Evaluation of the success rate of pit and fissure sealants on first molars, 12 months follow-up study

Survival Analysis of Glass Ionomer Cement and Resin-Based Sealant Retention: A 10-Year Follow-Up Study

Background and Objective: Sealant application is a proven method to prevent occlusal caries; however, long-term studies on this topic are scarce. This study aimed to assess the survival rate and clinical effectiveness of glass ionomer cement (GIC) and resin-based sealants (RBSs) on second permanent molars over a long-term follow-up period. Materials and methods: Sixteen patients aged 11-13 years with all four completely erupted permanent second molars were enrolled in the study. All patients attended 1-year and 3-year follow-ups; however, one participant did not respond after 10 years and was excluded from the final analyses. The oral health status evaluation was based on WHO criteria. A total of 32 teeth received an RBS (Clinpro), and a further 32 teeth were sealed with GIC (Fuji IX). The sealant retention was determined according to the Kilpatrick criteria after 1 year, 3 years, and 10 years, respectively. Statistical analysis included a chi-square test, the Kaplan-Meier method, and the Cox proportional hazard model. Results: At baseline, seven boys and eight girls participated in the study, with a mean age of 12.3 ± 0.9 years. The 1-year follow-up results revealed that 90% of the RBSs and 43.3% of the GIC sealants were completely retained, and no caries lesions were recorded (p = 0.01). The 3-year follow-up results showed that 23.3% of the RBSs and 0% of the GIC sealants demonstrated complete retention (p = 0.034). Moreover, 10.0% of the occlusal surfaces in the RBS group and 13.3% of the occlusal surfaces in the GIC group were filled (p > 0.05). A total of 6.7% of the RBSs showed complete retention. One-third of the sealed teeth (30.0% of the teeth sealed with RBSs and 36.7% of teeth applied with GIC) were filled after 10 years. The Kaplan-Meier analysis demonstrated a higher survival rate in the RBS group when compared with the GIC over the entire follow-up period (p = 0.001). Conclusions: Although the survival rate of RBSs was higher than GIC sealants, their effectiveness in preventing fissure caries in permanent second molars did not differ significantly over a 10-year follow-up.

Influence of incorporation of nanostructured silver vanadate decorated with silver nanoparticles on roughness, microhardness, and color change of pit and fissure sealants

Objective

The aim of this study was to evaluate the roughness, hardness, and color change of pit and fissure sealants of two commercial brands (Fluroshield ™ and Ultraseal XT ™) incorporated with nanostructured silver vanadate nanomaterial decorated with silver nanoparticles (β-AgVO3) in concentrations (0% - control, 2.5% and 5%).

Material and methods

Two commercial brands Fluroshield TM and Ultraseal XT ™ were used to make the samples with dimensions of 6 × 6 × 4 mm. The control group was made according to the manufacturer's instructions and in the groups with the addition of β-AgVO3, the nanomaterial was added proportionally by mass at percentages of 2.5% and 5%. Roughness properties were evaluated using a 3D Laser Confocal Microscope (n = 10), Knoop microhardness by Microdurometer (n = 10), and color change by Portable Color Spectrophotometer on the CIEDE2000 system (n = 10). Data were evaluated by one-way ANOVA with Bonferroni adjustment and Tukey's mean comparison test at a 5% significance level.

Results

Ultraseal XT ™ sealant roughness showed a significant difference between concentrations with the highest mean for the 5% group (P = 0.010). Regarding the hardness, both sealants showed no significant difference between the groups. Fluroshield ™ sealant showed a significant difference in ΔE00 between the control-2.5% 24.93 (3.49) and control-5% 28.41 (2.58).

Conclusion

It may be concluded that the incorporation of β-AgVO3 influenced the increase in roughness for Ultraseal XT ™ pit and fissure sealant, did not interfere with the microhardness of both sealants, and promoted a change in the color of Fluroshield ™ sealant within clinically acceptable limits.

Microleakage Assessment of Different Preparation Techniques and Pit and Fissure Sealants in Permanent Molars

BACKGROUND

This study aimed to evaluate the predisposition of microleakage in permanent molar teeth following different preparation techniques for pits and fissure sealants.

METHODS

In this cross-sectional analytical study, a dye penetration method was employed to evaluate microleakage in dental restorations. A total of 104 extracted molars were randomly assigned into two groups and further subdivided into two subgroups based on a class of sealant (filled/unfilled resin) containing 26 teeth each. Teeth in one group were prepared by a conventional method using pumice and acid etching with 37% phosphoric acid, and teeth in the other group were prepared with a 1/4-round carbide bur in a low-speed handpiece and then acid etched. In each group, 26 teeth were sealed with a filled sealant, and 26 teeth with an unfilled sealant. The chi-square test was used for the comparison of microleakage between the groups.

RESULTS

Unfilled sealants prepared with bur preparation showed the lowest degree of microleakage. The greater number of teeth (17) showed no microleakage in the group of teeth prepared using the bur preparation technique. Furthermore, in dye penetration analysis, the subgroup of teeth that were filled with unfilled sealants showed a greater number of teeth (57.6%), with zero penetration, and the dye penetration scores were statistically significant among the groups with different preparation techniques (p=0.002).

CONCLUSION

Teeth whose pits and fissures were prepared through 1/4 carbide bur and filled with unfilled pits and fissure sealants show less microleakage than those prepared with the conventional method and filled with filled sealants. Therefore, the choice of surface preparation technique for pit and fissure sealants can influence the effectiveness of the sealant in preventing microleakage.

Effect of Zinc Oxide Incorporation on the Antibacterial, Physicochemical, and Mechanical Properties of Pit and Fissure Sealants

This study aimed to evaluate the antibacterial, physicochemical, and mechanical properties of pit and fissure sealants containing different weight percentages of zinc oxide nanoparticles (ZnO NPs). The following amounts of ZnO NPs were added to a commercially available pit and fissure sealant (BeautiSealant, Shofu, Japan) to prepare the experimental materials: 0 wt.% (commercial control (CC)), 0.5 wt.% (ZnO 0.5), 1 wt.% (ZnO 1.0), 2 wt.% (ZnO 2.0), and 4 wt.% (ZnO 4.0). The antibacterial effect against S. mutans was confirmed by counting the colony-forming units (CFUs) and observing live/dead bacteria. In addition, ion release, depth of cure, water sorption and solubility, and flexural strength tests were conducted. When compared with the CC, the experimental groups containing ZnO NPs showed zinc ion emission and significantly different CFUs (p < 0.05) with fewer live bacteria. ZnO NP addition reduced the depth of cure and water solubility and increased water sorption in comparison with the CC (p < 0.05). However, all groups showed similar flexural strength (p > 0.05). The pit and fissure sealants containing ZnO NPs exhibited antibacterial activity against S. mutans with no negative effects on physicochemical and mechanical properties, and thus, these sealants can be ideal secondary caries prevention material.

Assessment of Physical/Mechanical Performance of Dental Resin Sealants Containing Sr-Bioactive Glass Nanoparticles and Calcium Phosphate

The aim of this study was to assess the chemical/mechanical properties of ion-releasing dental sealants containing strontium-bioactive glass nanoparticles (Sr-BGNPs) and monocalcium phosphate monohydrate (MCPM). Two experimental sealants, TS1 (10 wt% Sr-BGNPs and 2 wt% MCPM) and TS2 (5 wt% Sr-BGNPs and 4 wt% MCPM), were prepared. Commercial controls were ClinproXT (CP) and BeautiSealant (BT). The monomer conversion (DC) was tested using ATR−FTIR (n = 5). The biaxial flexural strength (BFS) and modulus (BFM) were determined (n = 5) following 24 h and 7 days of immersion in water. The Vickers surface microhardness (SH) after 1 day in acetic acid (conc) versus water was tested (n = 5). The bulk and surface calcium phosphate precipitation in simulated body fluid was examined under SEM-EDX. The ion release at 4 weeks was analyzed using ICP-MS (n = 5). The DC after 40 s of light exposure of TS1 (43%) and TS2 (46%) was significantly lower than that of CP (58%) and BT (61%) (p < 0.05). The average BFS of TS1 (103 MPa), TS2 (123 MPa), and BT (94 MPa) were lower than that of CP (173 MPa). The average BFM and SH of TS1 (2.2 GPa, 19 VHN) and TS2 (2.0 GPa, 16 VHN) were higher than that of CP (1.6 GPa, 11 VHN) and BT (1.3 GPa, 12 VHN). TS1 showed higher Ca, P, and Sr release than TS2. Bulk calcium phosphate precipitation was detected on TS1 and TS2 suggesting some ion exchange. In conclusion, the DC of experimental sealants was lower than that of commercial materials, but their mechanical properties were within the acceptable ranges. The released ions may support remineralizing actions.