Developing Bioactive Dental Resins for Restorative Dentistry

Physicochemical characterization of experimental resin-based materials containing calcium orthophosphates or calcium silicate

OBJECTIVE

To evaluate experimental dimethacrylate-based materials containing calcium orthophosphates or calcium silicate particles in terms of their optical, mechanical and Ca2+ release behaviour.

METHODS

Dicalcium phosphate dihydrate (DCPD), hydroxyapatite (HAp), beta-tricalcium phosphate (β-TCP) or calcium silicate (CaSi) particles were added to a photocurable BisGMA/TEGDMA resin (1:1 in mols) at a 30 vol% fraction. Materials containing silanized or non-silanized barium glass particles were used as controls. Degree of conversion (DC) at the top and base of 2-mm thick specimens was determined by ATR-FTIR spectroscopy (n = 5). Translucency parameter (TP) and transmittance (%T) were determined using a spectrophotometer (n = 3). Biaxial flexural strength (BFS) and flexural modulus (FM) were determined by biaxial flexural testing after 24 h storage in water (n = 10). Ca2+ release in water was determined during 28 days by inductively coupled plasma optical emission spectrometry (n = 3). Statistical analysis was performed using ANOVA/Tukey test (DC: two-way; TP, %T; BFS and FM: one-way; Ca2+ release: repeated measures two-way, α = 5 %).

RESULTS

CaSi and β-TCP particles drastically reduced DC at 2 mm, TP and %T (p < 0.001). Compared to both controls, all Ca2+-releasing materials presented lower BFS (p < 0.001) and only the material with DCPD showed significantly lower FM (p < 0.05). The material containing CaSi presented the highest Ca2+ release, while among materials formulated with calcium orthophosphates the use of DCPD resulted in the highest release (p < 0.001).

SIGNIFICANCE

CaSi particles allowed the highest Ca2+ release. Notwithstanding, the use of DCPD resulted in a material with the best compromise between optical behaviour, DC, strength and Ca2+ release.

Ion release mechanisms in composites containing CaP particles and hydrophilic monomers

OBJECTIVE

To investigate the effect of hydrophilic/permeable polymer matrices on water sorption/solubility (WS/SL), Ca2+ release, mechanical properties and hydrolytic degradation of composites containing dicalcium phosphate dihydrate (DCPD) particles.

METHODS

Six composites were tested, all with 10 vol% of glass particles and either 30 vol% or 40 vol% DCPD. Composites containing 1BisGMA:1TEGDMA in mols (at both inorganic levels) were considered controls. Four materials were formulated where 0.25 or 0.5 of the BisGMA/TEGDMA was replaced by pyromellitic dianhydride glycerol dimethacrylate (PMGDM)/ polyethylene glycol dimethacrylate (PEGDMA). Composites were tested for degree of conversion (FTIR spectroscopy), WS/SL (ISO 4049) and Ca2+ release (inductively coupled plasma optical emission spectroscopy). Fracture toughness (FT) and biaxial flexural strength/modulus (BFS/FM) were determined after 24 h and 60 days in water. The contributions of diffusional and relaxational mechanisms to Ca2+ release kinetics were analyzed using the semi-empirical Salim-Peppas model. Data were analysed by ANOVA/Tukey test (alpha: 0.05).

RESULTS

WS/SL was higher for composites containing PMGDM/PEGDMA compared to the controls (p < 0.001). Only at 40% DCPD the 0.5 PMGDM/PEGDMA composite showed statistically higher Ca2+ release than the control. Relaxation diffusion was the main release mechanism. Initial FT was not negatively affected by matrix composition. BFS (both DCPD fractions) and FM (30% DCPD) were lower for composites with hydrophilic/permeable networks (p < 0.01). After 60 days in water, composites with PMGDM/PEGDMA presented significant reductions in FT, while all composites had reductions in BFS/FM.

SIGNIFICANCE

Increasing matrix hydrophilicity/permeability significantly increased Ca2+ release only at a high DCPD fraction.

Engineering Interfacial Integrity with Hydrolytic-Resistant, Self-Reinforcing Dentin Adhesive

The leading cause of composite restoration failure is secondary caries, and although caries is a multifactorial problem, weak, damage-prone adhesives play a pivotal role in the high susceptibility of composite restorations to secondary caries. Our group has developed synthetic resins that capitalize on free-radical polymerization and sol-gel reactions to provide dental adhesives with enhanced properties. The resins contain γ-methacryloxypropyltrimethoxysilane (MPS) as the Si-based compound. This study investigated the properties of methacrylate-based resins containing methacryloxymethyltrimethoxysilane (MMeS) as a short-chain alternative. The degree of conversion (DC), polymerization kinetics, water sorption, mechanical properties, and leachates of MMeS- and MPS-resins with 55 and 30 wt% BisGMA-crosslinker were determined. The formulations were used as model adhesives, and the adhesive/dentin (a/d) interfaces were analyzed using chemometrics-assisted micro-Raman spectroscopy. The properties of the 55 wt% formulations were comparable. In the 30 wt% BisGMA formulations, the MMeS-resin exhibited faster polymerization, lower DC, reduced leachates, and increased storage and loss moduli, glass transition (Tg), crosslink density, and heterogeneity. The spectroscopic results indicated a comparable spatial distribution of resin, mineralized, and demineralized dentin across the a/d interfaces. The hydrolytically stable experimental short-chain-silane-monomer dental adhesive provides enhanced mechanical properties through autonomous strengthening and offers a promising strategy for the development of restorative dental materials with extended service life.

A Historical Perspective on Dental Composite Restorative Materials

This review article will discuss the origin of resin-based dental composite materials and their adoption as potentially useful adjuncts to the primary material used by most dentists for direct restorations. The evolution of the materials, largely driven by the industry's response to the needs of dentists, has produced materials that are esthetic, strong, and versatile enough to be used in most areas of the oral cavity to replace or restore missing tooth structures. Significant advancements, such as the transition from chemical to light-curing materials, refinements in reinforcing particles to produce optimum polishing and wear resistance, formulating pastes with altered viscosities to create highly flowable and highly stiff materials, and creating materials with enhanced depth of cure to facilitate placement, will be highlighted. Future advancements will likely reflect the movement away from simply being a biocompatible material to one that is designed to produce some type of beneficial effect upon interaction within the oral environment. These new materials have been called "bioactive" by virtue of their potential effects on bacterial biofilms and their ability to promote mineralization of adjacent tooth structures.

A Review on the Current State of Microcapsule-Based Self-Healing Dental Composites

Resin-based dental composites, commonly used in dentistry, offer several advantages including minimally invasive application, esthetically pleasing appearance, and good physical and mechanical properties. However, these dental composites can be susceptible to microcracks due to various factors in the complex oral environment. These microcracks can potentially lead to clinical restoration failure. Conventional materials and methods are inadequate for detecting and repairing these microcracks in situ. Consequently, incorporating self-healing properties into dental composites has become a necessity. Recent years have witnessed rapid advancements in self-healing polymer materials, drawing inspiration from biological bionics. Microcapsule-based self-healing dental composites (SHDCs) represent some of the most prevalent types of self-healing materials utilized in this domain. In this article, we undertake a comprehensive review of the most recent literature, highlighting key insights and findings related to microcapsule-based SHDCs. Our discussion centers particularly on the preparation techniques, application methods, and the promising future of self-healing microcapsules in the field of dentistry.

Special Issue "Recent Process Design and Development Strategies for Dental Materials"

The field of dental materials is rapidly evolving, and this Special Issue of the International Journal of Molecular Sciences offers a comprehensive examination of the latest advancements in process design and development strategies [...].

Composite Containing Calcium Phosphate Particles Functionalized with 10-MDP

The phosphate ester monomer 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP) is capable of bonding to hydroxyapatite and, for this reason, is a key component of several self-etch adhesives. In this study, dicalcium phosphate dihydrate particles (DCPD; CaHPO4.2H2O) were functionalized with 10-MDP and used to formulate an experimental composite with 50 vol% inorganic content (3:1 DCPD:silanated barium glass ratio) dispersed in a BisGMA/TEGDMA matrix. The tested hypothesis was that DCPD functionalization would improve the composite's mechanical performance without compromising Ca2+ release. Composites containing nonfunctionalized DCPD or only reinforcing glass (in both cases, with or without 10-MDP mixed in the resin phase) were used as controls. Materials were tested for degree of conversion (DC; by Fourier transform infrared spectroscopy), water sorption (WS) and solubility (SL; according to ISO 4049), biaxial flexural strength (BFS)/modulus (FM) after 24 h and 5 mo in water, and 28-d Ca2+ release in water (by plasma-coupled optical emission spectroscopy). Data were analyzed using analysis of variance/Tukey test (alpha: 5%). DCPD functionalization did not interfere with DC. The composite containing functionalized DCPD showed significantly lower WS and SL in comparison with the material formulated with nonfunctionalized particles. The presence of 10-MDP (as a functionalizing agent or dispersed in the resin phase) reduced the composite's initial BFS and FM. After 5 mo in water, the composite with functionalized DCPD and both glass-only composites were able to maintain their mechanical properties at levels statistically similar to what was observed after 24 h. Ca2+ release was significantly reduced in both formulations containing 10-MDP. In conclusion, DCPD functionalization with 10-MDP increased the composite's resistance to hydrolytic degradation, improving its mechanical stability after prolonged water storage. However, the impaired water transit at the particle-matrix interface led to a reduction in Ca2+ release.

Development of Antibacterial Resin Composites Incorporating Poly(METAC) Clusters

This study examined the antibacterial effects and physical properties of a novel resin composite incorporating poly[{2-(methacryloyloxy)ethyl}trimethylammonium chloride] (poly(METAC)), a methacrylate cationic polymer comprising quaternary ammonium compounds (QACs). Resin composites incorporating poly(METAC) were fabricated by adding 6 wt.% METAC aqueous solution to a commercially available resin composite. The FE-SEM/EDS and Raman spec-troscopy analyses showed that METAC was assembled and polymerized in the resin composites after curing. The antibacterial effect was evaluated by inoculating Streptococcus mutans or Strepto-coccus sobrinus suspensions on the surface of cured resin composites, and the experimental resin composites incorporating poly(METAC) clusters exhibited bactericidal effects even after 28 days of ageing. The physical properties of the experimental resin composites were within the ISO-stipulated ranges. Newly fabricated resin composites containing the QAC-based poly(METAC) cluster ex-hibited long-term bactericidal effects against oral bacteria on their surfaces and demonstrated ac-ceptable physical properties for clinical use.

Multifunctional Dental Adhesives Formulated with Silane-Coated Magnetic Fe3O4@m-SiO2 Core-Shell Particles to Counteract Adhesive Interfacial Breakdown

The process of bonding to dentin is complex and dynamic, greatly impacting the longevity of dental restorations. The tooth/dental material interface is degraded by bacterial acids, matrix metalloproteinases (MMPs), and hydrolysis. As a result, bonded dental restorations face reduced longevity due to adhesive interfacial breakdown, leading to leakage, tooth pain, recurrent caries, and costly restoration replacements. To address this issue, we synthesized and characterized a multifunctional magnetic platform, CHX@SiQuac@Fe3O4@m-SiO2, to provide several beneficial functions. The platform comprises Fe3O4 microparticles and chlorhexidine (CHX) encapsulated within mesoporous silica, which was silanized by an antibacterial quaternary ammonium silane (SiQuac). This platform simultaneously targets bacterial inhibition, stability of the hybrid layer, and enhanced filler infiltration by magnetic motion. Comprehensive experiments include X-ray diffraction, FT-IR, VSM, EDS, N2 adsorption-desorption (BET), transmission electron microscopy, scanning electron microscopy, thermogravimetric analysis, and UV-vis spectroscopy. Then, CHX@SiQuac@Fe3O4@m-SiO2 was incorporated into an experimental adhesive resin for dental bonding restorations, followed by immediate and long-term antibacterial assessment, cytotoxicity evaluation, and mechanical and bonding performance. The results confirmed the multifunctional nature of CHX@SiQuac@Fe3O4@m-SiO2. This work outlined a roadmap for (1) designing and tuning an adhesive formulation containing the new platform CHX@SiQuac@Fe3O4@m-SiO2; (2) assessing microtensile bond strength to dentin using a clinically relevant model of simulated hydrostatic pulpal pressure; and (3) investigating the antibacterial outcome performance of the particles when embedded into the formulated adhesives over time. The results showed that at 4 wt % of CHX@SiQuac@Fe3O4@m-SiO2-doped adhesive under the guided magnetic field, the bond strength increased by 28%. CHX@SiQuac@Fe3O4@m-SiO2 enhanced dentin adhesion in the magnetic guide bonding process without altering adhesive properties or causing cytotoxicity. This finding presents a promising method for strengthening the tooth/dental material interface's stability and extending the bonded restorations' lifespan.