Epoxidized natural rubber and hydrotalcite compounds: rheological and thermal characterization

Systematic Literature Review of the Effect of Layered Double Hydroxides on the Mechanical Properties of Rubber

Layered double hydroxides (LDHs) have attracted interest as reinforcing fillers in elastomers due to their ease of synthesis and customisability. A systematic review was performed on the effect of LDHs on the mechanical properties of elastomers using the Scopus database. Of the 61 articles relevant to the search criteria, the majority were published on polyurethane (PU) and nitrile butadiene rubber (NBR). Mg-Al LDH was used in most of the studies and Zn-Al LDH was used second most common. LDH can act as a reinforcing filler, typically increasing tensile strength even at low concentrations, so it could be used as an alternative to traditional reinforcing fillers for elastomers. LDH can also be made a functional filler by selecting the right metals and interlayer anions. It was found that Mg-Al LDH and Zn-Al LDH can both participate in crosslinking reactions and can replace MgO and ZnO, respectively. Less Zn ions are required for crosslinking when LDH is used than when ZnO is used, making LDH more environmentally friendly. Organic modification is usually required to improve compatibility with the elastomer matrix, especially in non-polar elastomers. It enables exfoliation of the LDH and intercalation of polymer chains into the LDH interlayer to occur. Organic modifiers can also be used to functionalise the LDH. Stearic acid used in crosslinking systems can be replaced by stearate anions from stearate-modified LDH.

Influence of the Silica Specific Surface Area and Ionic Liquids on the Curing Characteristics and Performance of Styrene-Butadiene Rubber Composites

In this work, we present the effect of silica’s specific surface area (180 m²·g⁻¹ and 380 m²·g⁻¹, respectively) on the crosslinking of styrene–butadiene rubber (SBR) composites, as well as their crosslink density and functional properties, such as thermal stability, damping behavior, resistance to thermo-oxidative aging, and tensile properties. Ionic liquids (ILs) with a bromide anion and different cations, i.e., 1-butyl-3-methylimidazolium (Bmi), 1-butyl-3-methylpyrrolidinium (Bmpyr), and 1-butyl-3-methylpiperidinium (Bmpip), were used to enhance the cure characteristics of SBR compounds and the functional properties of SBR vulcanizates. It was proven that apart from the silica’s specific surface area, the filler–polymer and filler–filler physical interactions have a significant impact on the vulcanization kinetics of silica-filled SBR composites. Additionally, the performed studies have shown that ILs positively affected the dispersion of silica’s particles and reduced their ability to form agglomerates in the elastomer matrix, which enhanced the functional properties of the SBR vulcanizates.

Influence of Fillers and Ionic Liquids on the Crosslinking and Performance of Natural Rubber Biocomposites

This work concerns the effect of fillers and ionic liquids on the cure characteristics of natural rubber (NR) compounds, as well as the mechanical and thermal properties of the vulcanizates. Three types of white filler were applied, such as cellulose, nanosized silica and hydrotalcite, to modify the performance of NR composites. Additionally, ionic liquids (ILs) with bromide anion and different cations, i.e., 1-butyl-3-methylimidazolium (Bmi) and 1-butyl-3-methylpyrrolidinium (Bmpyr), were used to improve the cure characteristics of NR compounds and functional properties of the vulcanizates. The type of filler and the structure of ILs were proved to affect the rheometric properties and cure characteristics of NR compounds as well as the performance of the NR vulcanizates. Owing to the adsorption of curatives onto the surface, silica reduced the activity of the crosslinking system, prolonging the optimal vulcanization time of NR compounds and reducing the crosslinking degree of the elastomer. However, silica-filled NR exhibited the highest thermal stability. Hydrotalcite increased the crosslink density and, consequently, the mechanical properties of the vulcanizates, but deteriorated their thermal stability. ILs beneficially influenced the cure characteristics of NR compounds, as well as the crosslink density and mechanical performance of the vulcanizates, particularly those filled with silica. Cellulose did not significantly affect the vulcanization of NR compounds and crosslink density of the vulcanizates compared to the unfilled elastomer, but deteriorated their tensile strength. On the other hand, cellulose improved the thermal stability and did not considerably alter the damping properties of the vulcanizates.