Efficiency of dry versus wet Er,Cr:YSGG laser debonding of lithium disilicate veneers using different power outputs

STATEMENT OF PROBLEM

Since water is the chromophore for the erbium, chromium-yttrium scandium gallium garnet (Er,Cr:YSGG) laser, the laser energy reaching the restoration decreases as part of it is absorbed by water. Theoretically, reducing the water or implementing dry debonding could reduce the energy consumed by water, increasing laser efficiency. Studies on whether it is suitable for removing veneers without using coolant are lacking.

PURPOSE

The purpose of this in vitro study was to evaluate the debonding time, intrapulpal temperature, and translucency of veneers during wet versus dry debonding with an Er,Cr:YSGG laser using different power outputs.

MATERIAL AND METHODS

Sixty-three maxillary central incisors were flattened labially to receive ceramic specimens. After cementation, ceramic specimens were irradiated with an Er,Cr:YSGG laser for debonding with different power outputs and water percentages (N=70): subgroup A1, 4 W and 1% water; A20, 4 W and 20% water; A40, 4 W and 40% water; B1, 5 W and 1% water; B20, 5 W and 20% water; B40, 5 W and 40% water; C1, 6 W and 1% water; C20, 6 W and 20% water; C40, 6 W and 40% water, and a control group of unbonded ceramic specimens. During debonding, the temperature rise and debonding time were evaluated, followed by the evaluation of the translucency and surface topography of the debonded specimens. Two-way analysis of variance (ANOVA) and the Dunnett test were used to analyze the data (α=.05).

RESULTS

The mean intrapulpal temperature rise varied significantly among groups B and C (P<.001), with the highest mean temperature rise found in subgroup B1 (4.00 ±0.00 ºC) and the lowest mean temperature rise in subgroup C20 (1.20 ±0.45 ºC). For the debonding time, the mean values of time required for debonding varied significantly among different groups (P<.001), with the longest time recorded in subgroup A1 (333.4 ±74.8 s) and the shortest time recorded in subgroup C20 (17.0 ±6.0 s). Only subgroups C1 (18.89 ±0.2) and C40 (18.60 ±0.2) showed a significantly lower translucency than the control group (19.44 ±0.06) (P<.001).

CONCLUSIONS

Dry Er,Cr:YSGG laser debonding resulted in increased intrapulpal temperature when using high power outputs, but without exceeding the critical threshold of dental pulp temperature. Dry debonding also limited the transmission of laser energy, affecting the debonding efficiency. A power output of 5 W and 20% water can be considered efficient and safe laser parameters for debonding lithium disilicate veneers if their reuse is intended.

Clinical performance of laminate veneers: A review of the literature

PURPOSE

This narrative review aimed to survey the clinical outcomes of laminate veneers (LVs), including their survival and success rates.

STUDY SELECTION

An electronic search of MEDLINE/PubMed, Web of Science, Cochrane Library, and Google Scholar from 2000 to April 2023 was conducted using the keywords "laminate" OR "veneer" OR "porcelain" OR "feldspathic" OR "lithium disilicate" OR "composite resin" OR "zirconia" OR "survival" OR "success." Case reports, case series, reviews, abstracts, in vitro studies, and observational studies were excluded. Five researchers independently evaluated the titles and abstracts of all identified studies.

RESULTS

A total of 55 studies were identified. None of the studies met the criteria for zirconia LVs. According to the studies in this review, LVs fabricated with feldspathic porcelain, leucite-reinforced glass ceramics (LRG), and lithium disilicate ceramics (LDS) exhibited satisfactory survival and success rates. Furthermore, hydrofluoric acid etching followed by silane priming of the surface of ceramic LVs is necessary for improved clinical outcomes. The extent of dentin exposure significantly decreases the success rate of ceramic LVs. An appropriate adhesive luting process is required to achieve the long-term success of ceramic LVs. Dentin exposure should be minimized or sealed during tooth preparation to achieve a reliable and durable bond between LVs and abutment teeth.

CONCLUSIONS

Based on this narrative review of the literature, the use of silica-based ceramic feldspathic porcelain, LRG, and LDS is recommended for LVs.

Replacement of unsatisfactory ceramic veneers with the aid of a digital workflow

This case report focuses on the replacement of ceramic laminate veneers with suboptimal marginal fit and design, employing a digital workflow and CAD-CAM technology. The patient, a woman in her 30s, expressed concerns about the appearance and hygiene challenges of her existing veneers. A comprehensive assessment, including clinical examination, facial photographs and intraoral scanning, was conducted. Utilising CAD software, facial photographs and 3D models merged to create a digital wax-up, crucial in designing suitable veneers and addressing issues like overcontouring and a poor emergence profile. Following the removal of old veneers, a mock-up was performed and approved. Preparations ensured space for restorations with well-defined margins. The final restorations, milled with Leucite-reinforced vitreous ceramic, were cemented. At the 1 year follow-up, improved aesthetics, gingival health and functional restorations were observed. This report highlights the efficacy of digital workflows in achieving consistent and aesthetically pleasing outcomes in ceramic laminate veneer replacement.

Shear bond strength of adhesive cement to zirconia: Effect of added proportion of yttria for stabilization

STATEMENT OF PROBLEM

Zirconium dioxide (zirconia) cannot be etched in a clinical setting, but zirconia restorations with minimal to no micromechanical bonding are approved and widely used in contemporary dentistry. However, information on the shear bond strength of zirconia and adhesive cement, on the effect of an added proportion of yttria, and on the effect of aging is lacking.

PURPOSE

The purpose of this in vitro study was to evaluate the shear bond strength of cement luted to zirconia and the effect of aging.

MATERIAL AND METHODS

A total of 131 test specimens were made from 4 zirconia materials with different amounts of yttria added to formulate yttria-partially stabilized zirconia (Y-PSZ); 3Y-PSZ (n=32), 4Y-PSZ (n=34), and 2 5Y-PSZs (n=32 and n=33). A dual-polymerizing cement and 10-methacryloyloxydecyl dihydrogen phosphate-containing primer were used. All specimens were stored in water at 37 °C, half of them for 24 hours and the other half for 6 months. After aging, the specimens were subjected to a shear bond strength test with a notched crosshead according to the International Organization for Standardization (ISO) 29022:2013 standard. The data were analyzed using the independent 2-sample t test, ANOVA, and the Levene test (α=.05).

RESULTS

The 3Y-PSZ material had higher mean ±standard deviation shear bond strength (31.83 ±12.80 MPa) compared with 4Y-PSZ (23.34 ±7.66 MPa) after 24 hours of aging in water and higher (28.98 ±14.03 MPa) than 4Y-PSZ (14.35 ±9.62 MPa) and one of the 5Y-PSZ (16.05 ±11.34 MPa) after 6 months. Debonding before loading occurred in all groups except for one of the 5Y-PSZ groups.

CONCLUSIONS

Zirconia without macromechanical retention, regardless of an added proportion of yttria, showed high shear bond strength, but the tested materials also had a high coefficient of variance, which, in practice, leads to the risk of the occasional debonding of zirconia restorations.

Clinical survival and complication rate of ceramic veneers bonded to different substrates: A systematic review and meta-analysis

STATEMENT OF PROBLEM

Evidence on the long-term clinical assessment and longevity of ceramic veneers bonded to different substrates is limited.

PURPOSE

The purpose of this systematic review and meta-analysis was to evaluate the effect of various substrates, including enamel, dentin, or an existing composite resin restoration, on the clinical survival and complication rates of ceramic veneers.

MATERIAL AND METHODS

The PubMed, Scopus, and the Cochrane Library electronic databases were searched, and related journals were hand searched without time or language restrictions to identify clinical trials that compared the survival rate and clinical complication rates when bonding ceramic veneers to different tooth substrates. The success rate of the included participants was estimated by the number of veneers that did not require a clinical intervention, and the survival rate by all veneers that did not fail absolutely. The risk difference (RD) with 95% confidence intervals (CIs) for dichotomous outcomes was used to quantify the intervention effect.

RESULTS

Of 973 screened articles, 6 clinical studies were included. The survival and success rates varied depending on the bonding substrate. Enamel-bonded veneers had almost perfect rates of survival (99% with a range of 98% to 100%) and success (99% with a range of 98% to 100%). Veneers bonded to composite resin or surfaces with minimal dentin exposure had slightly lower survival rates (94% with a range of 91% to 97% and 95% with a range of 91% to 100%, respectively) and success rates (70% with a range of 60% to 80% and 95% with a range of 90% to 99%). Severe dentin exposure significantly decreased both survival rates (91% with a range of 84% to 98%) and success rates (74% with a range of 64% to 85%). The combined findings suggested that ceramic veneers bonded to enamel had fewer clinical complications (RD: -0.04; 95% CI: -0.09 to 0.02) and lower failure rates (RD: -0.13; 95% CI: -0.32 to 0.07) compared with those bonded to exposed dentin. Additionally, veneers attached to teeth with minimal dentin exposure were significantly less likely to require clinical interventions (RD: -0.16; 95% CI: -0.31 to -0.01) and had a reduced incidence of failure (RD: -0.08; 95% CI: -0.17 to 0.01) compared with those with severe dentin exposure.

CONCLUSIONS

Ceramic veneers bonded to enamel showed higher survival and success rates with lower clinical incidences of complications and failure than those bonded to dentin or teeth with existing composite resin restorations.

Age and sex related change in tooth enamel thickness of maxillary incisors measured by cone beam computed tomography

BACKGROUND

To measure adequate enamel thickness of maxillary incisors in planning enamel reduction for a porcelain laminate veneer restoration in relation to chronological age and sex by using cone beam computed tomography (CBCT) in an Iraqi subpopulation.

METHODS

From 81 CBCT images, 324 maxillary incisors were examined. Enamel thickness was measured at both mesial and distal regions of the tooth in three different levels: cervical, middle, and incisal (occlusal) 1/3 at a sagittal section. Measurements were made for the following tooth areas using CBCT: facial enamel thickness at 1, 3, and 5 mm from the cementoenamel junction (CEJ), palatal enamel thickness at 5 mm from the CEJ (5 mm P), facial and palatal enamel thickness at the incisal edge (IFP), mid incisal enamel thickness (IET), and the incisal edge enamel-pulp distance (IEPD). Relationships of enamel thickness with age and sex were evaluated using Independent t-test, Mann-Whitney U-test and the Pearson correlation coefficient, a simple linear regression analysis used for statistical analysis.

RESULTS

Significant differences (P < 0.05) were found in terms of an inverse association between enamel thickness and chronological age at all measurements above the CEJ and the regression model for the mid-incisal enamel thickness was (R2 of 0.4). In contrast, there was an increase in IFP, palatal, and IPED enamel thickness with age. Also, significant differences were found in enamel thickness between males and females, the enamel being thicker in females in relation to facial enamel thickness, enamel palatal thickness above CEJ and IET, while for IEPD, the enamel thickness was greater in males compared to females.

CONCLUSION

The measurements for enamel thickness outcome variables in relation to chronological age revealed significant differences for each measured distance and there were statistically significant differences in enamel thickness between males and females at all measurements except at IFP. These results demonstrate that CBCT can be used for noninvasive, accurate measurements of enamel thickness in both sex.

Accuracy of the preparation depth in mixed targeted restorative space type veneers assisted by different guides: An in vitro study

PURPOSE

Most veneers are mixed targeted restorative space (MTRS)-type restorations that are partially within the original tooth and require inconsistent preparation depths. This study aimed to evaluate the accuracy of the preparation depth for MTRS veneer preparation.

METHODS

MTRS veneer preparation models were developed using the twisted maxillary central incisor (MCI) as the original tooth and the standard MCI as the waxing. Veneer preparations were performed using freehand (MF), silicone (MS), thermoplastic (MT), 3D-printed uniform (MD), and auto-stop (MA) guides. The prepared and original MCI were scanned and superimposed using a custom-made base. The mean absolute differences (MADs) were measured to evaluate the accuracy of the preparation depth. Statistical analysis was performed using the multivariate analysis of variance (MANOVA) test (α=0.05).

RESULTS

The accuracy of the preparation depth was 0.237±0.090, 0.191±0.099, 0.149±0.078, 0.093±0.050, and 0.059±0.040 mm in MF, MS, MT, MD, and MA, respectively. The MADs between the groups were significant (P<0.05). The accuracy of the trial restoration was 0.140±0.081 mm in the MS, and the accuracy of the guiding tube was 0.055±0.033, 0.036±0.011, and 0.033±0.010 mm in the MT, MD, and MA, respectively.

CONCLUSIONS

In MTRS veneer preparation for MCI, tooth preparation guides improved the accuracy of the preparation depth by visualizing the TRS profile and providing clear measurement points. The accuracy of the guide is influenced by its flexibility, and the accuracy of the preparation depth is affected by the accuracy of the measurement points.

The Influence of a Novel, Crenelated Design of CAD-CAM Ceramic Veneers on the Debonding Strength

(1) Background: Aesthetic dentistry has become one of the most dynamic fields in modern dental medicine. Ceramic veneers represent the most appropriate prosthetic restorations for smile enhancement, due to their minimal invasiveness and highly natural appearance. For long-term clinical success, accurate design of both tooth preparation and ceramic veneers is of paramount importance. The aims of this in vitro study were to assess the stress in anterior teeth restored with Computer-Aided Design (CAD) and Computer-Aided Manufacturing (CAM) ceramic veneers and compare the resistance to detachment and the fracture of ceramic veneers prepared using two different designs. (2) Methods: Sixteen lithium disilicate ceramic veneers were designed and milled using the CAD-CAM technology and divided into two groups according to the preparations (n = 8): Group 1, conventional (CO), with linear marginal contour and Group 2, crenelated (CR), the latter with our novel (patented) sinusoidal marginal design. All samples were bonded to anterior natural teeth. The mechanical resistance to detachment and fracture was investigated by applying bending forces on the incisal margin of the veneers in order to determine which type of preparation leads to better adhesion. An analytic method was employed, as well, and the results of the two approaches were compared. (3) Results: The mean values of the maximum force recorded at the veneer detachment were 78.82 ± 16.55 N for the CO group and 90.20 ± 29.81 N for the CR group. The relative increase, equal to 14.43%, demonstrated that the novel CR tooth preparation provided higher adhesive joints. In order to determine the stress distribution within the adhesive layer, a finite element analysis (FEA) was performed. The statistical t-test showed that the mean value of the maximum normal stresses is higher for the CR-type preparations. (4) Conclusions: The patented CR veneers represent a practical solution to augment the adhesion and mechanical properties of ceramic veneers. The obtained results demonstrated that CR adhesive joints triggered higher mechanical and adhesive forces, which subsequently led to a higher resistance to detachment and fracture.

Perception of Minimum Interventional Dentistry among Dental Undergraduate Students and Interns

Background: The philosophy of minimum interventional dentistry (MID) is to integrate prevention, remineralization, and minimal intervention for the placement and replacement of restorations. All branches of dentistry play an important role in practicing MID, and their primary goal is to realize that any restoration is of less biological significance than the healthy original tissue Objectives: The objective of this study was to assess the perception of MID among dental undergraduate students and interns in terms of knowledge, attitude, and practice at the College of Dentistry. Materials and Methods: This cross-sectional study was conducted among undergraduate students and interns at the College of Dentistry, Qassim University, Saudi Arabia. A self-administered questionnaire was distributed, which included basic demographic profiles and questions about the knowledge, attitude, and practices toward MID. The data were tabulated in MS Excel, and all statistical analyses were performed using SPSS version 21. Results: A total of 163 dental students were recruited, with senior students comprising 73% and interns comprising 27%. Male students were slightly more prevalent (50.9%) than female students (49.1%). About 37.6% of participants received training about MID during educational courses, while 10.3% received it during their internship. A statistical test revealed that the prevalence of interns who were trained in performing MID was significantly higher (p < 0.001). Conclusions: The majority of the participants demonstrated proper knowledge, attitude, and practice in different aspects of MID. Interns reported a higher rate of knowledge, attitude, and practice in MID compared to undergraduate students. However, more education and hands-on training about MID concepts during the college curriculum are necessary to attain better knowledge, attitude, and practices that could be useful for more conservative clinical practice.

The influence of pulse duration and exposure time of Er,Cr:YSGG laser on lithium disilicate laminate debonding, an in vitro study

Problem statement

Grinding restorations, such as veneers, with rotary instruments, is the conventional removal approach. It may be accompanied by micro-fractures that affect the adjacent healthy dental structures. Differentiation of the veneer from the dental structure, as well as the resin cement, is not a highly selective procedure when rotary instruments are used. Moreover, the rotary instruments may lead to scratches and overheating of the enamel. Patient discomfort is another disadvantage, due to the noise of the drill.

Purpose

The purpose of this in vitro study was to examine the effectiveness of a 2790 nm Er,Cr:YSGG laser to debond lithium disilicate laminate, utilizing two distinct pulse durations and various exposure times. The shear bond strength, intrapulpal temperature, and adhesive remaining index were evaluated.

Methods and materials

This study included three groups of 75 extracted permanent mandibular incisors: G1, G2 (laser-treated groups were classified according to the pulse duration) and C (control group). Twenty five samples were regarded for each group. Both test groups were irradiated with a 3 W output power of Er,Cr:YSGG laser, for a variety of time intervals (20 s, 30 s, 40 s, 50 s, and 60 s). Five samples were tested for each time interval. During irradiation, the temperature in the pulp chamber was monitored using a K-type thermocouple connected to a digital multilogger thermometer that was introduced into the prepared sample pulp chamber. Subsequently, the shear bond strength was measured for G1 and G2, in addition to the control group (no irradiation). The adhesive remaining index was examined microscopically. The area was measured and analysed, and then, transformed into scores for comparisons. Finally, One untreated sample and two other samples of the highest power value from laser-treated groups were examined for their surface morphology by scanning electron microscope (SEM).

Results

The debonding protocols were safe relative to the intrapulpal protocol. The temperature rise after an exposure time of 50 s and 60 s was significantly different from an exposure time of 20 s, 30 s, and 40 s, in both groups (p < 0.05). Both G1 and G2 significantly outperformed the control group in shear bond strength. There was no significant difference between G1 and G2 at any of the tested exposure times (p > 0.05). Nevertheless, the 60 s exposure time showed the lowest shear bond strength.

Conclusion

Regarding intralpulpal temperature, both modes can be safely used to remove laminate veneers. In sum, an exposure time of 50 s and a pulse duration of 60 μs demonstrated superior results for SBS, adhesive remaining index, and temperature values.

Clinical implication

Lithium disilicate laminate veneers may be removed quickly, safely, and comfortably. Laser-assisted debonding of porcelain laminate veneer is recommended and does not cause any damage to the veneer or enamel surface.

Porcelain Veneers in Vital vs. Non-Vital Teeth: A Retrospective Clinical Evaluation

Nowadays, the ceramic veneer approach can be considered more predictable than direct composite veneer. To date, there is a lack of studies comparing the clinical performance of anterior veneers cemented on vital teeth (VT) and non-vital teeth (NVT). This longitudinal clinical study investigated the performance of ceramic veneers in VT or anterior NVT. A total of 55 patients were evaluated in the study. Two groups were defined based on the vitality status of the teeth (93 teeth-vital and 61 teeth-non-vital). The United States Public Health Service (USPHS) criteria were used to assess the clinical status. The data were evaluated statistically with the Mann-Whitney U test. All restorations were considered acceptable, and only one veneer in VT failed for the criteria of secondary caries. There were no statistically significant differences in any of the criteria evaluated (p ≤ 0.671). The ceramic veneers evaluated showed a satisfactory clinical performance both in VT and NVT.

Retrospective clinical evaluation of a no-prep porcelain veneer protocol

STATEMENT OF PROBLEM

Porcelain laminate veneers without tooth preparation (no-prep veneers) might represent a convenient and conservative option for the esthetic rehabilitation of anterior teeth. However, controversy exists about their predictability.

PURPOSE

The purpose of this clinical study was to retrospectively evaluate the performance of no-prep porcelain veneers placed as per the recently proposed "CH no-prep" protocol, which claimed to overcome many of the drawbacks of previous no-prep veneer solutions.

MATERIAL AND METHODS

One hundred eight no-prep porcelain laminate veneers based on the CH no-prep protocol were placed in 21 patients between 2015 and 2017. All participants were contacted, and 15 received a recall examination: a total of 78 veneers were evaluated as per the Clinical-Photographic-Micromorphologic coding. Plaque and gingival indexes and any increase in gingival recession were recorded. Pulp vitality was verified. A survival rate based on the count of absolute failures and a success rate summarizing the effect of both absolute and relative failures were calculated.

RESULTS

The mean observation period was 43.1 months, with an observation interval of 36 to 60 months and a survival rate of 97.4%. From the 5 relative failures (3 minimal fractures or chips and 2 limited marginal discolorations) and the 2 absolute failures (unrepairable fractures), an overall success rate of 91.0% was recorded, with 71 restorations that were judged excellent in terms of clinical acceptance after the recall examination. From the Clinical-Photographic-Micromorphologic evaluation, 5 restorations (6.4%) showed minimal issues for marginal integrity, while a limited porcelain overhang was identified on 2 restorations (2.8%). Micromorphologic analyses confirmed the clinical evaluations. No periodontal recession was observed, and plaque and gingival indexes appeared stable.

CONCLUSIONS

Porcelain laminate veneers placed as per the CH no-prep protocol demonstrated excellent performances after 36 to 60 months of clinical service. The achieved outcomes, in terms of color match and overall esthetic and anatomic integration, confirmed that a prepless approach may be safely adopted provided that strict rules for patient selection and finish line placement are adopted.

Assessment of the Accuracy in Measuring the Enamel Thickness of Maxillary Incisors with Optical Coherence Tomography

Although the clinical assessment of enamel thickness is important, hardly any tools exist for accurate measurements. The purpose of this study was to verify the precision of enamel thickness measurements using swept-source optical coherence tomography (SS-OCT). Human extracted maxillary central and lateral incisors were used as specimens. Twenty-eight sites were measured in each specimen. The optical path length (OPL) at each measurement site was measured on the OCT images, and enamel thickness (e1) was calculated by dividing OPL by the mean refractive index of enamel, 1.63. The specimens were then sectioned, and a light microscope was used to measure enamel thickness (e2). e1 and e2 were then compared. Measurement errors between e1 and e2 for the central and lateral incisors were 0.04 (0.02; 0.06) mm and 0.04 (0.02; 0.07) mm [median value: (25%, 75% percentile)], respectively. No significant differences between measurement sites were noted for measurement errors between e1 and e2. These results demonstrate that OCT can be used for noninvasive, accurate measurements of enamel thickness.

Dentin Exposure after Tooth Preparation for Laminate Veneers: A Microscopical Analysis to Evaluate the Influence of Operators' Expertise

Background: To assess the quantity of dentin exposure detected by 3 operators with different clinical expertise for 2 designs of tooth preparation for laminate veneers: window (WI) and butt joint (BJ). Methods: 20 intact maxillary central incisors were collected and then prepared for laminate veneers to a depth of 0.6 mm, with a cervical mini-chamfer finish line of 0.3 mm. Each prepared tooth was analyzed by 3 operators with different expertise: undergraduate student (ST), general practitioner (GP), and prosthodontist (PR), at sight under magnification. Besides descriptive statistics (CI 95%), 2-way ANOVA and Games−Howell tests were used to analyze differences among groups (α = 0.05). Results: The means of percentage and area of detected dentin exposure were WI = 30.48%, 21.57 mm2; BJ = 30.99%, 21.97 mm2; ST/WI = 22.82%, 16.44 mm2; GP/WI = 58.05%, 40.64 mm2; PR/WI = 10.55%, 7.63 mm2; ST/BJ = 28.99%, 20.83 mm2; GP/BJ = 40.56%, 28.32 mm2; PR/BJ = 23.42%, 16.75 mm2. Significant differences were found between ST/WI vs. GP/WI (p = 0.005) and GP/WI vs. PR/WI (p < 0.001). Conclusions: There was no difference in detection of exposed dentin among operators with different expertise for BJ preparation, whereas differences were found between the general practitioner and the other 2 operators in WI. Moreover, the quantity of exposed dentin was not related to different tooth preparation designs.

Shear bond strength of ceramic laminate veneers to finishing surfaces with different percentages of preserved enamel under a digital guided method

Background

The purpose of this in vitro study was to evaluate the effect of the percentages of preserved enamel on ceramic laminate veneers’ (CLVs) shear bond strength (SBS).

Methods

Seventy extracted human maxillary central incisors were scanned and reconstructed into three-dimensional models. The extracted teeth were then embedded and randomly divided into seven groups (n = 10 per group). Based on digital analyses of the three-dimensional models, guided tooth preparation and bonding procedures were performed individually to form seven different percentages (100%, 80%, 60% 50%, 40%, 20% and 0%) of remaining enamel thickness on the bonding surface. Finally, the SBS test was performed, and the data were statistically analysed by one-way ANOVA with LSD post hoc test (α = 0.05).

Results

The complete enamel surface exhibited the highest SBS (19.93 ± 4.55 MPa), followed by 80% enamel (19.03 ± 3.66 MPa), 60% enamel (18.44 ± 3.65 MPa), 50% enamel (18.18 ± 3.41 MPa), 40% enamel (17.83 ± 3.01 MPa) and 20% enamel (11.32 ± 3.42 MPa) group. The lowest SBS (9.63 ± 3.46 MPa) was detected in 0% enamel group. No significant difference was observed among the 40–100% enamel groups, while the 20% or 0% enamel group demonstrated a significantly lower mean SBS than the 40% enamel group (p < 0.05).

Conclusion

The SBS value of CLVs bonded to 100% enamel on the finishing surfaces (nearly 20 MPa) was twice that which bonded to 0% enamel (nearly 10 MPa). Bonding to 100% enamel is the most reliable treatment. When dentin exposure is inevitable, enamel should be preserved as much as possible to maintain good bonding. In addition, 40% of preserved enamel on the bonding surface was the minimal acceptable value to fulfil the requirements of good bonding strength.

Accuracy of Reduction Depths of Tooth Preparation for Porcelain Laminate Veneers Assisted by Different Tooth Preparation Guides: An In Vitro Study

PURPOSE

To evaluate the accuracy (trueness and precision) of reduction depths of guided veneer preparation assisted by four tooth preparation guides.

MATERIALS AND METHODS

Fifty resin artificial teeth were randomly divided into five groups (n = 10): a freehand group (F), silicone guide group (S), thermoplastic guide group (T), 3D printed uniform guide group (D), and 3D printed auto-stop guide group (A). A preparation for a window veneer on the maxillary right central incisor was performed by two surgeons who used tooth preparation guides for assistance. The maxillary right central incisors were scanned before and after the preparation. The reduction depths were measured in the cervical, middle, and incisal thirds of the prepared surface, and depth maps were created using Geomagic Control X software. The accuracy of the reduction depths at each third was evaluated using both trueness and precision values. The trueness of the reduction depths was determined by calculating the mean absolute differences (MADs) compared to the planning depth, and precision was determined by the standard deviation (SD). The collected data were statistically analyzed using one-way ANOVA and the least significant difference test (α = 0.05).

RESULTS

The MAD ± SD values of the reduction depths in the cervical-third region in groups F, S, T, D, and A were 0.19 ± 0.04, 0.12 ± 0.03, 0.09 ± 0.02, 0.07 ± 0.02, and 0.05 ± 0.01 mm, respectively. In the middle-third region, the MAD ± SD values of groups F-A were 0.19 ± 0.05, 0.13 ± 0.02, 0.09 ± 0.01, 0.06 ± 0.01, and 0.05 ± 0.01 mm. In the incisal-third region, the MAD ± SD values were 0.27 ± 0.05, 0.16 ± 0.04, 0.11 ± 0.03, 0.07 ± 0.01, and 0.05 ± 0.01 mm, respectively. Significant differences in trueness and precision values were found across different groups (F = 45.378, p = 0.000), where group F showed higher MADs than the other 4 groups (p = 0.000), and the highest MADs were detected in group S among the 4 groups in all regions (p = 0.000). Group T showed significantly higher MADs than groups D (P = 0.008) and A (p = 0.001), except in the cervical-third region, where no significant difference was observed between groups T and D (p = 0.077). There was no significant difference between groups D and A (p = 0.148). The deviation map showed significant differences among groups (F = 15.963, p = 0.000), group T presented less deviation than group F (p = 0.000) and group S (p = 0.027) and showed more deviation than group A (p = 0.007).

CONCLUSION

Tooth preparation guides provided more accuracy for veneer preparation than freehand preparation. Among the 4 guides, the 3D printed auto-stop guide presented the lowest absolute difference (0.05 mm) and the silicone guide showed the highest absolute difference of preparation (0.12-0.16 mm).

Micro-CT and Microscopy Study of Internal and Marginal Gap to Tooth Surface of Crenelated versus Conventional Dental Indirect Veneers

Background and Objectives: Ceramic veneers represent the most appropriate treatment option for minimally invasive aesthetic rehabilitation. For long-term clinical success, the accurate marginal and internal adaptation of dental restorations are of paramount importance. The aim of this in vitro study is to assess the effect of a novel (patented) design of veneers compared to conventional ones on their marginal and internal gap to the prepared tooth surface. Materials and Methods: Twenty-four lithium disilicate ceramic veneers are obtained using Computer-Aided-Design (CAD) and then milled using Computer-Aided-Manufacturing (CAM). The samples are divided into two groups: 12 conventional (CO) veneers (i.e., with a linear marginal contour) and 12 crenelated (CR) veneers, the latter with the novel sinusoidal marginal design. All samples are bonded to frontal teeth, and the adhesive interfaces are analyzed using two methods, optical microscopy and micro-Computed Tomography (CT): the former for the accuracy of the marginal gap and the latter for the internal gap (as well as for the homogeneity of the luting cement) of ceramic veneers. Results: STATA and one-way ANOVA tests reveal significant differences between CO and CR veneers: (i) the marginal gap is smaller for CR (64 μm) than for CO veneers (236 μm); (ii) the internal adaptation is better for CR veneers: for a cement width of up to 120 μm, the covered surface for the CR group is 81.5%, while for the CO group it is 64.5%; (iii) the mean of the porosities within the cement is not significantly different (3.4·10⁶ μm³ for CO and 3.9·10⁶ μm³ for CR veneers), with a higher standard deviation for the CO group. Analytical modeling is achieved for internal gaps using the micro-CT results. The characteristic functions obtained allow us to compare the volume of luting cement for the two types of veneers. Conclusion: The novel veneers design produces an improvement in the marginal and internal adaptation of the restorations to the prepared tooth surface. Thus, it provides favorable premises for better clinical performances.

Substantial in-vitro and emerging clinical evidence supporting immediate dentin sealing

The application of resin adhesive to freshly cut dentin after teeth preparation, the so-called immediate dentin sealing (IDS) has been suggested as an alternative to the delayed dentin sealing (DDS), a technique in which resin adhesive is applied just before final bonding of indirect restorations.

The aim of this review is to demonstrate the evidence of the claimed advantages made by the proponents of IDS technique.

The results of this review revealed substantial in-vitro evidence supporting the IDS benefits including improved bond strength, reduced dentin permeability, improved restorations’ adaptation, and increased fracture strength of the restorations. Clinical studies have shown that IDS improves survival of ceramic laminate veneers bonded to prepared teeth with increased exposure of dentin. Moreover, it has been shown that IDS reduces post-cementation hypersensitivity in full coverage restorations, which is characterized by exposure of a large number of dentinal tubules. The selection of filled resin adhesive that is capable of producing thick adhesive layer appears to contribute to the success of the technique. Furthermore, careful management of the oxygen inhibition layer before conventional impression making and proper cleaning of the residual temporary cement used with provisional restorations appears to affect the outcome of the restorations.

Immediate Dentin Sealing: A Literature Review

Purpose

The immediate application of a dentin-bonding agent after tooth preparation and before impression-taking (immediate dentin sealing [IDS]) has been suggested to provide several advantages concerning bacterial microleakage, hypersensitivity, and bonding quality. We reviewed the literature and clarified certain aspects related to each step of IDS application.

Materials and Methods

The search strategy comprised an electronic research in MEDLINE, Cochrane, Ovid and Scopus for studies published from January 1990 to December 2020 regarding the IDS technique and including both in vitro and clinical studies.

Results

After exclusion of irrelevant or duplicate articles, 88 articles focusing on aspects of the IDS technique were assessed. IDS seems to be advantageous with regard to bond strength, gap formation, bacterial microleakage, and dentin hypersensitivity. However, issues arising from interaction with impression materials, the provisional phase, and conditioning methods before cementation require further investigation.

Conclusion

There are no documented reasons preventing clinicians applying IDS in their everyday practice. On the contrary, the presented technique seems to be beneficial in certain aspects regarding indirect restorations.

Predictable 3D guided adhesive bonding of porcelain veneers using 3D printed trays

OBJECTIVE

This clinical report describes a novel digital technique to facilitate and improve the porcelain laminate veneers adhesive bonding procedure using a customized 3D printed guide.

CLINICAL CONSIDERATIONS

Porcelain veneers can be stabilized in their fully seated position with a digitally design 3D printed guide before the resin cement is polymerized. The excess cement can be carefully and predictably removed without the risk of dislodgement, rotation or misfit, allowing the clinician to light cure them under controlled pressure in the correct seating position without the risk of fracturing the ceramic material.

CONCLUSIONS

Fabricating a custom 3D printed guide for veneer bonding provides significant assistance to an otherwise cumbersome and daunting clinical procedure.

CLINICAL SIGNIFICANCE

Adhesive bonding of multiple ceramic veneers is a challenging and technique sensitive procedure. The use of a custom 3D printed guide presented in this article offers a practical aid to achieve a more predictable and precise outcome.

The effect of pre-treatment levels of tooth wear and the applied increase in the vertical dimension of occlusion (VDO) on the survival of direct resin composite restorations

OBJECTIVES

To investigate the effects of the level of pre-treatment tooth wear and increasing the VDO on the performance of direct resin composite restorations for the rehabilitation of pathological tooth wear.

METHODS

Full-mouth (pre-treatment) grading was performed on digital greyscale scan records for 34 participants (35.3 ± 8.4 years) with signs of moderate-to-severe generalised tooth wear, using the Tooth Wear Evaluation System and the Basic Erosive Wear Examination. Each participant received full-mouth direct resin composite restorations, with increased VDO. The post-treatment increase in the VDO was determined. Recalls were planned after 1 month, and after 1, 3, and 5 years. Three 'levels' of restoration failure were described. The effects of the variables on the frequencies of restoration failure were calculated with a multivariable Cox regression, (p < 0.05).

RESULTS

1269 restorations were placed with a mean observation period of 62.4 months. Increasing the VDO by 1 mm significantly reduced the risks of all levels of anterior restoration failure (HR ≤ 0.62, p ≤ 0.025). A higher anterior BEWE surface score was associated with increased risks of Level 2- & 3- failures, (HR ≥ 1.29, p ≤ 0.019). Premolar restorations showed lower risks of Level 2- & 3- failure, compared to the molar restorations, (HR ≤ 0.5, p ≤ 0.005).

CONCLUSION

Levels of pre-treatment wear and the applied change in the VDO significantly affected failure risk.

CLINICAL RELEVANCE

Direct resin composite restorations for the rehabilitation of wear should be made as voluminous as possible, respecting the presenting biological, functional, and esthetic constraints.

A multidisciplinary minimally invasive approach for the esthetics of the smile

The aim of this work is to define a new multidisciplinary pathway for dental and gingival problems. The method consists of three different instruments that can resolve dental, labial, and periodontal imperfections with minimal invasiveness.

Marginal discrepancy and load to fracture of monolithic zirconia laminate veneers: The effect of preparation design and sintering protocol

To investigate and analyze the impact of teeth preparation designs and sintering protocol on marginal fit and fracture resistance of monolithic translucent zirconia laminate veneers. A total of 40 extracted intact human maxillary central incisors were assigned into 4 groups (n=10/each group) to investigate 2 variables: (1) the design of tooth preparation (a 1.5 mm incisal reduction with or without palatal chamfer) and (2) the two different sintering programs used for translucent zirconia restoration (standard or speed sintering procedure). Marginal discrepancy was evaluated using a digital microscope. The specimens were loaded to failure in the compression mode, using a universal testing machine with a crosshead speed of 0.5 mm/min. Marginal adaptation of monolithic translucent zirconia laminates are affected by both tooth preparation design and sintering protocol. However, resistance to fracture of translucent zirconia laminates has affected mainly by sintering procedure regardless the teeth preparation design used.

Effect of an Er,Cr:YSGG Laser on the Debonding of Lithium Disilicate Veneers With Four Different Thicknesses

Introduction: The objective of this study was to compare in vitro the resistance and type of failure in the debonding of lithium disilicate veneers with four different thicknesses using an erbium chromium yttrium-scandium gallium-garnet (Er,Cr:YSGG) laser. Methods: Sixty-eight bovine teeth were used to bond round lithium disilicate veneers with a 6-millimeter diameter and four different thicknesses: group 1 (0.4 mm), group 2 (0.8 mm), group 3 (1.2 mm) and group 4 (1.6 mm). Each sample was irradiated with an Er,Cr:YSGG laser with 4 W of power and a frequency of 50 Hz, during 60 seconds, scanning concentrically. The energy density per pulse or fluency applied was 5.33 J/cm2 for the four groups. The samples were subjected to a force in a universal testing machine and then observed under a microscope to determine the type of failure. Data were statistically analyzed with the non-parametric Kruskal-Wallis test. Results: The tendency in the results revealed that the thicker veneers showed more resistance to the debonding process. The debonding strength for group 3 was the highest (5.62 MPa), followed by group 4 (5.20 MPa), then group 2 (0.85 MPa) and finally group 1 (0.0 MPa). The most frequent type of failure was cohesive failure in cement (CC) for all groups, with 73.53% (P ≤ 0.083). Conclusion: Er,Cr:YSGG laser irradiation influences the debonding of lithium disilicate veneers with different thicknesses: the smaller thickness showed the greater debonding. The thickness of veneers was not associated with the type of failure.

Survival Rates for Porcelain Laminate Veneers: A Systematic Review

The aim of this systematic review was to analyze and compare the most up-to-date information available on long-term, medium-term, and short-term survival rates of porcelain laminate veneers (PLVs) and investigate the homogeneity in current studies or lack of it. An electronic search was performed using PubMed, Ovid MEDLINE, Cochrane Library, Web of Science, EBSCO, Science Direct, Wiley, and Scopus databases. Based on the PRISMA guidelines, the main inclusion criteria consisted of research articles published after the year 2000, in vivo studies with a follow-up period of at least 1 year and reporting of the Kaplan–Meier estimated cumulative survival rates. Quality assessment of the included studies was performed using the modified systematic assessment list consisting of 24 items. Thirty full-text articles were reviewed in detail. A total of 30 articles met the inclusion criteria and were selected for qualitative synthesis. The remaining 27 publications were retained to discuss the heterogeneity in the current literature and reported longevity of veneer restorations. A conclusive estimation of the longevity of PLVS beyond 20 years is lacking. The availability of evidence in the current literature is limited in terms of sample size and duration of follow-up. However, the majority of studies have concluded that PLVs have high-success rates and predictable patient outcomes. The present literature indicates an increased heterogeneity among research study designs. Researchers should aim for homogeneous study designs that can be included in systematic reviews and meta-analyses.

Fracture load of CAD/CAM ultrathin occlusal veneers luted to enamel or dentin

OBJECTIVES

To evaluate, in vitro, the fracture load of IPS e.max CAD occlusal veneers at thicknesses of either 0.3 or 0.6 mm luted to enamel or dentin.

MATERIALS AND METHODS

Fifty human molars were randomly distributed into five groups (n = 10): G1 - healthy teeth (control); G2-0.3-mm-thick veneers luted to enamel; G3-0.6-mm-thick veneers luted to enamel; G4-0.3-mm-thick veneers luted to dentin; and G5-0.6-mm-thick veneers luted to dentin. After the luting procedures, the specimens were immersed in distilled water at 37°C for 24 hours and then subjected to mechanical loading (10⁶  cycles at 200 N load). The specimens were subjected to a fracture load test in a universal testing machine. Two-way ANOVA and Tukey's test (α = 0.05) were used to analyze data.

RESULTS

Only the thickness factor was significant (P = .002). Values of fracture load followed by distinct letters represent significant differences (P < .05): G1 (3204 N ± 730)^ab ; G2 (3144 N ± 729)^ab ; G3 (2489 N ± 606)^b ; G4 (3591 N ± 776)^a ; and G5 (2770 N ± 598)^ab .

CONCLUSION

IPS e.max ultrathin occlusal veneers luted to enamel or dentin obtained fracture load comparable to that of the healthy tooth.

CLINICAL SIGNIFICANCE

IPS e.max CAD ultrathin occlusal veneers at 0.3 or 0.6-mm-thick seem to provide good perspectives in relation to the clinical use.

Retrospective evaluation of extended glass-ceramic ceramic laminate veneers after a mean observational period of 10 years

PURPOSE

A retrospective evaluation of extended anterior ceramic laminate veneers (EACVs) after a mean observational period of 10 years.

METHODS

Thirty-one patients (20 females/11 males) underwent restoration with 101 adhesively luted, heat-pressed EACVs (maxilla, n = 65; mandible, n = 36).

RESULTS

The 10 year survival rate was 91.8% (95% confidence interval [95%-CI]: 0.87;0.97). Eight ceramic fractures, one biological failure, and one change in treatment plan caused the observed failures. Seventy-seven of the 101 restorations remained intervention-free in service (success rate: 78.6% [95%-CI: 0.70;0.88]). Fourteen interventions were needed (nine recementations, two endodontic treatments, two composite fillings, and one fracture polishing). The jaw position (maxilla/mandible, survival P = .578/success P = .056) had no influence on the clinical performance. EACVs covering large areas of exposed dentin (>50%) were associated with a significantly increased risk (hazard ratio 2.98, P = .019) of needing a clinical intervention (success rate: 68.0% [95%-CI: 0.52; 0.84]). However, the degree of dentin exposure had no effect on the survival rate (P = .761).

CONCLUSIONS

After a mean observational period of 10 years, mandibular and maxillary EACVs exhibited survival and success rates that were comparable. Significantly lower success rates were associated with large areas of exposed dentin (>50%).

CLINICAL SIGNIFICANCE

Mandibular and maxillary EACV revealed 10-year survival rates comparable to those published for anterior metal-ceramic and glass-ceramic full-coverage crowns. Precaution should be taken not to expose dentin, and when large areas of dentin are exposed, different conditioning/luting strategies should be used.

Bond strength of surface-treated novel high translucent zirconia to enamel

Aim: The aim of the present study was to evaluate the shear bond strength of zirconia, stabilised with 5% yttria, luted to enamel and to evaluate the fracture pattern at loss of retention.

Methods: A total of 53 test specimen were manufactured from two partially stabilised zirconia materials, Zirkonzahn Prettau Anterior (ZPA) (n = 16) and Whitepeaks CopraSmile Symphony 5 layer (WCS) (n = 18), and a lithium disilicate (Ivoclar e.Max Press) (n = 19) acting as control. All test specimens were cemented to human enamel with Variolink Esthetic DC and then subjected to a shear bond strength test. Fracture and surface analysis were performed using light and scanning electron microscope.

Results: No significant differences in shear bond strength were detected when analysing the three groups. Dividing them according to the fracture pattern significant difference in shear bond strength between the two zirconia groups could be seen analysing test bodies with failure of adhesion to the test body, but not to enamel. The ZPA had higher shear bond strength (23.68 MPa) than WCS (13.00 MPa). No significant differences were seen compared to the control group (19.02 MPa).

Conclusion: Partially stabilised zirconia shows potential as a material to be used where macro mechanical bonding is not possible, although this study does not reveal how or if the bonding deteriorates over time.

Advances in materials and concepts in fixed prosthodontics: a selection of possible treatment modalities

The introduction of adhesive techniques in combination with translucent restorative materials has greatly influenced treatment concepts in fixed prosthodontics. Modern production technologies offer access to new polymer materials that provide innovative pre-treatment options for complex prosthetic rehabilitations. Additionally, computer-aided design and manufacturing (CAD/CAM) provides access to new ceramic types and thus extends the range of indications for metal-free restorative options. With these developments, important changes of treatment concepts in fixed prosthodontics have occurred which affect the professional life of dental practitioners with a focus on prosthetic dentistry. This article gives an overview of the advances in selected fields of fixed prosthodontics and provides support in material selection for different kinds of indications, from single-tooth restorations to fixed dental prostheses.

Fracture resistance of veneers in premolars

Objective

The purpose of the study was to compare the fracture resistance of ceramic veneers and composite resin veneers with and without dental preparation.

Materials and Methods

Forty freshly extracted mandibular premolars were selected and randomly assigned into four groups (n = 10): Group NPR = no dental preparation and direct veneer with 0.2 mm thick composite resin (Amelogen Plus, Ultradent); Group NPC = no dental preparation and 0.2 mm thick lithium disilicate ceramic veneer (IPS e.max Press, Ivoclar Vivadent); Group P2C = Tooth preparation of 0.2 mm and 0.2 mm thick ceramic veneer (IPS e.max Press); and Group P5C = Tooth preparation of 0.5 mm and 0.5 mm-thick ceramic veneer (IPS e.max Press). In all groups, the restorations covered 1 mm of the occlusal surface of the buccal cusp, and the thickness of this area was the same of the buccal area (0.2 mm or 0.5 mm). After the luting procedure, all groups were thermocycled (10,000 cycles, 5°C-55°C) and subjected to fracture resistance test under compression (Instron 4444 with a crosshead speed of 0.5 mm/min). The mode of failure analysis was performed under a ×10 magnification. Data were subjected to one-way ANOVA and Duncan's post hoc test (P < 0.05).

Results

The mean fracture resistance (men ± standard deviation) was NPR = 690.33 ± 233, NPC = 790.52 ± 408, P2C = 1131.34 ± 341, and P5C = 983.56 ± 202. There were significant differences of the fracture resistance values between all groups (P = 0.013). NPR and NPC groups showed mean values of fracture resistance significantly lower than P2C. However, P5C presented intermediate values without a significant difference from the other groups. The mode of failure for all groups was mixed (60%), cohesive failures (20%), root failures (15%), and adhesive failures (5%).

Conclusion

Minimally invasive tooth preparation (0.2-mm) allowed to achieve higher fracture resistance in premolars restored with lithium disilicate ceramic veneers. Attention should be given to the 0.5 mm preparation since catastrophic fractures only happened when this preparation depth was performed.

Influence of bonding surface and bonding methods on the fracture resistance and survival rate of full-coverage occlusal veneers made from lithium disilicate ceramic after cyclic loading

OBJECTIVES

The purpose of this laboratory study was to evaluate the influence of bonding method and type of dental bonding surface on fracture resistance and survival rate of resin bonded occlusal veneers made from lithium disilicate ceramic after cyclic loading.

METHODS

Fourty-eight extracted molars were divided into three groups (N=16) depending on the preparation: within enamel, within dentin/enamel or within enamel/composite resin filling. Lithium disilicate occlussal veneers were fabricated with a fissure-cusp thickness of 0.3-0.6mm. Restorations were etched (5% HF), silanated and adhesively luted using a dual-curing luting composite resin. Test groups were divided into two subgroups, one using a only a self-etching primer, the other additionally etching the enamel with phosphoric acid. After water storage (37°C; 21d) and thermocycling (7500 cycles; 5-55°C), specimens were subjected to dynamic loading in a chewing simulator (600,000 cycles; 10kg/2Hz). Surviving specimens were loaded until fracture using a universal testing machine.

RESULTS

All specimens survived artificial aging, several specimens showed some damage. ANOVA revealed that enamel etching provided statistically significantly (p≤0.05) higher fracture resistance than self-etching when bonding to enamel and dentin. Self-etching provided statistically significant (p≤0.05) higher fracture resistance for the enamel-composite group than for the enamel group. Enamel etching provided statistically significant (p≤0.05) higher fracture resistance for the enamel and dentin group than for groups enamel and enamel-composite.

SIGNIFICANCE

Etching enamel improved the fracture resistance of occlusal veneers when bonding to dentin and enamel and increased the survival rate when bonding to enamel.

Clinical performance of pressable glass-ceramic veneers after 5, 10, 15, and 20 years: A retrospective case series study

OBJECTIVES

To evaluate the long-term clinical performance and survival rate of pressable lithium-disilicate glass-ceramic veneers (LDSVs).

MATERIALS AND METHODS

A total of 413 LDSVs were bonded to anterior and posterior teeth by three experienced clinicians between 1998 and 2012. The LDSVs were examined for color/ esthetic match of the glass-ceramic surface (esthetic evaluation), fracture rate, marginal discoloration (staining of the luting cement), and marginal integrity (including caries, clinical evaluation). For clinical and esthetic evaluations, the modified United States Public Health Services (USPHS) score was used in this study. The success rate was determined with a Kaplan-Meier survival analysis.

RESULTS

The mean observation time was 11.33 ± 4.85 years. There was no loss to follow-up, all restorations were accounted for in the final analysis. The probability of survival of the 413 veneers was 98% after 5 years, 95% at 10 years, 91% at 15, and 87% at 20 years, indicating a very low clinical failure rate. Of the 413 restorations, complications were occurred in 15 (3.63%) of all restorations, and fractures and debonding in 6 (1.45%) and 9 (2.18%), respectively.

CONCLUSIONS

The LDSVs showed high survival rate and very good results for color match and anatomic form and marginal integrity in the long-term analysis.

CLINICAL SIGNIFICANCE

The long-term performance of LDSVs can be considered as highly favorable when carefully planned.

Effect of surface removal following bleaching on the bond strength of enamel

Background

A reduction in bond strength of bleached enamel has been confirmed in the literature. Although limited information is available, it is conceivable that the veneer preparation process may remove the impacted enamel and further eliminate the compromised bond strength between the composite resin and bleached enamel. This study aimed to evaluate the effect of surface removal following bleaching on the micro-shear bond strength (μSBS) of bleached enamel.

Methods

Forty-eight specimens were prepared from bovine incisors and were randomly divided into 2 groups (n = 24): group B (bleaching with 40% hydrogen peroxide for 2 × 45 min with a 1-week interval) and group C (control group without bleaching treatment). Immediately after receiving the treatments, 0.5 mm of the enamel was removed from the specimen surface, followed by bonding of composite resin to the enamel surface. Each group was further divided into 2 subgroups of 12 specimens each: subgroup T (with 5000 thermocycles in water baths at 5 °C and 55 °C), and subgroup N (without thermocycling). The μSBS values were measured using a universal testing machine and subjected to two-way analysis of variance (α = 0.05). The fracture modes of the specimens were observed using a stereomicroscope.

Results

The μSBS values of the different groups ranged from 21.42 to 25.21 MPa. Following a surface reduction of 0.5 mm, bleaching treatment and thermocycling did not significantly affect the μSBS values (P = 0.348 and P = 0.507, respectively). No significant interaction was found between the bleaching treatment and thermocycling (P = 0.514). All the groups exhibited a high percentage of mixed failures. Compared with group C, group B exhibited higher percentage of adhesive failure.

Conclusion

The results suggested that the bonding procedure could be performed on the bleached enamel following a surface reduction of 0.5 mm immediately after the bleaching treatment.

Fracture Resistance of Ceramic Laminate Veneers Bonded to Teeth with Class V Composite Fillings after Cyclic Loading

Purpose

Porcelain laminate veneers (PLVs) are sometimes required to be used for teeth with composite fillings. This study examined the fracture strength of PLVs bonded to the teeth restored with different sizes of class V composite fillings.

Materials and Methods

Thirty-six maxillary central incisors were divided into three groups (n=12): intact teeth (control) and teeth with class V composite fillings of one-third or two-thirds of the crown height (small or large group, resp.). PLVs were made by using IPS e.max and bonded with a resin cement (RelyX Unicem). Fracture resistance (N) was measured after cyclic loading (1 × 10⁶ cycles, 1.2 Hz). For statistical analyses, one-way ANOVA and Tukey test were used (α=0.05).

Results

There was a significant difference between the mean failure loads of the test groups (P=0.004), with the Tukey-HSD test showing lower failure loads in the large-composite group compared to the control (P=0.02) or small group (P=0.05). The control and small-composite groups achieved comparable results (P > 0.05).

Conclusions

Failure loads of PLVs bonded to intact teeth and to teeth with small class V composite fillings were not significantly different. However, extensive composite fillings could compromise the bonding of PLVs.

The restorative management of microdontia

Microdontia is a dental abnormality that will often present to the dental practitioner due to the aesthetic concerns of the patient. Treatment is therefore aimed at addressing the aesthetics issue of the patient and this can present a number of challenges which may require a multidisciplinary approach in its management. This article presents the restorative management of localised and generalised microdontia.

Ceramic Laminate Veneers for Reestablishment of Esthetics in Case of Lateral Incisor Agenesis

The increasing demand of patients looking for esthetics has resulted in the development of several techniques to restore anterior teeth. Conservative treatments should always be the first therapeutic option for the solution of aesthetic problems involving morphological changes and usually provide the result that the patient expects. In this context, ceramic laminate veneers, also known as "contact lenses," are capable to provide an extremely faithful reproduction of natural teeth with great color stability and periodontal biocompatibility. Minimal or no preparation veneers are heavily advertised as the answer to patients' cosmetic needs, when properly indicated by the dentist. This paper reports a clinical case where lateral incisor agenesis was aesthetically corrected using ceramic laminates.

Effect of tooth substrate and porcelain thickness on porcelain veneer failure loads in vitro

STATEMENT OF PROBLEM

Bonded porcelain veneers are widely used esthetic restorations. High success and survival rates have been reported, but failures do occur. Fractures are the commonest failure mode. Minimally invasive or thin veneers have gained popularity. Increased enamel and porcelain thickness improve the strength of veneers bonded to enamel, but less is known about dentin or mixed substrates.

PURPOSE

The purpose of this in vitro study was to measure the influences of tooth substrate type (all-enamel, all-dentin, or half-dentin-half-enamel) and veneer thickness on the loads needed to cause initial and catastrophic porcelain veneer failure.

MATERIAL AND METHODS

Model discoid porcelain veneer specimens of varying thicknesses were bonded to the flattened facial surfaces of incisors with different enamel and dentin tooth substrates, artificially aged, and loaded to failure with a small sphere. Initial and catastrophic fracture events were identified and analyzed statistically and fractographically.

RESULTS

Fracture events included initial Hertzian cracks, intermediate radial cracks, and catastrophic gross failure. All specimens retained some porcelain after catastrophic failure. Cement failure occurred at the cement-porcelain interface not at the cement-tooth interface. Porcelain veneers bonded to enamel were substantially stronger and more damage-tolerant than those bonded to dentin or mixed substrates. Increased porcelain thickness substantially raised the loads to catastrophic failure on enamel substrates but only moderately raised the loads to catastrophic failure on dentin or mixed substrates. The veneers bonded to half-dentin-half-enamel behaved remarkably like those bonded wholly to dentin.

CONCLUSIONS

Porcelain veneers bonded to enamel were substantially stronger and more damage-tolerant than those bonded to dentin or half-enamel-half dentin.

Effect of Preparation Designs on the Prognosis of Porcelain Laminate Veneers: A Systematic Review and Meta-Analysis

Objective:

To investigate the association between preparation designs and prognosis of porcelain laminate veneers (PLVs).

Methods:

Electronic and manual literature searches were performed in Medline, Embase, CENTRAL, and Scopus databases for randomized controlled trials and retrospective and prospective cohort studies comparing any two of three preparation designs. The quality of the included studies was assessed using the Newcastle-Ottawa scale. Pooled hazard ratios and risk ratios were used to evaluate the difference between two preparation designs. Subgroup analyses, sensitivity analysis, and evaluation of publication bias were performed if possible.

Results:

Of 415 screened articles, 10 studies with moderate to high quality were included in the meta-analysis. Comparison of preparations with incisal coverage to preparations without coverage revealed a significant result based on time-to-event data (hazard ratio=1.81, 95% confidence interval [CI]=1.18-2.78, I2=12.5%), but the result was insignificant based on dichotomous data (risk ratio=1.04, 95% CI=0.59-1.83, I2=42.3%). The other comparisons between any two of overlap, butt-joint, and window types revealed no statistically significant difference. Subgroup analyses regarding the porcelain materials, location of prosthesis, and tooth vitality could account for only part of the heterogeneity. No evidence of publication bias was observed.

Conclusions:

Within the limitation of the present study, it can be concluded that preparation design with incisal coverage for PLVs exhibits an increased failure risk compared to those without incisal coverage. The failure risk of the overlap type may be higher than the butt-joint type but must be validated in further studies.

Influence of various bonding techniques on the fracture strength of thin CAD/CAM-fabricated occlusal glass-ceramic veneers

OBJECTIVES

To evaluate the efficiency of immediate dentin sealing and the effects of different bonding protocols on the fracture strength of CAD/CAM occlusal veneers bonded to exposed dentin.

METHODS

Ninety-six extracted maxillary premolars were initially divided into three main groups with 32 specimens each: without immediate dentin sealing, immediate dentin sealing/total etching and immediate dentin sealing/selective etching. Teeth were identically prepared in the dentin to receive occlusal veneers of 0.8mm thickness, milled from lithium disilicate ceramic blocks (IPS e.max CAD). Each main group was later subdivided, according to the pre-cementation surface etching protocol (total/selective), into two subgroups with 16 specimens each. All restorations were adhesively bonded using a resin cement (Variolink Esthetic). Half of the specimens of each subgroup were subjected to thermo-dynamic loading in a chewing simulator with 1,200,000 cycles at 10kg load. The other half and the surviving specimens were subjected to quasi-static loading until failure. Statistical analysis was performed using three-way ANOVA and Tukey's post-hoc tests.

RESULTS

All specimens except one survived the artificial aging. A significantly higher fracture strength of restorations (p ≤ 0.001) was obtained when immediate dentin sealing was followed regardless of the etching method with values ranging from a minimum of 1122 ± 336N to a maximum of 1853 ± 333N. Neither the pre-cementation treatment nor the artificial aging had a statistical significant effect on the fracture strength.

SIGNIFICANCE

Immediate dentin sealing protocol is recommended whenever dentin is exposed during the preparation for thin glass-ceramic occlusal veneers.

Systematic development of esthetics and function in a young patient with maxillary dental aplasia

OBJECTIVES

Full-arch rehabilitations in young patients suffering from dental agenesis should compensate for the reduced vertical dimension of occlusion and restore both esthetics and function at minimal biological cost. This requires precise planning and maximum patient compliance during the preprosthetic phase. The pretreatment period with tooth-colored splints promotes a predictable outcome of the final restorations. Clinical considerations: Thanks to better restorative materials and adhesive techniques and increased knowledge of how to preserve sound tooth structures, prosthetic dentistry has increasingly turned toward minimally invasive procedures. The present clinical case documents a minimally/non-invasive maxillary full-arch rehabilitation of an agenesis patient with multiple dental aplasia, primary tooth persistence, and deficits in bone growth. The patient was pretreated with a tooth-colored CAD/CAM polycarbonate splint. Adequate esthetics and function were achieved by two zirconia-based single-wing adhesive fixed dental prostheses to replace the upper lateral incisors, lithium disilicate ceramic partial crowns for the posterior regions, and two feldspathic veneers for the upper central incisors.

CONCLUSIONS

Non-invasive pretreatment with a removable tooth-colored splint realizes the treatment goal simply and safely, reduces treatment time, increases predictability, and facilitates the transfer of the prototype to the final restorations. New restorative options permit the minimally invasive treatment of such patients.

CLINICAL SIGNIFICANCE

A pretreatment with a removable tooth-colored splint offers a simple and safe way to define the treatment goal, reduces treatment time, increases predictability, and facilitates the transfer of the results to the final restorations even in complex cases. New restorative options permit minimally invasive treatments of young patients with multiple dental agenesis.

Comparing marginal microleakage of three different dental materials in veneer restoration using a stereomicroscope: an in vitro study

Objectives:

The objectives were to evaluate the degree of dye penetration of three different dental materials as esthetic veneer restorations on anterior teeth using stereomicroscope, and to provide reference for clinical choice.

Materials and Methods:

Sixty freshly extracted human maxillary central incisors were selected and randomly divided into three main groups of 20 each. Respectively, the teeth were prepared for veneer restoration by fiber-reinforced composite (FRC) (Everstick NET, Stick Tech), porcelain laminate veneer (PLV) (IPS Empress II(E-Max Press)) and 3M composites (3M ESPE) bonding with G-Cem resin cement (GC). After exposed to thermocycling (500cycles per day (5–55 °C, intervals: 30 s)) and immersed in 2% basic fuchsin dye solution for 24 h, the specimens were then sectioned buccolingual into three halves in a vertical plane parallel and measured dye penetration using stereomicroscope (Zeiss). The data collected was recorded by the dye penetration index (0–5) and statistically analysed using one-way analysis of variance (ANOVA) and T-tests using SPSS 13.

Results:

It is evident that the FRC group showed the lowest mean score of 0.333 mm, and the PLV group showed a highest mean score of 0.749 mm, as compared with the FRC group and the 3M composites group. Overall, when the three groups were compared for microleakage using ANOVA, there was significant difference among the groups.

Conclusions:

To evaluate the dye penetration of microleakage, the FRC showed a better marginal adaptability for veneer restoration. Therefore, within the limitation of this study, the use of FRC as veneer on anterior teeth can be suggested.