Factors affecting the bond strength of denture base and reline acrylic resins to base metal materials

Effect of Surface Textures and Fabrication Methods on Shear Bond Strength Between Titanium Framework and Auto-Polymerizing Acrylic Repair Resin

The aim of the study was to evaluate the effect of airborne particle abrasion (using different sizes of alumina particles) on the shear bond strength (SBS) between cast and milled titanium metal frameworks and auto-polymerizing acrylic repair resin. Forty flat cylindrical titanium disks were divided into two main divisions: cast and milled titanium. The two divisions were further subdivided into four groups based on metal surface treatment. Three particle sizes of aluminum oxide air abrasive powders (50µm, 110µm, and 250µm) were used for metal surface treatment by airborne particle abrasion. One group was the control group with no surface treatment. Auto-polymerizing acrylic repair resin was applied to all titanium disks. The specimens were subjected to SBS testing using a universal testing machine (Instron Corporation, Norwood, Massachusetts, United States). Surface evaluation was performed using a scanning electron microscope. One-way ANOVA was used for statistical analysis. The results showed a significant increase in SBS after airborne particle abrasion of both milled and cast titanium groups (p<0.001). The SBS was directly proportional to the size of the aluminum oxide particles. The milled titanium group showed higher SBS values than the cast group when the surface was not treated with alumina particles (p < 0.001) and when the surface was treated with the smaller particle sizes of 50 µm, whereas the cast group demonstrated higher SBS values than the milled group (p < 0.01) when the particle size was increased to 110 µm and 250 µm. It could be concluded that SBS between titanium metal frameworks and auto-polymerizing repair acrylic resin was directly related to the size of the alumina airborne particle abrasives. The fabrication method of the titanium framework also influenced the SBS as the untreated milled frameworks demonstrated favorable SBS values compared to the untreated cast frameworks.

Bonding of resin luting materials to titanium and titanium alloy

Recently in Japan, due to the increased prices of palladium and gold, cast titanium restorations have been included in the Japanese national health insurance system. The purpose of this review was to survey the available literature on titanium bonding systems, focusing on the adhesive monomer in the luting agent in order to expand the application of resin-bonded fixed prostheses made of titanium or titanium alloys. It was found that adhesive monomers are effective for bonding to titanium, and provide results equal to the procedures of silanization and tribochemical silica coating. A primer or a luting agent, including 10-methacryloyloxydecyl dihydrogen phosphate (MDP), methacryloyloxyalkyl thiophosphate derivative (MEPS), 6-methacryloxyhexyl phosphonoacetate (6-MHPA), and 4-methacryloyloxyethl trimellitate anhydride (4-META) promotes bonding characteristics between titanium and the resin material.

Evaluation of the effect of ultraviolet light polymerized clear adhesive on shear and tensile bond strength of heat cure denture base resin to the cobalt-chromium retentive minor connector: An in vitro study

Aim:

The aim of this study is to evaluate the efficacy of new material ultraviolet (UV) light polymerized clear adhesive on shear and tensile bond strength of heat cure denture base resin (Polymethylmethacrylate (PMMA)) to cobalt-chromium (Co-Cr) retentive minor connector.

Setting and Design:

Comparative evaluation- In-vitro study.

Materials and Methods:

Sixty samples of Co-Cr plates mimicking minor connectors were fabricated. Thirty samples were coated with new material UV light polymerized clear adhesive and cured under UV light source for 10 min. In gun-metal flask, metal plates were placed in the lower compartment over it. Heat cure acrylic resin was packed in the dough stage with the help of clamps and processed according to the manufacturer's instructions. Samples were kept in artificial saliva for 90 days. Shear and tensile bond strengths were calculated of each sample with a Universal testing machine, and results were statistically analyzed. Type of bond failure was observed for each sample under stereomicroscope.

Statistical Analysis Used:

Unpaired t test.

Results:

Tensile bond strength, as well as shear bond strength, showed that 0.93 N and 1.64 N respectively for without application of new adhesive was more as compared to that of samples with the application of new adhesive which is 0.75 N and 1.54 N respectively. Bond failure was found to be an adhesive failure in resin–metal interface.

Conclusions:

Excellent bonding seen between the new adhesive and acrylic interface but limited effect on the metal interface. To increase bond strength between metal and resin interface, some surface treatment with the metal surface is needed to increase the bonding of the new adhesive to the metal surface.

Shear bond strength of a denture base acrylic resin and gingiva-colored indirect composite material to zirconia ceramics

PURPOSE

To evaluate the shear bond strengths of two gingiva-colored materials (an indirect composite material and a denture base acrylic resin) to zirconia ceramics and determine the effects of surface treatment with various priming agents.

METHODS

A gingiva-colored indirect composite material (CER) or denture base acrylic resin (PAL) was bonded to zirconia disks with unpriming (UP) or one of seven priming agents (n=11 each), namely, Alloy Primer (ALP), Clearfil Photo Bond (CPB), Clearfil Photo Bond with Clearfil Porcelain Bond Activator (CPB+Act), Metal Link (MEL), Meta Fast Bonding Liner (MFB), MR. bond (MRB), and V-Primer (VPR). Shear bond strength was determined before and after 5000 thermocycles. The data were analyzed with the Kruskal-Wallis test and Steel-Dwass test.

RESULTS

The mean pre-/post-thermalcycling bond strengths were 1.0-14.1MPa/0.1-12.1MPa for the CER specimen and 0.9-30.2MPa/0.1-11.1MPa for the PAL specimen. For the CER specimen, the ALP, CPB, and CPB+Act groups had significantly higher bond strengths among the eight groups, at both 0 and 5000 thermocycles. For the PAL specimen, shear bond strength was significantly lower after thermalcycling in all groups tested. After 5000 thermocycles, bond strengths were significantly higher in the CPB and CPB+Act groups than in the other groups.

CONCLUSIONS

For the PAL specimens, bond strengths were significantly lower after thermalcycling in all groups tested. The MDP functional monomer improved bonding of a gingiva-colored indirect composite material and denture base acrylic resin to zirconia ceramics.

Allergic effects of the residual monomer used in denture base acrylic resins

Denture base resins are extensively used in dentistry for a variety of purposes. These materials can be classified as chemical, heat, light, and microwave polymerization materials depending upon the factor which starts the polymerization reaction. Their applications include use during denture base construction, relining existing dentures, and for fabrication of orthodontic removable appliances. There have been increased concerns regarding the safe clinical application of these materials as their biodegradation in the oral environment leads to harmful effects. Along with local side effects, the materials have certain occupational hazards, and numerous studies can be found in the literature mentioning those. The purpose of this article is to outline the cytotoxic consequences of denture base acrylic resins and clinical recommendations for their use.

Effect of nonthermal plasma treatment on surface chemistry of commercially-pure titanium and shear bond strength to autopolymerizing acrylic resin

The effect of nonthermal plasma on the surface characteristics of commercially pure titanium (cp-Ti), and on the shear bond strength between an autopolymerizing acrylic resin and cp-Ti was investigated. A total of 96 discs of cp-Ti were distributed into four groups (n=24): Po (no surface treatment), SB (sandblasting), Po+NTP and SB+NTP (methane plasma). Surface characterization was performed through surface energy, surface roughness, scanning microscopy, energy dispersive spectroscopy, and X-ray diffraction tests. Shear bond strength test was conducted immediately and after thermocycling. Surface treatment affected the surface energy and roughness of cp-Ti discs (P<.001). SEM-EDS showed the presence of the carbide thin film. XRD spectra revealed no crystalline phase changes. The SB+NTP group showed the highest bond strength values (6.76±0.70 MPa). Thermocycling reduced the bond strength of the acrylic resin/cp-Ti interface (P<.05), except for Po group. NTP is an effective treatment option for improving the shear bond strength between both materials.