Bioactive Materials Subjected to Erosion/Abrasion and Their Influence on Dental Tissues

Clinical evaluation of Giomer and self-etch adhesive compared with nanofilled resin composite and etch-and-rinse adhesive - Results at 8 years

OBJECTIVE

This study aimed to evaluate the long-term clinical performance of Giomer and a self-etch adhesive system compared with a nanofilled resin composite and etch-and-rinse adhesive system in Class I and Class II restorations.

METHOD

The study was designed to be double-blinded with intra-individual control. 48 patients with 54 pairs of cavities (class I or class II) were recruited. Each pair of restorations was placed with either BEAUTIFIL II (BF) and FL-BOND II (FL) or Filtek Z350 (Z350) and Scotchbond Multi-Purpose (SMP). Clinical evaluation was performed at baseline, 6-month, 18-month, 4-year and 8-year after placement according to modified USPHS criteria. Kaplan-Meier survival analysis and log rank tests were performed (SPSS 20.0, IBM Corporation, US) to compare the survival probability of different restorations.A generalized linear mixed model (GLMM) was adopted to assess the performance of the materials. The McNemar test was used to show significant changes for all the evaluation criteria and difference between them.

RESULTS

At the eight-year recall, 32 patients with 67 restorations were present. There were twelve restorations in total recorded as failure due to loss of retention, restoration fracture, secondary caries, tooth fracture or endodontic treatment due to pulp necrosis. The survival probabilities and calculated annual failure rate(AFR) of BF and Z350 restorations at 8-year were 87.2 % vs 87.8 % and 1.6 % vs 1.5 % respectively with no significant difference (p > 0.05)between the two materials. Over the recall time range of eight years, decreased possibility of alpha rating was observed for retention, marginal adaptation, marginal staining and surface roughness for both materials (p < 0.05). Decreased possibility of alpha rating was observed for surface staining and secondary caries for Z350 (p < 0.05) and restoration fracture for BF (p < 0.05), respectively. Comparing the two restorative systems over eight years, no significant difference was seen for linear decline of the possibility of alpha rating for any of the criteria evaluated (p > 0.05).

CONCLUSION

Giomer material and the self-etch adhesive system had comparable clinical performance with nanofilled resin composite and etch-and-rinse adhesive system over the observation period of eight years.

Are S-PRG composites able to resist against erosive and abrasive challenges and protect surrounding enamel in situ?

OBJECTIVES

This study evaluated the resistance of S-PRG (Surface Pre-Reacted Glass-ionomer) composites and other restorative materials against erosive and abrasive challenges and their protective effect on enamel adjacent to the restorations.

MATERIALS AND METHODS

Bovine enamel blocks were prepared and randomized into 12 groups, including 6 types of material, each of them subjected to erosion_e or erosion+abrasion_ea: Beautifil II (S-PRG); Beautifil Bulk Restorative (S-PRG); Filtek Z250 XT; Filtek Bulk Fill; EQUIA Forte; Riva Light Cure. Cavities were prepared in the middle of enamel blocks and restored with the materials. Initial profiling measurement was performed on the material and on adjacent enamel (100, 200, 300, 600 and 700 μm from the restoration margin). Palatal intraoral appliances with the restored enamel blocks were used by the volunteers (n = 10). During 5 days appliances were immersed in 2.5 % citric acid for 2 min; 6 × /day (erosion_e). For ea condition, blocks were brushed for 1 min after each acid immersion. Final profile assessment was performed. Data were analysed by two and three way ANOVA followed by Tukey's test (p < 0.05).

RESULTS

Material wear: Riva Light Cure showed the highest wear followed by EQUIA Forte and then all resin composites, including the ones with S-PRG (p = 0.000). Enamel wear: there was significant interaction among type of restorative material, wear condition and distance (p = 0.014), enamel around materials showed similar wear (p = 0.983) and the enamel subjected to ea exhibited highest wear (p = 0.000).

CONCLUSION

SPRG based composites showed resistance against erosive and abrasive challenges but were not able to protect enamel adjacent to the restorations.

CLINICAL SIGNIFICANCE

S-PRG composites exhibit resistance to material wear comparable to resin composites. However, they have shown an inability to effectively protect the adjacent enamel under in situ erosive-abrasive conditions, despite the presence of mineral-loss-preventing ions surrounding materials.

Characterization of a Novel TiF4 Inclusion Complex and in vitro Evaluation of Its Effect on Inhibiting Enamel Demineralization

INTRODUCTION

Titanium tetrafluoride (TiF4) is an anticariogenic agent with high remineralizing potential. However, the acidic pH of TiF4 solution can limit its clinical application. The present study aimed to prepare and characterize a new TiF4-dendrimer inclusion complex and evaluate its ability to inhibit enamel demineralization under pH cycling conditions.

METHODS

PEG-citrate dendrimer and TiF4-dendrimer inclusion complex were synthesized and their molecular structures were evaluated using Fourier-transform Infrared Spectroscopy (FTIR), Hydrogen Nuclear Magnetic Resonance (HNMR), and Liquid Chromatography-Mass Spectrometry (LC-MS) tests. Forty-eight enamel samples were prepared and randomly divided into four groups: distilled water (negative control), TiF4 solution (T), dendrimer solution (D), and TiF4-dendrimer solution (TD). The microhardness of the samples was measured initially. Next, the samples underwent pH cycling, were exposed to the solutions, the microhardness was measured again, and microhardness loss was calculated. EDX analysis was performed on the surface and cross-sectional segments of the samples.

RESULTS

The microhardness loss was significantly higher in control (-65.1 ± 6.0) compared to other groups. No significant difference was observed between T (-47.9 ± 5.6) and D (-41.7 ± 12.0) and also D and TD (-40.5 ± 9.4) in this regard. Microhardness loss was significantly higher in T compared to TD group. The TD samples showed similar fluoride and titanium content in both surface and subsurface regions, while the T group had higher concentrations in the surface region. Moreover, the TD solution had a higher pH of 3.4 compared to the T solution's pH of 1.1.

CONCLUSION

No significant difference was observed between the efficacy of TiF4-dendrimer and TiF4 solution in inhibiting demineralization while TiF4-dendrimer solution had the added advantage of having a higher pH.

Efficacy of bioactive materials in preventing Streptococcus mutans-induced caries on enamel and dentine

The study investigated the ability of bioactive materials used to restore enamel and dentine specimens to prevent caries. Enamel (n = 50) and dentine (n = 50) specimens were obtained from bovine incisors, prepared, and randomly allocated to one of five groups according to the restorative treatment: alkasite without adhesive system; alkasite with adhesive system; high viscosity glass ionomer cement; resin composite; no restoration; negative control group. Specimens were restored, exposed to a thermal cycling aging protocol, sterilized, and exposed to a cariogenic challenge induced by Streptococcus mutans and then submitted to surface and subsurface microhardness tests and polarized light microscopy to verify the caries lesion development in enamel or dentine surrounding the restorative materials. Data were analyzed using one-way ANOVA. In enamel and dentine, glass ionomer cement, alkasite without and with adhesive system presented a lower percentage surface microhardness loss than resin composite and negative control. Enamel subsurface microhardness presented no statistically significant differences between glass ionomer cement, alkasite without and with adhesive system. Glass ionomer cement also did not present statistically significant differences from resin composite and the negative control. In dentine, glass ionomer cement showed the highest subsurface microhardness values. In conclusion, bioactive restorative materials provide greater protection to enamel and dentine against surface caries development than resin composite.

Effects of Different Toothpastes on the Nanomechanical Properties and Chemical Composition of Resin-Modified Glass Ionomer Cement and Composite Resin Restorations

PURPOSE

This study evaluates the effects of different toothpastes on the nanohardness and chemical compositions of restorative materials and dental surfaces.

METHODS

Bovine enamel (n = 72) and dentin (n = 72) blocks were obtained and restored using RMGIC (n = 36) or CR (n = 36) to create the following surfaces: dentin adjacent to RMGIC (DRMGIC), enamel adjacent to RMGIC (ERMGIC), dentin adjacent to CR (DCR), and enamel adjacent to CR (ECR). After restoration, one hemiface of each specimen was coated with an acid-resistant varnish to facilitate the creation of control (C) and eroded (E) sides; the latter were achieved by erosion-abrasion cycles as follows: erosion with 1% citric acid: 5 days, four times for 2 min each day; 1% citric acid/abrasion, two times for 15 s, followed by immersion in a toothpaste slurry for 2 min. Toothpastes without fluoride (WF; n = 12), with sodium fluoride (NaF; n = 12), and with stannous fluoride (SnF₂; n = 12) were used for RMGIC or CR. The specimens were analyzed for nanohardness (H), and chemical composition using energy-dispersive X-ray spectroscopy and Raman microscopy. The data were statistically analyzed using two-way repeated measures ANOVA and Tukey's test (α = 0.05).

RESULTS

Lower H values were obtained with NaF for DRMGIC-C, with a statistically significant difference from the H value obtained with WF (p < 0.05). The calcium and phosphorus concentrations in DCR-E were significantly lower with WF than with the other types of toothpaste (p < 0.05). Fluoride-containing toothpastes are capable of preserving the main chemical components of the dentin adjacent to the restorative materials under erosive-abrasive conditions.

Anti-erosion effect of an experimental varnish on eroded dentin

This in vitro study evaluated the effect of an experimental varnish containing 20% nano-hydroxyapatite (nHAP) associated with 5% stannous chloride (SnCl2) against erosive-abrasive wear on bovine dentin. Samples of bovine cervical dentin were pre-eroded (0.3% citric acid, pH 2.6 for 10 minutes) and randomized into 4 groups (n=10): Control group - experimental varnish without active ingredient (CG); experimental varnish containing 20% nHAP (nHG); experimental varnish containing 5% SnCl2 (24.800 ppm Sn2+) (SnG); experimental varnish containing 20% nHAP associated with 5% SnCl2 (18.300 ppm Sn2+) (nHSnG). After applying the materials, the erosive-abrasive challenges were performed for five days. Erosive dentin loss and analysis of the pattern of dentinal obliteration were performed by 3D confocal laser microscopy. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The SnG and nHSnG experimental groups presented more effectiveness in preventing erosive wear when compared to the other groups (p<0.05). There was no statistically significant difference between the SnG and nHSnG groups (p = 0.731) in tooth structure dentin loss. Regarding the amount of open dentinal tubules, the highest amount of obstructed dentinal tubules was demonstrated in SnG and nHSnG (p < 0.05) when compared to the others. Between SnG and nHSnG there was no significant difference (p = 0.952) in the amount of closed dentinal tubules in the dentin. Experimental varnishes containing 5% SnCl2 associated or not with 20% nHAP showed to be a promising strategy in preventing erosive-abrasive wear of dentin. In addition, nHSnG was able to obliterate dentinal tubules.

Impact of different brushing/abrasion protocols on erosive tooth wear for in vitro studies

OBJECTIVE

To investigate the influence of different toothbrushing (with dentifrice) protocols on the progression of erosive tooth wear for in vitro studies.

DESIGN

Bovine enamel specimens were randomly distributed into 12 experimental groups (n = 10), according to the study factors: (1) brushing movement (horizontal or circular); (2) slurry diluent (artificial saliva or distilled water); (3) toothpaste dilution ratio (1:2, 1:3 or 1:4). A 5-day erosion-abrasion cycling model was performed, each consisting of 4 erosive challenges (0.3 % citric acid, pH=2.6) followed by 60 min exposure to artificial saliva. Brushing with fluoride toothpaste (15 s, 1400 ppm F^-, AmF) was carried out 2x/day. Enamel surface loss (SL) was determined by optical profilometry. Data were statistically analyzed with three-way ANOVA and Tukey tests (α = 0.05).

RESULTS

SL was lower for the horizontal movement than for the circular (p = 0.044). There were no significant differences among the dilution ratios for artificial saliva. For distilled water, the more concentrated slurry (1:2) presented greater surface loss than the less concentrated slurries (1:3 and 1:4, p = 0.049 and p = 0.014, respectively). Dilutions with artificial saliva at ratios 1:3 and 1:4 presented higher surface loss than with distilled water (p = 0.008 and p < 0.001, respectively); however, for 1:2 ratio, there were no significant differences between the diluents.

CONCLUSIONS

The in vitro progression of enamel SL was influenced by the brushing movement, as well as the combination of the dilution ratio and the diluent of the toothpaste slurry, and therefore, all these factors must be considered when comparing results from different studies.

Effects of in vitro erosion on surface texture, microhardness, and color stability of resin composite with S-PRG fillers

OBJECTIVES

To evaluate the effect of acid erosion on different physical properties of resin composite with S-PRG (surface pre-reacted glass) fillers, by conducting simulations of intrinsic and extrinsic sources.

MATERIALS AND METHODS

Cylindrical samples (Ø6 vs. 2 mm) of a conventional nanohybrid resin composite (Forma, Ultradent) and of a nanohybrid resin composite with S-PRG filler (Beautifil II, Shofu) were exposed to erosive cycling (5 days), based on (n=12) remineralizing solution (control); 0.3% citric acid (pH=2.6); or 0.01 M hydrochloric acid (pH=2). Roughness (Ra), microhardness (KHN), and color (CIEL*a*b*, CIEDE2000, and Vita scale (SGU)) factors were analyzed at the initial and final time points, and the general color changes (ΔE_ab, ΔE₀₀, ΔSGU) were calculated. Final images were obtained using scanning electron microscopy (SEM). The data were evaluated by generalized models, Mann-Whitney, Wilcoxon, Kruskal-Wallis, and Dunn tests (α=0.05).

RESULTS

Regarding KHN, there was no difference between the groups or the time periods (p = 0.74). As for Ra, there was a significant increase in the Ra of both composites after cycling with hydrochloric acid, but only the resin composite with S-PRG filler showed a change in Ra after cycling with citric acid (p = 0.003). After cycling with citric and hydrochloric acid, the highest Ra values were found for the resin composite with S-PRG filler (p < 0.0001), corroborating the result of images (SEM) indicating loss of filler and porosities in this material. The resin composite with S-PRG filler showed higher ΔE_ab and ΔE₀₀, in addition to more negative ΔSGU values and lower L* values after exposure to both acids, compared to the control (p < 0.05).

CONCLUSION

The acidic conditions altered the roughness and color stability of the materials tested, pointing out that the resin composite containing S-PRG filler showed greater degradation of its physical properties than the conventional resin composite.

CLINICAL RELEVANCE

Bioactive materials are relevant, considering that their properties interact with dental hard tissues; however, the S-PRG-based resin composite showed greater degradation under acidic conditions than the conventional resin composite.

Effect of a modified adhesive system with encapsulated arginine and calcium carbonate on dentin permeability

To modify an adhesive system with halloysite clay nanotubes (HNTs) containing arginine and calcium carbonate and to evaluate their cytocompatibility, viscosity and efficacy in reducing dentin permeability. HNTs containing arginine and calcium carbonate were incorporated into the primer and adhesive of a three-step adhesive system (SBMP), and their viscosity was measured. Discs (n = 4/group) were prepared: SBMP (control), HNT-PR (modified primer), HNT-ADH (modified adhesive) and HNT-PR + ADH (modified primer and adhesive) were evaluated regarding cell death and viability. Dentin discs were prepared and randomly assigned into the following treatments (n = 10): NC (no treatment), SBMP, HNT-PR, HNT-ADH, HNT-PR + ADH and COL (Colgate® Sensitive Pro-relief™ prophylaxis paste). After, they were submitted to an erosive-abrasive cycling. Dentin permeability (hydraulic conductance) was evaluated at baseline, 24 h after treatment and after cycling. Both the modified primer and adhesive showed significantly higher viscosity than their controls. Group HNT-PR resulted in significantly higher cytotoxicity when compared to SBMP and HNT-PR + ADH groups. Group HNT-ADH resulted in the highest cell viability compared to all other groups. All groups showed significantly lower dentin permeability when compared to the NC group. Post-cycling, SBMP and HNT-ADH groups showed significantly lower permeability when compared to COL group. The addition of encapsulated arginine and calcium carbonate did not affect the cytocompatibility of the materials nor their ability to reduce dentin permeability.

Crown Reconstruction of Erosive Wear Using High-viscosity Glass Ionomer Cement: A Case Report

The aim of this clinical report is to present a possible alternative treatment, with 24-month follow-up, for restoring tooth loss due to extensive erosive tooth wear. A 21-year-old male patient, complaining of intense sensitivity in the maxillary posterior teeth, and presenting severe wear on maxillary premolar and molar teeth due to gastroesophageal reflux, sought care in the university clinics. The planned treatment was to refer for medical treatment and perform restorations with the high-viscosity glass ionomer cement Equia Forte (GC Corporation, Tokyo, Japan), aiming to restore the dental anatomy and to consequently decrease the pain symptomatology. A silicone guide, obtained from a diagnostic waxing, was used during the restorative approach considering the patient's occlusion. After all the clinical steps of the restorative technique, an occlusal adjustment of restorations was performed. During monthly recalls up to 24 months, the treatment was stable and in service. In addition, the patient reported no pain and improved chewing, leading to a better quality of life.

Anti-erosive profile of an experimental 5% SnCl₂ varnish containing different concentrations of NaF

Abstract This in vitro study evaluated the anti-erosive effect of an experimental varnish containing 5% stannous chloride (SnCl₂) associated with different concentrations of NaF (NaF-free, 2.5% NaF, or 5.2% NaF) on bovine enamel and root dentin. One hundred samples were pre-eroded (0.3% citric acid, pH 2.6, 10 min) and randomized into five groups (n=10 for each substrate): Negative control - milli-Q water; NaF-free - Experimental varnish SnCl₂-free and NaF-free; 2.5 NaF - Experimental varnish 5% SnCl₂ associated with 2.5% NaF; 5.2 NaF: Experimental varnish 5% SnCl₂ associated with 5.2% NaF and positive control - Commercial varnish containing 5% NaF (Duraphat). After the varnishes were applied, the erosive and abrasive challenges were carried out for five days. Loss of tooth structure (TSL) was determined by optical profilometry, and the loss of calcium (ΔCa2+) using atomic absorption spectroscopy. Dentin analysis was also performed by SEM. A one-way ANOVA/Bonferroni test was performed to analyze the data (α=0.05). The experimental 2.5 NaF and 5.2 NaF groups showed greater effectiveness in preventing TSL when compared to the other groups (p <0.05), regardless of the substrate. In addition, these groups showed lower loss in Ca2+ content when compared to the other groups (p <0.05), for enamel and dentin. Dentin showed greater TSL and ΔCa2+ loss when compared to enamel in all treatments (p <0.05). The 5.2% and 2.5% NaF-containing experimental varnishes showed promising results in both, the prevention of TSL and the loss of Ca2+, regardless of the substrate studied.

Influence of pH Cycling on Erosive Wear and Color Stability of High-Viscosity Glass Ionomer Cements

The purpose of this in vitro study was to evaluate erosive wear and change in color of high-viscosity glass ionomer cements after pH cycling in two erosive media. There were 3 experimental groups with 22 samples each, (I) EQUIA Forte HT without coat, (II) Fuji IX and (III) Ketac Universal Aplicap. Each group was randomly divided into three subgroups (n = 6–8) further exposed to different environments, (1) distilled water, (2) green tea (pH 3.78) and (3) Aceto balsamico vinegar (pH 3.0). Mass and L* a* b* values were recorded before and after pH cycling. The samples in subgroups 2 and 3 were exposed to the acidic media two times a day for 10 min, over a period of 14 days. The differences among materials and erosive effects of the three media were tested using three-way analyses of variance with post hoc LSD test at the significance level p < 0.05. The effect of pH cycling in Aceto balsamico and green tea was degrading for all three materials. pH cycling in Aceto balsamico caused significantly higher erosive wear than pH cycling in Fuzetea and storage in distilled water, in all materials (p < 0.05). pH cycling in both acidic media and in the control group resulted in a significant change in L* a* and b* (p < 0.05). The L* value decreased significantly and the a* and b* values increased significantly (p < 0.05).

S-PRG-based composites erosive wear resistance and the effect on surrounding enamel

This study evaluated Surface Pre-Reacted Glass-ionomer (S-PRG)-based-composites' surface resistance against erosive wear and their protective effect on surrounding enamel. Bovine enamel was randomized into 12 groups (n = 10/group) [erosion (e) or erosion + abrasion (a)]: nanohybrid-S-PRG-based composite (SPRGe/SPRGa), nanohybrid-S-PRG-based bulk-fill (SPRGBFe/SPRGBFa), nanoparticle-composite (RCe/RCa), nanohybrid-bulk-fill (BFe/BFa), Glass Hybrid Restorative System (GHRSe/GHRSa), and resin-modified glass-ionomer-cement (RMGICe/RMGICa). Cavities were prepared and restored. Initial profile assessment was performed on material and on adjacent enamel at distances of 100, 200, 300, 600, and 700 μm from margin. Specimens were immersed in citric acid (2 min; 6×/day for 5 days) for erosion. Erosion + abrasion groups were brushed for 1 min after erosion. Final profile assessment was performed. Two-way ANOVA and Tukey-test showed: for erosion, the GHRSe and RMGICe presented greater material wear compared to the other groups (p = 0.001); up to 300 μm away from restoration, GHRSe and SPRGBFe were able to prevent enamel loss compared to RMGICe and other composite groups (p = 0.001). For erosion + abrasion, none of the materials exhibited a significant protective effect and S-PRG-based groups showed lower wear than RMGICa and GHRSa, and higher wear than composites (p = 0.001). S-PRG-based-composites can diminish surrounding enamel loss only against erosion alone, similarly to GIC, with advantage of being a more resistant material.

Investigating a Commercial Functional Adhesive with 12-MDPB and Reactive Filler to Strengthen the Adhesive Interface in Eroded Dentin

To compare the adhesive interface of eroded dentin formed by a functional dental adhesive and a gold standard strategy, by testing microtensile bond strength (μTBS), hardness/elastic modulus. Permanent sound human molars were randomly allocated to four experimental groups, all subject to artificial erosion (0.05 M citric acid; 3× daily, 5 days). Groups included control Clearfil SE Bond 2 (CFSE), and experimental group Clearfil SE Protect (CFP), at two different time points-immediate (24 h) and long term (3 months–3 M). Samples were sectioned into microspecimens for μTBS (n = 8) and into 2-mm thick slabs for nanoindentation assays (n = 3). Groups CFSE_3M and CFP_3M were stored in artificial saliva. Statistical analysis included two-way ANOVA for μTBS data, while hardness/modulus results were analyzed using Kruskal–Wallis H Test (significance level of 5%; SPSS v.27.0). Although no significant differences were found between mean μTBS values, for different adhesives and time points (p > 0.05), a positive trend, with μTBS rising in the CFP_3M group, was observed. Regarding hardness, no significant differences were seen in the hybrid layer, considering the two variables (p > 0.05), while the reduced elastic modulus rose in CFP_3M when compared to 24 h. Thus, CFP shows similar mechanical and adhesive performance to CFSE in eroded dentin, although it may comprise promising long-term results. This is advantageous in eroded substrates due to their increased enzymatic activity and need for remineralization.

Analysis of laboratory adhesion studies in eroded enamel and dentin: a scoping review

Aim

To summarize and report laboratory studies of adhesion in eroded substrates, which used bond strength as an outcome measure. To determine the strategies available to overcome bonding difficulties, the quality and consistency of the methodology and to find evidence gaps.

Materials and Methods

The present review followed PRISMA-ScR guidelines. A search was conducted on PubMed/Medline, Scopus and EMBASE (Ovid) databases to identify published peer-reviewed papers (2010–2020). For final qualitative synthesis, 29 articles were selected which respected the inclusion criteria. Data charting was carried out, independently, by two reviewers and quality assessment of the articles was performed.

Results

The primary studies included fall into four major categories: comparison of restorative materials and application modes, enzymatic inhibitors, surface pretreatments or remineralization strategies. Most studies found evaluated dentin (76%), while 17% evaluated enamel, and 7% evaluated both substrates. The majority of the studies reported an effective intervention (83%). Bond strength to eroded dentin is significantly reduced, while in enamel erosion is beneficial. The bond strength to eroded dentin is material-dependent and favored in systems containing 10-MDP. Great disparities among the erosion models used were found, with citric acid in different concentrations being the preferred method, although standardization is lacking.

Conclusions

Adhesives containing 10-MDP show beneficial results in eroded dentin, and surface preparation methods should be considered. Studies which evaluated adhesion to eroded enamel/dentin show high heterogeneity in what concerns aims and methodology. Strategies that focus on remineralizing dentin and strategies to protect bond longevity in this substrate require further research.

Effect of fluoride varnish on glass ionomer microhardness changes in endogenous acid erosion challenge

OBJECTIVE

This study aimed to assess the effect of fluoride varnish on glass ionomer microhardness changes after endogenous acid erosion challenge.

METHODOLOGY

In this study, 40 conventional glass ionomer (CGI; Fuji IX) and 40 resin-modified glass ionomer (RMGI; Fuji IILC) discs were fabricated and divided into 4 subgroups (n = 10) for immersion in synthetic gastric acid or saliva for 27 h with/without fluoride varnish application. The surface microhardness was measured at baseline and after immersion, and the change in microhardness was calculated. Data were analyzed using analysis of variance and T-test.

RESULTS

A reduction in microhardness was noted in all subgroups following immersion. The lowest change in microhardness of both CGI and RMGI occurred in artificial saliva. In CGI groups, the highest reduction in microhardness occurred in synthetic gastric acid with fluoride varnish application, and the reduction was significantly different from that of the CGI group with fluoride varnish application (p value = .01). In RMGI groups, the highest reduction in microhardness was noted in synthetic gastric acid without fluoride varnish application, and the reduction was significantly different from that of the other groups (p value < .05).

CONCLUSIONS

Exposure to synthetic gastric acid caused a significant reduction in microhardness of RMGI. Varnish application significantly decreased the acid susceptibility of RMGI, but not that of CGI.