Solvent-Free Method for the Copolymerization of Labile Sugar-Derived Building Blocks into Polyamides

This research focuses on the preparation of biobased copolyamides containing biacetalized galactaric acid (GalX), namely, 2,3:4,5-di-O-isopropylidene-galactaric acid (GalXMe) and 2,3:4,5-di-O-methylene-galactaric acid (GalXH), in bulk by melt polycondensation of salt monomers. In order to allow the incorporation of temperature-sensitive sugar-derived building blocks into copolyamides at temperatures below the degradation temperature of the monomers and below their melting temperatures, a clever selection of salt monomers is required, such that the sugar-derived salt monomer dissolves in the other salt monomers. The polymerization was investigated by temperature dependent FT-IR and optical microscopy. The structure of the obtained copolyamides was elucidated by NMR and matrix-assisted laser desorption ionization-time-of-flight (MALDI-TOF) techniques. The positive outcome of this modified polycondensation method depends on the solubility of sugar-derived polyamide salts in polyamide salts of comonomers and the difference between their melting temperatures, however does not depend on the melting temperature of the used sugar-derived monomer. A variety of comonomers was screened in order to establish the underlying mechanisms of the process.

Poly(ether urethane)s incorporating long alkyl side-chains with terminal carboxyl groups as fatty acid mimics: synthesis, structural characterization and protein adsorption

The object of this work was to produce polyurethanes with greater affinity for albumin (Alb) and improved hemocompatibility by introduction of carboxyl-terminated alkyl side-chains that better mimic fatty acids, in contrast to methyl terminated alkyl side-chains used previously. Synthesis of poly(ether urethane)s (PEUs) with long alkyl side-chains via a multi-step solution addition polymerization is described. The synthesis is based upon the polymerization of a diisocyanate pre-polymer with various chain extenders and reaction with Br-terminated compound in the final stage. The side-chains had terminal methyl or carboxylic groups, and were attached either directly to the polymer backbone or to an oligo(ethylene glycol) spacer. The bulk structure of the PEUs was confirmed by 1H-NMR and the surface polymer structure was characterized by ToF-SIMS. The influence of the incorporated C16-alkyl, C16-carboxyalkyl and oxyethylene-C16-carboxyalkyl side-chains attached to the polymer backbone on fibrinogen (Fg) and Alb adsorption from blood plasma, and Fg adsorption from buffer solutions and binary mixtures with Alb was measured. Incorporation of C16-alkyl or C16-carboxyalkyl side-chains into PEUs caused relatively small changes in Fg and Alb adsorption. PEUs with oxyethylene-C16-carboxyalkyl side-chains exhibited the lowest Fg adsorption and the highest Alb adsorption among all the tested polymers.