteolysis has been the limiting factor in the long-term success of Richards Modular Hip System. Achievement of good canal fill in both the proximal and distal stem portions did not contribute to the good long-term result of the stem.

Total hip replacement in patients with multiple epiphyseal dysplasia with a mean follow-up of 15 years and survival analysis

The hip joint is commonly involved in multiple epiphyseal dysplasia and patients may require total hip replacement before the age of 30 years.

We retrospectively reviewed nine patients (16 hips) from four families. The diagnosis of multiple epiphyseal dysplasia was based on a family history, genetic counselling, clinical features and radiological findings. The mean age at surgery was 32 years (17 to 63), with a mean follow-up of 15.9 years (5.5 to 24).

Of the 16 hips, ten required revision at a mean of 12.5 years (5 to 15) consisting of complete revision of the acetabular component in three hips and isolated exchange of the liner in seven. No femoral component has loosened or required revision during the period of follow-up.

With revision for any reason, the 15-year survival was only 11.4% (95% confidence interval 1.4 to 21.4). However, when considering revision of the acetabular shell in isolation the survival at ten years was 93.7% (95% confidence interval 87.7 to 99.7), reducing to 76.7% (95% confidence interval 87.7 to 98.7) at 15 and 20 years, respectively.