Reduction of Tribocorrosion Products When Using the Platform-Switching Concept

Fretting-corrosion at the Implant-Abutment Interface Simulating Clinically Relevant Conditions

OBJECTIVE

Implant treatment is provided to individuals with normal, idealized masticatory forces and also to patients with parafunctional habits such as grinding, clenching, and bruxing. Dental erosion is a common increasing condition and is reported to affect 32 % of adults, increasing with age. This oral environment is conducive to tribocorrosion and the potential loss of materials from the implant surfaces and interfaces with prosthetic components. Although several fretting-corrosion studies have been reported, until now, no study has simulated clinically relevant micromotion. Therefore, our aim is to investigate fretting-corrosion using our new micro-fretting corrosion system, simulating clinical conditions with 5 µm motion at the implant-abutment interface under various occlusal loads and acidic exposures.

METHODS

We simulated four conditions in an oral environment by varying the contact load (83 N and 233 N) and pH levels (3 and 6.5). The commonly used dental implant material, Grade IV titanium, and abutment material Zirconia (ZrO2)/ Grade IV titanium were selected as testing couple materials. Artificial saliva was employed to represent an oral environment. In addition, a standard tribocorrosion protocol was followed, and the pin was controlled to oscillate on the disk with an amplitude of 5 μm during the mastication stage. After the testing, 3D profilometry and scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) were utilized to analyze the worn surfaces. Inductively coupled plasma mass spectrometry (ICP-MS) was also used to measure the metal ion release.

RESULTS

Energy ratios were below 0.2, indicating a fretting regime of partial slip for all groups. Open-circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) were analyzed to compare the electrochemical behavior among groups. As a result, corrosive damage was observed to be more in the Ti4- Ti4 groups than in Zr-Ti4 ones, whereas more mechanical damage was found in the Zr-Ti4 groups than in the Ti4-Ti4 groups. Possible mechanisms were proposed in the discussion to explain these findings.

SIGNIFICANCE

The results observed from this study might be helpful to clinicians with implant selection. For example, for patients with bruxism, a titanium implant paired with a titanium abutment may be preferable, while patients with GERD may benefit more from a titanium implant paired with a zirconia abutment.

Emerging factors affecting peri-implant bone metabolism

Implant dentistry has evolved to the point that standard implant osseointegration is predictable. This is attributed in part to the advancements in material sciences that have led toward improvements in implant surface technology and characteristics. Nonetheless, there remain several cases where implant therapy fails (specifically at early time points), most commonly attributed to factors affecting bone metabolism. Among these patients, smokers are known to have impaired bone metabolism and thus be subject to higher risks of early implant failure and/or late complications related to the stability of the peri-implant bone and mucosal tissues. Notably, however, emerging data have unveiled other critical factors affecting osseointegration, namely, those related to the metabolism of bone tissues. The aim of this review is to shed light on the effects of implant-related factors, like implant surface or titanium particle release; surgical-related factors, like osseodensification or implanted biomaterials; various drugs, like selective serotonin reuptake inhibitors, proton pump inhibitors, anti-hypertensives, nonsteroidal anti-inflammatory medication, and statins, and host-related factors, like smoking, diet, and metabolic syndrome on bone metabolism, and aseptic peri-implant bone loss. Despite the infectious nature of peri-implant biological complications, these factors must be surveyed for the effective prevention and management of peri-implantitis.

Inflammatory Gene Profile and Particle Presence in Peri-Implant Mucosa: a Pilot Study on 9 Patients

Objectives

The purpose of this pilot study is to compare gene expression in mucosa around dental implants with zirconia abutment to titanium and investigate presence of particles in mucosa samples and on implant heads.

Material and Methods

Ten patients with a single implant supported prosthesis connected to zirconia or titanium abutments were invited at the five-year control. A clinical examination and a survey on experience of function and appearance were conducted. A mucosa biopsy taken in close vicinity to the implant were analysed by real-time polymerase chain reaction (qPCR) and presence of particles in a scanning electron microscope/energy-dispersive X-ray spectroscope (SEM/EDX). Cytological smear samples were collected and analysed through inductively coupled plasma mass spectrometry (ICP-MS) to investigate presence of particles on implant heads.

Results

In total, 9 patients participated in the study, five with titanium abutments and four with zirconia abutments. All patients were satisfied with function and aesthetics. Titanium and iron particles were detected in mucosa biopsies. The ICP - MS analysis demonstrated presence of zirconia and titanium. Several proinflammatory genes were upregulated in the zirconia abutment group.

Conclusions

Around zirconia abutments a slight increase in proinflammatory response and amount of wear particles was seen as compared to titanium. Wear particles of titanium were present in all soft tissue samples, however zirconia particles only in the samples from implants heads/mucosa with zirconia abutments.

The Progress in Tribocorrosion Research (2010-21): Focused on the Orthopedics and Dental Implants

Tribocorrosion is an integration of two areas-tribology and corrosion. It can be defined as the material degradation caused by the combined effect of corrosion and tribological process at the material interfaces. Significant development has occurred in the field of tribocorrosion over the past years. This development is due to its applications in various fields, such as aerospace, marine, biomedical, and space. Focusing on biomedical applications, tribocorrosion finds its applications in the implants used in cardiovascular, spine, orthopedics, trauma, and dental areas. It was reported that around 7.2 million Americans are living with joint implants. Implant surgery is a traumatic and expensive procedure. Tribocorrosion can affect the lifespan of the implants, thus leading to implant failure and a potential cause of revision surgery. Hence, it is essential to understand how tribocorrosion works, its interaction with the implants, and what procedures can be implemented to protect materials from tribocorrosion. This paper discusses how tribocorrosion research has evolved over the past 11 years (2010-2021). This is a comprehensive overview of tribocorrosion research in biomedical applications.

Effect of Titanium and Zirconia Nanoparticles on Human Gingival Mesenchymal Stromal Cells

Nano- and microparticles are currently being discussed as potential risk factors for peri-implant disease. In the present study, we compared the responses of human gingival mesenchymal stromal cells (hG-MSCs) on titanium and zirconia nanoparticles (<100 nm) in the absence and presence of Porphyromonas gingivalis lipopolysaccharide (LPS). The primary hG-MSCs were treated with titanium and zirconia nanoparticles in concentrations up to 2.000 µg/mL for 24 h, 72 h, and 168 h. Additionally, the cells were treated with different nanoparticles (25−100 µg/mL) in the presence of P. gingivalis LPS for 24 h. The cell proliferation and viability assay and live−dead and focal adhesion stainings were performed, and the expression levels of interleukin (IL)-6, IL-8, and monocyte chemoattractant protein (MCP)-1 were measured. The cell proliferation and viability were inhibited by the titanium (>1000 µg/mL) but not the zirconia nanoparticles, which was accompanied by enhanced apoptosis. Both types of nanoparticles (>25 µg/mL) induced the significant expression of IL-8 in gingival MSCs, and a slightly higher effect was observed for titanium nanoparticles. Both nanoparticles substantially enhanced the P. gingivalis LPS-induced IL-8 production; a higher effect was observed for zirconia nanoparticles. The production of inflammatory mediators by hG-MSCs is affected by the nanoparticles. This effect depends on the nanoparticle material and the presence of inflammatory stimuli.

Calprotectin and N-telopeptide of Type I Collagen (NTx) as Gingival Crevicular Fluid (GCF) Biomarker in Peri-Implantitis Patients

Introduction: Formulation of various preventive and therapeutic strategies is possible only by a better understanding of the immune-inflammatory profile of peri-implant diseases. For understanding the changes and turnover of bone, various markers have been used in the past literature, out of which, N-telopeptide of Type I Collagen (NTx) is acknowledged to be the most reliable marker.

Aims and objectives: Assessment of calprotectin and NTx concentration in gingival crevicular fluid (GCF) around the implant sites in subjects suffering from peri-implantitis.

Materials and methods: In total, 70 healthy individuals were included in the present study. These patients had opted for dental implants within the last decade. After collecting the peri-implant crevicular fluid (PICF) and GCF, various examinations were carried out. PICF samples were obtained with the help of sterile paper available in the form of strips. The enzyme-linked immunosorbent assay (ELISA) technique was used for measuring the calprotectin and NTx. All the readings were obtained in nanograms per microliter of PICF. All the results were recorded and analyzed.

Results: The overall mean calprotectin and NTx values were observed to be in a significantly higher range within the sites suffering from peri-implantitis when compared with healthy locations. The calprotectin values and NTx levels were positively correlated with the mean values of periodontal parameters observed clinically.

Conclusion: Both calprotectin and NTx could be used as a biomarker signifying the presence of inflammation as well as bone resorption in patients suffering from peri-implantitis.

Postsurgical Pain and Implant Osseointegration Failure: A Case Control Study

Aim. The relationship between postsurgical pain and osseointegration was evaluated and analyzed in this study. Material and method. 27 patients, ranging in age from 35 to 72 years old, 12 males and 15 females, who received dental implants and failed to achieve osseointegration from Tianjin Medical University Second Hospital, were analyzed and studied in the following aspects: bone density, initial torque, one- or two-stage surgery, postsurgical pain, postsurgical swelling, and radiographic evidence of osseointegration failure. Result. 5 patients were assessed to be D4 bone density and 7 cases were assessed to be D3 bone density, 2 patients were assessed to be D2 bone density and 13 patients were assessed to be D1 bone density. All cases were documented with clinically acceptable initial torque. Among the 27 cases, 2 of them were one-stage nonsubmerged surgery and 25 cases were two-stage submerged surgery. 25 out of 27 patients reported moderate to severe pain lasting for more than 72 hours. Radiologic examinations failed to offer any indication of poor osseointegration in the 7-day postsurgical follow-up. Conclusion. Moderate to severe postsurgical pain lasting more than 72 hours displays high odd ratio of poor osseointegrate. The radiological examinations alone failed to offer any valuable evidence for the early detection of osseointegration failure in this study.

Comparison of Corrosion Products From Implant and Various Gold-Based Abutment Couplings: The Effect of Gold Plating

This study compared titanium (Ti), palladium (Pd), platinum (Pt), and gold (Au) ion release following induced accelerated tribocorrosion from three Au alloy abutment groups coupled with Ti implants over time; investigated contacting surface structural changes; and explored the effect of Au plating. Three abutment groups, G (n = 8, GoldAdapt, Nobel Biocare), N (n = 8, cast UCLA, Biomet3i), and P (n = 8, cast UCLA, Biomet3i, Au plated), coupled with implants (Nobel Biocare), immersed in 1% lactic acid, were cyclically loaded. Ions released (ppb) at T1, T2, and T3, simulating 3, 5, and 12 months of function, respectively, were quantified by inductively coupled plasma mass spectrometry (ICP-MS) and compared. Surface degradation and fretted particle composition after T3 were evaluated with scanning electron microscopy and energy-dispersive X-ray spectroscopy (SEM/EDX). ICP-MS data were nonparametric, expressed as medians and interquartile ranges. SEM/EDX showed pitting, crevice corrosion, and fretted particles on the components. Released ion concentrations in all groups across time significantly decreased for Pd (P < .001, median range: 1.70-0.09), Pt (P = .021, 0.55-0.00), and Au (P < .001, 1.01-0.00) and increased for Ti (P = .018, 2.49-5.84). Total Ti release was greater than other ions combined for G (P = .012, 9.86-2.30) and N (P < .001, 13.59-5.70) but not for P (P = .141, 8.21-3.53). Total Ti release did not differ between groups (P = .36) but was less variable across group P. On average, total ion release was 13.77 ppb (interquartile range 8.91-26.03 ppb) across the 12-month simulation. Tribocorrosion of Ti implants coupled with Au abutments in a simulated environment was evidenced by fretted particles, pitting, and crevice corrosion of the coupling surfaces and release of ions. More Ti was released compared with Pd, Pt, and Au and continued to increase with time. Abutment composition influenced ion release. Au-plated abutments appeared to subdue variation in and minimize high-concentration spikes of titanium.

The unfavorable role of titanium particles released from dental implants

Titanium is considered to be a metal material with the best biological safety. Studies have proved that the titanium implanted in the bone continuously releases titanium particles (Ti particles), significantly increasing the total titanium content in human body. Generally, Ti particles are released slowly without causing a systemic immune response. However, the continuous increased local concentration may result in damage to the intraepithelial homeostasis, aggravation of inflammatory reaction in the surrounding tissues, bone resorption and implant detachment. They also migrate with blood flow and aggregate in the distal organ. The release of Ti particles is affected by the score of the implant surface structure, microenvironment wear and corrosion, medical operation wear, and so on, but the specific mechanism is not clear. Thus, it difficult to prevent the release completely. This paper reviews the causes of the Ti particles formation, the damage to the surrounding tissue, and its mechanism, in particular, methods for reducing the release and toxicity of the Ti particles.

Biomarkers associated with periodontitis and peri-implantitis: a systematic review

Purpose

The pathology of peri-implantitis is still not fully understood and there have been recent challenges to the consensus on its aetiology and pathology, especially in comparison with periodontitis. The assessment of biomarkers allows a comparison of the pathology of these diseases. The aim of this systematic review was to answer the research question: “Is there a difference in the biomarkers associated with peri-implantitis compared with periodontitis in adult humans?”

Methods

Electronic databases were searched and screened, and a manual search was also undertaken. The inclusion criteria were adults with peri-implantitis who had been compared to adults with periodontitis with the outcome of biomarkers assessed via biopsies or crevicular fluid samples in primary or secondary care settings, as recorded in case-control, case series and retrospective, prospective and cross-sectional observational studies. Two reviewers independently screened titles and abstracts and assessed full text articles for eligibility and inclusion. Both reviewers independently extracted data and assessed risk of bias. Differences in biomarker levels were the primary outcome and a narrative review was undertaken due to the heterogeneity of studies.

Results

In total, 2,374 articles were identified in the search, of which 111 full-text articles were assessed for eligibility and 13 were included in the qualitative synthesis. Five of the 13 included studies were deemed to be at high risk of bias, with the others having moderate risk. All studies were cross-sectional and performed at university hospitals. Nine of the 13 included studies found significant differences in the levels of biomarkers or their ratios between peri-implantitis and periodontitis. Four of the studies found no significant differences.

Conclusions

Within the limitations of the included studies, it appears that there may be a difference in biomarker levels and ratios between peri-implantitis and periodontitis, suggesting that these disease processes are somewhat distinct.

Breaking the wave of peri-implantitis

Peri-implant diseases are prevalent with a weighted mean prevalence rate of 43% across Europe and 22% across South and North America. Although the main etiologic agent is bacterial biofilm, a myriad of factors influence the initiation and progression of the disease. Unfortunately, the treatment of peri-implant diseases is at best favorable in the short term with a high rate of persistent inflammation and recurrence. Therefore, it is sensible to consider and control all potential factors that may predispose an implant to peri-implant tissue inflammation in an attempt to avoid the disease. This paper reviews recent evidence on factors that may predispose implants to peri-implantitis and measures that can be taken to prevent it.

A Comprehensive Review on the Corrosion Pathways of Titanium Dental Implants and Their Biological Adverse Effects

The main aim of this work was to perform a comprehensive review of findings reported by previous studies on the corrosion of titanium dental implants and consequent clinical detrimental effects to the patients. Most studies were performed by in vitro electrochemical tests and complemented with microscopic techniques to evaluate the corrosion behavior of the protective passive oxide film layer, namely TiO2. Results revealed that bacterial accumulation, dietary, inflammation, infection, and therapeutic solutions decrease the pH of the oral environment leading to the corrosion of titanium. Some therapeutic products used as mouthwash negatively affect the corrosion behavior of the titanium oxide film and promote changes on the implant surface. In addition, toothpaste and bleaching agents, can amplify the chemical reactivity of titanium since fluor ions interacting with the titanium oxide film. Furthermore, the number of in vivo studies is limited although corrosion signs have been found in retrieved implants. Histological evaluation revealed titanium macro- and micro-scale particles on the peri-implant tissues. As a consequence, progressive damage of the dental implants and the evolution of inflammatory reactions depend on the size, chemical composition, and concentration of submicron- and nanoparticles in the surrounding tissues and internalized by the cells. In fact, the damage of the implant surfaces results in the loss of material that compromises the implant surfaces, implant-abutment connections, and the interaction with soft tissues. The corrosion can be an initial trigger point for the development of biological or mechanical failures in dental implants.