Thickness-dependent glass transition temperature and charge mobility in cross-linked polyfluorene thin films

Eliminating the Tg-confinement and fragility-confinement effects in poly(4-methylstyrene) films by incorporation of 3 mol % 2-ethylheyxl acrylate comonomer

Nanoconfined poly(4-methylstyrene) [P(4-MS)] films exhibit reductions in glass transition temperature (Tg) relative to bulk Tg (Tg,bulk). Ellipsometry reveals that 15-nm-thick P(4-MS) films supported on silicon exhibit Tg - Tg,bulk = - 15 °C. P(4-MS) films also exhibit fragility-confinement effects; fragility decreases ∼60% in going from bulk to a 20-nm-thick film. Previous research found that incorporating 2-6 mol  % 2-ethylhexyl acrylate (EHA) comonomer in styrene-based random copolymers eliminates Tg- and fragility-confinement effects in polystyrene. Here, we demonstrate that incorporating 3 mol  % EHA in a 4-MS-based random copolymer, 97/3 P(4-MS/EHA), eliminates the Tg- and fragility-confinement effects. The invariance of fragility with nanoconfinement of 97/3 P(4-MS/EHA) films, hypothesized to originate from the interdigitation of ethylhexyl groups, indicates that the presence of EHA prevents the free surface from perturbing chain packing and the cooperative mobility associated with Tg. This method of eliminating confinement effects is advantageous as it relies on the simplest of polymerization methods and neat copolymer only slightly altered in composition from homopolymer. We also investigated whether we could eliminate the Tg-confinement effect with low levels of 2-ethylhexyl methacrylate (EHMA) in 4-MS-based or styrene-based copolymers. Although EHMA is structurally nearly identical to EHA, 4-MS-based and styrene-based copolymers incorporating 4 mol  % EHMA exhibit Tg-confinement effects similar to P(4-MS) and polystyrene. These results support the special character of EHA in eliminating confinement effects originating at free surfaces.

Influences of Non-fullerene Acceptor Fluorination on Three-Dimensional Morphology and Photovoltaic Properties of Organic Solar Cells

Fluorination of conjugated molecules has been established as an effective structural modification strategy to influence properties and has attracted extensive attention in organic solar cells (OSCs). Here, we have investigated optoelectronic and photovoltaic property changes of OSCs made of polymer donors with the non-fullerene acceptors (NFAs) ITIC and IEICO and their fluorinated counterparts IT-4F and IEICO-4F. Device studies show that fluorinated NFAs lead to reduced V_oc but increased J_sc and fill-factor (FF), and therefore, the ultimate influence to efficiency depends on the compensation of V_oc loss and gains of J_sc and FF. Fluorination lowers energy levels of NFAs, reduces their electronic band gaps, and red-shifts the absorption spectra. The impact of fluorination on the molecular order depends on the specific NFA, and the conversion of ITIC to IT-4F reduces the structural order, which can be reversed after blending with the donor PBDB-T. Contrastingly, IEICO-4F presents stronger π-π stacking after fluorination from IEICO, and this is further strengthened after blending with the donor PTB7-Th. The photovoltaic blends universally present a donor-rich surface region which can promote charge transport and collection toward the anode in inverted OSCs. The fluorination of NFAs, however, reduces the fraction of donors in this donor-rich region, consequently encouraging the intermixing of donor/acceptor for efficient charge generation.

Polymer-Polymer Interfacial Perturbation on the Glass Transition of Supported Low Molecular Weight Polystyrene Thin Films

Clarifying interfacial perturbation on polymer relaxation is important for polymer material development. Herein we investigated polymer-polymer interfacial perturbation on low molecular weight (MW) polystyrene (PS) thin film (15-180 nm) glass transition by depositing various polymers atop PS films. Overall, rubbery topcoats induced T_g depression of PS thin film (below 60 nm), while glassy topcoats induced T_g elevation of PS thin film (below 30 nm). Importantly, for the rubbery topcoat, T_g perturbation strength is largely dependent on the T_g difference between interfacial polymers and a larger T_g difference would induce stronger perturbation, while for the glassy topcoat this dependence is inconspicuous. Meanwhile, the interfacial perturbation length during PS glass transition by rubbery topcoats is estimated to be around 8 nm, while it is considered to be about 3.5 nm for glassy topcoats. The different interfacial perturbation length induced by disparate topcoats was accounted for by their different perturbation strength on adjacent PS molecules and disparate interfacial roughness. The results can promote the understanding of polymer interfacial perturbation and benefit the design and development of polymer-based materials.

Molecular weight dependence of the intrinsic size effect on Tg in AAO template-supported polymer nanorods: A DSC study

Many studies have established a major effect of nanoscale confinement on the glass transition temperature (T_g) of polystyrene (PS), most commonly in thin films with one or two free surfaces. Here, we characterize smaller yet significant intrinsic size effects (in the absence of free surfaces or significant attractive polymer-substrate interactions) on the T_g and fragility of PS. Melt infiltration of various molecular weights (MWs) of PS into anodic aluminum oxide (AAO) templates is used to create nanorods supported on AAO with rod diameter (d) ranging from 24 to 210 nm. The T_g (both as T_g,onset and fictive temperature) and fragility values are characterized by differential scanning calorimetry. No intrinsic size effect is observed for 30 kg/mol PS in template-supported nanorods with d = 24 nm. However, effects on T_g are present for PS nanorods with M_n and M_w ≥ ∼175 kg/mol, with effects increasing in magnitude with increasing MW. For example, in 24-nm-diameter template-supported nanorods, T_{g, rod} - T_{g, bulk} = -2.0 to -2.5 °C for PS with M_n = 175 kg/mol and M_w = 182 kg/mol, and T_{g, rod} - T_{g, bulk} = ∼-8 °C for PS with M_n = 929 kg/mol and M_w = 1420 kg/mol. In general, reductions in T_g occur when d ≤ ∼2R_g, where R_g is the bulk polymer radius of gyration. Thus, intrinsic size effects are significant when the rod diameter is smaller than the diameter (2R_g) associated with the spherical volume pervaded by coils in bulk. We hypothesize that the T_g reduction occurs when chain segment packing frustration is sufficiently perturbed by confinement in the nanorods. This explanation is supported by observed reductions in fragility with the increasing extent of confinement. We also explain why these small intrinsic size effects do not contradict reports that the T_g-confinement effect in supported PS films with one free surface exhibits little or no MW dependence.