Effect of a 3-second Off-label Exposure on the Depth of Cure of Eight Resin-based Composites

OBJECTIVES

This study evaluated the depth of cure (DoC) of eight resin-based composites (RBCs) photocured using one multipeak light-curing unit (LCU) on the standard output setting for the manufacturer's RBC recommended exposure time and at a higher irradiance for 3 seconds.

METHODS

Three conventional RBCs: Tetric EvoCeram (Evo), Tetric N-Ceram (Cer), Tetric Prime (Pri); and five bulk-fill: Tetric N-Ceram Bulk Fill (CerBF), Opus Bulk Fill APS (OpusBF), Opus Bulk Fill Flow APS (OpusF), Tetric PowerFill (PFill) and Tetric PowerFlow (PFlow) were examined. Only PFill and PFlow are formulated to be photocured in 3 seconds. The RBCs were packed into a metal mold and photocured using a Bluephase PowerCure LCU for the RBC manufacturer's recommended exposure time on the standard mode and using the 3-second high irradiance mode. After photocuring, the specimens were immersed in a solvent for 1 hour. The length of the remaining RBC was measured and divided by 2. Data were analyzed using two-way analysis of variance (ANOVA) followed by the Tukey post hoc multiple comparison test (α=0.05).

RESULTS

There was no significant difference in the DoC values for PFill and PFlow when photocured using the 3-second high irradiance protocol compared to the lower irradiance standard mode protocol. All other RBCs had significantly lower DoC values (p<0.001) when photocured off-label using the 3-second high irradiance mode.

CONCLUSION

Of the eight RBCs tested, only PFill and PFlow achieved the same DoC when the high irradiance 3-second curing method was used compared to when their longer lower irradiance protocol was used.

Marginal integrity in minimally invasive molar resin composite restorations: Impact of polymerization shrinkage

OBJECTIVES

This study utilized non-linear finite element (FE) models to explore polymerization shrinkage and its impact on marginal integrity in molars following both selective caries removal (SCR) and conventional treatment. Specifically, we performed 2D in silico simulations to study residual stresses post-resin polymerization shrinkage and their influence on the marginal integrity of various restoration types.

METHODS

Initially, FE models were developed based on a cohesive zone framework to simulate crack propagation along the bonded interfaces between restoration and tooth structure in SCR-treated molars with class I and class II restorations. The modeled resin composite restorations first underwent polymerization shrinkage and were then subjected to various occlusal loading conditions. Stress magnitudes and distributions were identified to evaluate the margin integrity and predict the mechanism and location of interfacial failure.

RESULTS AND DISCUSSION

The FE models computed polymerization shrinkage stresses of less than 1 MPa, exerting a minor influence on the composite/tooth interface. Occlusal loading, however, significantly impacted the load-bearing capacity of the composite/tooth (c/t) interface, potentially jeopardizing the restoration integrity. Especially under bi-axial occlusal loading, interfacial debonding occurred in the vertical cavity walls of the class I restorations, increasing the risk of failure. Notably, SCR-treated teeth exhibited better margin integrity than restored teeth after complete caries removal (NCR). These findings provide valuable insights into the mechanical behavior of SCR-treated teeth under different loading conditions and highlight the importance of considering the load scenarios that may lead to failure at the c/t interface. By investigating the factors influencing crack initiation and delamination, this novel research contributes to the optimization of restorative treatments and aids in the design of more resilient dental restorations.

Polymerization shrinkage of contemporary dental resin composites: Comparison of three measurement methods with correlation analysis

The aim of this study was to evaluate a novel approach for measuring the polymerization shrinkage of dental resin composites - measurement of sample depth variation. This new method was compared with two testing methodologies used for assessing the polymerization shrinkage (buoyancy and strain gauge methods). Eleven commercial resin composites were investigated (EverX Posterior; EverX Flow Bulk & Dentin; G-aenial Anterior, Posterior, A'chord & Universal Injectable; Filtek One Bulk Fill & Universal Restorative; SDR + Flow and Aura Bulk Fill). In addition, filler content (wt. %), flexural modulus, and the degree of conversion were evaluated. Shrinkage values, obtained by the buoyancy method, are greater than shrinkage evaluated by the strain gauge. There are significant differences in polymerization shrinkage among the tested resin composite materials. There is a strong correlation between the newly proposed method of shrinkage measurement and the buoyancy method (r2 = 0.8; p < 0.01). There is no correlation between volumetric shrinkage measurement (depth changes and buoyancy method) and linear strain measurement. Volumetric filler amount correlates with shrinkage values evaluated by all three methods. The degree of conversion for the tested resin composites ranges from 36 % to 52 %. There are some differences (around 10 %) between the filler content (wt. %) measured by the ashing-in-air method and the data given by the manufacturers. The highest flexural modulus is 14.8 GPa and the lowest 6.6 GPa. New formulations may introduce unknown relationships between the fundamental properties of dental resin composites.

Effect of Radiant Exposure on the Physical and Mechanical Properties of 10 Flowable and High-viscosity Bulk-fill Resin Composites

OBJECTIVES

To evaluate the effect of the different radiant exposures from a multipeak light curing unit on the physical and mechanical properties of flowable and high-viscosity bulk-fill resin-based composites (RBC).

METHODS

Five flowable bulk-fill RBCs (Tetric N-Flow Bulk-fill, Ivoclar Vivadent; Filtek Bulk Fill Flow, 3M Oral Care; Opus Bulk Fill Flow APS, FGM; Admira Fusion x-base, Voco and; and SDR Plus Bulk Fill Flowable, Dentsply Sirona) and five high-viscosity bulk-fill RBCs (Tetric N-Ceram Bulk-fill, Ivoclar Vivadent; Filtek One Bulk Fill, 3M Oral Care; Opus Bulk Fill APS, FGM; Admira Fusion x-tra, Voco; and SonicFill 2, Kerr) were photo-cured using a VALO Cordless light (Ultradent) for 10, 20, and 40 seconds at an irradiance of 1200, 800, or 400 mW/cm2, resulting in the delivery of 4, 8, 12, 16, 24, 32, or 48 J/cm2. Post-gel shrinkage (Shr) was calculated using strain-gauge test. The degree of conversion (DC, %) was calculated using FTIR. Knoop hardness (KH, N/mm2) and elastic modulus (E, MPa) were measured at the top and bottom surfaces. Logarithmic regressions between the radiant exposures and mechanical properties were calculated. Radiodensity was calculated using digital radiographs. Data of Shr and radiodensity were analyzed using two-way analysis of variance (ANOVA), and the DC, KH, and E data were analyzed with two-way ANOVA using split-plot repeated measurement tests followed by the Tukey test (a = 0.05).

RESULTS

Delivering higher radiant exposures produced higher Shr values (p<0.001) and higher DC values (R2=0.808-0.922; R2=0.648-0.914, p<0.001), KH (R2=0.707-0.952; R2=0.738-0.919; p<0.001), and E (R2=0.501-0.925; R2=0.823-0.919; p<0.001) values for the flowable and high-viscosity RBCs respectively. Lower KH, E and Shr were observed for the flowable bulk-fill RBCs. All bulk-fill RBCs had a radiopacity level greater than the 4-mm thick aluminum step wedge. The radiant exposure did not affect the radiopacity.

CONCLUSION

The Shr, DC, KH, and E values were highly correlated to the radiant exposure delivered to the RBCs. The combination of the higher irradiance for longer exposure time that resulted in radiant exposure between 24 J/cm2 to 48 J/cm2 produced better results than delivering 400 mW/cm2 for 40 s (16 J/cm2), and 800 mW/cm2 for 20 seconds (16 J/cm2) or 1200 mW/cm2 for 10 seconds (12 J/cm2). All the bulk-fill RBCs were sufficiently radiopaque compared to 4 mm of aluminum.

Dental trauma splints for the mixed dentition - A finite element analysis of splint material, splint extension, missing teeth, and PDL representation

BACKGROUND/AIMS

Dental traumatic injuries are common in children during the mixed dentition stage. These injuries usually require splinting for stabilization, which is complicated by the various stages of the permanent tooth development and primary tooth exfoliation. The aim of this study was to evaluate the effect on mobility of splint materials and extensions for an avulsed central incisor, stabilized with and without the adjacent incisor under intrusive and extrusive loading with different periodontal ligament (PDL) conditions.

MATERIALS AND METHODS

Seventeen 3D model variations were created from a CBCT scan of a 7-year-old patient without erupted permanent upper lateral incisors. A 1000 N palatal load on the right central incisor simulated the avulsion injury and created an increased alveolus and bone deformation, resulting in an increased PDL thickness of 0.45 mm. Wire-resin composite splints with 0.9 mm cross-section (WCS) or 1.0 mm diameter nylon-resin composite splints (NCS) were created. The models simulated conditions with and without the adjacent upper central incisor. Two PDL conditions were investigated, simulating detached PDL or PDL with polyether impression material-like properties. Mobility was calculated under simulated biting loads in horizontal and vertical (intrusive and extrusive) directions.

RESULTS

The NCS allowed greater tooth mobility of the avulsed incisor than the WCS, irrespective of splint extension, PDL condition, or load application. During horizontal loading, polyether-like properties for the PDL allowed around 0.2 mm mobility of the avulsed tooth with the WCS, similar to the intact tooth, whereas a simulated detached PDL allowed 25% more mobility with a WCS than with a NCS.

CONCLUSIONS

Based on the FEA analysis, a 1.0 mm NCS may be suitable for splinting avulsion injuries during the mixed dentition stage compared to the considerably more rigid WCS. The NCS models provided flexibility for PDL healing while maintaining stability, even when missing adjacent teeth increased span widths. Extensions beyond directly adjacent teeth did not alter the mobility with the NCS but should still be considered an extra protection in case of bond failure or exfoliation.

Comparison of polymerization shrinkage of a new bulk-fill flowable composite with other composites: An in vitro study

OBJECTIVE

Since composites still face a critical problem called polymerization shrinkage and bulk-fill composites have reported acceptable results for this issue, this study aims to assess the polymerization shrinkage of a new bulk-fill flowable composite (G-aenial bulk injectable [GBI]) and compare it to other bulk-fill and conventional composites.

MATERIALS AND METHODS

In this in vitro study, 25 composite discs were fabricated using three bulk-fill and two conventional composites. They were bonded to a microscopic slide and were covered by a coverslip. This assembly was transferred to a linear variable differential transformer and composite samples were cured from underneath the slides. Dimensional changes formed in composite samples were recorded. Data were analyzed using analysis of variance followed by post hoc Tukey's and Dunnett's tests.

RESULTS

The groups were significantly different regarding polymerization shrinkage. G-aenial bulk injectable and G-aenial universal flo showed significantly higher polymerization shrinkage than other composites at 30, 60, and 1800 s after light irradiation, while X-tra fil and Filtek Z250 showed the lowest polymerization shrinkage at the aforementioned time points.

CONCLUSION

According to the results, the new composite had polymerization shrinkage similar to the conventional one. Bulk-fill composites reported similar or lower shrinkage to conventional composites.

The effect of filling technique on the cuspal strain, polymerization shrinkage stress, enamel crack formation and depth of cure of restored molars

OBJECTIVE

Evaluate the effect of different restorative filling techniques on the residual shrinkage stress (ShrS), cuspal strain (CS), depth of cure (DC), and enamel crack formation (Ec) in molars with MOD restorations.

METHODS

Post-gel shrinkage, elastic modulus, compressive and diametral tensile strength of the Filtek One Bulk Fill composite were calculated. Sixty molars with MOD preparations were restored using four filling techniques: Bulk; Horizontal; Oblique; Natural enamel and dentin substitution (NEDS) technique. CS was measured using a strain gauge (n = 10). The DC (n = 5) was measured using Knoop hardness. Shrinkage stress/strain was analyzed using 3D finite element analysis. The Ec analysis was carried out by transillumination. Two-way ANOVA with repeated measures and Tukey's HSD test (α = 0.05) was performed for the CS data. Two-Way ANOVA and Tukey's HSD test was performed for the DC data (α = 0.05).

RESULTS

CS was higher at the lingual cusp for the horizontal and NEDS technique. No statistical difference was found between the buccal and lingual CS values for the Bulk (p = 0.367) or Oblique techniques (p = 0.192). CS values were lower for the Bulk. More enamel cracks were found for the Bulk. DC was lower at 4 mm regardless the filling technique. The Horizontal showed the highest ShrS values. The Bulk generated the lower ShrS values.

SIGNIFICANCE

A Bulk technique caused the lowest shrinkage stress/strain. An Oblique technique yielded the best balance between stress, strain and crack formation. NEDS technique is a good alternative to decrease the number of increments while maintaining the stress levels nearby the Oblique technique.

Mechanical evaluation of dental trauma splints fabricated using recentlydeveloped photo-polymerizable composites

This study aimed to determine functionality and mechanical properties of dental splints. Five splints were tested: a control splint Filtek Z350XT (ZF), two splints with G-Fix (GF) and Light Fix (LF), and two wire-composite splints with ZF (ZW) and Ortho Connect Flow (CW). Periotest values, elastic modulus, flexural, compressive, and diametral tensile strength were measured. ZW and CW showed no significant differences in flexibility in labial or occlusal pressure of upper central incisors. LF, GF, and ZF did not differ in labial or palatal pressure. ZW and CW had higher flexibility than LF, GF, and ZF. LF had the lowest flexural and compressive strength but the highest diametral tensile strength. This study showed that ZW and CW might be options for flexible splints, whereas LF and GF would be options for rigid splints. Additionally, CW and LF/GF might be simpler alternatives to ZW and ZF, respectively.

Splint stiffness and extension effects on a simulated avulsed permanent incisor-A patient-specific finite element analysis

BACKGROUND/AIM

Splinting is an important procedure after avulsion. However, the role of splint stiffness and extension is not fully understood. The aim of this study was to evaluate the effect of splint stiffness and extensions on the mobility and stress on an injured tooth under physiological biting load.

MATERIALS AND METHODS

Three-dimensional (3D) finite element models were created from a cone beam computer tomogram of a patient with normal occlusion. An avulsion injury of the right central incisor was created with a 1000 N load application on the palatal of the injured tooth, causing increased socket width. Splints made from four materials were tested: 0.9 mm diameter wire-composite splint (WCS1), 0.4 mm diameter wire-composite splint (WCS2), 1.0 mm diameter nylon-composite splint (NCS), and a 2 mm high by 0.2 mm thick plastic strip composite splint (PSS). Three splint extensions (involving 6, 5, and 3 teeth) were evaluated. Mobility of the avulsed tooth and the maximum principal stress distributions in the adjacent teeth were calculated.

RESULTS

The injured incisor tooth mobility was not affected by the splint extensions. The NCS and PSS stabilized the avulsed incisor but allowed, respectively, 10 and 20 times more mobility under horizontal loading than the WCS1, which inhibited most mobility, while the WCS2 allowed double the mobility compared with WCS1. The NCS and PSS allowed more tooth mobility, mainly in the extrusion direction. Splints were 2-3 times more effective in limiting mobility under intrusive loads than extrusive loads. High levels of stress were found at the base of the composite attachments in the adjacent incisors.

CONCLUSION

Splinting an avulsed tooth to one or two teeth bilaterally using a nylon splint or a plastic strip is appropriate for tooth stabilization and should be recommended over the 0.4mm wire-composite splint, while the 0.9 mm orthodontic wire is too rigid and not recommended.