The Tubular Penetration Depth and Adaption of Four Sealers: A Scanning Electron Microscopic Study

Comparative evaluation of dentinal tubule penetration and push-out bond strength of new injectable hydraulic calcium disilicate based root canal sealer: A single blinded in vitro study

Objective

To evaluate and compare dentinal tubule penetration and push-out bond strength of BIO-C ION+, AH Plus and NanoSeal-S using Confocal Laser Scanning Microscopy (CLSM) and Universal Testing Machine (UTM).

Materials & method

Sixty human mandibular premolars were prepared using ProTaper Gold till F3. Samples were then divided into 3 groups: Group I (n = 20) BIO-C ION + sealer, Group II (n = 20) AH Plus and Group III (n = 20) NanoSeal-S sealer. Groups were then sub-divided into two sub groups: In Subgroup A (n = 10) samples were obturated using single-cone with 0.1 % Rhodamine B dye and in Subgroup B (n = 10) samples were obturated using single cone. The samples were then transversely sectioned into coronal, middle and apical segments, samples in subgroup A & B were then submitted to CLSM analysis and UTM respectively.

Results

The Bond Strength data showed following means (MPa): Group I Subgroup B: (BIO-C ION+) coronal (1.64), middle (1.25), apical (0.93); Group II Subgroup B: (AH Plus) coronal (2.20), middle (1.85) apical (1.38) and Group III Subgroup B: (NanoSeal-S) coronal (1.26), middle (0.94), apical (0.58). The dentinal tubule penetration data showed following means: (μm) Group I Subgroup A (BIO-C ION+) coronal (1184.69), middle (997.03), apical (637.26); Group II Subgroup-A AH Plus (864.14) and NanoSeal-S (495.64). Statistical analysis (two-way ANOVA, Tukey's Post Hoc Test) showed significant difference among sealers (p < 0.001) and root canal thirds (p < 0.001).

Conclusion

The results of the study concluded that BIO-C ION + sealer showed maximum dentinal tubule penetration and AH Plus demonstrated maximum push-out bond strength.

Effect of collagen cross-linking agents on the depth of penetration of bioceramic sealer and release of hydroxyproline: An in vitro study

Context

During endodontic treatment, sealers seal off dentinal tubules and prevent microbial attack. Bioceramic sealers have excellent bioactivity, but its high alkalinity is found to have detrimental effects on radicular collagen. Collagen cross linkers have the ability to chemically modify collagen and can prevent the detrimental effects of the sealer.

Aim

This research was aimed to assess the effect of collagen cross-linking agents on the integrity of radicular collagen matrix and depth of penetration of sealer.

Materials and Methods

Mandibular premolars (n = 48) were taken. Teeth were decoronated; canals were prepared till ProTaper size F2 and were irrigated with 5 mL of 2.5% NaOCl, followed by 3 mL of 17% ethylenediaminetetraacetic acid between instrumentation and finally rinsed with saline following which teeth were divided into three groups based on the surface treatments: Group 1: 6.5% proanthocyanin (PA), Group 2: chlorhexidine (CHX), and Group 3: saline. Teeth were obturated using gutta-percha and bioceramic sealer and stored in artificial saliva. Hydroxyproline (HYP) release was assessed after 14 and 21 days using spectrophotometer. Sealer penetration was assessed using the scanning electron microscope.

Statistical Analysis

Wilcoxon signed-rank test and Kruskal-Wallis test for release of HYP and paired t-test and ANOVA for sealer penetration were performed.

Results

Significantly lower release of HYP was seen in proanthocyanin-treated group. Sealer penetration was better for both the proanthocyanin- and CHX-treated groups when compared to saline.

Conclusion

Surface treatment with collagen cross-linkers caused a decrease in the amount of HYP released, indicating lesser degradation of collagen. Sealer penetration was better due to the removal of smear layer following the surface treatments.

Effect of ultrasonic agitation on marginal adaptation, intratubular penetration and bonding strength of calcium-silicate-based endodontic sealers: A laboratory study

The effect of ultrasonic activation (UA) on marginal adaptation, intratubular penetration and bond strength provided by three calcium silicate-based sealers was evaluated. Ninety-six distobuccal root canals of maxillary molars were randomly divided into 8 groups (n = 12) according to the sealer and UA application: EndoSequence BC sealer (ESBC), Sealer Plus BC (SPBC) and Bio-C Sealer (BCS), using AH Plus (AH) as a control group. The specimens were sectioned at 2, 4 and 6 mm from the apex. The data were statistically analysed using Kruskall-Wallis, Dunn, Mann-Whitney and chi-squared tests. UA improved the marginal adaptation of ESBC (6 mm), SPBC (all levels), BCS (2/4 mm) and AH (4 mm) (p < 0.05); the bond strength of SBPC (2 mm) and BCS (6 mm) were also improved (p < 0.05). The UA of endodontic silicate-based sealers improved the marginal adaptation in all levels and the bond strength of SBPC and BCS sealer.

Calcium Silicate-Based Sealer Dentinal Tubule Penetration-A Systematic Review of In Vitro Studies

The aim of this systematic review was to perform a qualitative synthesis of in vitro studies which evaluate and compare the penetration of calcium silicate-based sealers into dentinal tubules. A systematic advanced search was performed in Scopus, Embase, Medline (via PubMed), Web of Science, and Cochrane databases on the 1 December 2022. In vitro studies that compared the tubular penetration of at least two calcium silicate-based sealers in extracted human teeth were eligible. PRILE 2021 guidelines were used for the assessment of the risk of bias included studies. The search identified a total of 680 preliminary records, among which 12 studies were eligible for review. The most used methodology to evaluate sealer penetration was the use of a fluorochrome together with the tested sealers and the analysis of their penetration under confocal laser microscopy. Regarding the results of the included studies, calcium silicate-based sealers exhibit a favorable dentinal tubule penetration. Tubular penetration, however, can be affected by factors such as the irrigation protocol, sealer activation, the filling method used, and root canal morphology. EndoSequence BC Sealer showed the highest sealer penetration among the tested sealers. The influence of different fluorochromes on the results of dentinal tubule penetration studies should also be further explored. The in vitro nature of the included studies limits the applicability of the results into the clinical setting. Prospero registration: CRD42022383896.

Dislodgment Resistance, Adhesive Pattern, and Dentinal Tubule Penetration of a Novel Experimental Algin Biopolymer-Incorporated Bioceramic-Based Root Canal Sealer

The currently available bioceramic-based sealers still demonstrate low bond strength with a poor seal in root canal despite desirable biological properties. Hence, the present study aimed to determine the dislodgment resistance, adhesive pattern, and dentinal tubule penetration of a novel experimental algin-incorporated bioactive glass 58S calcium silicate-based (Bio-G) sealer and compared it with commercialised bioceramic-based sealers. A total of 112 lower premolars were instrumented to size 30. Four groups (n = 16) were assigned for the dislodgment resistance test: control, gutta-percha + Bio-G, gutta-percha + BioRoot RCS, and gutta-percha + iRoot SP, with exclusion of the control group in adhesive pattern and dentinal tubule penetration tests. Obturation was done, and teeth were placed in an incubator to allow sealer setting. For the dentinal tubule penetration test, sealers were mixed with 0.1% of rhodamine B dye. Subsequently, teeth were cut into a 1 mm-thick cross section at 5 mm and 10 mm levels from the root apex, respectively. Push-out bond strength, adhesive pattern, and dentinal tubule penetration tests were performed. Bio-G showed the highest mean push-out bond strength (p < 0.05), while iRoot SP showed the greatest sealer penetration (p < 0.05). Bio-G demonstrated more favourable adhesive patterns. No significant association was noted between dislodgment resistance and dentinal tubule penetration (p > 0.05).

Evaluation of dentin penetration of three different endodontic sealers in the presence and absence of the smear layer

INTRODUCTION

A sealer's ability to effectively and stably penetrate the dentinal tubules is an essential factor for selecting an effective root canal obturation material. Evaluation of the sealers' penetration into the dentinal tubules provides valuable data in the endodontic treatment outcome.

Effect of the Modified Methacrylate-Based Root Canal Sealer in Single-Cone Technique

This study aimed to modify EndoREZ with 2.5% dimethylaminododecyl methacrylate (DMADDM) and 1% magnetic nanoparticles (MNP) to study its sealing property, penetration and long-term antibacterial and therapeutic effect in the single-cone technique (SCT) compared with EndoREZ and iRoot SP. Thirty single-root human maxillary premolars were assigned into three groups and obturated with three different root canal sealers by SCT. Every specimen was then scanned using micro-CT to analyze void fraction, and void volumes and confocal laser scanning microscope (CLSM) was used to study the dentin penetration. The long-term antimicrobial effects were tested in vitro before and after aging 1 and 4 weeks by the single-strain Enterococcus faecalis biofilm model. In addition, the beagle canine model of apical periodontitis (AP) was utilized to judge and compare the therapeutic effect of three sealers in SCT. The void fraction and void volumes of the modified root canal sealer were not significantly different from iRoot SP (p > 0.05) but were lower than EndoREZ (p < 0.05). The modified root canal sealant displayed a greater penetration, long-term antibacterial property, and treatment effect than the other groups (p < 0.05). This indicated that after being modified with DMADDM and MNP, it showed better performance in SCT.

Intratubular penetration capacity of HiFlow bioceramic sealer used with warm obturation techniques and single cone: A confocal laser scanning microscopic study

Objective

The aim of this paper was to evaluate the intratubular penetration area of a bioceramic sealer, using continuous wave (CW), vertical condensation (VC) with two different types of gutta-percha (conventional (NG) and bioceramic-coated (BG)) and single cone (SC) technique with BG gutta-percha, in different root thirds.

Methods

A total of 150 mature single-root human teeth (including incisors, canines and premolars) were prepared and randomly divided into five groups (n = 30). Teeth were filled using a bioceramic sealer (TotalFill BC Sealer HiFlow ®) and two different types of gutta-percha, with CW and VC techniques, the teeth in the control group were filled with SC technique and BG gutta-percha. The teeth were sectioned and evaluated as one-third portions in each case under a confocal laser microscope. The penetration area measurements were carried out with the Autocad ® programme. Data was analyzed using the one-factor ANOVA test (p < 0.05) and Post Hoc Test (p < 0.05).

Results

The ANOVA Test showed significant differences in the penetration areas of the five obturation techniques (P < 0.05). The Post Hoc Test exhibited significant differences in multiple comparisons (P < 0.05). There was more dentinal tubule penetration in the coronal third than in the apical third in all techniques.

Conclusions

The intratubular penetration of the bioceramic sealer was influenced by the obturation techniques tested, but not by the different gutta-percha tested. There was more penetration of sealer in the warm obturation techniques than the SC, regardless of the type of gutta-percha used.

Evaluation of Bond Strength of Four Different Root Canal Sealers

The purposes of the study were to evaluate the influence of the sealer’s chemical composition on the interfacial strength between root canal dentin and root filling material, for two different classes of endodontic sealers, and to assess their failure modes. Methods: Forty extracted single-rooted teeth were randomly divided into four groups using the following endodontic sealers: RealSeal SE and Resilon (RSSE); EndoSequence BC sealer and BC Point (EBCS); Endoseal MTA and gutta-percha (EDS); Bioroot RCS and gutta-percha (BRS). Teeth were embedded in acrylic resin, and the roots were sectioned horizontally into 1 mm slices. For each slice, the perimeter was measured. A push-out test was performed using an Instron universal testing machine. For each sample, bond strength was calculated. Specimens were examined by SEM investigation in order to analyze the dentin−sealer−core interface. Results were assessed using analysis of variance (ANOVA) and Tukey and Bonferroni test. Results: Statistical analysis revealed that EDS and gutta-percha had significantly higher resistance to dislodgement compared to the other three groups (p < 0.05). EBCS and BC Point showed significantly greater push-out bond strength values compared to RSSE and Resilon (p < 0.05). Conclusions: Bioceramic endodontic sealers showed a higher bond strength to root dentin than methacrylate resin-based endodontic sealer.

Glioma-Targeted Therapeutics: Computer-Aided Drug Design Prospective

Amongst the several types of brain cancers known to humankind, glioma is one of the most severe and life-threatening types of cancer, comprising 40% of all primary brain tumors. Recent reports have shown the incident rate of gliomas to be 6 per 100,000 individuals per year globally. Despite the various therapeutics used in the treatment of glioma, patient survival rate remains at a median of 15 months after undergoing first-line treatment including surgery, radiation, and chemotherapy with Temozolomide. As such, the discovery of newer and more effective therapeutic agents is imperative for patient survival rate. The advent of computer-aided drug design in the development of drug discovery has emerged as a powerful means to ascertain potential hit compounds with distinctively high therapeutic effectiveness against glioma. This review encompasses the recent advances of bio-computational in-silico modeling that have elicited the discovery of small molecule inhibitors and/or drugs against various therapeutic targets in glioma. The relevant information provided in this report will assist researchers, especially in the drug design domains, to develop more effective therapeutics against this global disease.

Web-Based Quantitative Structure-Activity Relationship Resources Facilitate Effective Drug Discovery

Traditional drug discovery effectively contributes to the treatment of many diseases but is limited by high costs and long cycles. Quantitative structure-activity relationship (QSAR) methods were introduced to evaluate the activity of compounds virtually, which saves the significant cost of determining the activities of the compounds experimentally. Over the past two decades, many web tools for QSAR modeling with various features have been developed to facilitate the usage of QSAR methods. These web tools significantly reduce the difficulty of using QSAR and indirectly promote drug discovery. However, there are few comprehensive summaries of these QSAR tools, and researchers may have difficulty determining which tool to use. Hence, we systematically surveyed the mainstream web tools for QSAR modeling. This work may guide researchers in choosing appropriate web tools for developing QSAR models, and may also help develop more bioinformatics tools based on these existing resources. For nonprofessionals, we also hope to make more people aware of QSAR methods and expand their use.

Dentinal Tubule Penetration and Adaptation of Bio-C Sealer and AH-Plus: A Comparative SEM Evaluation

OBJECTIVE

The aim of this study was to compare and evaluate the dentinal tubule penetration and adaptation of a premixed bioceramic sealer and an epoxy-resin based sealer in the three radicular thirds.

METHODS

30 wide roots, with single straight canals and totally formed apexes, were endodontically prepared and divided into two groups (n=14) according to the sealer used for root canal filling: AH-Plus (AHP) and Bio-C Sealer (BIOC). Two samples were left as controls. After the canals were filled, the samples were cut and viewed under Scanning Electron Microscopy by taking images to analyse the tubular penetration and adaptation of the sealers. The results were statistically analysed with the Shapiro Wilk, Levene and Mann-Whitney tests (P<0.05).

RESULTS

BIOC showed significantly higher penetration in dentinal tubules than AHP in the cervical, middle and apical thirds of the root canal (P<0.05) and better adaptation to the dentinal tubule walls.

CONCLUSION

Under the parameters of this study, BIOC exhibits higher penetration and better adaptation to the dentinal tubules compared to AHP.

A comparative study of dentinal tubule penetration and the retreatability of EndoSequence BC Sealer HiFlow, iRoot SP, and AH Plus with different obturation techniques

Objectives

This study aimed to evaluate dentinal tubule penetration and the retreatability of EndoSequence BC Sealer HiFlow (HiFlow), iRoot SP, and AH Plus when using the single-cone (SC) or continuous wave condensation (CWC) technique.

Materials and methods

Sixty-five single-rooted teeth were instrumented and randomly divided into 5 groups: group 1, AH Plus/CWC; group 2, iRoot SP/CWC; group 3, iRoot SP/SC; group 4, HiFlow/CWC; and group 5, HiFlow/SC. The ability to re-establish patency during endodontic retreatment was recorded, as was the time taken to reach the working length. Dentinal tubule penetration and remaining debris after retreatment were evaluated by confocal microscopy and scanning electron microscopy. Data were analyzed by Kruskal-Wallis test and Dunn’s multiple comparisons test (α = 0.05).

Results

The HiFlow/CWC and iRoot SP/CWC groups required more time to reach the working length than groups that underwent the SC technique regardless of the sealer used (P < .05). The HiFlow/CWC group showed a significantly higher percentage of sealer penetration area than that of the iRoot SP/SC at 4 mm from the apex (P < .05) and penetrated deeper into dentinal tubules than iRoot SP/SC at both 8-mm and 12-mm levels (P < .05). Moreover, the HiFlow/CWC and HiFlow/SC groups demonstrated less remaining sealer along the canal wall than AH Plus/CWC group at 4-mm level (P < .05).

Conclusions

HiFlow/CWC technique showed better performance in dentinal tubule penetration than that of iRoot SP/SC. Both HiFlow and iRoot SP combined with CWC technique groups required more retreatment time than the other groups. Furthermore, using HiFlow with either the CWC or SC technique left less remaining sealer at 4-mm level than using AH Plus with the CWC technique during retreatment.

Clinical relevance

With favorable performance in dentinal tubule penetration and retreatability in endodontic retreatment, the combined use of EndoSequence BC Sealer HiFlow with the recommended continuous wave condensation technique may be a worthwhile choice in root canal treatment.

Comparison of warm vertical compaction and cold lateral condensation of α, β gutta-percha and resilon on apically extruded debris during retreatment

Background

This study was performed to evaluate the amount of apically extruded debris removed from a root canal filled with cold lateral condensation (CLC), and warm vertical compaction (WVC) techniques, using b or a phase gutta-percha with AH-Plus (Dentsply DeTrey, Konstanz, Germany) or Resilon (Resilon Research LLC, Madison, WI) with RealSeal SE (SybronEndo, Amersfoort, The Netherlands).

Materials and Methods

About 100 human incisor teeth were prepared with a #25.06 NiTi rotary system and divided into five groups according to the filling material used: Group 1: CLC (gutta-percha, AH-Plus); Group 2: WVC (b phase gutta-percha, AH-Plus); Group 3: WVC (a phase gutta-percha, AH-Plus); Group 4: CLC (Resilon, RealSeal SE); and Group 5: WVC (Resilon, RealSeal SE). Extruded debris during the retreatment procedure was collected in preweighed Eppendorf tubes. The times required for retreatment were recorded.

Results

The amount of debris extrusion was significantly greater with WVC than CLC in the gutta-percha and Resilon groups (P < 0.001). Using a phase gutta-percha resulted in significantly more debris extrusion than b phase gutta-percha (P < 0.001). In the WVC groups, Resilon caused significantly more debris extrusion than gutta-percha (P < 0.05). Retreatment was faster for CLC than WVC (P < 0.05).

Conclusions

In the retreatment procedure, the amount of apically extruded debris and retreatment duration were dependent on the type of obturation material and technique used.

Effect of ultrasonic activation on dentinal tubule penetration of calcium silicate-based cements

This study investigated the dentinal tubule penetration of mineral trioxide aggregate (MTA), NeoMTA Plus and Biodentine placed by either manual condensation or ultrasonic activation in simulated open apex model. Standardized divergent open apex models were created using palatal roots of 60 human maxillary molars and divided into six groups according to the used cements and activation methods (n = 10): MTA-manual condensation, MTA-ultrasonic activation, NeoMTA Plus-manual condensation, NeoMTA Plus-ultrasonic activation, Biodentine-manual condensation, Biodentine-ultrasonic activation. For the measurement of penetration, the cements were mixed with 0.1% Rhodamin B and 6-mm apical portions of each root canal were obturated in an orthograde direction. The roots were embedded into acrylic blocks, and 1-mm-thick sections were obtained at 3 mm from the apex. Specimens were mounted onto glass slides and scanned under a confocal laser scanning microscope (CLSM) and stereomicroscope. Dentinal tubule penetration areas, depth and percentage were measured using LSM and ImageJ software. The data were analyzed using two-way analysis of variance (anova) with Bonferroni correction (α = 0.05). No correlation was found between stereomicroscope and CLSM analyses (p > .05). CLSM analysis showed no significant differences between MTA, NeoMTA Plus, and Biodentine groups when manual condensation was used (p > .05). Ultrasonic activation did not increase the tubular penetration of MTA, NeoMTA Plus or Biodentine as compared to manual condensation of each material (p > .05). MTA, NeoMTA Plus and Biodentine showed similar tubular penetration when manual condensation was used. Ultrasonic activation of these cements had no effect on tubular penetration of each material as compared to the manual condensation counterparts.