A Novel Processing for CNT-Reinforced Mg-Matrix Laminated Composites to Enhance the Electromagnetic Shielding Property

Preparation of Structure-Function Integrated Layered CNT/Mg Composites

Magnesium (Mg)-matrix composites have excellent damping and electromagnetic shielding properties. However, the mismatch between their strength and toughness limits their wide application. The aim of this work is to overcome the strength-toughness mismatch by constructing micro- and nanostructures while maintaining the good functional properties of Mg-matrix composites. Electrophoretic deposition (EPD) was used to spread carbon nanotubes (CNTs) out evenly on a Mg foil matrix. After spark plasma sintering (SPS), the grain organisation was refined, and the interlayer bonding was strengthened by hot rolling deformation. Finally, the microstructure, mechanical properties, damping properties, and electromagnetic shielding properties of the composites were analysed. Compared with the pure Mg laminates, the tensile strength and elongation of the CNT/Mg laminates were increased by 6.4% and 108.4%, respectively, with the significant improvement in toughness resulting from the increase in energy required for crack propagation due to the laminate structure. When the total rolling deflection reaches 80%, the interlayer bond strength of the material is significantly increased, the grain is further refined, and the strength and elongation of the composite material reaches the optimum, with the tensile strength reaching 241.70 MPa and the elongation reaching 6.90%. The interlayer interface and grain refinement also affected the damping Mg and electromagnetic shielding effect of the composites. This work provides an experimental idea for the preparation of high-performance structure-function integrated Mg-based materials.

A Comprehensive Study on EMI Shielding Performance of Carbon Nanomaterials-Embedded CFRP or GFRP Composites

The rapid advancement of electrical and telecommunication facilities has resulted in increasing requirements for the development of electromagnetic interference (EMI) shielding composites. Accordingly, an experimental study was conducted to evaluate the EMI shielding performance of carbon nanomaterial (CNM)-embedded carbon-fiber-reinforced polymer (CFRP) or glass-fiber-reinforced polymer (GFRP) composites. Nine combinations of CNMs and carbon or glass fibers were used to fabricate the composites. The synergistic effects of CNMs on the EMI shielding performance were systematically investigated. The results indicated that plate-type CNMs (i.e., graphene and graphite nanoplatelets) have more prominent effects than fiber-type CNMs (carbon nanofibers). The composites fabricated with CFRP afforded higher EMI shielding than the GFRP-based composites. Among the eighteen samples, 3% CNT-GNP in CFRP composites, which included plate-typed CNM, exhibited the best EMI shielding performances, showing 38.6 dB at 0.7 GHz. This study helps understand the shielding performance of CNM-embedded CFRP and GFRP composites in electrical and telecommunication facilities.

Microstructure, Interface and Strengthening Mechanism of Ni-CNTs/AZ91 Magnesium Matrix Composites

Ni-CNTs/AZ91 magnesium matrix composites were fabricated by ultrasound treatment combined with a semi-solid stirred method for the first time. The agglomerated spherical Ni-CNTs transferred from spherical shape to clear tubular shape after pre-dispersion treatment. For the Ni-CNTs/AZ91 magnesium matrix composite prepared by semi-solid stirring followed by ultrasonic treatment, Ni-CNTs were evenly distributed in the magnesium matrix or wrapped on the β (Mg₁₇Al₁₂) phase. Mg₂Ni were formed at the interface of the magnesium matrix and CNTs by in-situ reaction, which significantly improved the interface bonding strength of CNTs and the Mg matrix. The tensile strength and elongation of 1.0wt.% Ni-CNTs/AZ91 magnesium matrix composites were improved by 36% and 86%, respectively, compared with those of AZ91 matrix alloy. After Ni-CNTs were added to AZ91 matrix alloy, more dimples were observed at the fracture surface. The fracture behavior of Ni-CNTs/AZ91 composite was transformed from a cleavage fracture of AZ91 matrix alloy to a quasi-cleavage fracture. Meanwhile, the CNTs dispersed near the fracture showed a "pull-out" state, which would effectively bear and transfer loads. The strengthening mechanism of CNTs was also discussed.

Effect of Al Layer Thickness on the Bonding and Mechanical Behavior of a Mg-(Al-)Ti Laminated Sheet Prepared by Hot-Rolling after Differential Preheating Treatment

Mg-(Al-)Ti laminated sheets with large bonding interfaces were prepared by a differential temperature hot-rolling process, in which the preheating treatment of Ti was 25–100 °C higher than that of Mg. The rolled sheets contained different Al layer thicknesses (≤0.05 mm), and the thickness of the diffused region at the interface of 3–7 μm was formed by rolling at 175 °C. The interfaces were the solid-solution regions of Mg(Al) and Ti(Al), and no intermetallic compounds were generated during both the rolling process and annealing treatment. The hardness of the interfaces was 16–30% greater than that of the Mg matrix and Ti matrix. The results of mechanical tests displayed that the Mg-(Al-)Ti sheets exhibited higher strength and elastic modulus compared to those of the rolled AZ31B sheet. Their UTS and YTS were about 223–460 MPa and 303–442 MPa, respectively, with an elongation of 0.04–0.17 and high elastic modulus of 52–68 GPa. The Mg-Ti (containing about 62 at.% Mg) rolled sheet exhibited the most excellent strength. The UTS and YTS were about 460 MPa and 442 MPa, with an elongation of 0.04 and elastic modulus of 61.5 GPa. Additionally, Mg-Ti sheets with thin Ti thickness possessed a higher work-hardening rate (n), as well as hardening rate, than the rolled Mg-Al-Ti sheets. This is because fractured Ti pieces around the interfaces have a significant strengthening effect. This study provides a simple method for fabricating Mg-(Al-)Ti sheets with high elastic modulus.

Synergistic Strengthening of Mechanical Properties and Electromagnetic Interference Shielding Performance of Carbon Nanotubes (CNTs) Reinforced Magnesium Matrix Composites by CNTs Induced Laminated Structure

In this study, we reported a laminated CNTs/Mg composite fabricated by spray-deposition and subsequent hot-press sintering, which realized simultaneous enhancement effects on strength and electromagnetic interference (EMI) shielding effectiveness (SE) by the introduced CNTs and CNT induced laminated 'Mg-CNT-Mg' structure. It was found that the CNTs/Mg composite with 0.5 wt.% CNTs not only exhibited excellent strength-toughness combination but also achieved a high EMI SE of 58 dB. The CNTs increased the strength of the composites mainly by the thermal expansion mismatch strengthening and blocking dislocation movements. As for toughness enhancement, CNTs induced laminated structure redistributes the local strain effectively and alleviates the strain localization during the deformation process. Moreover, it could also hinder the crack propagation and cause crack deflection, which resulted in an increment of the required energy for the failure of CNTs/Mg composites. Surprisingly, because of the laminated structure induced by introducing CNTs, the composite also exhibited an outperforming EMI SE in the X band (8.2-12.4 GHz). The strong interactions between the laminated 'Mg-CNT-Mg' structure and the incident electromagnetic waves are responsible for the increased absorption of the electromagnetic radiation. The lightweight CNTs/Mg composite with outstanding mechanical properties and simultaneously increased EMI performance could be employed as shell materials for electronic packaging components or electromagnetic absorbers.

The Corrosion Resistance of Al Film on AZ31 Magnesium Alloys by Magnetron Sputtering

Nano Al films were prepared on AZ31 magnesium alloy samples by DC magnetron sputtering. The effects of sputtering power on the microstructure and corrosion resistance of the Al film were investigated. The results show that the surface of aluminum film is dense and polycrystalline state, and it is oriented along the Al (111) crystal plane. The grain size of Al film first increases and then decreases with the increase of sputtering power. When the sputtering power exceeds 100 W, there is no insignificant effect on the orientation of the Al crystals and the corrosion current density of the samples with Al film are reduced by two orders of magnitude. The corrosion resistance of the magnesium alloy samples with the Al film magnetron sputtered varies with the sputtering power. Compared with low sputtering power, the Al film sputtered by high power has the most excellent corrosion resistance, but too high sputtering power will lead to micro cracks on the Al film, which will adversely affect the corrosion resistance.