Implant surface roughness alterations induced by different prophylactic procedures: an in vitro study

The Effects of Ultrasonic Scaling and Air-Abrasive Powders on the Topography of Implant Surfaces: Scanning Electron Analysis and In Vitro Study

OBJECTIVES

 This in vitro study aimed to investigate the impact of bicarbonate air-abrasive powders and ultrasonic scaling with stainless steel tips on the micro- and nanotopography and roughness of three different implant-abutment junction titanium surfaces.

MATERIALS AND METHODS

 Three types of sterile and decontaminated titanium surfaces (RS, UTM, XA) were used for analysis. Nine disks per surface type were subjected to micro- and nanotopography analysis, scanning electron microscopy (SEM), roughness analysis, and fibroblast cultivation. Ultrasonic debridement and air polishing were performed on the surfaces. Human dermal fibroblasts were cultured on the surfaces for 5 days.

STATISTICAL ANALYSIS

 Data analysis adhered to ISO 25178 standards for surface texture assessment. SEM micrographs were used to reconstruct areas for extracting roughness parameters. Excel and Mex 6.0 software were utilized for quantitative and stereoscopic analysis.

RESULTS

 The study found varying effects on surface roughness posttreatment. RS Disco samples exhibited higher surface roughness compared with UTM and XA samples, both in average and nanoscale roughness. Decontamination led to increased surface roughness for all samples, particularly RS Disco. Fibroblast growth tests revealed enhanced cell network formation on decontaminated discs, possibly due to increased nanoscale roughness or the presence of bicarbonate salts.

CONCLUSION

 The study underscores the complex interplay between surface topography, microbial biofilm, and treatment efficacy in peri-implant disease management. While smoother surfaces may resist biofilm accumulation, increased nanoscale roughness postdecontamination can enhance fibroblast attachment and soft tissue integration. This dichotomy highlights the need for tailored treatment protocols that consider material-specific factors, emphasizing that successful implant therapy should balance microbial control with conducive surface characteristics for long-term osseointegration and soft tissue stability.

Efficacy of Biofilm Removal on the Dental Implant Surface by Sodium Bicarbonate and Erythritol Powder Airflow System

OBJECTIVE

 Peri-implantitis is a common complication in implant therapy and it is one of the main contributing factors to implant failure. This can be prevented by regular maintenance with mechanical debridement. One of the recent mechanical debridement methods is air abrasion therapy using different abrasive powders. This study aimed to evaluate the two common abrasive powders of different sizes (sodium bicarbonate and erythritol) for their biofilm cleaning efficacy on dental implant surfaces.

MATERIALS AND METHODS

 In an in vitro setting, a total of 33 implants were divided into three groups: Group 1 (n =11) = no treatment; group 2 (n = 11) = air abrasion therapy treated group using a sodium bicarbonate powder (AIRFLOW Powder Classic Comfort, EMS Electro Medical Systems, Nyon, Switzerland); and group 3 (n = 11) = air abrasion therapy treated group using an erythritol powder (AIRFLOW Powder Plus, EMS Electro Medical Systems, Nyon, Switzerland). The implants in each group were subjected to biofilm formation, and group 2 and group 3 were treated with air abrasion therapy of two different powders having different sizes with the same settings. The particle sizes were sodium bicarbonate (40 µm) and erythritol (14µm). The surface characteristics of the dental implants in three groups were studied from a digital camera and under the scanning electron microscope at different magnifications. The comparison of biofilm-removal efficacy between the three groups was performed by using a one-way analysis of variance with post-hoc Dunnett's T3 test. A p-value less than 0.05 was chosen to indicate statistical significance.

RESULTS

 There were no statistical differences (p > 0.05) between the two powder-treated groups for the biofilm cleaning efficacy. However, both groups showed significantly better biofilm-cleaning efficacy than the control group (p < 0.05).

CONCLUSION

 This suggests that both powders are effective in removing biofilm from the implant surface under ideal conditions. However, there was no clear distinction between the cleaning potential of the two powders, as both performed in a similar manner.

Osseointegration of Tantalum Trabecular Metal in Titanium Dental Implants: Histological and Micro-CT Study

This study aimed to investigate the impact of the Tantalum Trabecular Metal dental implant design on implant stability and the process of osseointegration following its placement in the rabbit femoral condyle. The subjects for the experiment consisted of 10 New Zealand white rabbits. Twenty implants, comprising 10 Trabecular Metal (TM) and 10 Traditional Screw Vent (TSV) implants, were placed into the femoral condyles of these rabbits. The implant type was alternated based on a random sequence. Following a healing period of 8 weeks, the implants were retrieved for further analysis using micro-computed tomography (micro-CT), histological studies, and histomorphometry evaluations. The Bone-to-Implant Contact (BIC) ratio and the Bone Volume (BV) percentage in the region of interest were subsequently assessed. The BIC and BV values between TM and TSV implants were compared using the Student t-test. The TM implants exhibited significantly greater BIC and BV scores. In particular, the BIC percentage was recorded as 57.9 ± 6.5 for the TM implants, as opposed to 47.6 ± 8 for the TSV implants. Correspondingly, the BV percentage was 57 ± 7.3 for the TM implants and 46.4 ± 7.4 for the TSV implants. The bone volume percentage measured using micro-CT evaluation was 89.1 ± 8.7 for the TM implants and 79.1 ± 8.6 for the TSV implants. Given the observed results, it is plausible to suggest that the bone growth surrounding the tantalum mesh could have improved the integration of the bone and facilitated its ingrowth into the TM implant.

Effect of addition of Ca2+ to titanium by a hydrothermal method on soft tissue sealing

The long-term stability of implants requires good peri-implant soft tissue sealing. Calcium ion (Ca²⁺ ) was loaded onto titanium surface by a hydrothermal method. In vitro, the morphology and composition of titanium surfaces were determined by scanning electron microscopy and energy-dispersive spectroscopy; proliferation of hGF-1 cells was measured by the CCK-8 assay; immunofluorescence staining was done to detect adherent proteins on titanium surface. In vivo, the degree of attachment between the implant and the surrounding soft tissue was measured by horseradish peroxidase (HRP). The percentage of hGF-1 cells adhering in the Ca group was significantly higher (p < .01); the fluorescence of integrin-β1 and F-actin in the Ca group was stronger; Ca group had the shorter length of HRP (p < .01). Ca²⁺ can be added to the surface of titanium by a hydrothermal method and it will be more beneficial for soft tissue early sealing.

Changes in the surface topography and element proportion of clinically failed SLA implants after in vitro debridement by different methods

OBJECTIVE

To evaluate the surface topography and element proportion changes in clinically failed implants after different modalities in vitro debridement and to compare the cleaning effect of different method combinations.

MATERIAL AND METHODS

Thirty clinical failed implants were treated by different debridement methods in vitro as follows: Group 1: physiologic saline irrigation; Group 2: glycine powder air polishing; Group 3: glycine powder air polishing + ethylenediaminetetraacetic acid (EDTA); Group 4: polyetheretherketone (PEEK) tip ultrasonic scaling; and Group 5: PEEK tip ultrasonic scaling + EDTA. The relative contaminated area reduction (RCAR), visual analogue scale (VAS, the higher value means, the better cleaning effect) and surface roughness were assessed using scanning electron microscopy (SEM), stereoscopic microscopy (SM) and white light interferometry (WLI). Surface chemistry was determined by energy dispersive spectroscopy (EDS).

RESULTS

Group 4 and Group 5 showed higher RCARs (82.90%, 82.89%), VAS scores (2.61, 2.33) and roughness reductions (-0.85 μm, -1.80 μm). Group 3 attained the highest decrease of C% (carbon, -26.67%), O% (oxygen, -13.71%) and N% (nitrogen, -5.66%), and the highest increase of Ti% (titanium, 49.67%). PEEK remnants were detected on the implant surface of Groups 4 and 5.

CONCLUSION

Within the limitation of the present in vitro design, PEEK tip ultrasonic scaling was more effective in eliminating visible contamination, while glycine powder air polishing combined with EDTA treatment was more conducive to expose the original surface element distribution. Both methods have their own advantages in decontamination, but none of them could reconstruct the surface as the pristine implant.

The impact of surface alteration on epithelial tissue attachment after the mechanical cleaning of titanium or zirconia surface

OBJECTIVE

Mechanical plaque removal may alter the surface morphology of the gingival penetration part of the implant. We applied an air-powered abrasive system (AP), titanium curette (TC), stainless curette (SC), ultrasound scaler (US), and titanium brush (TB) which are commonly used to remove plaque, to titanium or zirconia and the changes in surface morphology and the epithelial attach against substrata.

MATERIALS AND METHODS

(a) The morphological changes of titanium and zirconia after mechanical cleaning were assessed by scanning electron microscopy and a roughness analyser. (b) Oral epithelial cells of rats were inoculated on the surface of the materials after mechanical cleaning, and the adherence of epithelial cells was observed. (c) The maxillary first molars were extracted from the rats and replaced by experimental titanium or zirconia implants. The length of the immunoreactive laminin-332 band was observed at the implant-peri-implant epithelium interface.

RESULTS

(a) The surface roughness increased in experimental groups except the AP group. (b) Among the experimental groups, the AP group showed the highest number of attached cells. (c) The length of the immunoreactive laminin-332 band was longer in the control group than those in all five experimental groups. Among the experimental groups, the AP group showed the longest band.

CONCLUSION

All mechanical cleaning methods increased the surface roughness of the materials except AP. AP did not cause distinct implant surface alterations. Surface alteration caused by mechanical cleaning may evoke inferior for epithelial attachment and reduce resistance against foreign infiltration.

Ultrastructural changes of smooth and rough titanium implant surfaces induced by metal and plastic periodontal probes

Objectives

To determine the ultrastructural changes of titanium surfaces of dental implants induced by the tip of periodontal probes.

Materials and methods

A total of 40 samples of smooth and rough surfaces of titanium implants were randomly assigned for the treatment with metal or plastic periodontal probes under application angles of 20° and 60°. Titanium surfaces have been evaluated with CLSM prior and following to experimental probing determining various standardized 2D and 3D roughness parameters.

Results

The average profile and surface roughness (Ra and Sa) showed no significant difference between treated and untreated samples on smooth and rough surface areas irrespective of the probe material. On smooth surfaces several amplitude roughness parameters were increased with metal probes but reached significance only for Rp (p = 0.007). Rough surface parts showed a slight but not significant reduction of roughness following to the contact with metal probes. The surface roughness remained almost unchanged on smooth and rough implant surfaces using plastic probes. The surface roughness on implant surfaces was not dependent on the application angle irrespective of the probe material.

Conclusion

Probing of titanium implants with metal probes and even less with plastic probes causes only minor changes of the surface roughness. The clinical significance of these changes remains to be elucidated.

Clinical relevance

Using plastic probes for the clinical evaluation of the peri-implant sulcus might avoid ultrastructural changes to titanium implant surfaces.

Cleaning potential of different air abrasive powders and their impact on implant surface roughness

BACKGROUND

Implant surface roughness after air abrasive therapy has not been measured precisely in previous research. Debridement with air abrasion facilitates the mechanical removal of bacterial biofilms but may damage implant surfaces on a microscopic level.

PURPOSE

This study aimed to investigate the cleaning potential of various air abrasive powders and their effect on titanium implant surfaces.

MATERIALS AND METHODS

Twenty implants coated with red ink were inserted into three-dimensional printed circumferential bone defect models. Treatment was completed with three types of air abrasive powders: sodium bicarbonate (SB), glycine, and erythritol for 60 seconds. Water alone was used as control. The percentage of remaining ink was assessed using digital photography and graphic software. Implant surface topography/roughness was quantified using optical profilometry and examined via scanning electron microscopy. The microscopic analysis was performed at two implant areas: collar (Laser-Lok surface) and threads.

RESULTS

The cleaned surfaces (%, mean ± SD) after treatment with SB, glycine, and erythritol accounted for 49.3 ± 3.6%, 33.1 ± 1.2%, and 25.1 ± 0.7%, respectively. Statistically significant differences were found between all groups (P < .001). SB was the only powder that significantly increased the implant roughness (S_a ) on both the implant collar (1.53-2.10 μm) and threads (3.53-4.20 μm). Regardless of the abrasive powder used, the collar, emerging implant surfaces from the defect base, and surfaces beneath implants threads exhibited more post-treatment residual ink.

CONCLUSION

Large-sized powder showed the greatest cleaning capacity, but caused more alterations to the implant surface. Glycine and erythritol displayed no significant changes in surface roughness, however, demonstrated a limited ink removal capacity.

Effects of air abrasive decontamination on titanium surfaces: A systematic review of in vitro studies

BACKGROUND

Air abrasion (AA) is one of the decontamination methods that have demonstrated promising results in treating peri-implant diseases.

PURPOSE

This systematic review aimed at evaluating the in vitro effect of AA on surface change, cleaning efficacy, and biocompatibility of titanium surfaces and at comparing it with other decontamination methods.

MATERIALS AND METHODS

A comprehensive search was conducted up to April 2018 using PubMed, Scopus, and Google Scholar databases to identify studies on the decontamination effect of AA. All types of titanium surfaces, abrasive powders, contaminated surfaces, and measuring methods were included.

RESULTS

Overall, 1502 articles were identified. After screening the titles and abstracts, and carefully reading the full-texts, 48 articles published between 1989 and 2018 were selected. AA was considered almost safe, particularly for the nonmodified surfaces. Nevertheless, harder powders such as sodium bicarbonate tended to damage the surface more than glycine. AA resulted in surface change similar to plastic curettes and Er: YAG lasers. Regarding the cleaning efficacy, there was no significant difference between glycine and sodium bicarbonate, but different mixtures of calcium phosphate, hydroxyapatite, and erythritol were superior to glycine. AA was superior or equal to all other decontamination methods in cleaning. Regarding biocompatibility, AA was more successful in preserving biocompatibility for noncontaminated surfaces compared with contaminated surfaces and when used with erythritol and osteoinductive powders.

CONCLUSIONS

AA can efficiently remove contamination without serious damage to the surface. The main drawback of the AA method seems to be its limitation in restoring the biocompatibility of the surface.

Effects of various prophylactic procedures on titanium surfaces and biofilm formation

Purpose

The aim of this study was to evaluate the effects of various prophylactic treatments of titanium implants on bacterial biofilm formation, correlating surface modifications with the biofilms produced by Pseudomonas aeruginosa PAO1, Staphylococcus aureus, and bacteria isolated from saliva.

Methods

Pure titanium disks were treated with various prophylactic procedures, and atomic force microscopy (AFM) was used to determine the degree to which surface roughness was modified. To evaluate antibiofilm activity, we used P. aeruginosa PAO1, S. aureus, and saliva-isolated Streptococcus spp., Bacteroides fragilis, and Staphylococcus epidermidis.

Results

AFM showed that the surface roughness increased after using the air-polishing device and ultrasonic scaler, while a significant reduction was observed after using a curette or polishing with Detartrine ZTM (DZ) abrasive paste. In addition, we only observed a significant (P<0.01) reduction in biofilm formation on the DZ-treated implant surfaces.

Conclusion

In this study, both AFM and antibiofilm analyses indicated that using DZ abrasive paste could be considered as the prophylactic procedure of choice for managing peri-implant lesions and for therapy-resistant cases of periodontitis.

Simulated damage of two implant debridement methods: Nonsurgical approach with Teflon and stainless steel hand scalers

BACKGROUND

Mechanical scaling is the most common treatment of periodontal and peri-implant tissue infections.

AIMS

This study aimed to evaluate the effect of mechanical prophylactic therapy on the residual stresses in the implant and hand scaler.

SETTINGS AND DESIGN

For finite-element analysis, an implant-supported prosthesis was created using modeling software with 3 mm of exposed threads. For simulation of a prophylactic mechanical debridement, the active face of the shank was disposed of in contact with the last thread exposed at a 90° angle.

MATERIALS AND METHODS

In the analysis software, the contacts were defined as rough between the instrument and the implant. The cortical bone was fixed and a load of 10 N was applied to the instrument cable. Two simulations were performed according to the instrument material: stainless steel or Teflon. Von-Mises results were obtained.

STATISTICAL ANALYSIS USED

No statistical test was used, but, the 500 higher stress peaks in the implant and in the instrument were analyzed for qualitative comparison.

RESULTS

Mechanical prophylactic therapy generates higher residual stress on the implant with a stainless steel instrument. There was no difference between the materials for the active tip of the instrument, and the active portion of the shank was the region which concentrated more stress.

CONCLUSIONS

It is suggested that hand scalers in Teflon are less damaging to the implant, but more susceptible to deformation and possible early failures.