Clinical and radiological results with a 36-mm cobalt-chrome prosthetic head, cross-linked Durasul liners associated with Allofit cups: a more than 10-year follow-up period

Fourier-transform infrared spectroscopy imaging is a useful adjunct to routine histopathology to identify failure of polyethylene inlays in revision total hip arthroplasty

The use of highly crosslinked ultra-high molecular weight polyethylene (XLPE) has significantly reduced the volumetric wear of acetabular liners, thereby reducing the incidence of osteolysis. However, contemporary components tend to generate smaller wear particles, which can no longer be identified using conventional histology. This technical limitation can result in imprecise diagnosis. Here, we report on two uncemented total hip arthroplasty cases (~7 years in situ) revised for periprosthetic fracture of the femur and femoral loosening, respectively. Both liners exhibited prominent wear. The retrieved pseudocapsular tissue exhibited a strong macrophage infiltration without microscopically identifiable polyethylene particles. Yet, using Fourier-transform infrared micro-spectroscopic imaging (FTIR-I), we demonstrated the prominent intracellular accumulation of polyethylene debris in both cases. This study shows that particle induced osteolysis can still occur with XLPE liners, even under 10 years in situ. Furthermore, we demonstrate the difficulty of determining the presence of polyethylene debris within periprosthetic tissue. Considering the potentially increased bioactivity of finer particles from XLPE compared to conventional liners, an accurate detection method is required, and new histopathological hallmarks of particle induced osteolysis are needed. FTIR-I is a great tool to that end and can help the accurate determination of foreign body tissue responses.

Ceramic Femoral Heads Exhibit Lower Wear Rates Compared to Cobalt Chrome: A Meta-Analysis

BACKGROUND

Wear between the femoral head and acetabular liners continues to limit the longevity of total hip arthroplasty implants despite advances in implant materials. The purpose of this meta-analysis was to compare linear wear rates of cobalt-chromium (CoCr) and fourth-generation ceramic femoral heads on highly cross-linked polyethylene (XLPE) liners.

METHODS

A systematic review following Preferred Reporting Items for Systematic Reviews and Meta-Analyses guidelines was conducted to identify all studies between 2003 and 2020 that examined in vivo wear rates of either fourth-generation ceramics or CoCr femoral heads on XLPE liners. Studies were analyzed in a weighted means analysis of wear rates and a random effects meta-analysis.

RESULTS

A total of 36 studies met inclusion criteria (1,657 CoCr and 659 ceramic patients). The pooled, weighted mean wear rate was 0.063 mm/year (standard deviation [SD]: 0.061, confidence interval [CI]: 0.049-0.077) for CoCr and 0.047 mm/year (SD: 0.057, CI: 0.033-0.062; P < .01) for ceramic (P < .01). A meta-analysis of 4 studies directly comparing ceramic and CoCr found that CoCr heads demonstrated 0.029 mm/year more wear than ceramic heads (95% CI: 0.026-0.059, P = .306). Mean wear for 32-mm heads was significantly higher for ceramic (P < .01), while mean wear for 36-mm heads was significantly higher for CoCr (P < .01).

CONCLUSION

Fourth-generation ceramic femoral heads were found to have significantly lower wear rates than CoCr heads. Unlike previous studies, this meta-analysis included only in vivo studies and those with the same generation of highly XLPE liners.

New polyethylenes in total hip arthroplasty : a 20- to 22-year follow-up study

AIMS

A significant reduction in wear at five and ten years was previously reported when comparing Durasul highly cross-linked polyethylene with nitrogen-sterilized Sulene polyethylene in total hip arthroplasty (THA). We investigated whether the improvement observed at the earlier follow-up continued, resulting in decreased osteolysis and revision surgery rates over the second decade.

METHODS

Between January 1999 and December 2001, 90 patients underwent surgery using the same acetabular and femoral components with a 28 mm metallic femoral head and either a Durasul or Sulene liner. A total of 66 hips of this prospective randomized study were available for a minimum follow-up of 20 years. The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Dorr method on digitized radiographs with a software package.

RESULTS

In the Durasul group, no patients underwent revision due to loosening or showed radiological evidence of osteolysis. In the Sulene group, four patients (four hips) were revised due to femoral component loosening. The 20-year cumulative failure incidence in the presence of the competing event of death for revision surgery was 4.5% (95% confidence interval (CI) 0.8 to 13.6) in the Durasul group, and 8.9% (95% CI 2.8 to 19.5) in the Sulene group. The mean wear one year after surgery was 0.09 mm (SD 0.007) in the Durasul group and 0.24 (SD 0.015) in the Sulene group (p < 0.001). From one to 20 years after surgery, the mean total penetration was 0.32 mm (SD 0.045) in the Durasul group and 1.07 mm (SD 0.13) in the Sulene group (p < 0.001). Mean femoral head penetration at 20 years was approximately 70.0% less in the Durasul group than the Sulene group.

CONCLUSION

The significant reduction in femoral head penetration obtained with the Durasul compared with Sulene in uncemented THA resulted in lower osteolysis and revision rates after 20 years.Cite this article: Bone Joint J 2022;104-B(9):1032-1038.