Decalcification prevention around orthodontic brackets bonded to bleached enamel using different topical agents

Sustained antibacterial activity of orthodontic elastomeric ligature ties coated with a novel kombucha-derived bacterial nanocellulose: An in-vitro study

Incipient carious lesions, the most common complication in orthodontic patients with fixed appliances, call for the development of novel preventive dental materials that do not rely on patient adherence. The present study aimed to assess the ability of elastomeric ligatures coated with bacterial nanocellulose (BNC) to deliver sustained antibacterial activity, during the standard 28-day interval between orthodontic appointments, without compromising their mechanical properties. Kombucha membrane was used to produce cellulose as a secondary product from the fermentation of tea broth with symbiotic bacteria and yeast culture. Characterization of BNC-coated elastomeric ligatures was performed using Fourier Transform Infrared Spectroscopy and Energy Dispersive Spectroscopy analysis. The samples were pre-treated by immersion first in isopropyl alcohol, then in 8 mL nanocellulose solution for 7 days. Tensile strain and strength of the BNC-coated and conventional ligatures were evaluated using a tensile testing machine. Direct contact and agar diffusion tests were performed to assess the antibacterial activity of nanocellulose. In addition, the release profile of BNC was evaluated. Data analysis was performed by one-way analysis of variance (ANOVA) followed by post-hoc Tukey's test and Wilcoxon signed-rank test. P values less than 0.05 was regarded as significant. There was no statistically significant difference in tensile strain and strength between the BNC-coated and conventional ligatures. The coated ligatures provided sustained antibacterial activity during the required 28 days. The use of BNC-coated elastomeric ligatures in patients with fixed orthodontic appliances might be a promising solution to plaque formation and subsequent enamel decalcification.

Effect of bleaching treatments on the adhesion of orthodontic brackets: a systematic review

BACKGROUND

Nowadays bleaching procedures have gained popularity in orthodontic patients. Peroxide and Carbamide acids are the common agents which are used in in-office and at home bleaching techniques. Consequently, the Bonding adhesion to the enamel can be influenced by the orthodontic phase and the residual peroxide might interfere with the polymerization and the adhesion of the brackets. Frequent debonding of the brackets from teeth after the bleaching procedure could cause the lengthening of the therapy and promote irregularities on enamel surface derived from an additional bonding phase of the brackets. The aim of this systematic review is to appraise the influence regarding the effect of the bleaching procedure on the bond strength of orthodontic brackets.

METHODS

An electronic database search was performed. Search terms included: bleaching, brackets, adhesion; data were extracted and summarized. Risk of bias was assessed using the Chocrane risk of bias tool, adapted for in vitro studies.

RESULTS

A total of 8689 articles were screened and 11 studies met the inclusion criteria of this systematic review. 1000 teeth of human and bovine origin were analyzed for the shear bond strength (SBS) of stainless and ceramic brackets after the bleaching treatments. All the authors divided the groups in different subgroups with different bleaching agents and in different concentration. The SBS value allowed to demonstrate the necessity to delay the bonding of the brackets for two weeks after a bleaching treatment and its improvement when tooth mousse or antioxidants agents are used.

CONCLUSIONS

The SBS values and the delay of the bonding procedure must be considered in dental practice and clinical strategies are necessary in order to avoid drawbacks which could cause the debonding of the brackets after bleaching due to the alterations of the dental substrate, thus interfering with the orthodontic treatments.

Fluoride varnish, ozone and octenidine reduce the incidence of white spot lesions and caries during orthodontic treatment: randomized controlled trial

This randomized, parallel, controlled trial assessed the effect of fluoride varnish, ozone and octenidine on white spot lesions (WSLs) and caries during orthodontic treatment. Patients were enrolled between 1st September 2017 and 31st August 2020 at initiation of orthodontic treatment in Department of Interdisciplinary Dentistry Pomeranian Medical University in Szczecin, Poland. All participants were randomly assigned to four study and one control groups using number random generator. However, investigators were not blinded due to the nature of the study. Groups I, II, III, IV had professional cleaning and varnishing (5% NaF) every 4 weeks. Groups II and IV had in-office ozone therapy before varnishing, groups III and IV received domestic octenidine mouthrinse. Group K had no professional hygienic or prophylactic procedures. WSLs were assessed at T0 and then every 4 weeks (T1-T4) and caries-at T0 and T4. The specific objective was to assess the influence of fluoride varnish, ozone and octenidine on the incidence of white spot lesions and caries during orthodontic treatment. The primary outcome of this report was the highest number of WSLs in group K and the lowest percentage of patients with WSLs in group IV. Each group comprised 30 randomized participants; they were all analyzed. No WSLs were found at T0, but they were stated in all groups at T4. The numbers of patients with WSLs significantly increased between T0-T4 in groups I and K. Group IV had the lowest percentage of patients with WSLs in T1-T4. WSLs in group IV were found no earlier than at T2. Group K had the highest percentage of WSLs at T4: 26%. At T0 all the groups had DMFs above 0 with a significant increase at T4. No side effects of the introduced prophylaxis were observed in any group. Caries is an important problem of fixed orthodontic treatment. Even an extremely intensive prophylaxis could not completely prevent WSLs and caries. Simultaneous application of fluoride varnish, ozone gas exposure and octenidine appears to have a beneficial effect in limiting the development of WSLs.Trial registration: NCT04992481.

Comparative Evaluation of Influence of Nd:YAG Laser (1064 nm) and 980 nm Diode Laser on Enamel around Orthodontic Brackets: An In Vitro Study

(1) Background: The prevention of demineralizing lesions at the enamel structure level continues to represent a challenge in daily dental practice. When bacteria influence the pH level, this will decrease below the threshold for remineralization and the dissociation of hydroxyapatite will occur with a high percentage of phosphate and calcium loss. These elements continue to be studied by many authors in order to obtain a working protocol that will lead to their stabilization at the level of the enamel structure, thus preventing the demineralization process. The aim of this study is to evaluate and compare the influence of two types of laser wavelengths on the surface morphology and mineral components of the enamel through an examination with scanning electron microscopy (SEM) and energy-dispersive X-ray spectrometry (EDX). (2) Methods: Thirty permanent human incisors extracted for periodontal reasons from patients aged 25−40 years old were selected for this study. Metallic brackets (SS Standard 022 Slot, OC Orthodontics, McMinnville, OR, 97128, USA) were bonded onto each tooth. The buccal surface was randomly assigned three sections: Section A—negative control (no treatment), section B—treated with 980 nm Gallium−Aluminum−Arsenide diode laser (a 300 µm optic fiber was used with 0.8 W output power, energy density of 5.33 J/mm2, in continuous mode, for 30 s, oriented perpendicularly to the enamel surface in contact mode) (KaVo GENTLEray 980 Diode Laser, Kaltenbach & Voigt GmbH, Biberach, Germany), and section C—treated with Nd:YAG laser (a 300 µm fiber was carried out at a 1 mm distance from the enamel surface with 0.75 W power, 75 mJ pulse energy, pulse repetition rate of 10 Hz, 5 J/mm2 fluency, average exposure time of 30 s, and water cooling assisted) (LIGHTWALKER AT S, M021-5AF/1 S, Fotona d.o.o, Ljubljana, Slovenia). The elements evaluated in this study were calcium (Ca), phosphate (P), oxygen (O), and carbon (C). A one-way analysis of variance, paired t-tests, and independent t-tests were carried out to evaluate the results using the SPSS 19 IBM Statistical package software for Microsoft. (3) Results: The evaluation of the data indicated that both wavelengths produced an increase in Ca wt% (for diode laser the mean of Ca wt% before irradiation was 21.06, while that after treatment reached 28.24; and for Nd:YAG laser, the mean of Ca wt% before irradiation was 21.31, while that after treatment reached 33.88); as well, the 980 nm diode laser decreased P wt% (from 17.20 before irradiation to 16.92 after irradiation) and the Nd:YAG laser increased P wt% (from 17.46 before irradiation to 18.28 after irradiation). These results showed a statistically significant difference at the p < 0.05 level. (4) Conclusions: It can be concluded that the best improvement of enamel chemical composition was obtained with Nd:YAG irradiation.

Effect of Fluoride-based Varnishes with Added Calcium and Phosphate on Microhardness of Esthetic Restorative Materials: An In Vitro Study

Background and objectives

Fluoride varnishes are being used to prevent caries in children. The high concentration of fluoride in varnishes apart from caries prevention may cause changes in surface properties of esthetic restorations. The study aims to evaluate and compare the effect of four commercially available fluoride varnishes with added calcium and phosphate on microhardness of three esthetic materials namely conventional GIC (Fuji II), high viscosity GIC (Fuji IX), and nanocomposite (Filtek Z350).

Materials and methods

A total of 28 pellets were made of each material and stored in distilled water at 37 °C for 48 hours. The microhardness of the pellets was tested which served as a baseline. These were then randomly divided into four subgroups. In one subgroup Profluorid varnish was applied, second subgroup MI varnish was applied, third subgroup Embrace varnish was applied, and in the fourth subgroup Enamel Pro varnish was applied as per protocol. Thereafter, all the pellets were subjected to microhardness testing (load = 100 g for 15 seconds).

Results

The fluoride varnishes increased the microhardness of conventional GIC (Fuji II) whereas in case of high viscosity GIC (Fuji IX) the application of varnishes reduced the microhardness. In case of nanocomposite restorative material (Filtek Z350) only Profluorid varnish increased its microhardness.

Conclusion

Fluoride varnish and calcium-phosphate containing fluoride varnish effect on the microhardness of restorative material is material dependent. So, the choice of fluoride varnish with or without proprietary additives depends on the nature and composition of the restorative material.

How to cite this article

Shetty RS, Bhat SS, HK Sundeep, et al. Effect of Fluoride-based Varnishes with Added Calcium and Phosphate on Microhardness of Esthetic Restorative Materials: An In Vitro Study. Int J Clin Pediatr Dent 2022;15(2):187-193.

Comparative evaluation of fluoride varnishes, self-assembling peptide-based remineralization agent, and enamel matrix protein derivative on artificial enamel remineralization in vitro

Background

One of the most unfavorable side effects of fixed orthodontic treatment is white spot lesions (WSLs). Although the most important approach is prevention of WSLs, it is also essential to evaluate the efficacy of the remineralization agents. However, there is no concurrence in the literature with respect to the remineralization process of these agents. The objective of the present study was to evaluate the effects of different fluoride varnishes, enamel matrix protein, and self-assembling peptide derivatives with varying chemical compositions on remineralization of artificially created WSLs in vitro using quantitative light-induced fluorescence (QLF).

Methods

Artificial WSLs were created on bovine enamel samples using acidic buffer solution (pH 5, 10 days). Specimens were randomly allocated to six groups (n = 10/group): (1) Emdogain (Straumann, Basel, Switzerland), (2) Curodont Repair (Credentis AG, Switzerland), (3) Duraphat (Colgate-Palmolive, New York, NY), (4) Clinpro XT (3 M ESPE, Pymble, New South Wales, Australia), (5) Enamel Pro Varnish (Premier Dental Products, PA, USA), and (6) control (untreated). The agents were applied to the WSLs according to the manufacturers’ instructions. Fluorescence loss (ΔF), lesion area (area), and impact (ΔQ) values of enamel surfaces were quantified by QLF-D Biluminator^TM (Inspektor-Pro, Amsterdam, The Netherlands) at baseline and after 7, 14, and 21 days of application of the respective materials.

Results

ΔF value presented a significantly decreasing trend throughout the 21 days for all groups except the Duraphat and Enamel Pro varnishes. The changes between 14th and 21st days of the Clinpro XT varnish application were significantly higher than Emdogain, Curodont, and Enamel Pro. The Curodont group showed higher lesion area changes between the first and second week in comparison to the Emdogain, Clinpro XT, and Enamel Pro groups, whereas Clinpro XT assured the highest reduction from the second to the third week of the observation period.

Conclusions

The fluorescence loss was significantly reduced with enamel matrix protein, self-assembling peptide, and light-curable fluoride varnishes in the analysis for 21 days. Curodont and Clinpro XT were effective in diminishing the fluorescence loss and lesion area compared to the Duraphat, Enamel Pro fluoride varnishes, and Emdogain in different time points.

Shear bond strength of a flash-free orthodontic adhesive system after thermal aging procedure

Background

The aim of this study was to compare the shear bond strength (SBS) of a flash-free and precoated orthodontic adhesive with a compomer orthodontic adhesive before and after thermocycling. The adhesive remnant index (ARI) was also determined for both adhesives.

Material and Methods

The adhesive remnant index (ARI) was also determined for both adhesives. Material and Methods: A total of 120 human premolars were randomly divided into two groups (n=60) according to the orthodontic adhesive used: APC Flash-Free Adhesive Coated Appliance System (APC FF) or Transbond PLUS Color Change Adhesive (TP), as control. A SBS test was performed and ARI value for each specimen was also assessed. Results were analyzed by two-way ANOVA and Tukey's Chi-square test (p<0.05).

Results

SBS values were significantly influenced by thermocycling (p<0.01). Neither the orthodontic adhesive nor the interaction between adhesive and thermocycling statistically affected SBS results (p>0.05).

Conclusions

APC FF and TP showed similar bond strength results. Thermocycling induced a significant decrease in SBS values for the two adhesives tested, without differences between 10,000 and 20,000 thermal cycles. Moreover, APC FF left less adhesive remnants on the enamel compared to TP. Key words:APC Flash-Free, APC cement, aging, orthodontics, resin cements.