This study assessed the effect of a primer containing 10-methacryloyloxydecyl-(2-thiohydantoin-4-yl)propionate (MDTHP) on the bonding of noble metal alloys to an acrylic resin. Three noble metal alloys were selected as adherends, and V-Primer containing 6-(4-vinylbenzyl-n-propyl)amino-1,3,5-triazine-2,4-dithione was used as a comparative control. The disk specimens of each noble metal alloy were wet-ground and divided into three conditions: specimens primed with MDTHP primer or V-Primer, and specimens without priming. An acrylic resin was bonded to each specimen, and the specimens were performed the shear bond test. The MDTHP primer showed higher shear bond strength than the V-Primer for all specimens. X-ray photoelectron spectroscopic analysis showed that MDTHP was adsorbed on the Au-Pt-Pd alloy surface even after acetone cleaning. MDTHP binds not only with Cu but also with Au and Ag, promoting the bond strength of noble metal alloys. The effectiveness of MDTHP on dental noble metal alloys was suggested.

The Effect of Mechanical and Chemical Surface Preparation Methods on the Bond Strength in Repairing the Surface of Metal-Ceramic Crowns with Composite Resin: a Systematic Review and Meta-Analysis

The aim of this study was to find the most effective surface preparation methods to enhance the bond strength between the composite resin and surface remaining from ceramic fracture. In this systematic review and meta-analysis, 39 studies were examined. The information related to the studies was extracted and categorized based on the type of the substrate material and applying or not applying thermal cycles (p<0.05). In the meta-analysis of substrate metal-ceramic samples without aging, application of air abrasion resulted in a significant increase of the bond strength to composite resin when using chemical compounds of the group without the mentioned functional monomers. Application of mechanical and chemical surface preparation methods can result in enhanced bond strength of the composite to the substrate material, which depends on the type of substrate material.

Adhesive bonding of alumina air-abraded Ag-Pd-Cu-Au alloy with 10-methacryloyloxydecyl dihydrogen phosphate

The aim of this paper is to study changes in the Ag-Pd-Cu-Au alloy surfaces by alumina air-abrasion process and effect of those changes on the adhesive bonding characteristic. Surface roughness, surface composition and chemical state of the alumina air-abraded alloys were analyzed by a confocal laser scanning microscope, an energy dispersive X-ray spectroscopy and an X-ray photoelectron spectroscopy. The results showed that the alumina air-abrasion changed the alloy surface by mechanical roughening, alumina remain and copper oxidation. Effect of the changes in the alloy surface on the adhesive bonding characteristic was examined by using a methyl methacrylate/tri-n-butylborane derivative (MMA/TBB) resin cement with the 10-methacryloyloxydecyl dihydrogen phosphate (MDP) contained primer. The shear bond strength test results indicated that the surface oxidation by the abrasion is the main contributor that improved the adhesive bonding rather than other effects such as mechanical roughening or alumina remain.

Chemical alteration of Ag-Pd-Cu-Au alloy surface by alumina air-abrasion and its effect on bonding to resin cement

The goal of this study was to investigate the chemical alteration of a dental alloy surface by alumina air-abrasion and its effect on bonding to resin cement. Alumina air-abrasion was carried out on an Ag-Pd-Cu-Au alloy. The surface morphology and chemical state of the abraded alloy were characterized. The effect of the air-abrasion on the shear bond strength between the alloy and a methyl methacrylate/tri-n-butyl borane (MMA/TBB) resin cement with some primers was evaluated. The surface characterization revealed that the alumina air-abrasion mechanically roughened and chemically altered the surface. The chemical alterations had two effects: (1) abraded alumina particles remained on the alloy surface and (2) copper ions were oxidized in the alloy surface. As the result, the shear bond strength test indicated that 10-methacryloyloxydecyl dihydrogen phosphate (MDP) contained primer worked with the abraded alloy surface, whereas it did not work with the non-abraded alloy surface.

Trace of organic sulfur compounds detected from debonded interface between transparent acrylic resin and gold alloy

The purpose of the current study was to evaluate the bonding performance of two single-liquid primers, which contained 6-(4-vinylbenzyl-n-propyl) amino-1,3,5-triazine-2,4-dithione (VTD) or 6-methacryloyloxyhexyl 2-thiouracil 5-carboxylate (MTU-6), used for bonding between metals and an acrylic resin. A gold alloy and high-purity titanium were used as adherend materials, and a transparent acrylic resin initiated with tri-n-butylborane derivative was selected as the luting material. Both adherends were treated with one of the primers and bonded with the luting material, after which shear bond strength was determined. Fourier transform infrared spectroscopy was used to analyze debonded resin specimens. Shear bond strength to gold alloy was significantly greater than that to titanium for both the VTD and MTU-6 primers. A trace of thiol structure, probably derived from VTD and MTU-6, was detected on resin surfaces debonded from gold alloy. These results indicate that the two organic sulfur compounds, which are stable in an atmospheric environment, are tautomerized into a thiol structure, thus allowing adsorption onto noble metals. In addition, the adsorbed thiol compounds contribute to chemical bonding between the acrylic resin and noble metal alloy, as polymerizable adhesive functional monomers.

Effect of thione primers on adhesive bonding between an indirect composite material and Ag-Pd-Cu-Au alloy

The current study evaluated the effect of primers on the shear bond strength of an indirect composite material joined to a silverpalladium-copper-gold (Ag-Pd-Cu-Au) alloy (Castwell). Disk specimens were cast from the alloy and were air-abraded with alumina. Eight metal primers were applied to the alloy surface. A light-polymerized indirect composite material (Solidex) was bonded to the alloy. Shear bond strength was determined both before and after the application of thermocycling. Two groups primed with Metaltite (thione) and M. L. Primer (sulfide) showed the greatest post-thermocycling bond strength (8.8 and 6.5 MPa). The results of the X-ray photoelectron spectroscopic (XPS) analysis suggested that the thione monomer (MTU-6) in the Metaltite primer was strongly adsorbed onto the Ag-Pd-Cu-Au alloy surface even after repeated cleaning with acetone. The application of either the thione (MTU-6) or sulfide primer is effective for enhancing the bonding between a composite material and Ag-Pd-Cu-Au alloy.

Adhesive performance of silver-palladium-copper-gold alloy and component metals bonded with organic sulfur-based priming agents and a tri-n-butylborane initiated luting material

OBJECTIVE

The purpose of the current study was to evaluate the effect of thione-based metal priming agents on the adhesive behavior of a Ag-Pd-Cu-Au alloy and component metals bonded with an acrylic resin.

MATERIALS AND METHODS

Disk specimens (10 mm in diameter by 3 mm thick) were prepared from a silver-palladium-copper-gold (Ag-Pd-Cu-Au) alloy (Castwell M.C.12), high-purity silver, palladium, copper and gold. Four single-liquid priming agents containing organic sulfur compound (Alloy Primer, Metaltite, M.L. Primer and V-Primer) and three acidic priming agents (All Bond II Primer B, Estenia Opaque Primer and Super-Bond Liquid) were assessed. The metal specimens were flat-ground with abrasive papers, primed with one of the agents and bonded with a tri-n-butylborane initiated resin. The shear bond strengths were determined both before and after repeated thermocycling (5°C and 55°C, 1 min each, 20,000 cycles). The results were statistically analyzed with a non-parametric procedure (p = 0.05 level).

RESULTS

The post-thermocycling bond strengths in MPa (median; n = 11) associated with the Alloy Primer, Metaltite, M.L. Primer and V-Primer materials were, respectively, 20.8, 22.8, 17.8 and 18.4 for the Ag-Pd-Cu-Au alloy; 19.6, 21.9, 14.4 and 20.1 for silver; 5.4, 4.5, 12.8 and 5.3 for palladium; 17.1, 19.2, 0.7 and 6.6 for copper; and 18.5, 17.7, 22.8 and 15.4 for gold.

CONCLUSIONS

It can be concluded that the use of the four priming agents, which are based on organic sulfur compounds, effectively enhanced bonding to the Ag-Pd-Cu-Au alloy and the component metals, although the bonding performance varied among the priming agents and metal elements. The priming agents appeared to have more of an effect on the alloy, silver and gold than on the palladium and copper.