Repair of osteochondral defects with a new porous synthetic polymer scaffold

Biomechanical Aspects of Osteochondral Regeneration: Implications and Strategies for Three-Dimensional Bioprinting

Osteoarthritis is among the most prevalent of musculoskeletal disorders in the world that causes joint pain, deformity, and limited range of movement. The resulting osteochondral defect can significantly decrease the patient's quality of life, but current treatment options have not demonstrated the capacity to fully regenerate the entire osteochondral microenvironment. Structurally, the osteochondral unit is a composite system composed of three layers-articular cartilage, calcified cartilage, and subchondral bone. Collectively these distinct layers contribute to the distinct biomechanical properties that maintain the health and aid in load transfer during joint articulation. The purpose of this review was to examine the role of the osteochondral interface in tissue engineering. Topics of discussion include the biomechanics of the osteochondral unit and an overview of various strategies for osteochondral interface tissue engineering, with a specific focus on three-dimensional bioprinting. The goal of this review was to elucidate the importance of the osteochondral interface and overview some strategies of developing an interface layer within tissue engineered scaffolds. Impact Statement This review provides an overview of interface tissue engineering for osteochondral regeneration. It offers a detailed investigation into the biomechanics of the osteochondral unit as it relates to tissue engineering, and highlights the strategies that have been utilized to develop the osteochondral interface within tissue engineering scaffolds.

Chondrogenic Potential of Dental-Derived Mesenchymal Stromal Cells

The field of tissue engineering has revolutionized the world in organ and tissue regeneration. With the robust research among regenerative medicine experts and researchers, the plausibility of regenerating cartilage has come into the limelight. For cartilage tissue engineering, orthopedic surgeons and orthobiologists use the mesenchymal stromal cells (MSCs) of various origins along with the cytokines, growth factors, and scaffolds. The least utilized MSCs are of dental origin, which are the richest sources of stromal and progenitor cells. There is a paradigm shift towards the utilization of dental source MSCs in chondrogenesis and cartilage regeneration. Dental-derived MSCs possess similar phenotypes and genotypes like other sources of MSCs along with specific markers such as dentin matrix acidic phosphoprotein (DMP) -1, dentin sialophosphoprotein (DSPP), alkaline phosphatase (ALP), osteopontin (OPN), bone sialoprotein (BSP), and STRO-1. Concerning chondrogenicity, there is literature with marginal use of dental-derived MSCs. Various studies provide evidence for in-vitro and in-vivo chondrogenesis by dental-derived MSCs. With such evidence, clinical trials must be taken up to support or refute the evidence for regenerating cartilage tissues by dental-derived MSCs. This article highlights the significance of dental-derived MSCs for cartilage tissue regeneration.

Treatment of Full-Thickness Cartilage Defects with Pedunculated and Free Synovial Grafts: A Comparative Study in an Animal Model

AIMS AND OBJECTIVES

The purpose of this study was to compare the potential effects of pedunculated and free synovial grafts in the repair of full-thickness articular cartilage defects on an animal model with histological and immunohistochemical analysis.

MATERIALS AND METHODS

A comparative study in an animal model was performed with 24 rabbits, divided into two groups. Full-thickness cartilage defects were created bilaterally on the knees of all rabbits. Pedunculated and free synovial grafts were applied to the right knees of Group 1 and Group 2, respectively. Left knees were left as the control group. Six rabbits from each group were randomly selected for euthanasia 4 and 8 weeks postoperatively. All samples were examined histologically with a cartilage scoring system. For immunohistochemical analysis, the degree of collagen 2 staining was determined using a staging system. All data were statistically compared between the study groups with Student's t-test or Mann-Whitney U-test. The correlations between categorical variables were analyzed with Fisher's exact test and Chi-square test.

RESULTS

In Group 1, the mean defect size had significantly decreased at 8 weeks postsurgery. It was also significantly smaller than that of Group 2. Both pedunculated and free synovial grafts had significantly better histological and immunohistochemical outcomes compared with the controls. Contrastingly, the results of comparison between the study groups (Group 1 vs. 2) at the 4th and 8th week were not statistically significant with regard to histological scores and immunohistochemical staining.

CONCLUSION

Synovial tissue, whether pedunculated or free, provided much better cartilage recovery compared with the control. It can be used as a mesenchymal stem cell (MSC) source, and synovium-derived MSCs have the chondrogenic potential for the in vivo treatment of full-thickness cartilage defects.

Articular cartilage regeneration and tissue engineering models: a systematic review

INTRODUCTION

Cartilage regeneration and restoration is a major topic in orthopedic research as cartilaginous degeneration and damage is associated with osteoarthritis and joint destruction. This systematic review aims to summarize current research strategies in cartilage regeneration research.

MATERIALS AND METHODS

A Pubmed search for models investigating single-site cartilage defects as well as chondrogenesis was conducted and articles were evaluated for content by title and abstract. Finally, only manuscripts were included, which report new models or approaches of cartilage regeneration.

RESULTS

The search resulted in 2217 studies, 200 of which were eligible for inclusion in this review. The identified manuscripts consisted of a large spectrum of research approaches spanning from cell culture to tissue engineering and transplantation as well as sophisticated computational modeling.

CONCLUSIONS

In the past three decades, knowledge about articular cartilage and its defects has multiplied in clinical and experimental settings and the respective body of research literature has grown significantly. However, current strategies for articular cartilage repair have not yet succeeded to replicate the structure and function of innate articular cartilage, which makes it even more important to understand the current strategies and their impact. Therefore, the purpose of this review was to globally summarize experimental strategies investigating cartilage regeneration in vitro as well as in vivo. This will allow for better referencing when designing new models or strategies and potentially improve research translation from bench to bedside.

Three-dimensional (3D) printed scaffold and material selection for bone repair

Critical-sized bone defect repair remains a substantial challenge in clinical settings and requires bone grafts or bone substitute materials. However, existing biomaterials often do not meet the clinical requirements of structural support, osteoinductive property, and controllable biodegradability. To treat large-scale bone defects, the development of three-dimensional (3D) porous scaffolds has received considerable focus within bone engineering. A variety of biomaterials and manufacturing methods, including 3D printing, have emerged to fabricate patient-specific bioactive scaffolds that possess controlled micro-architectures for bridging bone defects in complex configurations. During the last decade, with the development of the 3D printing industry, a large number of tissue-engineered scaffolds have been created for preclinical and clinical applications using novel materials and innovative technologies. Thus, this review provides a brief overview of current progress in existing biomaterials and tissue engineering scaffolds prepared by 3D printing technologies, with an emphasis on the material selection, scaffold design optimization, and their preclinical and clinical applications in the repair of critical-sized bone defects. Furthermore, it will elaborate on the current limitations and potential future prospects of 3D printing technology. STATEMENT OF SIGNIFICANCE: 3D printing has emerged as a critical fabrication process for bone engineering due to its ability to control bulk geometry and internal structure of tissue scaffolds. The advancement of bioprinting methods and compatible ink materials for bone engineering have been a major focus to develop optimal 3D scaffolds for bone defect repair. Achieving a successful balance of cellular function, cellular viability, and mechanical integrity under load-bearing conditions is critical. Hybridization of natural and synthetic polymer-based materials is a promising approach to create novel tissue engineered scaffolds that combines the advantages of both materials and meets various requirements, including biological activity, mechanical strength, easy fabrication and controllable degradation. 3D printing is linked to the future of bone grafts to create on-demand patient-specific scaffolds.

3D-printing porosity: A new approach to creating elevated porosity materials and structures

We introduce a new process that enables the ability to 3D-print high porosity materials and structures by combining the newly introduced 3D-Painting process with traditional salt-leaching. The synthesis and resulting properties of three 3D-printable inks comprised of varying volume ratios (25:75, 50:50, 70:30) of CuSO₄ salt and polylactide-co-glycolide (PLGA), as well as their as-printed and salt-leached counterparts, are discussed. The resulting materials are comprised entirely of PLGA (F-PLGA), but exhibit porosities proportional to the original CuSO₄ content. The three distinct F-PLGA materials exhibit average porosities of 66.6-94.4%, elastic moduli of 112.6-2.7 MPa, and absorbency of 195.7-742.2%. Studies with adult human mesenchymal stem cells (hMSCs) demonstrated that elevated porosity substantially promotes cell adhesion, viability, and proliferation. F-PLGA can also act as carriers for weak, naturally or synthetically-derived hydrogels. Finally, we show that this process can be extended to other materials including graphene, metals, and ceramics.

STATEMENT OF SIGNIFICANCE

Porosity plays an essential role in the performance and function of biomaterials, tissue engineering, and clinical medicine. For the same material chemistry, the level of porosity can dictate if it is cell, tissue, or organ friendly; with low porosity materials being far less favorable than high porosity materials. Despite its importance, it has been difficult to create three-dimensionally printed structures that are comprised of materials that have extremely high levels of internal porosity yet are surgically friendly (able to handle and utilize during surgical operations). In this work, we extend a new materials-centric approach to 3D-printing, 3D-Painting, to 3D-printing structures made almost entirely out of water-soluble salt. The structures are then washed in a specific way that not only extracts the salt but causes the structures to increase in size. With the salt removed, the resulting medical polymer structures are almost entirely porous and contain very little solid material, but the maintain their 3D-printed form and are highly compatible with adult human stem cells, are mechanically robust enough to use in surgical manipulations, and can be filled with and act as carriers for biologically active liquids and gels. We can also extend this process to three-dimensionally printing other porous materials, such as graphene, metals, and even ceramics.

Application of combined porous tantalum scaffolds loaded with bone morphogenetic protein 7 to repair of osteochondral defect in rabbits<sup/>

PURPOSE

Porous tantalum (PT) has been widely used in orthopaedic applications for low modulus of elasticity, excellent biocompatibility, and the microstructures similar to cancellous bone. In order to improve the biological activity of PT, biologically active factors can be combined with the material. The purpose of this study was to investigate if bone morphogenetic protein 7 (BMP-7) modifications could enhance the repairing of cartilage of PT in osteochondral defect in medial femoral condyle of rabbits.

METHODS

A cylindrical osteochondral defect model was created on the animal medial femoral condyle of and filled as follows: PT modified with BMP-7 for MPT group, non-modified PT for the PT group, while no implants were used for the blank group. The regenerated osteochondral tissue was assessed and analyzed by histological observations at four, eight and 16 weeks post-operation and evaluated in an independent and blinded manner by five different observers using a histological score. Osteochondral and subchondral bone defect repair was assessed by micro-CT scan at 16 weeks post-operation, while the biomechanical test was performed at 16 weeks post-operation.

RESULTS

Briefly, higher overall histological score was observed in the MPT group compared to PT group. Furthermore, more new osteochondral tissue and bone formed at the interface and inside the inner pores of scaffolds of the MPT group compared to PT group. Additionally, the micro-CT data suggested that the new bone volume fractions and the quantity and quality of trabecular bone, as well as the maximum release force of the bone, were higher in the MPT group compared to PT group.

CONCLUSIONS

We demonstrated that the applied modified PT with BMP-7 promotes excellent subchondral bone regeneration and may serve as a novel approach for osteochondral defects repair.

Emerging Concepts in Treating Cartilage, Osteochondral Defects, and Osteoarthritis of the Knee and Ankle

The management and treatment of cartilage lesions, osteochondral defects, and osteoarthritis remain a challenge in orthopedics. Moreover, these entities have different behaviors in different joints, such as the knee and the ankle, which have inherent differences in function, biology, and biomechanics. There has been a huge development on the conservative treatment (new technologies including orthobiologics) as well as on the surgical approach. Some surgical development upraises from technical improvements including advanced arthroscopic techniques but also from increased knowledge arriving from basic science research and tissue engineering and regenerative medicine approaches. This work addresses the state of the art concerning basic science comparing the knee and ankle as well as current options for treatment. Furthermore, the most promising research developments promising new options for the future are discussed.

Evaluation of three-dimensional chitosan-agarose-gelatin cryogel scaffold for the repair of subchondral cartilage defects: an in vivo study in a rabbit model

In this study, the potential of a chitosan-agarose-gelatin (CAG) cryogel scaffold for the repair of subchondral cartilage defects was explored in female New Zealand white rabbits. Custom-made CAG cryogel scaffold was implanted in a surgically created subchondral defect (diameter of 4 mm, depth of 4 mm) in knee joint of rabbit. The repair of the subchondral defect was evaluated at regular time interval by both macroscopic as well as microscopic examinations. The gross evaluation of the scaffold-implanted site showed integration of the scaffold with the surrounding tissue. Scanning electron microscopy and histological staining of the remnants of implanted cryogel scaffold showed infiltration of the host cells. The repair of the subchondral defect along with well-integrated regenerated cartilage was confirmed by the histology analysis of the joint. Results showed significant cartilage regeneration by the fourth week until eighth week after implantation. Immunohistochemical analysis confirmed that regenerated tissue is hyaline cartilage and absence of hypertrophy marker was reported. In addition, the CAG scaffolds did not elicit any adverse immunological rejection as shown by hematological analysis. Enzyme-linked immunosorbent assay did not show any statistically significant change in the concentration of tumor necrosis factor-α in the serum, and remained in a nontoxic range. Rabbits with a surgically created defect but no scaffold did not show any cartilage regeneration throughout the experiment of 8 weeks. These results demonstrate that CAG cryogel scaffolds promote repair of an osteochondral defect at a load-bearing site in rabbits.

Temporary inductions of matrix metalloprotease-3 (MMP-3) expression and cell apoptosis are associated with tendon degeneration or rupture after corticosteroid injection

Corticosteroid injections are widely used to treat enthesopathy and tendinitis, but are also associated with possible side effects, such as tendon degeneration or rupture. However, the mechanism of tendon degeneration or rupture after corticosteroid injection remains controversial. The purpose of this study was to reveal the mechanism of tendon degeneration or rupture after injection of triamcinolone acetonide (TA) or prednisolone (PSL). Forty-two rats were divided into 3 groups: A normal saline injection group (control group), a TA injection group, and a PSL injection group; the normal saline or corticosteroid was injected around the Achilles tendon. One or 3 weeks after injection, the tendons were subjected to biomechanical testing and histological analysis. At 1 week, the biomechanical strength was significantly lower in the corticosteroid groups. Histological analysis, at 1-week post-injection, showed collagen attenuation, increased expression of MMP-3 and apoptotic cells in the corticosteroid groups. The histological changes and biomechanical weaknesses of the tendon were not seen at 3 weeks. These alterations appeared to be involved in tendon degeneration or rupture after corticosteroid injection.

Osteochondral articular defect repair using auricle-derived autologous chondrocytes in a rabbit model

Hypothesizing that the implantation of non-articular (heterotopic) chondrocytes might be an alternative approach to support articular cartilage repair, we analyzed joint cartilage defect healing in the rabbit model after implantation of autologous auricle-derived (auricular) chondrocytes. Autologous lapine articular and auricular chondrocytes were cultured for 3 weeks in polyglycolic acid (PGA) scaffolds before being implanted into critical sized osteochondral defects of the rabbit knee femoropatellar groove. Cell-free PGA scaffolds and empty defects served as controls. Construct quality was determined before implantation and defect healing was monitored after 6 and 12 weeks using vitality assays, macroscopical and histological score systems. Neo-cartilage was formed in the PGA constructs seeded with both articular and auricular chondrocytes in vitro and in vivo. At the histological level, cartilage repair was slightly improved when using autologous articular chondrocyte seeded constructs compared to empty defects and was significantly superior compared to defects treated with auricular chondrocytes 6 weeks after implantation. Although only the immunohistological differences were significant, auricular chondrocyte implantation induced an inferior healing response compared with the empty defects. Elastic auricular chondrocytes might maintain some tissue-specific characteristics when implanted into joint cartilage defects which limit its repair capacity.

Current concepts: tissue engineering and regenerative medicine applications in the ankle joint

Tissue engineering and regenerative medicine (TERM) has caused a revolution in present and future trends of medicine and surgery. In different tissues, advanced TERM approaches bring new therapeutic possibilities in general population as well as in young patients and high-level athletes, improving restoration of biological functions and rehabilitation. The mainstream components required to obtain a functional regeneration of tissues may include biodegradable scaffolds, drugs or growth factors and different cell types (either autologous or heterologous) that can be cultured in bioreactor systems (in vitro) prior to implantation into the patient. Particularly in the ankle, which is subject to many different injuries (e.g. acute, chronic, traumatic and degenerative), there is still no definitive and feasible answer to ‘conventional’ methods. This review aims to provide current concepts of TERM applications to ankle injuries under preclinical and/or clinical research applied to skin, tendon, bone and cartilage problems. A particular attention has been given to biomaterial design and scaffold processing with potential use in osteochondral ankle lesions.

Hydrophilic Gelatin and Hyaluronic Acid-Treated PLGA Scaffolds for Cartilage Tissue Engineering

Tissue engineering provides a new strategy for repairing damaged cartilage. Surface and mechanical properties of scaffolds play important roles in inducing cell growth.

Aim

The aim of this study was to fabricate and characterize PLGA and gelatin/hyaluronic acid-treated PLGA (PLGA-GH) sponge scaffolds for articular cartilage tissue engineering.

Methods

The PLGA-GH scaffolds were cross-linked with gelatin and hyaluronic acid. Primary chondrocytes isolated from porcine articular cartilages were used to assess cell compatibility. The characteristic PLGA-GH scaffold was higher in water uptake ratio and degradation rate within 42 days than the PLGA scaffold.

Results

The mean compressive moduli of PLGA and PLGA-GH scaffolds were 1.72±0.50 MPa and 1.86±0.90 MPa, respectively. The cell attachment ratio, proliferation, and extracellular matrix secretion on PLGA-GH scaffolds are superior to those of PLGA scaffolds.

Conclusions

In our study, PLGA-GH scaffolds exhibited improvements in cell biocompatibility, cell proliferation, extracellular matrix synthesis, and appropriate mechanical and structural properties for potential engineering cartilage applications.

Treatment of osteochondral defects in the rabbit's knee joint by implantation of allogeneic mesenchymal stem cells in fibrin clots

The treatment of osteochondral articular defects has been challenging physicians for many years. The better understanding of interactions of articular cartilage and subchondral bone in recent years led to increased attention to restoration of the entire osteochondral unit. In comparison to chondral lesions the regeneration of osteochondral defects is much more complex and a far greater surgical and therapeutic challenge. The damaged tissue does not only include the superficial cartilage layer but also the subchondral bone. For deep, osteochondral damage, as it occurs for example with osteochondrosis dissecans, the full thickness of the defect needs to be replaced to restore the joint surface (1). Eligible therapeutic procedures have to consider these two different tissues with their different intrinsic healing potential (2). In the last decades, several surgical treatment options have emerged and have already been clinically established (3-6). Autologous or allogeneic osteochondral transplants consist of articular cartilage and subchondral bone and allow the replacement of the entire osteochondral unit. The defects are filled with cylindrical osteochondral grafts that aim to provide a congruent hyaline cartilage covered surface (3,7,8). Disadvantages are the limited amount of available grafts, donor site morbidity (for autologous transplants) and the incongruence of the surface; thereby the application of this method is especially limited for large defects. New approaches in the field of tissue engineering opened up promising possibilities for regenerative osteochondral therapy. The implantation of autologous chondrocytes marked the first cell based biological approach for the treatment of full-thickness cartilage lesions and is now worldwide established with good clinical results even 10 to 20 years after implantation (9,10). However, to date, this technique is not suitable for the treatment of all types of lesions such as deep defects involving the subchondral bone (11). The sandwich-technique combines bone grafting with current approaches in Tissue Engineering (5,6). This combination seems to be able to overcome the limitations seen in osteochondral grafts alone. After autologous bone grafting to the subchondral defect area, a membrane seeded with autologous chondrocytes is sutured above and facilitates to match the topology of the graft with the injured site. Of course, the previous bone reconstruction needs additional surgical time and often even an additional surgery. Moreover, to date, long-term data is missing (12). Tissue Engineering without additional bone grafting aims to restore the complex structure and properties of native articular cartilage by chondrogenic and osteogenic potential of the transplanted cells. However, again, it is usually only the cartilage tissue that is more or less regenerated. Additional osteochondral damage needs a specific further treatment. In order to achieve a regeneration of the multilayered structure of osteochondral defects, three-dimensional tissue engineered products seeded with autologous/allogeneic cells might provide a good regeneration capacity (11). Beside autologous chondrocytes, mesenchymal stem cells (MSC) seem to be an attractive alternative for the development of a full-thickness cartilage tissue. In numerous preclinical in vitro and in vivo studies, mesenchymal stem cells have displayed excellent tissue regeneration potential (13,14). The important advantage of mesenchymal stem cells especially for the treatment of osteochondral defects is that they have the capacity to differentiate in osteocytes as well as chondrocytes. Therefore, they potentially allow a multilayered regeneration of the defect. In recent years, several scaffolds with osteochondral regenerative potential have therefore been developed and evaluated with promising preliminary results (1,15-18). Furthermore, fibrin glue as a cell carrier became one of the preferred techniques in experimental cartilage repair and has already successfully been used in several animal studies (19-21) and even first human trials (22). The following protocol will demonstrate an experimental technique for isolating mesenchymal stem cells from a rabbit's bone marrow, for subsequent proliferation in cell culture and for preparing a standardized in vitro-model for fibrin-cell-clots. Finally, a technique for the implantation of pre-established fibrin-cell-clots into artificial osteochondral defects of the rabbit's knee joint will be described.

Bioengineering of articular cartilage: past, present and future

The treatment of cartilage defects poses a clinical challenge owing to the lack of intrinsic regenerative capacity of cartilage. The use of tissue engineering techniques to bioengineer articular cartilage is promising and may hold the key to the successful regeneration of cartilage tissue. Natural and synthetic biomaterials have been used to recreate the microarchitecture of articular cartilage through multilayered biomimetic scaffolds. Acellular scaffolds preserve the microarchitecture of articular cartilage through a process of decellularization of biological tissue. Although promising, this technique often results in poor biomechanical strength of the graft. However, biomechanical strength could be improved if biomaterials could be incorporated back into the decellularized tissue to overcome this limitation.

Preparation of porous PLGA/Ti biphasic scaffold and osteochondral defect repair

In this study, a porous PLGA/Ti biphasic scaffold was prepared and its potential to repair osteochondral defects was evaluated. The microstructure and mechanical properties of porous PLGA and porous Ti and their interface were characterized. The as-prepared biphasic scaffolds were implanted into rabbit knees for 1 and 3 months (PLGA/Ti group), and the porous PLGA (PLGA group) or empty defect (Untreated group) was also used. The results showed that both porous PLGA and porous Ti had an interconnected porous structure. The mechanical strength of porous PLGA and porous Ti was similar to that of cartilage and subchondral bone, respectively. The interface analysis revealed that the as-prepared biphasic scaffold had good overall integrity and interface stability. The gross observation and histological evaluation of specimens showed that hyaline-like cartilage filled the defects to a certain extent at 3 months for both PLGA/Ti and PLGA groups while the defects remained in an untreated group. In the PLGA/Ti group, better cartilage and subchondral bone repair was observed, and quantitative macroscopic and histological score evaluations confirmed this result, indicating that the porous biphasic PLGA/Ti scaffold had good biocompatibility and the best osteochondral defect repair ability in this study. The as-prepared porous biphasic scaffold showed the potential to be used in osteochondral tissue engineering for osteochondral defect repair.

Localization of vascular endothelial growth factor during the early stages of osteochondral regeneration using a bioabsorbable synthetic polymer scaffold

Vascular endothelial growth factor (VEGF) plays a critical role in chondrogenic differentiation in the growth plate of the epiphysis. This function is necessary for chondrocyte survival in cartilage development. We investigated the localization of VEGF in the osteochondral regeneration process using a bioabsorbable polymer scaffold. Osteochondral defects (5 mm in diameter and 5 mm in depth) were made on the femoral condyle of forty-eight skeletally mature female Japanese white rabbits. In total, twenty-four defects were filled with poly(DL-lactide-co-glycolide) scaffolds and the others were left untreated. The regeneration process was investigated macroscopically, histologically, immunohistochemically, and by gene expression analysis. In the early stages of osteochondral regeneration, bone ingrowth was observed in the deep zone of the scaffold with continuous VEGF expression; cartilage regeneration was observed in the superficial zone of the scaffold with decreased VEGF expression. In contrast, when the defect was left untreated, VEGF localization was observed throughout the entire defect area, and cartilage regeneration at the articular surface was delayed. We conclude that decrease in localization of VEGF at the articular surface in the postoperative early stage is closely related to the progression of cartilage regeneration in osteochondral defects.

The combined effects of continuous passive motion treatment and acellular PLGA implants on osteochondral regeneration in the rabbit

We investigated the active role of clinical rehabilitation in osteochondral regeneration using continuous passive motion (CPM) treatment together with acellular PLGA implants. CPM treatment was performed and compared with immobilization (Imm) treatment and intermittent active motion (IAM) treatment upon full-thickness osteochondral defects either with or without an PLGA implant in the PI (PLGA-implanted) and ED (empty defect) models. The PI and ED tests were performed in 38 rabbits for 4 and 12 weeks. At the end of testing, the PI-CPM group had the best regeneration with nearly normal articular surfaces and no joint contracture or inflammatory reaction. In contrast, degenerated joints, abrasion cartilage surfaces and synovitis were observed in the Imm and IAM groups. The achieved bone volume/tissue volume (BV/TV) ratio, which was measured using micro-CT, was significantly higher in the CPM group compared with the Imm and IAM groups; in particular, the performance of the PI-CPM group exceeds that of the ED-CPM group. The thickness of the trabecular (subchondral) bone was visibly increased in all of the groups from 4 through 12 weeks of testing. However, a histological analysis revealed differences in cartilage regeneration. At week 4, compared with the ED samples, all of the PI groups exhibited better collagen alignment and higher GAG content in the core of their repaired tissues, particularly in the PI-CPM group. At week 12, sound osteochondral repair and hyaline cartilaginous regeneration was observed in the PI-CPM group, and this was marked by type II collagen expression, osteocyte maturation, and trabecular boney deposition. In contrast, the PI-Imm and PI-IAM groups exhibited fibrocartilaginous tissues that had modest GAG content. In summary, this study demonstrates that early CPM treatment together with acellular PLGA implantation has significant positive effects on osteochondral regeneration in rabbit knee joint models.

Novel nano-composite multilayered biomaterial for osteochondral regeneration: a pilot clinical trial

BACKGROUND

In recent years, there has been an increasing interest in and awareness of the importance of subchondral bone, for its role in the pathogenesis of articular surface damage and for the care that should be taken when treating such damage.

PURPOSE

The objective of this pilot clinical study was to test the safety and performance of a newly developed type I collagen-hydroxyapatite nanostructured biomimetic osteochondral scaffold that aims to regenerate cartilage and subchondral bone.

STUDY DESIGN

Case series; Level of evidence, 4.

METHODS

A multilayer gradient nano-composite scaffold was obtained by nucleating collagen type I fibrils with hydroxyapatite nanoparticles. Thirty patients (9 female, 21 male; mean age, 29.3 years) with knee chondral or osteochondral lesions were treated with scaffold implantation. Lesion size varied from 1.5 cm(2) to 6.0 cm(2). Twenty-eight patients were followed for 2 years and were clinically evaluated using the International Knee Documentation Committee and Tegner scores. At final follow-up, magnetic resonance imaging evaluation was performed in 24 patients, and they were evaluated with the MOCART (Magnetic Resonance Observation of Cartilage Repair Tissue) score.

RESULTS

The Tegner and International Knee Documentation Committee objective and subjective scores improved significantly from the baseline evaluation to the 6-, 12-, and 24-month follow-ups. Further analysis showed a slower recovery but the same results for patients who presented with adverse events, for older patients, for patients who underwent previous surgery, and for those with patellar lesions. In contrast, a faster recovery was observed in active patients. At magnetic resonance imaging evaluation, complete filling of the cartilage and complete integration of the graft was shown in 70% of the lesions. However, the subchondral lamina and bone were considered intact in a minority of cases (7% and 47%, respectively).

CONCLUSION

This open 1-step procedure was used for the treatment of chondral and osteochondral knee defects. The present pilot study highlighted the safety and potential clinical benefit of the graded biomimetic osteochondral scaffold in promoting bone and cartilage tissue restoration by itself and with good clinical and magnetic resonance imaging results at the 2-year follow-up.

TruFit CB bone plug: chondral repair, scaffold design, surgical technique and early experiences

The TruFit CB osteochondral scaffold plug is a commercially available and licensed scaffold implant for the treatment of chondral and osteochondral defects of the knee. A number of surgical techniques have been described that are designed to achieve neocartilaginous tissue cover of a chondral defect, but many result in fibrocartilage tissue, not type II collagen hyaline cartilage. This fibrocartilage layer can fail with high shear forces in the knee joint, and lead to ongoing articular surface irregularity and subsequent secondary arthritic change. Recent research and clinical interest has focused on employing tissue-engineering techniques utilizing scaffolds in an attempt to obtain cartilage repair tissue that is histologically and biomechanically superior. The TruFit CB implant is one such device. This article describes the techniques of attempted chondral repair and the problems that can be experienced. Current concepts in chondral scaffold design are discussed, and the surgical technique and early experiences with the TruFit CB implant are presented.

The subchondral bone in articular cartilage repair: current problems in the surgical management

As the understanding of interactions between articular cartilage and subchondral bone continues to evolve, increased attention is being directed at treatment options for the entire osteochondral unit, rather than focusing on the articular surface only. It is becoming apparent that without support from an intact subchondral bed, any treatment of the surface chondral lesion is likely to fail. This article reviews issues affecting the entire osteochondral unit, such as subchondral changes after marrow-stimulation techniques and meniscectomy or large osteochondral defects created by prosthetic resurfacing techniques. Also discussed are surgical techniques designed to address these issues, including the use of osteochondral allografts, autologous bone grafting, next generation cell-based implants, as well as strategies after failed subchondral repair and problems specific to the ankle joint. Lastly, since this area remains in constant evolution, the requirements for prospective studies needed to evaluate these emerging technologies will be reviewed.

Electrospun synthetic polymer scaffold for cartilage repair without cultured cells in an animal model

PURPOSE

The purpose of our study was to explore the possibility that an electrospun bioabsorbable scaffold could be used in the treatment of a full-thickness articular defect without the addition of exogenous cells in a rabbit model.

METHODS

Two types of poly(D,L-lactide-co-glycolide) (PLG) scaffolds, a solid cylindrical type and a cannulated tubular type, were made with the electrospinning method. Osteochondral defects, 5 mm in diameter and 5 mm in depth, made on the femoral condyles of rabbits were filled with these scaffolds, and the repair process was investigated histologically.

RESULTS

In the groups in which the defect was filled with the scaffold, fibrous tissue at the articular surface of the scaffold was observed at postoperative week 2. Thereafter cartilage at the articular surface and bone at the subchondral zone were regenerated, and the repaired cartilage was maintained through postoperative week 24. By contrast, the untreated defect was filled with hematoma at postoperative week 2; thereafter regenerated cartilage and bone were observed. However, the surface of the articular cartilage was not regular, and regenerated cartilage was not well organized. The histologic scores of the groups in which the defect was filled with cannulated tubular electrospun PLG scaffolds were significantly higher than those of the untreated defect group at postoperative weeks 12 and 24 (P < .01).

CONCLUSIONS

The electrospun PLG scaffold could repair a 5-mm osteochondral defect created in the rabbit model without exogenous cultured cells.

CLINICAL RELEVANCE

The electrospun PLG scaffold could repair full-thickness osteochondral defects. The cannulated type of PLG scaffold has the possibility to lead not only to good regeneration of cartilage but also to easy transplantation by use of a guidewire through the cannulas in the scaffold.

Orderly osteochondral regeneration in a sheep model using a novel nano-composite multilayered biomaterial

The objective of this article was to investigate the safety and regenerative potential of a newly developed biomimetic scaffold when applied to osteochondral defects in an animal model. A new multilayer gradient nano-composite scaffold was obtained by nucleating collagen fibrils with hydroxyapatite nanoparticles. In the femoral condyles of 12 sheep, 24 osteochondral lesions were created. Animals were randomized into three treatment groups: scaffold alone, scaffold colonized in vitro with autologous chondrocytes and empty defects. Six months after surgery, the animals were sacrificed and the lesions were histologically evaluated. Histologic and gross evaluation of specimens showed good integration of the chondral surface in all groups except for the control group. Significantly better bone regeneration was observed both in the group receiving the scaffold alone and in the group with scaffold loaded with autologous chondrocytes. No difference in cartilage surface reconstruction and osteochondral defect filling was noted between cell-seeded and cell-free groups. In the control group, no bone or cartilage defect healing occurred, and the defects were filled with fibrous tissue. Quantitative macroscopic and histological score evaluations confirmed the qualitative trends observed. The results of the present study showed that this novel osteochondral scaffold is safe and easy to use, and may represent a suitable matrix to direct and coordinate the process of bone and hyaline-like cartilage regeneration. The comparable regeneration process observed with or without autologous chondrocytes suggests that the main mode of action of the scaffold is based on the recruitment of local cells.

Evaluation of histological scoring systems for tissue-engineered, repaired and osteoarthritic cartilage

OBJECTIVE

Regeneration of hyaline cartilage has been the focus of an increasing number of research groups around the world. One of the most important outcome measures in evaluation of its success is the histological quality of cartilaginous tissue. Currently, a variety of histological scoring systems is used to describe the quality of osteoarthritic, in vivo repaired or in vitro engineered tissue. This review aims to provide an overview of past and currently used histological scoring systems, in an effort to aid cartilage researchers in choosing adequate and validated cartilage histological scoring systems.

METHODS

Histological scoring systems for analysis of osteoarthritic, tissue engineered and in vivo repaired cartilage were reviewed. The chronological development as well as the validity and practical applicability of the scoring systems is evaluated.

RESULTS

The Histological-Histochemical Grading System (HHGS) or a HHGS-related score is most often used for evaluation of osteoarthritic cartilage, however the Osteoarthritis Research Society International (OARSI) Osteoarthritis Cartilage Histopathology Assessment System seems a valid alternative. The O'Driscoll score and the International Cartilage Repair Society (ICRS) II score may be used for in vivo repaired cartilage. The 'Bern score' seems most adequate for evaluation of in vitro engineered cartilage.

CONCLUSION

A great variety of histological scoring systems exists for analysis of osteoarthritic or normal, in vivo repaired or tissue-engineered cartilage, but only few have been validated. Use of these validated scores may considerably improve exchange of information necessary for advances in the field of cartilage regeneration.

Gelatin-based haemostyptic Spongostan as a possible three-dimensional scaffold for a chondrocyte matrix?

The gelatin-based haemostyptic compound Spongostan was tested as a three-dimensional (3D) chondrocyte matrix in an in vitro model for autologous chondrocyte transplantation using cells harvested from bovine knees. In a control experiment of monolayer cultures, the proliferation or de-differentiation of bovine chondrocytes was either not or only marginally influenced by the presence of Spongostan (0.3 mg/ml).

In monolayers and 3-D Minusheet culture chambers, the cartilage-specific differentiation markers aggrecan and type-II collagen were ubiquitously present in a cell-associated fashion and in the pericellular matrix. The Minusheet cultures usually showed a markedly higher mRNA expression than monolayer cultures irrespective of whether Spongostan had been present or not during culture. Although the de-differentiation marker type-I collagen was also present, the ratio of type-I to type-II collagen or aggrecan to type-I collagen remained higher in Minusheet 3-D cultures than in monolayer cultures irrespective of whether Spongostan had been included in or excluded from the monolayer cultures. The concentration of GAG in Minusheet cultures reached its maximum after 14 days with a mean of 0.83 ± 0.8 μg/106 cells; mean ±, sem, but remained considerably lower than in monolayer cultures with/without Spongostan.

Our results suggest that Spongostan is in principle suitable as a 3-D chondrocyte matrix, as demonstrated in Minusheet chambers, in particular for a culture period of 14 days. Clinically, differentiating effects on chondrocytes, simple handling and optimal formability may render Spongostan an attractive 3-D scaffold for autologous chondrocyte transplantation.

Tissue engineering: state of the art in oral rehabilitation

More than 85% of the global population requires repair or replacement of a craniofacial structure. These defects range from simple tooth decay to radical oncologic craniofacial resection. Regeneration of oral and craniofacial tissues presents a formidable challenge that requires synthesis of basic science, clinical science and engineering technology. Identification of appropriate scaffolds, cell sources and spatial and temporal signals (the tissue engineering triad) is necessary to optimize development of a single tissue, hybrid organ or interface. Furthermore, combining the understanding of the interactions between molecules of the extracellular matrix and attached cells with an understanding of the gene expression needed to induce differentiation and tissue growth will provide the design basis for translating basic science into rationally developed components of this tissue engineering triad. Dental tissue engineers are interested in regeneration of teeth, oral mucosa, salivary glands, bone and periodontium. Many of these oral structures are hybrid tissues. For example, engineering the periodontium requires growth of alveolar bone, cementum and the periodontal ligament. Recapitulation of biological development of hybrid tissues and interfaces presents a challenge that exceeds that of engineering just a single tissue. Advances made in dental interface engineering will allow these tissues to serve as model systems for engineering other tissues or organs of the body. This review will begin by covering basic tissue engineering principles and strategic design of functional biomaterials. We will then explore the impact of biomaterials design on the status of craniofacial tissue engineering and current challenges and opportunities in dental tissue engineering.

Influence of scaffold stiffness on subchondral bone and subsequent cartilage regeneration in an ovine model of osteochondral defect healing

BACKGROUND

In osteochondral defects, subchondral bone, as a load-bearing structure, is believed to be important for bone and cartilage regeneration.

HYPOTHESIS

A stiff scaffold creates better conditions for bone formation and cartilage regeneration than does a softer one.

STUDY DESIGN

Controlled laboratory study.

METHODS

Critical osteochondral defects were created in the femoral condyles of 24 sheep. Subchondral bone was reconstructed with a stiff scaffold or a modified softer one, with untreated defects serving as controls. The repair response was evaluated with mechanical, histological, and histomorphometrical techniques at 3 and 6 months postoperatively.

RESULTS

The elastic modulus of regenerated fibrocartilage over the stiff scaffold tended to be higher than in the soft scaffold group (61% vs 46% of healthy cartilage) at 3 months. No difference was determined at 6 months; all were well below healthy cartilage. Treated defects showed substantial degradation of the soft scaffold with surrounding sclerotic bone at 3 and 6 months. In contrast, degradation of the stiff scaffold was slower and occurred together with continuous osseous replacement.

CONCLUSION

Stiff scaffolds were found to improve bone regeneration. In contrast, soft scaffolds provided less support, and consequently subchondral bone became sclerotic. Although regenerated cartilage formed over the stiff scaffolds at 3 months, and these exhibited better mechanical properties than did the soft scaffold group, the mechanical properties in both treated groups were the same at 6 months, not dissimilar to that of tissue formed in the untreated specimens and inferior to native articular cartilage.

CLINICAL RELEVANCE

The results imply that subchondral defect filling in clinical settings advances bone regeneration and should have a comparable stiffness to that of healthy subchondral bone rather than being too flexible. Degradation of resorbable materials and consequently the loss of stiffness may compromise the healing of critical defects.

The effect of porosity and mechanical property of a synthetic polymer scaffold on repair of osteochondral defects

We have made three types of poly (DL-lactide-co-glycolide) (PLG) scaffolds (porosity: scaffold I 80 +/- 0.9%, II 85 +/- 0.8%, III 92 +/- 0.7%; compression module determined with 10% strain: scaffold I 0.26 MPa, II 0.091 MPa, III 0.0047 MPa). Osteochondral defects made in the femoral condyle of rabbits were treated with these scaffolds and the possibilities of cartilage repair were investigated histologically. At post-operative weeks 6 and 12, histological scores in the groups of scaffolds II and III were significantly higher than the score in the group of scaffold I. Scaffolds II and III, which have higher porosity than scaffold I, allow better migration of bone marrow cells and better replacement of the scaffold with bone and cartilage than scaffold I. This study suggests that higher porosity allowing bone marrow cells to migrate to the scaffold is important in repairing osteochondral defects.