The Osteogenic Role of Barium Titanate/Polylactic Acid Piezoelectric Composite Membranes as Guiding Membranes for Bone Tissue Regeneration

Purpose

Biopiezoelectric materials have good biocompatibility and excellent piezoelectric properties, and they can generate local currents in vivo to restore the physiological electrical microenvironment of the defect and promote bone regeneration. Previous studies of guided bone regeneration membranes have rarely addressed the point of restoring it, so this study prepared a Barium titanate/Polylactic acid (BT/PLA) piezoelectric composite membrane and investigated its bone-formation, with a view to providing an experimental basis for clinical studies of guided bone tissue regeneration membranes.

Methods

BT/PLA composite membranes with different BT ratio were prepared by solution casting method, and piezoelectric properties were performed after corona polarization treatment. The optimal BT ratio was selected and then subjected to in vitro cytological experiments and in vivo osteogenic studies in rats. The effects on adhesion, proliferation and osteogenic differentiation of the pre-osteoblastic cell line (MC3T3-E1) were investigated. The effect of composite membranes on bone repair of cranial defects in rats was investigated after 4 and 12 weeks.

Results

The highest piezoelectric coefficient d33 were obtained when the BT content was 20%, reaching (7.03 ± 0.26) pC/N. The value could still be maintained at (4.47±0.17) pC/N after 12 weeks, meeting the piezoelectric constant range of bone. In vitro, the MC3T3-E1 cells showed better adhesion and proliferative activity in the group of polarized 20%BT. The highest alkaline phosphatase (ALP) content was observed in cells of this group. In vivo, it promoted rapid bone regeneration. At 4 weeks postoperatively, new bone formation was evident at the edges of the defect, with extensive marrow cavity formation; after 12 weeks, the defect was essentially completely closed, with density approximating normal bone tissue and significant mineralization.

Conclusion

The BT/PLA piezoelectric composite membrane has good osteogenic properties and provides a new idea for guiding the research of membrane materials for bone tissue regeneration.

Enhanced osteogenic differentiation of stem cells by 3D printed PCL scaffolds coated with collagen and hydroxyapatite

Bone tissue engineering uses various methods and materials to find suitable scaffolds that regenerate lost bone due to disease or injury. Poly(ε-caprolactone) (PCL) can be used in 3D printing for producing biodegradable scaffolds by fused deposition modeling (FDM). However, the hydrophobic surfaces of PCL and its non-osteogenic nature reduces adhesion and cell bioactivity at the time of implantation. This work aims to enhance bone formation, osteogenic differentiation, and in vitro biocompatibility via PCL scaffolds modification with Hydroxyapatite (HA) and Collagen type I (COL). This study evaluated the osteosupportive capacity, biological behavior, and physicochemical properties of 3D-printed PCL, PCL/HA, PCL/COL, and PCL/HA/COL scaffolds. Biocompatibility and cells proliferation were investigated by seeding human adipose tissue-derived mesenchymal stem cells (hADSCs) onto the scaffolds, which were analyzed by 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl tetrazolium bromide (MTT) assay, and 6-diamidino-2-phenylindole (DAPI) staining. In addition, the bone differentiation potential of the hADSCs was assessed using calcium deposition, alkaline phosphatase (ALP) activity, and bone-related protein and genes. Although all constructed scaffolds support hADSCs proliferation and differentiation, the results showed that scaffold coating with HA and COL can boost these capacities in a synergistic manner. According to the findings, the tricomponent 3D-printed scaffold can be considered as a promising choice for bone tissue regeneration and rebuilding.

Viscoelastic, Thermal, and Mechanical Properties of Melt-Processed Poly (ε-Caprolactone) (PCL)/Hydroxyapatite (HAP) Composites

Poly (ε-caprolactone) (PCL)/hydroxyapatite (HAP) composites represent a novel material with desired properties for various applications. In this work, PCL/HAP composites at low loadings were developed through melt-extrusion processing. The effects of HAP loading on viscoelastic, thermal, structural, and mechanical properties of PCL were examined. The morphological analysis revealed better dispersion of HAP at low loadings, while aggregation was noticed at high concentrations. The complex viscosity of the prepared composites increased with increasing concentration of HAP. In addition, a significant decrease in crystallinity was observed upon increase in HAP loading. However, the elongation at break increased with increasing the concentration of HAP, probably due to a decrease in crystallinity. The onset thermal degradation temperature of PCL was enhanced at low concentrations of HAP, whereas a decrease was observed at high loading. Overall, different degrees of HAP dispersion resulted into specific property improvement.

3D-Printed Scaffolds from Alginate/Methyl Cellulose/Trimethyl Chitosan/Silicate Glasses for Bone Tissue Engineering

Alginate-based hydrogel inks are commonly used in printing due to their biocompatibility, biodegradation, and cell adhesion. In the present work, 3D printing of hydrogels comprising alginate/methyl cellulose (MC)/trimethyl chitosan (TMC) and silicate glasses was investigated. It was found that TMC increased the stability of the scaffolds after immersion in normal saline solution in comparison with alginate/MC 3D constructs. The stability also remained after the incorporation of pure silicate glasses or bioactive glasses. Immersion in simulated body fluid (SBF) resulted in the formation of hydroxyapatite in all samples. Scanning electron microscopy (SEM) analysis revealed a good cell adhesion of pre-osteoblasts on all scaffold compositions, cell viability assessment displayed a proliferation increase up to seven days in culture, and alkaline phosphatase (ALP) activity was similar in all scaffold compositions without significant differences. Total collagen secretion by the pre-osteoblasts after 7 days in culture was significantly higher in scaffolds containing silicate glasses, demonstrating their ability to promote extracellular matrix formation. In conclusion, 3D-printed porous scaffolds based on alginate/methyl cellulose/TMC are promising candidates for bone tissue engineering applications.