1
|
Mishra S, Chaturvedi S, Ali M, Pandey KK, Alqahtani NM, Alfarsi MA, Addas MK, Vaddamanu SK, Al Ahmari NM, Alqahtani SM, Yaqoob A, Alqahtani WMS. Dimensional Stability of Light-Activated Urethane Dimethacrylate Denture Base Resins. Polymers (Basel) 2023; 15:polym15030744. [PMID: 36772044 PMCID: PMC9921156 DOI: 10.3390/polym15030744] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/20/2022] [Revised: 01/26/2023] [Accepted: 01/28/2023] [Indexed: 02/04/2023] Open
Abstract
An accurate and dimensionally stable trial denture base is required for a successful denture. The aim of this in vitro study was to assess the dimensional stability of a light-activated urethane dimethacrylate (UDMA) visible light cure (VLC) denture base with three fabrication techniques and different curing cycles. Forty-five VLC denture base samples were divided evenly into three groups. Group A used a conventional fabrication technique with a curing cycle of 5 min. Group B used a modified fabrication technique with two 4-min curing cycles. Group C used a multi-step fabrication technique with three curing cycles (4 min, plus 4 min, plus 2 min). The samples were sectioned and observed under a stereomicroscope to measure the discrepancy between the sample and the master cast. The mean dimensional discrepancy (mm) at the molar region at mid-palate, after 24 h in Group A, B and C was 0.790 mm, 0.741 mm and 0.379 mm, respectively; at the right ridge crest, it was 0.567, 0.408 and 0.185, while at the left ridge crest it was 0.475, 0.331 and 0.125, respectively. Statistical analysis showed significantly different dimensional discrepancies among the groups at all three sites; right ridge crest (F = 93.54, p < 0.001), left ridge crest (F = 105.96, p < 0.001) and mid-palate (F = 125.53, p < 0.001). Within the limitations of this laboratory study, it can be concluded that the denture base using a multi-step fabrication technique with three curing cycles provides better adaptation than the conventional technique. The significance of the study is that clinicians should consider performing denture base fabrication using a multi-step technique to enhance adaptation and hence the stability of the dentures for patients.
Collapse
Affiliation(s)
- Swati Mishra
- Department of Prosthodontics, Career Postgraduate Institute of Dental Sciences, Lucknow 226008, India
| | - Saurabh Chaturvedi
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
- Correspondence:
| | - Mariyam Ali
- Department of Prosthodontics, Career Postgraduate Institute of Dental Sciences, Lucknow 226008, India
| | - Kaushik Kumar Pandey
- Department of Prosthodontics, Career Postgraduate Institute of Dental Sciences, Lucknow 226008, India
| | - Nasser M. Alqahtani
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| | - Mohammed A. Alfarsi
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| | - Mohamed Khaled Addas
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| | - Sunil Kumar Vaddamanu
- Department of Dental Technology, College of Applied Medical Sciences, King Khalid University, Abha 61421, Saudi Arabia
| | - Nasser M. Al Ahmari
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| | - Saeed M. Alqahtani
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| | - Ashfaq Yaqoob
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| | - Waleed M. S. Alqahtani
- Department of Prosthetic Dentistry, College of Dentistry, King Khalid University, Abha 61421, Saudi Arabia
| |
Collapse
|
2
|
Fugolin AP, Ferracane JL, Pfeifer CS. "Fatigue-Crack Propagation Behavior in Microcapsule-Containing Self-Healing Polymeric Networks". MATERIALS & DESIGN 2022; 223:111142. [PMID: 36381607 PMCID: PMC9648420 DOI: 10.1016/j.matdes.2022.111142] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Indexed: 06/16/2023]
Abstract
Over the last years, research on the design of dental self-healing polymers has grown dramatically. It is related to the promising potential of maximizing the clinical lifespan of dental restorations that this strategy holds. In this manuscript, the microcapsule-based strategy is innovated by incorporating the high toughness component N,N-Dimethylacrylamide (DMAM) into the healing agent systems and analyzing in-depth the change in crack propagation behavior induced by the addition of microcapsules into the highly crosslinked polymeric network. In general, the addition of the hydrophilic and high vapor pressure DMAM into the healing agent systems imposed a challenge for the microencapsulation, which highlighted the importance of tailoring the properties of the capsules' shells according to the core composition. The addition of DMAM as cushioning agent proved to be a successful strategy since it resulted in increased G'/G" crossover time from 0.06 (control) to 0.57 s and decreased storage modulus from 8.0 (control) to 0.5GPa. In addition, the incorporation of microcapsules within the polymerized networks provided obstacles to crack propagation, which translated to an overall reinforcement of the polymeric network, as evidenced by the increase in toughness up to 50 % and energy required to propagate cracks up to 100 % in systems containing DMAM at 20 wt%.
Collapse
|
3
|
Khan AA, Fareed MA, Alshehri AH, Aldegheishem A, Alharthi R, Saadaldin SA, Zafar MS. Mechanical Properties of the Modified Denture Base Materials and Polymerization Methods: A Systematic Review. Int J Mol Sci 2022; 23:5737. [PMID: 35628546 PMCID: PMC9143457 DOI: 10.3390/ijms23105737] [Citation(s) in RCA: 16] [Impact Index Per Article: 8.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/23/2022] [Revised: 05/15/2022] [Accepted: 05/19/2022] [Indexed: 12/22/2022] Open
Abstract
Amidst growing technological advancements, newer denture base materials and polymerization methods have been introduced. During fabrication, certain mechanical properties are vital for the clinical longevity of the denture base. This systematic review aimed to explore the effect of newer denture base materials and/or polymerization methods on the mechanical properties of the denture base. An electronic database search of English peer-reviewed published papers was conducted using related keywords from 1 January 2011, up until 31 December 2021. This systematic review was based on guidelines proposed by the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA). The search identified 579 papers. However, the inclusion criteria recognized 22 papers for eligibility. The risk of bias was moderate in all studies except in two where it was observed as low. Heat cure polymethyl methacrylate (PMMA) and compression moulding using a water bath is still a widely used base material and polymerization technique, respectively. However, chemically modified PMMA using monomers, oligomers, copolymers and cross-linking agents may have a promising result. Although chemically modified PMMA resin might enhance the mechanical properties of denture base material, no clear inferences can be drawn about the superiority of any polymerization method other than the conventional compression moulding technique.
Collapse
Affiliation(s)
- Aftab Ahmed Khan
- Dental Biomaterials Research Chair, College of Applied Medical Sciences, King Saud University, Riyadh 11451, Saudi Arabia
| | - Muhammad Amber Fareed
- Department of Restorative Dentistry, College of Dentistry, Gulf Medical University, Ajman P.O. Box 4184, United Arab Emirates;
| | - Abdulkarim Hussain Alshehri
- Department of Prosthetic Dental Sciences, College of Dentistry, Jazan University, Jazan 45142, Saudi Arabia;
| | - Alhanoof Aldegheishem
- Department of Clinical Dental Science, College of Dentistry, Princess Nourah bint Abdulrahman University, P.O. Box 84428, Riyadh 11671, Saudi Arabia; (A.A.); (R.A.)
| | - Rasha Alharthi
- Department of Clinical Dental Science, College of Dentistry, Princess Nourah bint Abdulrahman University, P.O. Box 84428, Riyadh 11671, Saudi Arabia; (A.A.); (R.A.)
| | - Selma A. Saadaldin
- Prosthodontics Division, Schulich School of Medicine and Dentistry, Western University, London, ON N6A 5B9, Canada;
| | - Muhammad Sohail Zafar
- Department of Restorative Dentistry, College of Dentistry, Taibah University, Al Madinah Al Munawarah, Medina 42353, Saudi Arabia;
- Department of Dental Materials, Islamic International Dental College, Riphah International University, Islamabad 46000, Pakistan
| |
Collapse
|
4
|
Linear Dimensional Change and Ultimate Tensile Strength of Polyamide Materials for Denture Bases. Polymers (Basel) 2021; 13:polym13193446. [PMID: 34641261 PMCID: PMC8512380 DOI: 10.3390/polym13193446] [Citation(s) in RCA: 1] [Impact Index Per Article: 0.3] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/30/2021] [Revised: 10/01/2021] [Accepted: 10/02/2021] [Indexed: 11/17/2022] Open
Abstract
The aim of the current study was to evaluate the dimensional changes and ultimate tensile strength in three polyamide materials for denture bases fabrication through injection molding, subjected to artificial aging and different storage conditions. A total of 333 test specimens fabricated from Biosens (BS; Perflex, Netanya, Israel), Bre.flex 2nd edition (BF; Bredent, Senden, Germany) and ThermoSens (TS; Vertex Dental B.V., Soesterberg, The Netherlands)—n = 111 per material—were equally divided into three groups (n = 37) based on different treatments and storage conditions. Test samples allocated to the “Control group” were not artificially aged and stored in water for 24 h. Both “Treatment 1 group” and “Treatment 2 group” were subjected to thermocycling, the former dehydrated and the latter stored in water between cycle-sets. Linear changes and ultimate tensile strength were measured and analyzed for storage condition and material influence on the outcome variables. A Welch ANOVA test with Games–Howell post-hoc analysis was used to compare the influence of treatments across different materials. Significant differences were found for all three included materials with p values ranging from <0.05 to <0.001 for linear dimensional changes. The magnitude of alterations varied and was large for BS (Perflex, Israel) (ω2 = 0.62) and BF (Bredent, Germany) (ω2 = 0.47) and small but significant for TS (Vertex Dental B.V., The Netherlands) (ω2 = 0.05). However, results seem to fall into clinically acceptable range. Significant differences were also observed for the ultimate tensile strength test with the same range of p-values. All three materials showed different initial ultimate tensile strengths and varying reaction to artificial aging and storage with the lowest alterations observed for BF (Bredent, Germany) (ω2 = 0.05). Within the limitation of this study, it can be concluded that all three materials show different dimensional and mechanical properties when subjected to artificial aging and different storage. Although linear dimensions show significant changes, they seem to be clinically irrelevant, whereas the change in ultimate tensile strength after only 6-month equivalent clinical use was substantial for BS (Perflex, Israel) and TS (Vertex Dental B.V., The Netherlands).
Collapse
|
5
|
Comparison of Fracture Resistance in Thermal and Self-Curing Acrylic Resins-An In Vitro Study. Polymers (Basel) 2021; 13:polym13081234. [PMID: 33920377 PMCID: PMC8069947 DOI: 10.3390/polym13081234] [Citation(s) in RCA: 5] [Impact Index Per Article: 1.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/21/2021] [Revised: 04/08/2021] [Accepted: 04/09/2021] [Indexed: 02/03/2023] Open
Abstract
Thermal and self-curing acrylic resins are frequently and versatilely used in dental medicine since they are biocompatible, have no flavor or odor, have satisfactory thermal qualities and polishing capacity, and are easy and fast. Thus, given their widespread use, their fracture resistance behavior is especially important. In this research work, we comparatively analyzed the fracture resistance capacity of thermo and self-curing acrylic resins in vitro. Materials and Methods: Five prosthesis bases were created for each of the following acrylic resins: Lucitone®, ProBase®, and Megacryl®, which were submitted to different forces through the use of the CS® Dental Testing Machine, usually mobilized in the context of fatigue tests. To this end, a point was defined in the center of the anterior edge of the aforementioned acrylic resin bases, for which the peak tended until a fracture occurred. Thermosetting resins were, on average, more resistant to fracture than self-curable resins, although the difference was not statistically significant. The thermosetting resins of the Lucitone® and Probase® brands demonstrated behavior that was more resistant to fracture than the self-curing homologues, although the difference was not statistically significant. Thermosetting resins tended to be, on average, more resistant to fracture and exhibited the maximum values for impact strength, compressive strength, tensile strength, hardness, and dimensional accuracy than self-curing resins, regardless of brand.
Collapse
|