Cavity preparation machine for the standardization of in vitro preparations

Impact of refrigeration of different Resin composite restorative materials on the marginal adaptation in class II restorations

BACKGROUND

The pre-polymerization temperature of resin composite restorative materials could influence their adaptation to cavity details. As a current debate is existing about the refrigeration of resin composite restorative materials, this study was designed to assess the effect of refrigeration of 3 types of resin composite restorative materials with different matrix systems on their marginal adaptation in Class II restorations.

METHODS

Forty-two sound maxillary molars, each with two separated Class II cavities, were used in this study. The teeth were assigned into 3 main groups (n = 14) according to the restorative /adhesive system used; an Ormocer-based composite (Admira Fusion/Futurabond M+, Voco GmbH, Cuxhaven, Germany), a methacrylate modified Ormocer-based (Ceram.X SphereTEC One/Prime&Bond Universal, Dentsply Sirona GmbH Konstanz, Germany), and a methacrylate-based (Tetric N-Ceram/Tetric N-Bond Universal, Ivoclar Vivadent AG, Schaan, Liechtenstein). Each group was then divided into 2 subgroups (n = 14) according to the gingival margin location; 1 mm above and 1 mm below the cemento-enamel junction (C.E.J). Each subgroup was further divided into 2 categories (n = 7) according to the storage temperature; stored at room temperature or stored in refrigerator at 4°- 5° C. Epoxy resin replicas were observed under scanning electron microscope (SEM) to examine the marginal gaps. A gab scoring system was used to assess the marginal adaptation of each restoration by giving scores on the basis of measurements of the maximum marginal gaps. The data obtained were statistically analyzed using the Chi-square test at a significance level of p < 0.05.

RESULTS

None of the tested groups exhibited 100% gap-free margins irrespective of margin location or storage temperature. For both storage temperatures, no statistically significant difference was observed among all tested groups either with margins located above or below C.E.J (p > 0.05). As well, there was no statistically significant difference when comparing both marginal locations for each material (p > 0.05). Regarding the effect of storage temperature, statistically significant difference was only observed between the room-temperature stored groups with margins located above C.E.J and their corresponding groups stored in refrigerator (p < 0.05).

CONCLUSION

The refrigeration of resin composite restorative materials prior to the restorative procedures revealed a deleterious effect on marginal adaptation of the restorations with margins located in enamel regardless the type of material used.

Effect of the Sample Preparation and Light-curing Unit on the Microhardness and Degree of Conversion of Bulk-fill Resin-based Composite Restorations

OBJECTIVE

To evaluate the effect of the sample preparation and light-curing units (LCUs) on the Knoop hardness (KH, N/mm2) and degree of conversion (DC, %) of bulk-fill resin-based composite restorations.

METHODS

Two molds were made using human molar teeth embedded in acrylic resin. One was a conventional tooth mold where the molar received a mesio-occluso-distal (MOD) preparation. In the other, the tooth was sectioned in three slices (buccal, middle, and lingual). The center slice received a MOD preparation similar to the conventional mold. Both tooth molds were placed in the second mandibular molar position in a Dentoform with a 44-mm interincisal opening. Restorations were made using Opus Bulk Fill (FGM) high viscosity bulk-fill resin-based composite (RBC) and light cured using two different lights: VALO Cordless (Ultradent) and Bluephase G2 (Ivoclar Vivadent). The RBC was placed in one increment that was light-cured for a total of 80 seconds (40 seconds at the occluso-mesial and occluso-distal locations). The RBC specimens were then prepared as follows: EmbPol - tooth mold specimen was embedded in polystyrene resin and polished before testing; Pol - tooth mold specimen was not embedded, but was polished before testing; NotPol - sectioned tooth mold, specimen not embedded nor polished before testing. The KH was measured in different depths and regions of the specimens, and the DC was measured using Raman spectroscopy.

RESULTS

The results were analyzed using a 2-way analysis of variance (ANOVA) or repeated measures followed by the Tukey posthoc test (α=0.05). The preparation method (p<0.001), depth of restoration (p<0.001), and the interaction between method and depth (p=0.003) all influenced the KH values. Preparation method (p<0.001), tooth region (p<0.001), and the interaction between method and tooth region (p=0.002) all influenced DC values. The KH values were reduced significantly from the top to the bottom of the restorations and also at the proximal box when compared with the occlusal region. This outcome was most significant in the proximal boxes. The NotPol method was the most effective method to detect the effect of differences in KH or DC within the restoration. A lower DC and KH were found at the gingival regions of the proximal boxes of the restorations. When the KH and DC values were compared, there were no significant differences between the LCUs (KH p=0.4 and DC p=0.317).

CONCLUSION

Preparation methods that embedded the samples in polystyrene resin and polished the specimens reduced the differences between the KH and DC values obtained by different preparation techniques. The NotPol method was better able to detect differences produced by light activation in deeper areas.

Flowable fiber-reinforced versus flowable bulk-fill resin composites: Degree of conversion and microtensile bond strength to dentin in high C-factor cavities

OBJECTIVES

To compare flowable fiber-reinforced and flowable bulk-fill resin composites regarding their degree of conversion (DC) and microtensile bond strength (μTBS) to dentin in high C-factor class I cavities.

MATERIALS AND METHODS

One flowable fiber-reinforced (EverX Flow, GC) and two flowable bulk-fill composites (SDR, Dentsply, and Tetric N-flow Bulk fill, Ivoclar Vivadent) were tested. Regarding DC, 10 cylindrical-shaped specimens were prepared from each material (N = 30), measured using Fourier-Transform Infrared Spectroscopy (FTIR). Regarding µ TBS , class I cavities (4.5 × 4.5 × 3) were prepared on flat dentin surfaces of 30 molars, divided into three equal groups, restored with the three restorative materials, thermocycled, sectioned to create 1 mm × 1 mm cross-sectional beams, then tested using a universal testing machine. Failure mode was assessed using a stereomicroscope. Two-way ANOVA and Tukey's HSD post-hoc tests were used in DC, while One-way ANOVA was used for µ TBS .

RESULTS

The used materials showed statistically significant differences in DC with the fiber-reinforced composite having the highest value. No statistically significant differences were found between the materials regarding their µ TBS .

CONCLUSIONS

Flowable fiber-reinforced composite provided the most DC performance compared to the flowable bulk-fill composites. The three used restorative materials provided comparable bonding ability to dentin in high C-factor cavities.

CLINICAL SIGNIFICANCE

Flowable fiber-reinforced resin composite is preferred as a dentin-replacement material in high-stress bearing areas. However, both flowable fiber-reinforced and bulk-fill resin composites are equally effective in bonding to dentin in high C-factor cavities.

Effects of Adjacent Tooth Type and Occlusal Fatigue on Proximal Contact Force of Posterior Bulk Fill and Incremental Resin Composite Restoration

OBJECTIVES

To measure the proximal contact force in newtons (N) between incremental and bulk fill class II resin composite restorations and implant molar teeth or adjacent premolar teeth with simulated periodontal ligament.

METHODS

The model used was created with a typodont first molar tooth with two bilateral occlusal-proximal class II cavities, an adjacent tooth simulating an implanted molar tooth (Titamax CM, Neodent, Curtiba, PR, Brazil) and a premolar with simulated periodontal ligament. Two resin composite restorative techniques were used: Inc-Z350XT, (Filtek Z350, 3M Oral Care, St. Paul, MN, USA) inserted incrementally and Bulk-OPUS, (Opus Bulk Fill APS, FGM, Joinville, SC, Brazil) high viscosity bulk fill resin composite (n=10). As a control, a typodont having intact teeth without restorations was used. After the restorative procedure, each specimen was radiographed using a digital system (Dürr Dental, Bietigheim-Bissingen, Germany). The proximal contact force (N) was measured using dental floss with a microtensile machine (Microtensile ODEME, Luzerna, SC, Brazil). The specimens were then subjected to mechanical fatigue cycling to simulate 5 years of aging. All the parameters were measured after aging. The X-rays were blindly qualitatively analyzed by two operators to identify the loss of proximal contact. One-way ANOVA was used for comparing the initial contact force between restored and intact teeth. Two-way ANOVA followed by Tukey testing was performed for contact area data and for the contact force/contact area ratio. The proximal contact force data were analyzed using one-way repeated measurement ANOVA followed by Tukey testing (α=0.05). The X-ray proximal contact analyses were described by the frequency.

RESULTS

The initial proximal contact force was similar for intact and restored teeth. The contact force and contact area with the molar were significantly higher than with the premolar; however the contact force/contact area ratio was similar for all tested groups. The bulk fill technique showed a contact force similar to the incremental filling technique. Fatigue resulted in a significant reduction in the proximal contact force (p<0.001), irrespective of the region analyzed or restorative material used. The digital X-rays detected no alteration in the proximal contact after occlusal fatigue.

CONCLUSIONS

Larger contact area resulted in higher proximal contact force. Proximal contact force decreased with 5 years of simulated occlusal fatigue. The bulk fill technique showed a proximal contact force similar to that of the incremental filling technique.

Impact of Resin Composite Viscosity and Fill-technique on Internal Gap in Class I Restorations: An OCT Evaluation

The aim of this in vitro study was to quantitatively evaluate the internal gap of resin composites of high-and low-viscosity used in single- and incremental-fill techniques in Class I cavities exposed to thermal cycling (TC) using optical coherence tomography (OCT). Cavities of 4-mm depth and 3-mm diameter were prepared in 36 third molars randomly distributed into four groups, according to viscosity of restorative resin-based composite (high or low viscosity, all from 3M Oral Care) and technique application (bulk or incremental fill) used (n=9): RC, high-viscosity, incremental-fill, resin-based composite (Filtek Z350 XT Universal Restorative); BF, high-viscosity, bulk-fill, resin-based composite (Filtek One Bulk Fill); LRC, low-viscosity, incremental-fill, resin-based composite (Filtek Z350 XT Flowable Universal Restorative); and LBF, low-viscosity, bulk-fill, resin-based composite (Filtek Flowable Restorative). Single Bond Universal Adhesive system (3M Oral Care) was used in all the experimental groups. The incremental-fill technique was used for RC and LRC groups (2-mm increments), and a single-layer technique was used for BF and LBF groups, as recommended by the manufacturer. The internal adaptation of the resin at all dentin walls was evaluated before and after TC (5000 cycles between 5°C and 55°C) using OCT images. Five images of each restored tooth were obtained. Images were analyzed using ImageJ software that measured the entire length of the gaps at the dentin-restoration interface. The length of gaps (μm) was analyzed using two-way repeated measures ANOVA and the Tukey tests (α=0.05). There was a significant interaction between material types and TC (p=0.006), and a significant difference among all material types (p<0.0001), before and after TC (p<0.0001). Increased internal gaps at the dentin-restoration interface were noticed after TC for all groups. RC presented the lowest value of internal gap before and after TC, while LBF showed the highest values of internal gap after TC. In conclusion, TC negatively affected the integrity of internal gap, whereas high-viscosity, incremental-fill, resin-based composite presented better performance in terms of internal adaptation than low-viscosity, bulk-fill materials in Class I cavities.

Impact of the Porosity from Incremental and Bulk Resin Composite Filling Techniques on the Biomechanical Performance of Root-Treated Molars

OBJECTIVES

To analyze the effect of the porosity caused by incremental and bulk resin composite filling techniques using low- and high-viscosity composite resins on the biomechanical performance of root-treated molars.

METHODS

Forty intact molars received standardized mesio-occlusal-distal (MOD) cavity preparation, were root treated, and randomly divided into four groups with different filling techniques (n=10). The first involved two incremental filling techniques using VIT/Z350XT, a nanofilled composite resin (Filtek Z350XT, 3M ESPE) associated with a resinmodified glass ionomer cement, and resin-modified glass ionomer cement (RMGIC; Vitremer, 3M ESPE) for filling the pulp chamber. The second involved TPH/VIT, a microhybrid composite resin TPH3 Spectrum associated with Vitremer. The third and fourth involved two bulk-fill composite resins: SDR/TPH, a low-viscosity resin composite (Surefill SDR flow, Dentsply) associated with TPH3 Spectrum, and POST, a high-viscosity bulkfill resin composite (Filtek Bulk Fill Posterior, 3M ESPE). The volume of the porosity inside the restoration was calculated by micro-CT. The cusp deformation caused by polymerization shrinkage was calculated using the strain-gauge and micro-CT methods. The cusp deformation was also calculated during 100 N occlusal loading and loading to fracture. The fracture resistance and fracture mode were recorded. Data were analyzed by one-way analysis of variance and Tukey test. The fracture mode was analyzed by the χ2 test. The volume of the porosity was correlated with the cusp deformation, fracture resistance, and fracture mode (α=0.05).

RESULTS

Incremental filling techniques associated with RMGIC resulted in a significantly higher porosity than that of both bulk-fill techniques. However, no significant difference was found among the groups for the fracture resistance, fracture mode, and cusp deformation, regardless of the measurement time and method used. No correlation was observed between the volume of the porosity and all tested parameters.

CONCLUSIONS

The porosity of the restorations had no influence on the cuspal deformation, fracture resistance, or fracture mode. The use of the RMGIC for filling the pulp chamber associated with incremental composite resins resulted in similar biomechanical performance to that of the flowable or regular paste bulk-fill composite resin restorations of root-treated molars.

Detection of Simulated Periapical Lesion in Intraoral Digital Radiography with Different Brightness and Contrast

Objective:

To assess the detection of simulated periapical lesions in digital intraoral radiography with different levels of brightness and contrast combinations, and to investigate the observers’ preference of image quality for this diagnostic task.

Methods:

Digital radiographs were acquired prior to periapical lesion simulation and after each one of four defects enlargement. Original images were adjusted in 4 brightness and contrast combinations. Five observers evaluated the images according to the presence of periapical lesion on a 5-point scale. In a second moment, the observers ordinated the images subjectively, according to quality, from the best to the worst to detect the bone defect. The area under the receiver operating characteristic curve was calculated for the diagnostic values and compared by two-way ANOVA. The significance level was set at 5% (P<0.05).

Results:

No differences were found between the diagnostic values of the five combinations of brightness and contrast (P>0.05). The overall results showed low values of area under the Receiver Operating Characteristic (ROC) curve and sensitivity of the periapical radiography in the detection of periapical lesions of sizes from 1 to 3, which rose substantially in size 4. For image quality, combinations with the lowest brightness and highest contrast were preferred by the observers in 58% of the cases.

Conclusion:

Brightness and contrast adjustments do not influence the detection of simulated periapical lesions in digital intraoral radiography. Lower brightness and higher contrast images were preferred for this diagnostic task.

Effect of brightness and contrast variation for detectability of root resorption lesions in digital intraoral radiographs

OBJECTIVES

To evaluate the performance of periapical radiography assessed under different radiographic brightness and contrast variations in the detection of simulated internal (IRR) and external (ERR) root resorption lesions. Additionally, observers' preferences related to image quality for these diagnostic tasks were evaluated.

METHODS

Thirty single-root teeth were divided into two groups (n = 15): IRR, in which lesions were simulated using mechanical and biochemical processes; and ERR, in which cavities standardized with drills of different sizes were performed on the root surfaces. Digital radiographs were obtained and subsequently adjusted in 4 additional combinations, resulting in 5 brightness/contrast variations (V1-V5). Five radiologists evaluated the radiographs. The observers' preference on the image quality was also recorded.

RESULTS

For both conditions, there were no differences in the accuracy and specificity between the five brightness/contrast variations (p > 0.05), but the sensitivity for ERR was significantly lower in V4 (+ 15% brightness/-15% contrast) in the large size (p < 0.05). The observers classified V2 (- 15% brightness/+15% contrast) as the "best" image quality for IRR and ERR evaluation.

CONCLUSIONS

For IRR and ERR lesions, brightness and contrast variation does not affect the diagnostic performance of digital intraoral radiography within the tested range. The observers prefer images with a reasonable decrease in brightness and increase in contrast.

CLINICAL RELEVANCE

Brightness and contrast enhancement tools are commonly applied in digital radiographic assessment. The use of these tools for detection of root resorptions can be applied according to the observer preference without influence on diagnostic accuracy.

Effect of cavity preparation design and ceramic type on the stress distribution, strain and fracture resistance of CAD/CAM onlays in molars

Objective

This study aimed to evaluate the effect of the cavity preparation and ceramic type on the stress distribution, tooth strain, fracture resistance and fracture mode of human molar teeth restored with onlays.

Material and Methods

Forty-eight molars were divided into four groups (n=12) with assorted combinations of two study factors: BL- conventional onlay preparation with boxes made from leucite ceramic (IPS-Empress CAD, Ivoclar Vivadent); NBL- conservative onlay preparation without boxes made from leucite ceramic; BD- conventional onlay preparation with boxes made from lithium disilicate glass ceramic (IPS e.max CAD, Ivoclar Vivadent); NBL- conservative onlay preparation with boxes made from lithium disilicate glass ceramic cuspal deformation (µS) was measured at 100 N and at maximum fracture load using strain gauge. Fracture resistance (N) was measured using a compression test, and the fracture mode was recorded. Finite element analysis was used to evaluate the stress distribution by modified von Mises stress criteria. The tooth strain and fracture resistance data were analyzed using the Tukey test and two-way ANOVA, and the fracture mode was analyzed by the chi-square test (α=0.05).

Results

The leucite ceramic resulted in higher tooth deformation at 100 N and lower tooth deformation at the maximum fracture load than the lithium disilicate ceramic (P<0.001). The lithium disilicate ceramic exhibited higher fracture resistance than the leucite ceramic (P<0.001). The conservative onlay resulted in higher fracture strength for lithium disilicate ceramic. Finite element analysis results showed the conventional cavity preparation resulted in higher stress concentration in the ceramic restoration and remaining tooth than the conservative onlay preparation. The conservative onlays exhibited increased fracture resistance, reduced stress concentration and more favorable fracture modes.

Conclusion

Molars restored with lithium disilicate CAD-CAM ceramic onlays exhibited higher fracture resistance than molars restored with leucite CAD-CAM ceramic onlays.

Effect of selective carious tissue removal on biomechanical behavior of class II bulk-fill dental composite restorations

OBJECTIVES

This study aimed to develop a method to induce carious lesions in the pulpal floor dentin of a class II cavity preparation, and to determine the effects of this carious lesion on the biomechanical behavior of the dental composite restoration.

METHODS

The pulpal floor dentin of class I cavities in sound third molars were demineralised with acetic acid for 35days followed by a 7-day exposure to pooled human saliva biofilm and demineralization was verified by micro-CT. Subsequently, the proximal walls were removed forming a class II cavity and the caries lesion was left intact or was completely removed prior to restoration with a bulk-fill dental composite (n=10). Cuspal deflection was assessed by strain-gauge and micro-CT imaging. The presence of enamel cracks was assessed by transillumination before and after restoration, and again after 1,200,000 cycles of mechanical fatigue in a chewing simulator. Finally, resistance to fracture by axial compressive loading and failure mode was determined. Data were analyzed by 2-way repeated measures ANOVA, Fisher's exact test, and t-test (α=0.05).

RESULTS

The presence of carious lesions had no significant effect upon cuspal deflection, formation of enamel cracks, and fracture strength of the dental composite restorations. The restorative procedure increased the number of enamel cracks, which was not affected by mechanical cycling.

SIGNIFICANCE

Maintaining carious lesions does not affect the biomechanical behavior of class II restorations performed with bulk-fill dental composite.

Diagnostic performance of cone beam computed tomography in assessing peri-implant bone loss: A systematic review

OBJECTIVES

To evaluate the diagnostic performance of cone beam computed tomography (CBCT) in the assessment of peri-implant bone loss and analyze its influencing factors.

MATERIALS AND METHODS

Clinical and preclinical studies reporting diagnostic outcomes of CBCT imaging of peri-implant bone loss compared to direct reference measurements were sought by searching five electronic databases, PubMed, MEDLINE, EMBASE, Web of Science, and CINAHL Plus, and OpenGrey. QUADAS-2 criteria were adapted for quality analysis of the included studies. A qualitative synthesis was performed. Two meta-analysis models (random-effects and mixed-effects) summarized the area under receiver operating characteristic (AUC) curve observations reported in the selected studies. The mixed-effects meta-analysis model evaluated three possible influencing factors, "defect type," "defect size," and "study effect."

RESULTS

The initial search yielded 3,716 titles, from which 18 studies (13 in vitro and 5 animal) were included. Diagnostic accuracy of CBCT was fair to excellent in detecting in vitro circumferential-intrabony and fenestration defects, but moderate to low for peri-implant dehiscences, and tended to be higher for larger defect sizes. Both, over- and underestimation of linear measurements were reported for the animal models. The meta-analyses included 37 AUC observations from eight studies. The random-effects model showed significant heterogeneity. The mixed-effects model exhibited also significant but lower heterogeneity, and "defect type" and "study effect" significantly influenced the variability of AUC observations.

CONCLUSION

In vitro, CBCT performs well in detecting peri-implant circumferential-intrabony or fenestration defects but less in depicting dehiscences. Influencing factors due to other site-related and technical parameters on the diagnostic outcome need to be addressed further in the future studies.

Diagnostic accuracy of phosphor plate systems and conventional radiography in the detection of simulated internal root resorption

OBJECTIVE

To evaluate the performance of conventional radiography and photostimulable phosphor (PSP) plate in the detection of simulated internal root resorption (IRR) lesions in early stages.

MATERIALS AND METHODS

Twenty single-rooted teeth were X-rayed before and after having a simulated IRR early lesion. Three imaging systems were used: Kodak InSight dental film and two PSPs digital systems, Digora Optime and VistaScan. The digital images were displayed on a 20.1″ LCD monitor using the native software of each system, and the conventional radiographs were evaluated on a masked light box. Two radiologists were asked to indicate the presence or absence of IRR and, after two weeks, all images were re-evaluated. Cohen's kappa coefficient was calculated to assess intra- and interobserver agreement. The three imaging systems were compared using the Kruskal-Wallis test.

RESULTS

For interexaminer agreement, overall kappa values were 0.70, 0.65 and 0.70 for conventional film, Digora Optima and VistaScan, respectively. Both the conventional and digital radiography presented low sensitivity, specificity, accuracy, positive and negative predictive values with no significant difference between imaging systems (p = .0725).

CONCLUSIONS

The performance of conventional and PSP was similar in the detection of simulated IRR lesions in early stages with low accuracy.

Radiopacity and Porosity of Bulk-fill and Conventional Composite Posterior Restorations—Digital X-ray Analysis

Objectives:

To compare radiopacity and porosity as expressed by the presence of voids in restorations carried out using bulk-fill and incremental filling techniques to restore large mesio-occlusal-distal (MOD) cavities.

Methods:

Fifty-five molars with MOD preparations were incrementally filled with Filtek Z-350XT (Z350XT) or bulk-fill composite: Filtek Bulk Fill/Z-350XT (FBF/Z350XT), Venus Bulk Fill/Charisma Diamond (VBF/CHA), SDR/Esthet-X HD (SDR/EST-X), Tetric EvoCeram Bulk Fill (TEC). Digital radiographic images (Vistascan scanner) were taken of restored molars and analyzed at the gingival and isthmus floors. Radiodensity measurements were performed using standardized points symmetrically distributed over each region of composite and tooth structure. Three calibrated evaluators visually assessed the presence of voids. Confidence intervals were calculated, and data were analyzed using analysis of variance and χ2 tests.

Results:

TEC and VBF/CHA showed significantly higher radiodensities, while the lowest values were observed for FBF/Z350XT and Z350XT. Radiodensity at the cervical regions tended to be greater than that found at the isthmus floor. The lowest incidence of voids was found for VBF/CHA, whereas the incremental insertion technique resulted in the highest rate of voids.

Conclusion:

Bulk-fill composite resin demonstrated an adequate level of radiodensity and a reduced presence of voids compared with the incremental filling technique.

The Effects of Cavity Preparation and Composite Resin on Bond Strength and Stress Distribution Using the Microtensile Bond Test

OBJECTIVES

To evaluate the effect of flowable bulk-fill or conventional composite resin on bond strength and stress distribution in flat or mesio-occlusal-distal (MOD) cavity preparations using the microtensile bond strength (μTBS) test.

METHODS

Forty human molars were divided into two groups and received either standardized MOD or flat cavity preparations. Restorations were made using the conventional composite resin Z350 (Filtek Z350XT, 3M-ESPE, St Paul, MN, USA) or flowable bulk-fill (FBF) composite resin (Filtek Bulk Fill Flowable, 3M-ESPE). Postgel shrinkage was measured using the strain gauge technique (n=10). The Z350 buildup was made in two increments of 2.0 mm, and the FBF was made in a single increment of 4.0 mm. Six rectangular sticks were obtained for each tooth, and each section was used for μTBS testing at 1.0 mm/min. Polymerization shrinkage was modeled using postgel shrinkage data. The μTBS data were analyzed statistically using a two-way analysis of variance (ANOVA), and the postgel shrinkage data were analyzed using a one-way ANOVA with Tukey post hoc test. The failure modes were analyzed using a chi-square test (α=0.05).

RESULTS

Our results show that both the type of cavity preparation and the composite resin used affect the bond strength and stress distribution. The Z350 composite resin had a higher postgel shrinkage than the FBF composite resin. The μTBS of the MOD preparation was influenced by the type of composite resin used. Irrespective of composite resin, flat cavity preparations resulted in higher μTBS than MOD preparations ( p<0.001). Specifically, in flat-prepared cavities, FBF composite resin had a similar μTBS relative to Z350 composite resin. However, in MOD-prepared cavities, those with FBF composite resin had higher μTBS values than those with Z350 composite resin. Adhesive failure was prevalent for all tested groups. The MOD preparation resulted in higher shrinkage stress than the flat preparation, irrespective of composite resin. For MOD-prepared cavities, FBF composite resin resulted in lower stress than Z350 composite resin. However, no differences were found for flat-prepared cavities.

CONCLUSIONS

FBF composite resin had lower shrinkage stress than Z350 conventional composite resin. The μTBS of the MOD preparation was influenced by the composite resin type. Flat cavity preparations had no influence on stress and μTBS. However, for MOD preparation, composite resin with higher shrinkage stress resulted in lower μTBS values.

Effect of Light Activation of Pulp-Capping Materials and Resin Composite on Dentin Deformation and the Pulp Temperature Change

OBJECTIVES

To analyze the effect of pulp-capping materials and resin composite light activation on strain and temperature development in the pulp and on the interfacial integrity at the pulpal floor/pulp-capping materials in large molar class II cavities.

METHODS

Forty extracted molars received large mesio-occlusal-distal (MOD) cavity bur preparation with 1.0 mm of dentin remaining at the pulp floor. Four pulp-capping materials (self-etching adhesive system, Clearfil SE Bond [CLE], Kuraray), two light-curing calcium hydroxide cements (BioCal [BIO], Biodinâmica, and Ultra-Blend Plus [ULT], Ultradent), and a resin-modified glass ionomer cement- (Vitrebond [VIT], 3M ESPE) were applied on the pulpal floor. The cavities were incrementally restored with resin composite (Filtek Z350 XT, 3M ESPE). Thermocouple (n=10) and strain gauge (n=10) were placed inside the pulp chamber in contact with the top of the pulpal floor to detect temperature changes and dentin strain during light curing of the pulp-capping materials and during resin composite restoration. Exotherm was calculated by subtracting postcure from polymerization temperature (n=10). Interface integrity at the pulpal floor was investigated using micro-CT (SkyScan 1272, Bruker). The degree of cure of capping materials was calculated using the Fourier transform infrared and attenuated total reflectance cell. Data were analyzed using one-way analysis of variance followed by the Tukey test (α=0.05).

RESULTS

Pulpal dentin strains (μs) during light curing of CLE were higher than for other pulp-capping materials ( p<0.001). During resin composite light activation, the pulpal dentin strain increased for ULT, VIT, and CLE and decreased for BIO. The pulpal dentin strain was significantly higher during pulp-capping light activation. The temperature inside the pulp chamber increased approximately 3.5°C after light curing the pulp-capping materials and approximately 2.1°C after final restoration. Pulp-capping material type had no influence temperature increase. The micro-CT showed perfect interfacial integrity after restoration for CLE and ULT; however, gaps were found between BIO and pulpal floor in all specimens. BIO had a significantly lower degree of conversion than ULT, VIT, and CLE.

CONCLUSIONS

Light curing of pulp-capping materials caused deformation of pulpal dentin and increased pulpal temperature in large MOD cavities. Shrinkage of the resin composite restoration caused debonding of BIO from the pulpal floor.

Effect of Restorative System and Thermal Cycling on the Tooth-Restoration Interface – OCT Evaluation

The present study evaluated the tooth/noncarious cervical lesion restoration interface when using different adhesive systems and resin composites, submitted to thermal cycling (TC), using optical coherence tomography (OCT). Noncarious cervical lesion (NCCL) preparations (0.7 mm depth × 2 mm diameter) were performed on 60 human third molars and randomly divided into six groups, according to the adhesive system and resin composite used: group 1 = Adper Single Bond 2 (SB2) + Aelite LS Posterior (AP); group 2 = SB2 + Venus Diamond (VD); group = SB2 + Filtek Z250XT (Z250); group 4 = Clearfil SE Bond (CSE) + AP; group 5 = CSE + VD; group 6 = CSE + Z250. Selective enamel etching was performed for 30 seconds on groups 4, 5, and 6, while groups 1, 2, and 3 were etched for 30 seconds in enamel and 15 seconds in dentin. All groups were evaluated using OCT before and after TC (n=10). Images were analyzed using Image J software; enamel and dentin margins were separately evaluated. Data from OCT were submitted to PROC MIXED for repeated measurements and Tukey Kramer test (α = 0.05). No marginal gaps were observed in etched enamel, either before or after TC, for all adhesive and resin composite systems. A significant interaction was found between adhesive system and TC for the dentin groups; after TC, restorations with CSE showed smaller gaps at the dentin/restoration interface compared with SB2 for all resin composites. Increased gap percentages were noticed after TC compared with the gaps before TC for all groups. In conclusion, TC affected marginal integrity only in dentin margins, whereas etched enamel margins remained stable even after TC. Dentin margins restored with CSE adhesive system showed better marginal adaptation than those restored with SB2. Resin composites did not influence marginal integrity of NCCL restorations.

Effect of Restorative Protocol on Cuspal Strain and Residual Stress in Endodontically Treated Molars

Objectives

To evaluate the effect of the restorative protocol on cuspal strain, fracture resistance, residual stress, and mechanical properties of restorative materials in endodontically treated molars.

Methods

Forty-five molars received mesio-occlusal-distal (MOD) Class II preparations and endodontic treatment followed by direct restorations using three restorative protocols: composite resin (CR) only (Filtek Supreme, 3M-ESPE), resin modified glass ionomer cement in combination with CR (Vitremer, 3M-ESPE in pulp chamber and Filtek Supreme in MOD cavity), conventional glass ionomer cement in combination with composite resin (CGI-CR) (Ketac Fil, 3M-ESPE in pulp chamber and Filtek Supreme in MOD cavity). Cuspal strain was measured using strain gauges, and fracture resistance was tested with an occlusal load. Elastic modulus (EM) and Vickers hardness (VH) of the restorative materials were determined at different depths using dynamic microhardness indentation. Curing shrinkage was measured using the strain gauge technique. The restorative protocols were also simulated in finite element analysis (FEA). The shrinkage strain, cuspal strain, EM, VH, and fracture resistance data were statistically analyzed using split-plot analysis of variance and Tukey test (p=0.05). Residual shrinkage stresses were expressed in modified von Mises equivalent stresses.

Results

Shrinkage strain values (in volume %) were Ketac Fil (0.08±0.01) &lt; Vitremer (0.18±0.01) &lt; Filtek Supreme (0.54±0.03). Cuspal strain was higher and fracture resistance was lower when using CR only compared with the techniques that used glass ionomer. The EM and VH of the materials in the pulp chamber were significantly lower for glass ionomer. The FEA showed that using CR only resulted in higher residual stresses in enamel and root dentin close to the pulp chamber than the combinations with glass ionomers (RMGI-CR and CGI-CR).

Conclusions

The choice of restorative protocol significantly affected the biomechanical behavior of endodontically treated molars. Using glass ionomer to fill the pulp chamber is recommended when endodontically treated molars receive direct composite restorations because it reduces cuspal strain and increases fracture resistance.

Evaluation of Temperature and Stress Distribution on 2 Different Post Systems Using 3-Dimensional Finite Element Analysis

BACKGROUND The mouth is exposed to thermal irritation from hot and cold food and drinks. Thermal changes in the oral cavity produce expansions and contractions in tooth structures and restorative materials. The aim of this study was to investigate the effect of temperature and stress distribution on 2 different post systems using the 3-dimensional (3D) finite element method. MATERIAL AND METHODS The 3D finite element model shows a labio-lingual cross-sectional view of the endodontically treated upper right central incisor and supporting periodontal ligament with bone structures. Stainless steel and glass fiber post systems with different physical and thermal properties were modelled in the tooth restored with composite core and ceramic crown. We placed 100 N static vertical occlusal loading onto the center of the incisal surface of the tooth. Thermal loads of 0°C and 65°C were applied on the model for 5 s. Temperature and thermal stresses were determined on the labio-lingual section of the model at 6 different points. RESULTS The distribution of stress, including thermal stress values, was calculated using 3D finite element analysis. The stainless steel post system produced more temperature and thermal stresses on the restorative materials, tooth structures, and posts than did the glass fiber reinforced composite posts. CONCLUSIONS Thermal changes generated stresses in the restorative materials, tooth, and supporting structures.

Mechanical properties, shrinkage stress, cuspal strain and fracture resistance of molars restored with bulk-fill composites and incremental filling technique

OBJECTIVES

To compare bulk-fill with incremental filling techniques for restoring large mesio-occlusal-distal (MOD) restorations.

METHODS

Seventy-five molars with MOD preparations were divided into five groups: Z350XT, incrementally filled with Filtek Z350XT and four bulk-fills-FBF/Z350XT, Filtek Bulk Fill/Filtek Z350XT; VBF/CHA, Venus Bulk Fill/Charisma Diamond; SDR/EST-X, SDR/Esthet-X HD; TEC, TetricEvoCeram Bulk Fill. Cuspal strains were measured using strain-gauges (n=10): CSt-Re, during restorative procedure; CSt-100N, during 100N occlusal loading; CSt-Fr, at fracture load. Before fracture load, teeth were load-cycled. Fracture resistance, fracture mode, and enamel cracks were recorded. The other five teeth were used for Elastic modulus (E) and Vickers hardness (VH). Post-gel shrinkage (Shr), diametral tensile strength (DTS) and compressive strength (CS) were determined (n=10). Shrinkage stresses were analyzed using finite element analysis.

RESULTS

SDR had similar CS values as TEC, lower than all other composites. CHA had similar DTS values as Z350XT, higher than all other composites. Z350XT had the highest mean Shr and SDR the lowest Shr. New enamel cracks and propagation was observed after the restoration, regardless of filling technique. Z350XT had lower fracture resistance than bulk-fill composite techniques. No significant differences in failure modes were found. E and VH were constant through the depth for all techniques. Bulk-filling techniques had lower stresses compared to Z350XT.

CONCLUSIONS

Flowable bulk-fill composites had lower mechanical properties than paste bulk-fill and conventional composites. All bulk-fill composites had lower post-gel shrinkage than conventional composite. Bulk-fill filling techniques resulted in lower cusp strain, shrinkage stress and higher fracture resistance.

CLINICAL SIGNIFICANCE

Using bulk-fill composites cause lower CSt wich indicates lower stress in restored tooth. Furthermore, bulk-fill composites have a higher fracture resistance. Therefore, clinicians may choose the bulk-fill composite to decrease undesirable effects of restoration while simplifying filling procedure.

Incremental filling technique and composite material--part I: cuspal deformation, bond strength, and physical properties

OBJECTIVES

To evaluate the effect of composite resins (one conventional and two low-shrink composites) and filling techniques on cuspal strains (CS), microtensile bond strength (μTBS), composite ultimate tensile strength (UTS), and mechanical properties of the composites at various depths in molars with large Class II restorations.

MATERIALS AND METHODS

One hundred seventeen human molars received standardized Class II mesio-oclusal-distal cavity preparations and restorations with three composites (Filtek LS [3M-ESPE]; Aelite LS [BISCO]; and Filtek Supreme [3M-ESPE]) using three filling techniques (bulk, eight increments, and 16 increments). CS was measured using strain gauges, after which the same restored teeth were used to assess μTBS and UTS. The elastic modulus (E) and Vickers hardness (VH) at different depths were determined from microhardness indentations. The CS, μTBS, UTS, E, and VH data were statistically analyzed using split-plot analysis of variance and Tukey test (p=0.05).

RESULTS

The CS was higher when using 16 increments. The 'low-shrink' composites caused lower CS. The μTBS and UTS were similar for eight- and 16-increment techniques and higher when compared to the bulk filling in all composites. E and VH were constant through the depth when applied in eight or 16 increments.

CONCLUSIONS

Type of composite and filling technique affected the CS, μTBS, UTS, and mechanical properties of large Class II restorations. The eight-increments filling technique resulted in generally less CS with the same μTBS and UTS than was obtained with 16 increments, without affecting E and VH through the depth of the composites.

Enhancement cone beam computed tomography filters improve in vitro periimplant dehiscence detection

OBJECTIVE

To investigate whether cone beam computed tomography filters would improve periimplant dehiscence detection.

STUDY DESIGN

A hundred titanium implants were placed in bovine ribs in which defects simulating periimplant dehiscence had previously been created. After images acquisition, three oral radiologists assessed them with and without the following filters: Angio Sharpen high 5 × 5, Shadow, Sharpen 3 × 3, Sharpen Mild, and Smooth. The McNemar test verified the disagreement between all images versus the reference standard and original images versus images with filters; P < .05 was considered statistically significant.

RESULTS

Dehiscence detection using the original images and the Shadow filter disagreed from the reference standard (P < .05), as well as when using the filters instead of the original images (P < .05).

CONCLUSION

All the filters tested, with the exception of the Shadow, improved periimplant dehiscence detection. The Sharpen 3 × 3 filter was considered best for this task.

Detection of periimplant fenestration and dehiscence with the use of two scan modes and the smallest voxel sizes of a cone-beam computed tomography device

OBJECTIVE

To assess the accuracy of cone-beam computed tomography (CBCT) in periimplant fenestration and dehiscence detection, and to determine the effects of 2 voxel sizes and scan modes.

STUDY DESIGN

One hundred titanium implants were placed in bovine ribs in which periimplant fenestration and dehiscence were simulated. CBCT images were acquired with the use of 3 protocols of the i-CAT NG unit: A) 0.2 mm voxel size half-scan (180°); B) 0.2 mm voxel size full-scan (360°); and C) 0.12 mm voxel size full scan (360°). Receiver operating characteristic curves and diagnostic values were obtained. The Az values were compared with the use of analysis of variance.

RESULTS

The Az value for dehiscence in protocol A was significantly lower than those of B or C (P < .01). They did not statistically differ for fenestration (P > .05).

CONCLUSIONS

Protocol B yielded the highest values. The voxel sizes did not affect fenestration and dehiscence detection, and for dehiscence full-scan performed better than half-scan.