Influence of substratum hydrophobicity on salivary pellicles: organization or composition?

Different physico-chemical properties (eg adsorption kinetics, thickness, viscoelasticity, and mechanical stability) of adsorbed salivary pellicles depend on different factors, including the properties (eg charge, roughness, wettability, and surface chemistry) of the substratum. Whether these differences in the physico-chemical properties are a result of differences in the composition or in the organization of the pellicles is not known. In this work, the influence of substratum wettability on the composition of the pellicle was studied. For this purpose, pellicles eluted from substrata of different but well-characterized wettabilities were examined by means of sodium dodecyl sulphate polyacrylamide gel electrophoresis (SDS-PAGE). The results showed that substratum hydrophobicity did not have a major impact on pellicle composition. In all substrata, the major pellicle components were found to be cystatins, amylases and large glycoproteins, presumably mucins. In turn, interpretation of previously reported data based on the present results suggests that variations in substratum wettability mostly affect the organization of the pellicle components.

NanoWear of Salivary Films vs. Substratum Wettability

The pellicle serves as a multifunctional protective layer, providing, e.g., lubrication and remineralization and also acting as a diffusion barrier. In addition, since the formation of the pellicle precedes the adhesion of micro-organisms, it is also important as a conditioning film. We present a novel approach to study the influence of the water wettability of solid surfaces on the strength of adsorbed salivary films. It is based on studying the wear resistance of the films with an atomic force microscope operated in the friction force spectroscopy mode. This methodology provides the strength of the films in terms of the forces needed for breaking and removing them. Our results indicate that these forces are highly dependent on the water wettability of the underlying substrata, decreasing with increasing hydrophobicity. Thus, this study provides valuable information for the design of materials exposed in the oral cavity, i.e., materials that will minimize plaque formation and be easy to clean.

Lubrication and load-bearing properties of human salivary pellicles adsorbed ex vivo on molecularly smooth substrata

In a series of Surface Force Balance experiments, material from human whole saliva was adsorbed to molecularly smooth mica substrata (to form an 'adsorbed salivary film'). Measurements were taken of normal (load bearing, F (n)) and shear (frictional, F (s)*) forces between two interacting surfaces. One investigation involved a salivary film formed by overnight adsorption from undiluted, centrifuged saliva, with the adsorbed film rinsed with pure water before measurement. Measurements were taken under pure water and 70 mM NaNO(3). In a second investigation, a film was formed from and measured under a solution of 7% filtered saliva in 10 mM NaNO(3). F (n) results for both systems showed purely repulsive layers, with an uncompressed thickness of 35-70 nm for the diluted saliva investigation and, prior to the application of shear, 11 nm for the rinsed system. F (s)* was essentially proportional to F (n) for all systems and independent of shear speed (in the range 100-2000 nm s(-1)), with coefficients of friction μ ≈ 0.24 and μ ≈ 0.46 for the unrinsed and rinsed systems, respectively. All properties of the rinsed system remained similar when the pure water measurement environment was changed to 70 mM NaNO(3). For all systems studied, shear gave rise to an approximately threefold increase in the range of normal forces, attributed to the ploughing up of adsorbed material during shear to form debris that stood proud of the adsorbed layer. The results provide a microscopic demonstration of the wear process for a salivary film under shear and may be of particular interest for understanding the implications for in vivo oral lubrication under conditions such as rinsing of the mouth cavity. The work is interpreted in light of earlier studies that showed a structural collapse and increase in friction for an adsorbed salivary film in an environment of low ionic strength.

Intraoral lubrication of PRP-1, statherin and mucin as studied by AFM

The aim of this paper was to elucidate the mechanisms behind salivary lubrication with special emphasis on the lubricity of three key components of the pellicle, viz human acidic proline-rich protein 1 (PRP-1), human statherin and bovine submaxillary mucin (BSM). The lubricating properties of the proteins have been assessed by means of colloidal probe atomic force microscopy, and are discussed in relation to their adsorption behaviour. To various extents, the proteins investigated all showed a lubricating effect when adsorbed to silica surfaces. For comparable concentrations, PRP-1 was found to have a more pronounced lubricating effect than BSM, which in turn showed a higher lubricity than statherin. The relative lubricity is in accordance with previously reported relative adsorbed amounts of the three proteins, within the investigated concentration interval. It is concluded that PRP-1 has the highest lubricating capacity as a pure fraction among the preparations investigated, and that the lubricating effect of PRP-1 as a pure fraction is notably large as compared to the lubricity of human whole saliva.