Influence of intrapulpal pressure simulation on the bond strength of adhesive systems to dentin

Longevity of posterior direct versus indirect composite restorations: A systematic review and meta-analysis

OBJECTIVES

The goal of this systemic review and meta-analysis was to compare the longevity of direct and indirect composite restorations in posterior teeth.

DATA

Randomized controlled trials (RCT) investigating direct and indirect composite restorations in permanent posterior teeth.

SOURCES

Three electronic databases (PubMed, CENTRAL (Cochrane) and Embase) were screened. No language or time restrictions were applied. Study selection, data extraction and quality assessment were done in duplicate. Risk of bias and level of evidence was graded using Risk of Bias 2.0 tool and Grade Profiler 3.6.

RESULTS

A total of 3056 articles were found by electronic databases. Finally, five RCTs were selected. Overall, 627 restorations of which 323 were direct and 304 indirect composite restorations have been placed in 279 patients (age: 28-81 years). The highest annual failure rates (AFR) were found for indirect restorations ranging from 0 % to 15.5 %. Lower AFR were found for direct restorations ranging from 0 % to 5.4 %. The most frequent failures were found to be chipping and fracture of the restoration followed by caries. Meta-analysis revealed that the failure rate for direct restorations was significantly lower than for indirect restorations (Risk Ratio (RR) [95 %CI] = 0.61 [0.47; 0.79]; very low level of evidence). Furthermore, all studies showed a high risk of bias.

CONCLUSION

Direct and indirect composite restorations can be recommended for large class II cavities including cusp coverage in posterior teeth for single tooth restoration. Meta-analysis revealed significantly lower relative risk to fail for direct composite restorations than for indirect restorations but results are with high risk of basis.

Advanced statistical analyses to reduce inconsistencies in bond strength data focused on donor factors: A six-factor analysis using linear mixed and nonlinear regression models

PURPOSE

This study aimed to investigate the effects of the age and sex of tooth donors on dentin bond strength.

METHODS

A total of 38 extracted teeth (12 male and 26 female donors; age range: 17-82 years) were used in this study. In addition to donor age and sex, four other microtensile bond strength (μTBS) test specimen factors were evaluated: dentin position, bonding area, presence of voids at the interface, and computed tomography (CT) values of dentin. The μTBS was measured immediately (24 h) and 6 months after storage in water. After the μTBS testing, linear mixed and nonlinear regression models were used to analyze the effects of these factors on the μTBS data.

RESULTS

The results from the linear mixed model revealed that the bonding area (P = 0.02), presence of voids at the interface (P = 0.04), and storage time (P < 0.001) significantly affected bond strength. In contrast, no correlation was observed between the μ TBS and dentin position (P = 0.08) or sex (P = 0.07). The results of the nonlinear regression model with robust variance-covariance estimators revealed that age significantly affected bond strength (P < 0.001). In addition, a significant positive correlation was found between μTBS and age (P < 0.001), with nonlinearity (P = 0.002). However, no correlation was observed between the μTBS and CT values (P = 0.69) without nonlinearity (P = 0.39).

CONCLUSIONS

These findings suggest that bond strength increases with age until 60 years but not afterward.

Multifunctional Dental Adhesives Formulated with Silane-Coated Magnetic Fe3O4@m-SiO2 Core-Shell Particles to Counteract Adhesive Interfacial Breakdown

The process of bonding to dentin is complex and dynamic, greatly impacting the longevity of dental restorations. The tooth/dental material interface is degraded by bacterial acids, matrix metalloproteinases (MMPs), and hydrolysis. As a result, bonded dental restorations face reduced longevity due to adhesive interfacial breakdown, leading to leakage, tooth pain, recurrent caries, and costly restoration replacements. To address this issue, we synthesized and characterized a multifunctional magnetic platform, CHX@SiQuac@Fe3O4@m-SiO2, to provide several beneficial functions. The platform comprises Fe3O4 microparticles and chlorhexidine (CHX) encapsulated within mesoporous silica, which was silanized by an antibacterial quaternary ammonium silane (SiQuac). This platform simultaneously targets bacterial inhibition, stability of the hybrid layer, and enhanced filler infiltration by magnetic motion. Comprehensive experiments include X-ray diffraction, FT-IR, VSM, EDS, N2 adsorption-desorption (BET), transmission electron microscopy, scanning electron microscopy, thermogravimetric analysis, and UV-vis spectroscopy. Then, CHX@SiQuac@Fe3O4@m-SiO2 was incorporated into an experimental adhesive resin for dental bonding restorations, followed by immediate and long-term antibacterial assessment, cytotoxicity evaluation, and mechanical and bonding performance. The results confirmed the multifunctional nature of CHX@SiQuac@Fe3O4@m-SiO2. This work outlined a roadmap for (1) designing and tuning an adhesive formulation containing the new platform CHX@SiQuac@Fe3O4@m-SiO2; (2) assessing microtensile bond strength to dentin using a clinically relevant model of simulated hydrostatic pulpal pressure; and (3) investigating the antibacterial outcome performance of the particles when embedded into the formulated adhesives over time. The results showed that at 4 wt % of CHX@SiQuac@Fe3O4@m-SiO2-doped adhesive under the guided magnetic field, the bond strength increased by 28%. CHX@SiQuac@Fe3O4@m-SiO2 enhanced dentin adhesion in the magnetic guide bonding process without altering adhesive properties or causing cytotoxicity. This finding presents a promising method for strengthening the tooth/dental material interface's stability and extending the bonded restorations' lifespan.

Back to the multi-step adhesive system: A next-generation two-step system with hydrophobic bonding agent improves bonding effectiveness

This study evaluated the bonding effectiveness of a newly developed two-step hydrophobic bonding material. Three groups using different bonding systems were compared: BZF group, using the new bonding system (BZF-29; GC, Tokyo, Japan); GPB group, using a one-step bonding system (G-Premio Bond; GC); and SE2 group, using a two-step bonding system (CLEARFIL SE Bond 2; Kuraray Noritake Dental, Tokyo, Japan). Microtensile bond strength (µTBS) was measured after storage in water for 24 h, 3 months and 6 months (n=25/group). Fracture surfaces were observed under scanning electron microscopy. The BZF group showed significantly higher µTBS than the other groups (p<0.001). Dominant failure patterns were cohesive failure for the BZF group (48-84%), mixed failure for the SE2 group (48-60%) and interface failure between adhesive and resin composite for the GPB group (48-52%). The hydrophobicity of the BZF-29 bonding system improves the long-term bonding effectiveness between adhesive and resin composite.

The effect of vitality and dentin depth on resin tags length of resin-dentin interface in dogs' teeth

The aim of this study was to evaluate the effect of pulpal pressure and dentin depth on the quality of hybrid layer of bonded composite. Four healthy dogs, aged between 12 and 18 months, with intact dentitions were used for the experimental work. A total of 24 teeth were available for the study by using the six upper anterior teeth of each of the four dogs used in the study. The 24 teeth included in the study were divided according to presence or absence of pulpal pressure (P) into two groups with 12 teeth in each group. P₁ teeth with positive pulpal pressure and P₂ teeth with no pulpal pressure. Each of these two groups was further divided into two subgroups, according to the cavity depth (D) they received, where in D₁ a class V cavity with depth of 1 mm was performed, while in D₂ a class V cavity with depth of 2 mm was performed. The cavities were restored with micro hybrid composite restorative material and the samples were then left in the dogs’ mouth for 30 days. At the end of the experimental period, the dogs were euthanized by injecting an overdose of thiopental sodium. The anterior part of the upper jaw was sawed out of each dog’s mouth and the teeth were sectioned to evaluate the resin–dentin interface using Environmental Scanning Electronic Microscope. Results of the study showed that the mean resin tag length value was significantly affected by vitality and dentin depth. The presence of pulpal pressure together with depth of dentin could adversely affect the quality of hybridization.

Universal dental adhesives: Current status, laboratory testing, and clinical performance

Increasing demand for simplified and user-friendly adhesive systems has led to the development of a new class of adhesives termed as Universal Adhesives (UAs). The term "Universal" reflects manufacturers' claims that these adhesives can be applied with any adhesion strategy and offer the versatility of use with a variety of direct and indirect restorative materials. The aim of this review was to synthesize the literature regarding the current status of UAs, their adhesion potential to various substrates and their performance in different restorative situations. In vitro studies, clinical trials and systematic reviews were identified utilizing controlled vocabulary and keyword searches in Medline and EMBASE databases. About 282 studies (272 in vitro studies; 11 clinical studies) were included. Available laboratory and clinical evidence does not support the claim that UAs can be used with any adhesive strategy. Although, they can chemically bond to various tooth and direct/indirect restorative substrates, the stability of this bond is material-dependent and subject to hydrolytic degradation. Hence, additional measures are still needed to ensure long-term durability. which undermines the versatility of UAs. The lack of long-term data regarding the clinical performance of UAs further complicates clinical decision-making. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 2121-2131, 2019.

Application of Calcium Silicate Materials After Acid Etching May Preserve Resin-Dentin Bonds

INTRODUCTION

The aim of the present study was to evaluate the effect of the application of calcium silicate materials (CSMs), after acid etching, on the longevity of the hybrid layer and marginal adaptation of composite restorations.

METHODS AND MATERIALS

Eighty human permanent molars received an intrapulpal pressure of 15 cm H₂O. Sixty teeth received a mesial proximal slot preparation with the gingival margin extending 1 mm below the cemento-enamel junction. The samples were divided into two groups. Group 1 received restorations using two types of etch-and-rinse adhesives: ethanol based (Single Bond, 3M ESPE, St Paul, MN, USA) and acetone based (Prime & Bond NT, Dentsply, DeTrey GmbH, Germany). In group 2 samples, a commercially available CSM (ProRoot MTA) was allowed to set before grinding and placing into a distilled water solution. This solution was applied on the cavity floor after acid etching. The surface was washed after 30 seconds followed by application of adhesives and restorations as in group 1. The samples were stored in phosphate-buffered saline for six months, maintaining the intrapulpal pressure. An epoxy replica was made, and the marginal adaptation was evaluated using scanning electron microscopy. The percentage of continuous margin (CM) was recorded for each group. Another 20 samples were used for hybrid layer evaluation. The crowns were ground to expose dentin. Intrapulpal pressure was applied. The samples were divided into two groups and restored similar to samples restored for marginal adaptation evaluation. The samples were longitudinally cut in 1-mm slices. The slices were stored under 15 cm of phosphate-buffered saline to simulate the pulpal pressure. After six months, the adhesive interface was evaluated using a scanning electron microscope. Statistical analysis was done with two-way analysis of variance with Holm-Sidak's correction for multiple comparisons.

RESULTS

Application of CSMs improved the marginal adaptation values in both adhesive groups. In group 1, there were areas of incomplete penetration of resins along with evidence of partial degradation of resin tags. Samples receiving CSM application after acid etching demonstrated long and regular resin tags with very few signs of degradation.

CONCLUSIONS

Application of CSMs after acid etching can be a potential avenue in preserving the resin-dentin bonds.

Influence of dentin thickness on intrapulpal temperature under simulated pulpal pressure during Nd:YAG laser irradiation

The aim of this study was to evaluate the effects of dentin thickness and pulpal pressure simulation (PPS) on the variation of intrapulpal temperature (∆T) when submitted to an adhesive technique using laser irradiation. Sixty sound human molars were sectioned and randomly divided into two groups (n = 30): group 1-1 mm of dentin thickness; group 2-2 mm of dentin thickness. Each group was divided into two subgroups (n = 15): subgroup A-absence of PPS; subgroup P-presence of PPS (15 cm H₂O), sequentially treated with the following: 37 % phosphoric acid, adhesive system (Adper Single Bond), irradiation with Nd:YAG laser (1064 nm, 10 Hz, 60 s) using 60, 80, and 100 mJ/pulse energy parameters and light-curing (10 s). The ∆T was evaluated during the laser irradiation with a digital thermometer. Data were analyzed by three-way ANOVA and Tukey tests (p < 0.05). Three-way ANOVA revealed no significant differences for dentin thickness (p = 0.6512) on ∆T. PPS significantly reduced ∆T (p = 0.0001). The laser energy parameters (p = 0.0027) indicated that 100 mJ presented with significantly greater ∆T when compared to the groups irradiated with 80 and 60 mJ. Dentin thickness did not affect ∆T. The presence of PPS reduced the mean temperature values. The Nd:YAG laser energy parameters had a negative influence on the variation of temperature in the absence of PPS. In the presence of PPS, there was no risk to the pulp, since this study obtained temperature increases below 5.5 °C for all energy parameters, showing the technical viability for in vivo conditions.

Prolonged curing time reduces the effects of simulated pulpal pressure on the bond strength of one-step self-etch adhesives

The aim of this study was to evaluate the effects of extended light-curing procedures on the microtensile bond strength (μTBS) of one-step self-etch adhesives (1-SEAs) submitted to simulated pulpal pressure. Coronal deep-dentin specimens were bonded using Clearfil S3 Bond (S3), Adper Easy Bond (EB), or G-Bond Plus (GB) following the manufacturers' recommendations and light-cured for 10 seconds or 40 seconds. The dentin-bonded specimens were stored in distilled water for 24 hours without pulpal pressure (control) or submitted to 20 cm H2O simulated pulpal pressure for 24 hours. The specimens were cut into matchsticks and subjected to μTBS testing. The data were statistically analyzed using the three-way analysis of variance and Tukey's tests (p<0.05). Debonded sticks were investigated through scanning electron microscopy. EB obtained higher bond strengths than GB and S3. However, prolonged light activation (40 seconds) provided higher μTBS for all adhesives when submitted to pulpal pressure. Conversely, pulpal pressure caused a drop in μTBS in EB and S3 when light-cured for 10 seconds. A mixed failure mode was mainly attained for the control groups, whereas the specimens submitted to pulpal pressure failed in the adhesive mode. The μTBS of GB was not affected by pulpal pressure when light-cured for 10 seconds. Adhesive was the most prevalent failure mode, except when light-cured for 40 seconds, which showed predominantly cohesive failure. Extended curing times improved the resistance of 1-SEAs to simulated pulpal pressure.

Bonding efficacy of an acetone/based etch-and-rinse adhesive after dentin deproteinization

Objectives: to evaluate the effect of sodium hypochlorite (NaOCl) treatment on dentin bonding by means of shear bond strength (SBS) measurements when using Prime&Bond NT (PB NT) adhesive. Ultrastructure of the interfaces was examined by scanning electron microscopy (SEM). Study design: Extracted human third molars were sectioned and ground to expose flat surfaces of superficial or deep dentin. Specimens were randomly assigned to two equal groups, and bonded as follows: (1) according to the manufacturers’ directions, after 35% H3PO4 etching, (2) 5% NaOCl treated for 2 minutes, after 35% H3PO4 etching. Each sample was embedded in a Watanabe shear test assembly for a single plane lap shear. After PB NT bonding, specimens were stored in water for 24 h at 37ºC and thermocycled (500x). Samples were tested in shear to failure using a universal testing machine at 0.75 mm/min. Data were analyzed with ANOVA and Newman-Keuls multiple comparison test procedures. Two samples of each group were randomly selected to investigate the morphologic aspect of the resin/dentin interface with SEM. Results: After etching and after aqueous sodium hypochlorite (NaOClaq) application, SBS values were similar on superficial than deep dentin (p>0.05). SEM findings shows for H3PO4 etching conditioned samples a detectable hybrid layer and long resin tags; for NaOCl treated specimens, it may be observed a non apparent hybrid layer, and the adhesive contact directly with the neck of the cylindrical resin tags. Conclusions: The use of 5% NaOCl for 2 min after dentin demineralization when PB NT was employed did not improve the bond strength to dentin, probably due to nanofiller content and/or oxidative changes on collagen-depleted dentin.

Key words:Sodium hypochlorite, shear bond strength, SEM, Prime&Bond NT, superficial dentin, deep dentin.

Evaluation of tooth-fragment reattachment: a clinical and laboratory study

PURPOSE

To evaluate the restoration of fractured teeth by reattaching tooth fragment to its tooth remnant in a group of children and adolescents, and to compare the results with those of a laboratory study.

MATERIALS AND METHODS

The clinical study was conducted on 43 fractured incisors: 22 uncomplicated crown fractures (Group A) and 21 complicated crown fractures (Group B). The 43 incisal fragments: 23 were kept dry for 47 h and 20 were kept wet for 24 h by the patients before they were reattached. The fragments were kept in 0.9% saline solution for 30 min before reattachment. The fragments in Group A were reattached using a dentin bonding agent, a flowable and a hybrid resin composite, whereas the fragments in Group B were reattached to the tooth remnant after a pulpotomy was performed. The laboratory study was conducted on 56 extracted incisors. Teeth were divided equally into four groups: Group I - Uncomplicated crown fracture + wet medium; Group II - Uncomplicated crown fracture + dry medium; Group III - Complicated crown fracture + wet medium, and Group IV - Complicated crown fracture + dry medium. The fragments were then reattached in a manner that was similar to that used in the clinical study. The restored teeth were then re-fractured. All data were analyzed statistically.

RESULTS

In the clinical study, the restored teeth were followed up for 2 years. Neither the type of trauma nor the storage medium had any significant effect on the survival, color, and bond strength of the restored teeth when assessed in the clinical and laboratory study. The color disharmony that was encountered initially in restored teeth resolved significantly on its own accord within 12 months after reattachment of the fragment.

CONCLUSION

Fragment reattachment can be used to treat fractured teeth successfully in children and adolescents.

Direct comparison of the bond strength results of the different test methods: a critical literature review

OBJECTIVE

The goal of this paper is to undertake a literature search collecting all dentin bond strength data obtained for six adhesives with four tests (shear, microshear, tensile and microtensile) and to critically analyze the results with respect to average bond strength, coefficient of variation, mode of failure and product ranking.

METHOD

A PubMed search was carried out for the years between 1998 and 2009 identifying publications on bond strength measurements of resin composite to dentin using four tests: shear, tensile, microshear and microtensile. The six adhesive resins were selected covering three step systems (OptiBond FL, Scotch Bond Multi-Purpose Plus), two-step (Prime & Bond NT, Single Bond, Clearfil SE Bond) and one step (Adper Prompt L Pop).

RESULTS

Pooling results from 147 references showed an ongoing high scatter in the bond strength data regardless which adhesive and which bond test was used. Coefficients of variation remained high (20-50%) even with the microbond test. The reported modes of failure for all tests still included high number of cohesive failures. The ranking seemed to be dependant on the test used.

SIGNIFICANCE

The scatter in dentin bond strength data remains regardless which test is used confirming Finite Element Analysis predicting non-uniform stress distributions due to a number of geometrical, loading, material properties and specimens preparation variables. This reopens the question whether, an interfacial fracture mechanics approach to analyze the dentin-adhesive bond is not more appropriate for obtaining better agreement among dentin bond related papers.