Enhanced osteogenic activity of titania-modified zirconia implant by ultraviolet irradiation

[The effect of surface modification strategies on biological activity of titanium implant]

The surface morphology of titanium metal is an important factor affecting its hydrophilicity and biocompatibility, and exploring the surface treatment strategy of titanium metal is an important way to improve its biocompatibility . In this study , titanium (TA4) was firstly treated by large particle sand blasting and acid etching (SLA) technology, and then the obtained SLA-TA4 was treated by single surface treatments such as alkali-heat, ultraviolet light and plasma bombardment. According to the experimental results, alkali-heat treatment is the best treatment method to improve and maintain surface hydrophilicity of titanium. Then, the nanowire network morphology of titanium surface and its biological property, formed by further surface treatments on the basis of alkali-heat treatment, were investigated. Through the cell adhesion experiment of mouse embryonic osteoblast cells (MC3T3-E1), the ability of titanium material to support cell adhesion and cell spreading was investigated after different surface treatments. The mechanism of biological activity difference of titanium surface formed by different surface treatments was investigated according to the contact angle, pit depth and roughness of the titanium sheet surface. The results showed that the SLA-TA4 titanium sheet after a treatment of alkali heat for 10 h and ultraviolet irradiation for 1 h has the best biological activity and stability. From the perspective of improving surface bioactivity of medical devices, this study has important reference value for relevant researches on surface treatment of titanium implantable medical devices.

Fabrication and evaluation of silver modified micro/nano structured titanium implant

In order to enhance the antibacterial property of titanium implant without inducing obvious cytotoxicity, the combination of Ag nanolayer and micro/nano surface structure was conducted by magnetron sputtering and hot-alkali treatment in this study. A series of specimens (AH-Ti, AH-Ti/Ag0.25, AH-Ti/Ag1, AH-Ti/Ag2, and AH-Ti/Ag5) were prepared with different sputtering durations (0 min, 0.25 min, 1 min, 2 min, 5 min), respectively, all realizing long-term release of Ag+. In vitro experiments indicated that AH-Ti/Ag1 group possessed good cytocompatibility, nice osteogenic ability, and excellent antibacterial efficiency as well. In addition, AH-Ti/Ag0.25 showed good biocompatibility, while the reduction of S.aureus (78.5%) was not enough compared with AH-Ti/Ag1. Although the AH-Ti/Ag2 and AH-Ti/Ag5 group showed superior antibacterial activity, their obvious cytotoxicity caused low ALP and mineralization level. Therefore, the design of suitable Ag nanolayer coating combined with micro/nano surface structure (AH-Ti/Ag1) might be a promising strategy to enhance osteogenic property and maintain excellent antibacterial ability at the same time.

Biological properties of hydroxyapatite coatings on titanium dioxide nanotube surfaces using negative pressure method

Titanium (Ti) exhibits superior biocompatibility and mechanical properties but is bioinert, while hydroxyapatite (HA) possesses excellent osteogenesis and is widely used for the modification of Ti surface coatings. However, the synthesis of homogeneous and stable HA on metallic materials is still a major challenge. In this study, porous titanium dioxide nanotube arrays were prepared on Ti surface by anodic oxidation, loaded with calcium and phosphorus precursors by negative pressure immersion, and HA coating was formed by in situ crystallization of calcium and phosphorus on the surface by hydrothermal heating. Scanning electron microscopy (SEM), X-ray diffraction (XRD), and bonding strength were conducted to confirm the surface characteristics of each group. The cell proliferation, mineralization degree, and alkaline phosphatase (ALP) activity of MC3T3-E1 cells on samples were calculated and compared in vitro experiments. Cylindrical samples were implanted into rat femurs to evaluate biocompatibility and osteogenesis in vivo. The results showed that HA crystals successfully synthesized in TiO₂ nanotubes, enhancing the bonding strength of HA coating and Ti substrate under negative pressure. Moreover, HA coating on Ti substrate remarkably enhanced cell proliferation and osteogenic differentiation activity in vitro, and improved new bone formation as well as osseointegration in vivo.

In Vitro and In Vivo Studies of Hydrogenated Titanium Dioxide Nanotubes with Superhydrophilic Surfaces during Early Osseointegration

Titanium-based implants are often utilized in oral implantology and craniofacial reconstructions. However, the biological inertness of machined titanium commonly results in unsatisfactory osseointegration. To improve the osseointegration properties, we modified the titanium implants with nanotubular/superhydrophilic surfaces through anodic oxidation and thermal hydrogenation and evaluated the effects of the machined surfaces (M), nanotubular surfaces (Nano), and hydrogenated nanotubes (H-Nano) on osteogenesis and osseointegration in vitro and in vivo. After incubation of mouse bone marrow mesenchymal stem cells on the samples, we observed improved cell adhesion, alkaline phosphatase activity, osteogenesis-related gene expression, and extracellular matrix mineralization in the H-Nano group compared to the other groups. Subsequent in vivo studies indicated that H-Nano implants promoted rapid new bone regeneration and osseointegration at 4 weeks, which may be attributed to the active osteoblasts adhering to the nanotubular/superhydrophilic surfaces. Additionally, the Nano group displayed enhanced osteogenesis in vitro and in vivo at later stages, especially at 8 weeks. Therefore, we report that hydrogenated superhydrophilic nanotubes can significantly accelerate osteogenesis and osseointegration at an early stage, revealing the considerable potential of this implant modification for clinical applications.