The influence of hemostatic agents on dentin and enamel surfaces and dental bonding

Effect of cervical margin relocation on marginal adaptation and microleakage of indirect ceramic restorations

PURPOSE

This study evaluated the effect of cervical margin relocation (CMR) with two different materials and contamination with hemostatic agents on the margin adaptation and microleakage of ceramic restorations.

MATERIALS AND METHODS

Mesial-occlusal-distal cavities were prepared in 60 human first molars and distributed to 3 groups (n = 20) according to the margin relocation procedure. The groups were: group F; flowable composite applied in two 2 mm increments, group B; bulk-fill flowable composite applied as a bulk increment of 4 mm thickness and group C (control); no CMR was done. Each group was subdivided into two subgroups (subgroup N; no hemostatic agent applied and subgroup H; hemostatic agent was applied). In all groups, ceramic inlays were prepared and cemented. The samples were subjected to thermocycling (10,000 cycles). The adaptation of the cervical margin was evaluated with scanning electron microscopy (200×). Samples were then assessed for microleakage analysis with the dye penetration method. Marginal adaptation data were normally distributed and analyzed using two-way ANOVA followed by Tukey's post hoc test. Ordinal microleakage score data were analyzed using cumulative link models followed by the analysis of deviance using Wald chi-square tests.

RESULTS

Both CMR and contamination with a hemostatic agent had significant effects on the margin adaptation of the cervical margin. Group C showed the highest adaptation with no significant difference from group F. The lowest adaptation was revealed in group B with a significant difference from group C. Subgroup N (in all groups) showed a statistically higher adaptation than subgroup H. Regarding microleakage assessment, CMR had no significant effect but hemostatic agent application showed a significantly higher microleakage score for all groups.

CONCLUSIONS

Both the CMR procedure and contamination with AlCl3 hemostatic agent had a negative effect on marginal adaptation. For microleakage assessment, only contamination with hemostatic agent negatively affected the microleakage with no effect on the margin relocation procedure.

Bonding Protocols to Reverse the Bond Strength of a Universal Adhesive to Hemostatic Agent-contaminated Dentin

OBJECTIVE

To evaluate the effect of different bonding protocols on the microtensile bond strength (μTBS) of a universal adhesive to dentin contaminated with a hemostatic agent.

METHODS AND MATERIALS

Ninety-five extracted premolars were used in this study. For the μTBS test, 80 teeth were cut to expose mid-coronal dentin and randomly divided into two groups (uncontaminated dentin and hemostatic agent-contaminated dentin). Each group was further divided into five subgroups (n=8/group): 1) SE: no additional treatment, 2) ER: etching with 32% phosphoric acid, 3) CHX: rinsing with 0.2% chlorhexidine, 4) EDTA: rinsing with 17% EDTA, and 5) T40: application of universal adhesive for 40 seconds. A universal adhesive was applied followed by resin composite build-up. μTBS test was performed after 24 hours of water storage. Two-way analysis of variance (ANOVA) was calculated followed by the Duncan testing (α=0.05). The failure mode was analyzed using light microscopy. Additional teeth were prepared for energy-dispersive X-ray (EDX) analysis (n=1/group) and resin-dentin interface observation (n=2/group) using scanning electron microscopy.

RESULTS

Adverse effects of hemostatic agent contamination on the bonding performance of a universal adhesive was found in the SE, CHX, and T40 groups (p<0.05). Fewer and shorter resin tags were observed in the SE, CHX, and T40 groups. A higher percentage of adhesive failure and mixed failure was found in contaminated dentin. All bonding protocols revealed lower amounts of Al and Cl after dentin contamination, except for the SE group.

CONCLUSIONS

Hemostatic agent contamination adversely affected dentin bond strength. However, this bond strength could be reversed using the etch-and-rinse technique or rinsing with EDTA prior to adhesive application.

Noncarious cervical lesions: Morphology and progression, prevalence, etiology, pathophysiology, and clinical guidelines for restoration

PURPOSE

To synthesize the literature regarding noncarious cervical lesions (NCCLs) and propose clinical guidelines when lesion restoration is indicated.

MATERIAL AND METHODS

A PubMed search was performed related to NCCL morphology, progression, prevalence, etiology, pathophysiology, and restoration.

RESULTS

NCCLs form as either rounded (saucerlike) depressions with smooth, featureless surfaces that progress mainly in height or as V-shaped indentations that increase in both height and depth. Prevalence ranges from less than 10% to over 90% and increases with age. Common locations are the facial surfaces of maxillary premolars. They have a multifactorial etiology due to personal habits such as excessive horizontal toothbrushing and consumption of acidic foods and drinks. Occlusal factors have been identified as contributing to the prevalence of NCCLs in some studies, whereas other studies indicate there is no relationship. The concept of abfraction has been proposed whereby mechanical stress from occlusal loading plays a role in the development and progression of NCCLs with publications supporting the concept and others indicating it lacks the required clinical documentation. Regardless of the development mechanism, demineralization occurs and they are one of the most common demineralization diseases in the body. Treatment should be managed conservatively through preventive intervention with restorative treatment delayed until it becomes necessary due to factors such as lesion progression, impact on patient's quality of life, sensitivity, poor esthetics, and food collection may necessitate restoration. Composite resins are commonly used to restore NCCLs although other materials such as glass ionomer and resin-modified glass ionomer are also used. Sclerotic dentin does not etch like normal dentin and therefore it has been recommended to texture the dentin surface with a fine rotary diamond instrument to improve restoration retention. Some clinicians use mechanical retention to increase retention. Beveling of enamel is used to increase the bonding area and retention as well as enhance the esthetic result by gradually creating a color change between the restoration and tooth. Both multistep and single-step adhesives have been used. Dentin etching should be increased to 30 seconds due to the sclerotic dentin with the adhesive agent applied using a light scrubbing motion for 20 seconds but without excessive force that induces substantial bending of a disposable applicator. Both flowable and sculptable composite resins have been successfully used with some clinicians applying and polymerizing a layer of flowable composite resin and then adding an external layer of sculptable composite resin to provide enhanced resistance to wear. When caries is present, silver diamine fluoride has been used to arrest the caries rather than restore the lesion.

CONCLUSIONS

Noncarious cervical lesions (NCCLs) form as smooth saucerlike depressions or as V-shaped notches. Prevalence values as high as 90% and as low as 10% have been reported due to habits such as excessive toothbrushing and an acidic diet. Occlusal factors have been proposed as contributing to their presence but it remains controversial. Publications have both supported and challenged the concept of abfraction. They are one of the most common demineralization diseases in the body. Conservative treatment through prevention is recommended with restorative treatment delayed as long as possible. When treatment is needed, composite resins are commonly used with proposed restorative guidelines including texturing the sclerotic dentin, beveling the enamel, potential use of mechanical retention, 30 seconds of acid etching, and use of either multistep or single-step adhesives in conjunction with a light scrubbing motion for 20 seconds without excessive force placed on disposable applicators.

Universal adhesive application to contaminated/non-contaminated dentin with three different protocols: An in vitro shear bond strength and SEM analysis

This study aimed to comparatively evaluate the shear bond strength (SBS) of a universal adhesive to contaminated/non-contaminated dentin when applied with three different protocols. One-hundred-eighty dentin samples were divided randomly into 12 groups (n=15). The groups were created by combining four dentin contamination conditions (non-contaminated or contaminated with blood, hemostatic, or blood+hemostatic) with three application protocols for Single Bond Universal (no-preconditioning or preconditioning with the 35% phosphoric or 1% gallic acid). Following thermal cycling, the SBS test was performed. Data were analyzed using two-way-ANOVA and Tukey's HSD (p<0.05). Dentin surfaces subjected to phosphoric acid, gallic acid, or hemostatic were examined using scanning electron microscope (SEM) analysis. SBS results were influenced by both the dentin contamination (p<0.001) and application protocol (p<0.001). A significant interaction was found between the two factors (p=0.005). The highest bonding performance to contaminated dentin -at all contamination conditions- was achieved with the gallic acid preconditioning.

The Influence of Hemostatic Agents and Cordless Gingival Retraction Materials on Smear Layer: An Ex vivo Scanning Electron Microscope Analysis

Context:

Cordless gingival retraction materials are now routinely used method for gingival retraction. Although evidence-based information is available on the effect of gingival displacement cord and cordless system on the effectiveness of displacement and the periodontal health, there is a lack of literature regarding the effect of cordless retraction agents on enamel and dentin substrates.

Aim:

The purpose of this investigation was to analyze the changes on the smear layer induced by the hemostatic agent and cordless retraction material at scanning electron microscopic level.

Materials and Methods:

Ferric sulfate (15.5% m/v), expasyl, and magic foam cord were evaluated. Buccal surfaces of 16 recently extracted mandibular premolars were prepared for metal-ceramic crowns, and four teeth each were exposed to ferric sulfate solution, expasyl, and magic foam cord, respectively, for 5 min. Teeth in the control group were exposed to distilled water. The assessment of changes was performed using a scanning electron microscope (SEM).

Results:

SEM exhibited smear layer covering the dentin and occluding the dentinal tubules in the control group. Exposure to ferric sulfate caused the opening of few of the dentinal tubules whereas expasyl caused the partial removal of smear layer with dentinal plugs partially occluding the openings of most of the dentinal tubules. The specimens treated with magic foam exhibited a smear layer similar to the control group.

Conclusions:

The smear layer was affected most with ferric sulfate solution, followed by expasyl and magic foam cord. Magic foam cord did not affect the smear layer.

Effect of blood contamination and various hemostatic procedures on the push-out bond strength of Biodentine when used for furcation perforation repair

Background:

Perforations in the furcation area are common procedural accidents that can impact the outcome of treatment. There are many bioactive materials available to repair these defects.

Aim:

The purpose of this study was to determine and compare the effect of 25% aluminum chloride solution, 20% ferric sulfate solution, and a 980-nm diode laser, when used for hemostasis, on the dislocation resistance of Biodentine placed to repair furcation perforation.

Materials and Methods:

This in vitro study was conducted on fifty extracted human permanent mandibular molars, with ten teeth in each group. The stimulated perforations were contaminated with blood, except for one group. The contaminated groups were either treated with aluminum chloride, ferric sulfate, diode laser, or none at all. All the perforations were restored with Biodentine and tested for push-out bond strength.

Statistical Analysis Used:

One-way analysis of variance and Tukey's HSD post hoc test were applied with a level of significance set at 0.05.

Results:

The dislocation resistance of Biodentine was found to be highest when aluminum chloride or diode laser was used for arresting bleeding. In contrast, the ferric sulfate group gave the lowest value for push-out bond strength (P < 0.05).

Conclusions:

According to the present study, the use of ferric sulfate as a hemostatic agent showed a negative effect on the bond strength of the calcium silicate cement to dentin. Furthermore, Biodentine performed better when diode laser and aluminum chloride were used for hemostasis.

Reporting quality in systematic reviews of in vitro studies: a systematic review

Background: Systematic reviews (SRs) and/or meta-analyses of in vitro research have an important role in establishing the foundation for clinical studies. In this study, we aimed to evaluate the reporting quality of SRs of in vitro studies using the PRISMA checklist.Method: Four databases were searched including PubMed, Virtual Health Library (VHL), Web of Science (ISI) and Scopus. The search was limited from 2006 to 2016 to include all SRs and/or meta-analyses (MAs) of pure in vitro studies. The evaluation of reporting quality was done using the PRISMA checklist.Results: Out of 7702 search results, 65 SRs were included and evaluated with the PRISMA checklist. Overall, the mean overall quality score of reported items of the PRISMA checklist was 68%. We have noticed an increasing pattern in the numbers of published SRs of in vitro studies over the last 10 years. In contrast, the reporting quality was not significantly improved over the same period (p = .363). There was a positive but not significant correlation between the overall quality score and the journal impact factor of the included studies.Conclusions: The adherence of SRs of in vitro studies to the PRISMA guidelines was poor. Therefore, we believe that using reporting guidelines and journals paying attention to this fact will improve the quality of SRs of in vitro studies.

Effect of dentin contamination with two hemostatic agents on bond strength of resin-modified glass ionomer cement with different conditioning

This study evaluated the effect of two hemostatic agents on bond strength of resin-modified glass ionomer cement (RMGIC) to root dentin after using different pretreatment solutions compared to resin composite with a 2-step self-etch adhesive. Dentin specimens were either uncontaminated or contaminated with a ferric sulphate or aluminum chloride astringent, RMGIC was applied after conditioning with; Cavity Conditioner, Self Conditioner or Clearfil SE Primer, while a resin composite was bonded using Clearfil SE Bond. Microtensile bond strength (μTBS) values and failure modes were determined. Two-way ANOVA revealed that hemostatic agents did not significantly affect the RMGIC bond strength with any conditioning material (p>0.05). SE Primer pretreatment provided the highest μTBS values among RMGIC groups. For the resin composite, ferric sulphate astringent significantly reduced μTBS value (p≤0.001). Scanning electron micrographs of representative dentin surfaces contaminated with the hemostatic agents showed effects on smear layer removal and dentinal tubule occlusion.

The Effect of Hemostatic Agents on the Retention Strength of Zirconia Crowns Luted to Dentin Abutments

The purpose of this study was to investigate whether hemostatic agents (HA) show an effect on the retention strength (RS) of zirconia crowns luted to dentin abutments after cleaning with an air/water spray. Human molars (N = 60/n = 12) were prepared and zirconia crowns were milled. Prior to luting (Scotchbond Universal/RelyX Ultimate), molars were pretreated using HA: i. 25% AlCl₃ (VSC), ii. 20% Fe₂(SO₄)₃ (VS), iii. 15.5% Fe₂(SO₄)₃ (AS), iv. 12.7% iron ion solution (ASX) and v. no pretreatment (control). Mastication simulation and pull-out tests were performed. Failure types were defined: cohesive 1-tooth root; cohesive 2-tooth crown; adhesive 1-cement on tooth; adhesive 2-cement on tooth and crown; mixed-adhesive/cohesive. Data were analyzed using 1-way ANOVA, post-hoc Scheffé, Pearson's chi-square-test and Ciba⁻Geigy table (p = 0.05). No RS differences between the tested groups were observed (p = 0.200). ASX fractured more cohesive 2 than the control group. VSC showed more cohesive 2 than adhesive 1 fractures. VS showed more adhesive 2 than mixed fractures. AS showed more cohesive 2 than adhesive 1 and more adhesive 2 than mixed fractures. ASX showed predominantly cohesive 2 fractures. RS was not affected when HA were cleaned off by 30 s of air/water spray prior to luting. HA still seem to weaken the dentin abutment, making it prone to cohesive fractures.

Universal dental adhesives: Current status, laboratory testing, and clinical performance

Increasing demand for simplified and user-friendly adhesive systems has led to the development of a new class of adhesives termed as Universal Adhesives (UAs). The term "Universal" reflects manufacturers' claims that these adhesives can be applied with any adhesion strategy and offer the versatility of use with a variety of direct and indirect restorative materials. The aim of this review was to synthesize the literature regarding the current status of UAs, their adhesion potential to various substrates and their performance in different restorative situations. In vitro studies, clinical trials and systematic reviews were identified utilizing controlled vocabulary and keyword searches in Medline and EMBASE databases. About 282 studies (272 in vitro studies; 11 clinical studies) were included. Available laboratory and clinical evidence does not support the claim that UAs can be used with any adhesive strategy. Although, they can chemically bond to various tooth and direct/indirect restorative substrates, the stability of this bond is material-dependent and subject to hydrolytic degradation. Hence, additional measures are still needed to ensure long-term durability. which undermines the versatility of UAs. The lack of long-term data regarding the clinical performance of UAs further complicates clinical decision-making. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 2121-2131, 2019.

Influence of Hemostatic Solution on Bond Strength and Physicochemical Properties of Resin Cement

The aim of this study was to evaluate the degree of conversion, color stability, chemical composition, and bond strength of a light-cured resin cement contaminated with three different hemostatic solutions. Specimens were prepared for the control (uncontaminated resin cement) and experimental groups (resin cement contaminated with one of the hemostatic solutions) according to the tests. For degree of conversion, DC (n = 5) and color analyses (n = 10), specimens (3 mm in diameter and 2 mm thick) were evaluated by Fourier transform infrared spectroscopy (FTIR) and CIELAB spectrophotometry (L*, a*, b*), respectively. For elemental chemical analysis (n = 1), specimens (2 mm thick and 6 mm in diameter) were evaluated by x-ray energy-dispersive spectroscopy (EDS). The bond strengths of the groups were assessed by the microshear test (n = 20) in a leucite-reinforced glass ceramic substrate, followed by failure mode analysis by scanning electron microscopy (SEM). The mean values, except for the elemental chemical evaluation and failure mode, were evaluated by ANOVA and Tukey's HSD test. The color stability was influenced by storage time (p<0.001) and interaction between contamination and storage time (p<0.001). Hemostop and Viscostat Clear contamination did not affect the DC, however Viscostat increased the DC. Bond strength of the resin cement to ceramic was negatively affected by the contaminants (p<0.001). Contamination by hemostatic agents affected the bond strength, degree of conversion, and color stability of the light-cured resin cement tested.

Effect of hemostatic agent on marginal gaps of class V giomer restorations

Background

Contamination of dentin with hemostatic agents might exert a deleterious effect on adhesive procedures on dentin. The present study was undertaken to investigate the effect of aluminum chloride hemostatic agent on marginal gaps in Cl V giomer restorations.

Material and Methods

Fifty sound bovine permanent incisors were selected for the purpose of this in vitro study and Cl V cavities were prepared on their buccal surfaces; the gingival margins of the cavities were placed in dentin. The tooth samples were randomly assigned to two groups (n=25). The samples in groups 1 and 2 underwent a restorative procedure without and with the application of aluminum chloride hemostatic agent in the cavity, respectively, before application of the adhesive. BeautiBond one-step self-etch adhesive and Beautifil II giomer restorative material were used for the restoration of the cavities in both groups. The samples were thermocycled and sectioned, followed by measuring the gap sizes at gingival margins in µm under a stereomicroscope. The marginal gaps were compared with Mann-Whitney U test. Statistical significance was set at P<0.05.

Results

The results showed significant differences in the mean marginal gaps between the two groups under study (P<0.001); the mean marginal gaps were higher in group 2 (with hemostatic agent) compared to those in group 1 (without hemostatic agent) (P<0.0005).

Conclusions

Contamination with aluminum chloride hemostatic agent in giomer restorations gave rise to higher gingival margin gaps.

Key words:Dental adhesives, giomer restorative material, hemostatic agent, marginal adaptation.

Effects of Contamination by Hemostatic Agents and Use of Cleaning Agent on Etch-and-Rinse Dentin Bond Strength

Abstract The aim of this study was to evaluate the influence of contamination by hemostatic agents and rinsing with chlorhexidine on bond strength between dentin and resin composite. Ninety-six bovine teeth were sectioned to expose a flat dentin surface area. A standardized cavity with 2.0 mm in thickness, superficial diameter of 4.0 mm and bottom diameter of 3.0 mm was prepared with a diamond bur in each dentin specimen. The teeth were divided into four groups according to the hemostatic employed: G1: control; G2: use of ViscoStat, Ultradent; G3: Hemosthasegel, FGM; and G4: Hemostop, Dentsply. The groups were divided into two subgroups according to the cleaning protocol method (n=12): A: without any further cleaning; and B: cleaning with chlorhexidine at 0.2%. All cavities were filled using a dentin adhesive and a resin composite, following the manufacturer's instructions. After 24 h, the specimens were aged by thermal and mechanical cycling. The bond strength was determined by the push out bond test (MPa), Statistical analysis was performed using two-way ANOVA and Tukey test (p<0.05). Statistically significant differences were detected among all groups treated with hemostatic agents and the control group. The post-hoc test showed that cleaning the cavity with chlorhexidine significantly improves the bond strength between dentin and resin composite. Our results suggested that the use of chlorhexidine can reestablish the bond strength between dentin and resin composite when a hemostatic agent was applied.

Marginal integrity of low-shrinkage and methacrylate-based composite resins: Effect of three different hemostatic agents

Background

Moisture control is very important in restorative procedures in dentistry. Use of hemostatic agents helps control moisture; however, they might result in changes on enamel and dentin surfaces, affecting composite resin bond quality. The aim of this in vitro study was to evaluate the marginal microleakage of two different composite resins with the use of three different hemostatic agents.

Material and Methods

Standardized Class V cavities were prepared on the buccal and lingual surfaces of 48 premolars with cervical margins 1 mm apical to the cementoenamel junction (CEJ). The samples were randomly divided into 8 groups. In groups 1 to 4, an etch-and-rinse adhesive (Adper Single Bond) was applied as the bonding system, followed by exposure to different hemostatic agent: group 1: no hemostatic agent (control); group 2: ViscoStat; group 3: ViscoStat Clear; and group 4: trichloracetic acid, as hemostatic agents. The cavities were restored with Z-250 composite resin. In group 5 to 8 Silorane System Adhesive (Filtek P90 Adhesive) was applied as a bonding agent, followed by exposure to different hemostatic agents in a manner similar to that in groups 1to 4. The cavities were restored with Filtek P90, a low-shrinkage composite resin. The samples in each group were evaluated for dye penetration under a stereomicroscope at ×36 after 24 hours and a 500-round thermocycling procedure at enamel and dentin margins. Statistical analysis was carried out using Kruskal-Wallis and Mann-Whitney tests (α=0.05).

Results

Z-250 composite resin exhibited significantly higher dentin microleakage scores compared to Filtek P90 (P = 0.004). Trichloracetic acid increased dentin microleakage with Filtek P90 (P=0.033).

Conclusions

Under the limitations of this in vitro study, application of hemostatic agents did not affect microleakage of the two tested composite resins except for trichloracetic acid that increased marginal microleakage when used with Filtek P90.

Key words:Composite resin, dental leakage, hemostatics, silorane system adhesive.